CN101463565A - Hydrolytic resistant leather and method of producing the same - Google Patents
Hydrolytic resistant leather and method of producing the same Download PDFInfo
- Publication number
- CN101463565A CN101463565A CNA2007103020717A CN200710302071A CN101463565A CN 101463565 A CN101463565 A CN 101463565A CN A2007103020717 A CNA2007103020717 A CN A2007103020717A CN 200710302071 A CN200710302071 A CN 200710302071A CN 101463565 A CN101463565 A CN 101463565A
- Authority
- CN
- China
- Prior art keywords
- finished product
- semi
- time
- coating
- resistant leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses hydrolytic resistance leather and a preparation method thereof. The hydrolytic resistance leather consists of a semi-finished product and a facing; wherein, the formulation of the semi-finished product is as follows: 45.70% of urethane resin, 43.42% of dimethyl formamide, 9.14% of paper pulp powder, 0.55% of penetrating agent, 0.09% of defoaming agent, 0.18% of flatting agent and the rest is industrial stock white; the formulation of the facing comprises shell fabric and base fabric, wherein, the formulation of the shell fabric is as follows: 51.28% of polyurethane, 41.02% of butanone and the rest is industrial white sheets; the formulation of the base fabric is as follows: 55.56% of urethane resin, 38.90% of butanone and the rest is industrial white sheets. The preparation method comprises the process method of the semi-finished product and that of the facing: release paper and the qualified semi-finished product are jointed by facing; in the process, washing, coating and drying are carried out repeatedly. The problem of poor hydrolytic resistance of synthetic leather is solved, the service life is greatly prolonged and the cracking phenomenon caused by temperature difference is greatly reduced.
Description
Technical field
A kind of hydrolytic resistant leather of the present invention and manufacture method thereof relate to the prescription and the manufacture method of the hydrolysis synthetic leather in a kind of leather field.
Background technology
Though the synthetic leather developing history is not long, the large-scale production synthetic leather is to begin in the nineties in China, and the PU leather is at ability large-scale promotion application at the end of the nineties.At present, the synthetic leather of Sheng Chaning has obtained using widely in industries such as clothes, gloves, bag, case and bag, furniture, vamps all over China, but because the minimizing day by day of corium quantity, the manufacturing development speed of synthetic leather is but very fast, all has higher requirement for the kind of synthetic leather and ABRASION RESISTANCE and hydrolytic resistance simultaneously.
Summary of the invention
The objective of the invention is to, by a kind of hydrolytic resistant leather and manufacture method thereof are provided, to change the problem of the hydrolytic resistance difference that present leather exists, to improve the service life and the added value of finished product.
The present invention adopts following technological means to realize:
A kind of hydrolytic resistant leather is made up of semi-finished product and veneer; Wherein said semi-finished product prescription is: 45.70% polyurethane resin, 43.42% dimethyl formamide, 9.14% pulp powder, 0.55% bleeding agent, 0.09% defoamer, 0.18% levelling agent, all the other are industrial stock white;
Described veneer prescription comprises: lining and bed material; Wherein said lining prescription is: 51.28% polyurethane resin, 41.02% butanone, all the other are industrial white tablets;
Described backing material formula is: 55.56% polyurethane resin, 38.90% butanone, all the other are industrial white tablets.
A kind of manufacture method of hydrolytic resistant leather comprises: perching, and with the cloth roll after the perching for becoming web-like, also comprise the step of semi-finished product processing method and veneer processing method:
Wherein, the semi-finished product processing method may further comprise the steps:
The web-like cloth is put into the dimethyl formamide aqueous solution to be flooded; Carry out squezzing by several rolls; Plate; Carrying out coating then handles; Solidify; Washing once more, oven dry; Enter rolling and finished product inspection after the cooling;
The veneer processing method may further comprise the steps:
Release liners is unreeled, carry out the coating processing first time according to the lining prescription; Oven dry for the first time; After supercooling through the second time coating handle; Carry out the oven dry second time; Qualified semi-finished product are unreeled, carry out veneer and fit; Oven dry for the third time; Rolling; The bundling of testing at last.
The dimethyl formyl is 20% in the aforesaid dimethyl formyl aqueous solution.
Aforesaid squezzing, wherein roll is 1 group, and pressure is 6 kilograms/square metre, scalds 8 on roller, and oily temperature is 120 ℃ in the roller.
Aforesaid washing is through the washing of 12 roads, and the dimethyl formyl content of the wherein last rinsing bowl of washing together is less than 0.5%.
The coating layer thickness that the aforesaid first time, coating was handled is 0.12mm, and bake out temperature is 120 ℃, and the layer thickness that the described second time, coating was handled is 0.15mm, and bake out temperature is 100 ℃.
The aforesaid temperature of oven dry for the third time is 120 ℃~140 ℃.
The present invention compared with prior art has following remarkable advantages and beneficial effect:
A kind of hydrolytic resistant leather of the present invention and manufacture method thereof, it is short service life to have overcome original synthetic leather material, the phenomenon that is easy to generate mouldy, premature aging and causes because of temperature difference problem ftractureing.Solve the problem of synthetic leather poor water resistance, be greatly improved the service life of this finished product, simultaneously, also solved synthetic leather mildew-resistant, deodorization, problem such as anti-aging, significantly reduced the cracking phenomena that causes because of the temperature difference.
