CN101429356A - General adhesion promoter for paint and method of producing the same - Google Patents
General adhesion promoter for paint and method of producing the same Download PDFInfo
- Publication number
- CN101429356A CN101429356A CNA2008102385291A CN200810238529A CN101429356A CN 101429356 A CN101429356 A CN 101429356A CN A2008102385291 A CNA2008102385291 A CN A2008102385291A CN 200810238529 A CN200810238529 A CN 200810238529A CN 101429356 A CN101429356 A CN 101429356A
- Authority
- CN
- China
- Prior art keywords
- adhesion promoter
- water
- paint
- phosphoric acid
- chlorinated polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an adhesive force accelerant for a universal coating and a preparation method thereof. The adhesive force accelerant consists of the following raw materials in weight percentage: 20 to 40 percent of epoxy resin, 10 to 30 percent of chlorinated polypropylene resin, 20 to 40 percent of propylene glycol methyl ether acetate, 10 to 20 percent of n-butyl alcohol, 2 to 5 percent of water and 5 to 20 percent of phosphoric acid. According to the proportion, the propylene glycol methyl ether acetate, the n-butyl alcohol and the water are sequentially added into a vessel, are started to stir and are added with the chlorinated polypropylene resin; and upon complete dissolve, the solution is added with the epoxy resin, is evenly stirred, is dripped with the phosphoric acid and is continuously stirred for 2 to 3 hours to obtain the adhesive force accelerant. The adhesive force accelerant has the advantages of strong universality, excellent intermiscibility, low cost, small use amount, simple production process and convenient use.
Description
Technical field
The present invention relates to a kind of adhesion promoter for paint and preparation method thereof, particularly a kind of general adhesion promoter for paint that can be applicable to metal base, various plastic basis materials simultaneously can effectively improve the sticking power of paint coatings and base material.
Background technology
Adhesion promoter is the compound that can improve coating and base material cohesive strength.The end of general this type of compound molecule chain contains two kinds of different functional groups, and wherein a kind of functional group can react with substrate surface, another kind of functional group can with the coating matrix resin reaction.
The kind of adhesion promoter is by different be broadly divided into two classes of coating with the ground interface, one class is for improving the adhesion promoter of cohesive strength between coating and the inorganic ground, and is another kind of for improving the adhesion promoter of cohesive strength between coating and the organic ground.Existing adhesion promoter is difficult to accomplish general.As application number is 01809511 Chinese patent " adhesion promoter application system and method ", and disclosed adhesion promoter mainly comprises the grafting polychloroprene, adopts in the amine and water soluble resin and the moist improving agent crossed.This kind adhesion promoter only be fit to improve the coating adhesion on TPO surface, and this adhesion promoter can only construct separately, thereby has increased operational procedure.Application number is that 200810052434.0 the described adhesion promoter of patent " a kind of steel drum paint special for baking type alcohol acid amido and production method thereof " is a divinol, mainly is applicable to the metal substrate surface.Application number is the preparation that 93106438.4 patent " water-based anticorrosive paint and preparation method thereof " relates to a kind of epoxy phosphate ester: directly use high molecular (solid) bisphenol A type epoxy resin, heating for dissolving in the mixed solvent of a small amount of pimelinketone, propyl carbinol and ethylene glycol monobutyl ether, reacted 2～5 hours down at 90～140 ℃ with phosphoric acid, make epoxy phosphate ester, wherein phosphoric acid accounts for 0.05～5% of Resins, epoxy, the epoxy phosphate ester of its preparation has improved paint film adhesion, but only be used for anti-corrosion of metal, and complex process.
Summary of the invention
In order to overcome the deficiency of above technology, the invention provides a kind of general adhesion promoter for paint, can be applicable to metal base and various plastic basis material simultaneously, effectively improve the sticking power of paint coatings and base material.
The present invention also provides the preparation method of described general adhesion promoter for paint.
