CN101462888A - Formula of high performance strong wear resistance ramming mass - Google Patents
Formula of high performance strong wear resistance ramming mass Download PDFInfo
- Publication number
- CN101462888A CN101462888A CNA2009100954377A CN200910095437A CN101462888A CN 101462888 A CN101462888 A CN 101462888A CN A2009100954377 A CNA2009100954377 A CN A2009100954377A CN 200910095437 A CN200910095437 A CN 200910095437A CN 101462888 A CN101462888 A CN 101462888A
- Authority
- CN
- China
- Prior art keywords
- powder
- emergy
- grain thickness
- ramming mass
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-performance strong wear-resistant ramming mass formula. The formula comprises the following components by weight percentage: 31%-41% of pulverized corundum with a particle size of 1-3mm, 10%-20% of the pulverized corundum with the particle size of 3-6mm, 34%-42% of ball-milled powder of 260 meshes, 2%-4% of 98 AL2O3 powder, 1%-3% of 95 SiO2 powder, 4%-10% of solid Al(H2PO4)3, 1%-2% of cyanite powder and 1%-2% of chrome ore powder. The ramming mass is prepared by taking the high-quality pulverized corundum, the ball-milled corundum material, silicon micropowder, a control expansion agent and solid aluminum dihydrogen phosphate as bonding agents; curing is unnecessary in construction, and the ramming mass is used for construction after stirring without using a die, automatic crystallization occurs after 2h upon the construction without a drying oven, compassion strength thereof increases by 20% compared with the conventional strength, and the ramming mass has strong corrosion resistance, strong stripping resistance, strong thermal shock resistance and high compassion resistance, and can prolong the service life of a furnace.
Description
Technical field
The present invention relates to a kind of formula of high performance strong wear resistance ramming mass.
Background technology
The prescription of the wear resistance ramming mass of industrial production is as follows: comprise that 36% grain thickness is the emergy of 1-3mm, 15% grain thickness is the emergy of 3-6mm, 39% 18 order ball milling powder, ZhangZhou mud of 10%, the liquid phosphoric acid aluminium of 10-11%.This product is at needs shelving 24 hours before construction, and such as shelving not, material expands after the construction, can directly affect compressive resistance, wears no resistance, easily peels off, corrosion resistance is poor, affect and store stove service life.
Summary of the invention
The object of the present invention is to provide a kind of formula of high performance strong wear resistance ramming mass, compare erosion resistance height, antistripping with conventional formulation, heat-shock resistance is strong, resistance to pressure is high, prolong cellar for storing things stove work-ing life.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions: a kind of formula of high performance strong wear resistance ramming mass, comprise following composition (percentage by weight): the grain thickness of 31%-41% is the emergy of 1-3mm, the grain thickness of 10%-20% is the emergy of 3-6mm, the 260 order ball milling powders of 34%-42%, 98 AL of 2%-4%
2O
3Powder, 95 SiO of 1%-3%
2Powder, the solid Al (H of 4%-10%
2PO
4)
3, the aquamarine powder of 1%-2%, the chromite ore fine of 1%-2%.
Preferably, the each component percentage by weight: 36% grain thickness is the emergy of 1-3mm, and 16% grain thickness is the emergy of 3-6mm, 38% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 1% chromite ore fine.
Optionally, the each component percentage by weight: 31% grain thickness is the emergy of 1-3mm, and 11% grain thickness is the emergy of 3-6mm, 42% 260 order ball milling powders, 4% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 7% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Optionally, the each component percentage by weight: 41% grain thickness is the emergy of 1-3mm, and 14% grain thickness is the emergy of 3-6mm, 34% 260 order ball milling powders, 2% 98 AL
2O
3Powder, 2% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 1% chromite ore fine.
Optionally, the each component percentage by weight: 32% grain thickness is the emergy of 1-3mm, and 20% grain thickness is the emergy of 3-6mm, 36% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Optionally, the each component percentage by weight: 35% grain thickness is the emergy of 1-3mm, and 17% grain thickness is the emergy of 3-6mm, 34% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 6% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Optionally, the each component percentage by weight: 37% grain thickness is the emergy of 1-3mm, and 14% grain thickness is the emergy of 3-6mm, 35% 260 order ball milling powders, 4% 98 AL
2O
3Powder, 2% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Optionally, the each component percentage by weight: 38% grain thickness is the emergy of 1-3mm, and 13% grain thickness is the emergy of 3-6mm, 36% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 3% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 2% chromite ore fine.
Optionally, the each component percentage by weight: 39% grain thickness is the emergy of 1-3mm, and 12% grain thickness is the emergy of 3-6mm, 38% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 2% chromite ore fine.