Description of drawings
Fig. 1 is the manufacture method flow chart of hydrolytic resistant leather.
The specific embodiment
Below in conjunction with accompanying drawing specific embodiments of the invention are illustrated:
A kind of hydrolytic resistant leather is made up of semi-finished product and veneer; Wherein said semi-finished product prescription is: 45.70% polyurethane resin, 43.42% dimethyl formamide, 9.14% pulp powder, 0.55% bleeding agent, 0.09% defoamer, 0.18% levelling agent, all the other are industrial stock white;
Described veneer prescription comprises: lining and bed material; Wherein said lining prescription is: 51.28% polyurethane resin, 41.02% butanone, all the other are industrial white tablets;
Described backing material formula is: 55.56% polyurethane resin, 38.90% butanone, all the other are industrial white tablets.
See also shown in Figure 1ly, be the flow chart of the manufacture method of hydrolytic resistant leather; As can be seen from the figure, processing method of the present invention mainly is divided into semi-finished product processing 1 and veneer processing method 2.
Wherein the key step of semi-finished product processing method 1 is: unreel 11, will flood the 20% dimethyl formamide aqueous solution 12, at pressure is by squezzing 13 under 6 kilograms of/square metre situations, under the situation of moisture 15~20%, plate 14 by 120 ℃ of eight roller, in the 20% dimethyl formamide aqueous solution, carry out coating and handle 15, solidify and handle 16, handle by 12 rinsing bowls then, enter oven dry then and handle 18, the temperature of oven dry is 140 degree~180 degree; Cool off 19 then, rolling 110, finished product inspection 111, produce qualified semi-finished product 112.
What here need to replenish is, the content of the above-mentioned dimethyl formamide that passes through last rinsing bowls of 12 rinsing bowls in handling is less than 0.5%.
Wherein the key step of veneer processing method 2 is: after release liners 21 is unreeled 22, through carrying out drying the first time 24 after the coating processing first time 23, cooling off 25, then through coating processing for the second time 26, the second time drying 27; At this moment, qualified semi-finished product are unreeled 28, carry out joint place reason 29, dry 210 for the third time then, carry out rolling 211 and check bundling 212 with the release liners after handling and on the semi-finished product after unreeling.
Finish the manufacture process of hydrolysis leather by above step.
It should be noted that at last: above embodiment only in order to the explanation the present invention and and unrestricted technical scheme described in the invention; Therefore, although this specification has been described in detail the present invention with reference to each above-mentioned embodiment,, those of ordinary skill in the art should be appreciated that still and can make amendment or be equal to replacement the present invention; And all do not break away from the technical scheme and the improvement thereof of the spirit and scope of invention, and it all should be encompassed in the middle of the claim scope of the present invention.
Claims (7)
1, a kind of hydrolytic resistant leather is made up of semi-finished product and veneer; It is characterized in that: wherein said semi-finished product prescription is:
45.70% polyurethane resin, 43.42% dimethyl formamide, 9.14% pulp powder, 0.55% bleeding agent, 0.09% defoamer, 0.18% levelling agent, all the other are industrial stock white;
Described veneer prescription comprises: lining and bed material; Wherein said lining prescription is: 51.28% polyurethane resin, 41.02% butanone, all the other are industrial white tablets;
Described backing material formula is: 55.56% polyurethane resin, 38.90% butanone, all the other are industrial white tablets.
2, a kind of manufacture method of hydrolytic resistant leather comprises: perching, and with the cloth roll after the perching for becoming web-like, it is characterized in that: the step that also comprises semi-finished product processing method and veneer processing method:
Wherein, the semi-finished product processing method comprises following:
The web-like cloth is put into the dimethyl formamide aqueous solution to be flooded; Carry out squezzing by several rolls; Plate; Carrying out coating then handles; Solidify; Washing once more, oven dry; Enter rolling and finished product inspection after the cooling;
The veneer processing method may further comprise the steps:
Release liners is unreeled, carry out the coating processing first time according to the lining prescription; Oven dry for the first time; After supercooling through the second time coating handle; Carry out the oven dry second time; Qualified semi-finished product are unreeled, carry out veneer and fit; Oven dry for the third time; Rolling; The bundling of testing at last.
3, the manufacture method of hydrolytic resistant leather according to claim 2 is characterized in that: the dimethyl formyl is 20% in the described dimethyl formyl aqueous solution.
4, the manufacture method of hydrolytic resistant leather according to claim 2 is characterized in that: described squezzing, and one group of nip pressure is 6 kilograms/square metre, and wherein scalding roller is 8, and oily temperature is 120 ℃ in the roller.
5, the manufacture method of hydrolytic resistant leather according to claim 2 is characterized in that: described washing is for washing through 12 roads, and the dimethyl formyl content of the wherein last rinsing bowl of washing together is less than 0.5%.
6, the manufacture method of hydrolytic resistant leather according to claim 2, it is characterized in that: the coating layer thickness that the described first time, coating was handled is 0.12mm, bake out temperature is 120 ℃, and the layer thickness that the described second time, coating was handled is 0.15mm, and bake out temperature is 100 ℃.
7, the manufacture method of hydrolytic resistant leather according to claim 2 is characterized in that: the described temperature of oven dry for the third time is 120 ℃~140 ℃.