The present invention is achieved by the following technical solutions:
Described general adhesion promoter for paint, make by the raw material of following weight per-cent meter:
Resins, epoxy 20～40%
Chlorinated polypropylene 10～30%
1-Methoxy-2-propyl acetate 20～40%
Propyl carbinol 10～20%
Water 2～5%
Phosphoric acid 5～20%.
Above-mentioned general adhesion promoter for paint, preferably make by the raw material of following weight per-cent meter:
Resins, epoxy 25～35%
Chlorinated polypropylene 12～25%
1-Methoxy-2-propyl acetate 25～35%
Propyl carbinol 12～18%
Water 2～5%
Phosphoric acid 5～20%.
The preferred bisphenol A-type of described Resins, epoxy, molecular weight≤500, oxirane value〉0.42, normal temperature is liquid resin down.
Described chlorinated polypropylene, chlorinity are 20～40%, and at 25 ℃, the viscosity with rotary viscosity design determining in 20% toluene solution is 200～2000mpas, and the pH value is 4.0～8.0, and outward appearance is white or little yellow granular solids.
Described water can be pure water, deionized water or distilled water.
Described phosphoric acid, mass concentration are 80～85%, and purity is technical grade, and preferred mass concentration is 85%.
Described 1-Methoxy-2-propyl acetate is a colourless transparent liquid, density 0.96, fusing point-87 ℃, 146 ℃ of boiling points, specific refractory power 1.401-1.403,42 ℃ of flash-points.
Described propyl carbinol is a colourless liquid, and vinosity is arranged, relative density 0.8109,117.7 ℃ of boiling points, fusing point-90.2 ℃, specific refractory power (n20D) 1.3993, flash-point 35-35.5 ℃, the solubleness 7.7% (weight) in the time of 20 ℃ in water, water in propyl carbinol solubleness 20.1% (weight).With Yi Chun ether and other multiple immiscible organic solvents, steam and air form explosive mixture, limits of explosion 1.45-11.25 (volume).
The preparation method of general adhesion promoter for paint of the present invention, mainly adopt following steps:
(1) add 1-Methoxy-2-propyl acetate, propyl carbinol and water in the container successively in proportion;
(2) start stirring, add chlorinated polypropylene, treat that it dissolves fully after, add Resins, epoxy;
(3) back that stirs drips phosphoric acid, continues to stir 2～3 hours promptly.
Product of the present invention is compared with prior art products has following characteristics:
(1) highly versatile can improve inorganic ground adhesive force of coatings, can improve organic ground adhesive force of coatings again.
(2) have excellent intermiscibility, can be used for other various cold coatings such as phthalic resin coating, acrylic resin paint, Polyester resin lacquer, urethane resin.
(3) cost is low, and consumption is few, and 0.01～0.5% interpolation of pressing coating weight gets final product.
(4) production technique is simple.
(5) easy to use, all can in any stage adding of coating material production.
Embodiment
Embodiment 1
In 500 milliliters there-necked flask, add 30% 1-Methoxy-2-propyl acetate successively, 10% propyl carbinol, 5% deionized water, start stirring, the chlorinated polypropylene of adding 15%, its chlorinity is 35%, at 25 ℃, viscosity in 20% toluene solution is 260mpa.s, the pH value is 6.3, treat that chlorinated polypropylene dissolves fully after, adding 30% oxirane value is 0.44, molecular weight is 380 bisphenol A type epoxy resin, after the continuation dispersed with stirring was even, the mass concentration of dropping 10% was 85% phosphoric acid, continued stirring and promptly got product of the present invention in 2.5 hours.
Embodiment 2
In 500 milliliters there-necked flask, add 20% 1-Methoxy-2-propyl acetate, 20% propyl carbinol, 2% deionized water successively, start stirring, the chlorinated polypropylene of adding 20%, its chlorinity is 25%, at 25 ℃, viscosity in 20% toluene solution is 680mpas, the pH value is 7.0, treat that chlorinated polypropylene dissolves fully after, adding 40% oxirane value is 0.51, molecular weight is 210 bisphenol A type epoxy resin, after the continuation dispersed with stirring was even, the mass concentration of dropping 20% was 85% phosphoric acid, continued stirring and promptly got product of the present invention in 3 hours.