Compared with prior art, advantage of the present invention is: adopt high-quality emergy, corundum ball milling material, silicon powder, control swelling agent, solid phosphoric acid aluminum dihydrogen to make wedding agent, do not need shelving during construction, can construct after the stirring, not need mould, adopt the ramming construction to finish, the crystallization automatically in back 2 hours of constructing, do not need baker, compressive strength brings up to 20% than traditional intensity, and anticorrosive, antistripping, heat-shock resistance is strong, resistance to pressure is high, prolong cellar for storing things stove work-ing life.
Embodiment
Embodiment one:
A kind of formula of high performance strong wear resistance ramming mass comprises: 36% grain thickness is the emergy of 1-3mm, and 16% grain thickness is the emergy of 3-6mm, 38% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 1% chromite ore fine.
Embodiment two:
A kind of formula of high performance strong wear resistance ramming mass comprises: 31% grain thickness is the emergy of 1-3mm, and 11% grain thickness is the emergy of 3-6mm, 42% 260 order ball milling powders, 4% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 7% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Embodiment three:
A kind of formula of high performance strong wear resistance ramming mass comprises: 41% grain thickness is the emergy of 1-3mm, and 14% grain thickness is the emergy of 3-6mm, 34% 260 order ball milling powders, 2% 98 AL
2O
3Powder, 2% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 1% chromite ore fine.
Embodiment four:
A kind of formula of high performance strong wear resistance ramming mass comprises: 32% grain thickness is the emergy of 1-3mm, and 20% grain thickness is the emergy of 3-6mm, 36% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Embodiment five:
A kind of formula of high performance strong wear resistance ramming mass comprises: 35% grain thickness is the emergy of 1-3mm, and 17% grain thickness is the emergy of 3-6mm, 34% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95SiO
2Powder, 6% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Embodiment six:
A kind of formula of high performance strong wear resistance ramming mass comprises: 37% grain thickness is the emergy of 1-3mm, and 14% grain thickness is the emergy of 3-6mm, 35% 260 order ball milling powders, 4% 98 AL
2O
3Powder, 2% 95SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
Embodiment seven:
A kind of formula of high performance strong wear resistance ramming mass comprises: 38% grain thickness is the emergy of 1-3mm, and 13% grain thickness is the emergy of 3-6mm, 36% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 3% 95SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 2% chromite ore fine.
Embodiment eight:
A kind of formula of high performance strong wear resistance ramming mass comprises: 39% grain thickness is the emergy of 1-3mm, and 12% grain thickness is the emergy of 3-6mm, 38% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 2% chromite ore fine.
Claims (9)
1, a kind of formula of high performance strong wear resistance ramming mass, it is characterized in that: comprise following composition, the each component percentage by weight is: the grain thickness of 31%-41% is the emergy of 1-3mm, the grain thickness of 10%-20% is the emergy of 3-6mm, the 260 order ball milling powders of 34%-42%, 98 AL of 2%-4%
2O
3Powder, 95 SiO of 1%-3%
2Powder, the solid Al (H of 4%-10%
2PO
4)
3, the aquamarine powder of 1%-2%, the chromite ore fine of 1%-2%.
2, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 36% grain thickness is the emergy of 1-3mm, 16% grain thickness is the emergy of 3-6mm, 38% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 1% chromite ore fine.
3, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 31% grain thickness is the emergy of 1-3mm, 11% grain thickness is the emergy of 3-6mm, 42% 260 order ball milling powders, 4% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 7% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
4, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 41% grain thickness is the emergy of 1-3mm, 14% grain thickness is the emergy of 3-6mm, 34% 260 order ball milling powders, 2% 98 AL
2O
3Powder, 2% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 1% chromite ore fine.
5, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 32% grain thickness is the emergy of 1-3mm, 20% grain thickness is the emergy of 3-6mm, 36% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
6, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 35% grain thickness is the emergy of 1-3mm, 17% grain thickness is the emergy of 3-6mm, 34% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 6% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
7, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 37% grain thickness is the emergy of 1-3mm, 14% grain thickness is the emergy of 3-6mm, 35% 260 order ball milling powders, 4% 98 AL
2O
3Powder, 2% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 2% aquamarine powder, 2% chromite ore fine.
8, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 38% grain thickness is the emergy of 1-3mm, 13% grain thickness is the emergy of 3-6mm, 36% 260 order ball milling powders, 3% 98AL
2O
3Powder, 3% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 2% chromite ore fine.
9, a kind of formula of high performance strong wear resistance ramming mass as claimed in claim 1, it is characterized in that: the each component percentage by weight: 39% grain thickness is the emergy of 1-3mm, 12% grain thickness is the emergy of 3-6mm, 38% 260 order ball milling powders, 3% 98 AL
2O
3Powder, 1% 95 SiO
2Powder, 4% solid Al (H
2PO
4)
3, 1% aquamarine powder, 2% chromite ore fine.