Embodiment 3
In 500 milliliters there-necked flask, add 26% 1-Methoxy-2-propyl acetate, 13% propyl carbinol, 3% pure water successively, start stirring, the chlorinated polypropylene of adding 18%, its chlorinity is 30%, at 25 ℃, viscosity in 20% toluene solution is 1340mpas, the pH value is 5.3, treat that chlorinated polypropylene dissolves fully after, adding 20% oxirane value is 0.56, molecular weight is 180 bisphenol A type epoxy resin, after the continuation dispersed with stirring was even, the mass concentration of Dropwise 5 % was 83% phosphoric acid, continued stirring and promptly got product of the present invention in 2 hours.
Embodiment 4
In 500 milliliters there-necked flask, add 40% 1-Methoxy-2-propyl acetate, 16% propyl carbinol, 4% distilled water successively, start stirring, the chlorinated polypropylene of adding 10%, its chlorinity is 40%, at 25 ℃, viscosity in 20% toluene solution is 930mpas, the pH value is 7.3, treat that chlorinated polypropylene dissolves fully after, adding 35% oxirane value is 0.53, molecular weight is 187 bisphenol A type epoxy resin, after the continuation dispersed with stirring was even, the mass concentration of dropping 15% was 80% phosphoric acid, continued stirring and promptly got product of the present invention in 2.5 hours.
Test case:
Choose the common acrylic coating of selling on a kind of market, with embodiment 1,2,3,4 product adds by 0.1% of coating weight respectively, Comparative Examples 1 is selected commercial metals ground coating special adhesion promoter for use, add by aforesaid propylene acid coating weight 0.1%, Comparative Examples 2 is selected commercially available plastic bottom material coating special adhesion promoter for use, add by aforesaid propylene acid coating weight 0.1%, blank example does not then add any adhesion promoter, adopt spraying method, be sprayed at respectively on tinplate and the polyvinyl chloride plastic materials and parts, after treating the whole dryings of coating,, measure each adhesive force of coatings to draw the circle method.Sticking power is divided into 0～7 grade, and 0 grade of performance is best, and 7 grades the poorest.The performance test results such as following table:
Claims (7)
1. general adhesion promoter for paint, it is characterized in that: the raw material by following weight per-cent meter is made
Resins, epoxy 20～40%
Chlorinated polypropylene 10～30%
1-Methoxy-2-propyl acetate 20～40%
Propyl carbinol 10～20%
Water 2～5%
Phosphoric acid 5～20%.
2. general adhesion promoter for paint according to claim 1 is characterized in that: the raw material by following weight per-cent meter is made
Resins, epoxy 25～35%
Chlorinated polypropylene 12～25%
1-Methoxy-2-propyl acetate 25～35%
Propyl carbinol 12～18%
Water 2～5%
Phosphoric acid 5～20%.
3. general adhesion promoter for paint according to claim 1 and 2 is characterized in that: described Resins, epoxy is bisphenol A-type, molecular weight≤500, oxirane value〉0.42, normal temperature is down for liquid.
4. general adhesion promoter for paint according to claim 1 and 2 is characterized in that: described chlorinated polypropylene, chlorinity are 20～40%, and at 25 ℃, the viscosity in 20% toluene solution is 200～2000mpas, and the pH value is 4.0～8.0.
5. general adhesion promoter for paint according to claim 1 and 2 is characterized in that: described water is pure water, deionized water or distilled water.
6. general adhesion promoter for paint according to claim 1 and 2 is characterized in that: described phosphoric acid, mass concentration are 80～85%.
7. the preparation method of the described general adhesion promoter for paint of claim 1 is characterized in that adopting following steps:
(1) add 1-Methoxy-2-propyl acetate, propyl carbinol and water in the container successively in proportion;
(2) start stirring, add chlorinated polypropylene, treat that it dissolves fully after, add Resins, epoxy;
(3) back that stirs drips phosphoric acid, continues to stir 2～3 hours promptly.