CN101402777B - ABS/vinyl cyanide-styrene resin composite material with function of generating negative ion, far-infrared ray or antimicrobial mildew resistant function - Google Patents
ABS/vinyl cyanide-styrene resin composite material with function of generating negative ion, far-infrared ray or antimicrobial mildew resistant function Download PDFInfo
- Publication number
- CN101402777B CN101402777B CN2008102190823A CN200810219082A CN101402777B CN 101402777 B CN101402777 B CN 101402777B CN 2008102190823 A CN2008102190823 A CN 2008102190823A CN 200810219082 A CN200810219082 A CN 200810219082A CN 101402777 B CN101402777 B CN 101402777B
- Authority
- CN
- China
- Prior art keywords
- percent
- abs
- styrene resin
- matrix material
- negative ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an ABS/acrylonitrile-styrene resin composite material which can generate negative ions and far infrared and has an antimicrobial and antifungal function. The composite material consists of components with following weight percentages: 70 percent to 90 percent of the mixture of the ABS and the acrylonitrile-styrene resin, 1 percent to 18 percent of inorganic functional additives, 0.5 percent to 1 percent of coupling agent, 1 percent to 10 percent of compatilizers and 0.1 percent to 1 percent of antioxidant. The composite material can generate negative ions and far infrared and has the antimicrobial and antifungal function, thus being capable of being used in the preparation of air cleaners, bracelets, necklaces, aquarium supplies and insoles. The obtained product has a negative-iron release amount up to 1000/s/cubic centimeter, an Escherichia-coli antibacterial rate of higher than 90 percent, an Escherichia-coli and Staphylococcus aureus antibacterial rate of more than 90 percent, mouldproof grade of zero and sample normal emissivity of more than 0.8.
Description
Technical field
The present invention relates to have the ABS/ acrylonitrile styrene resin (AS) matrix material that produces negative ion, far infrared rays and antibacterial and antimildew function.
Background technology
As far back as 1889, Germany scientist Elst and Ge Teer found the existence of negative aeroion, and 1902, the biological significance of negative aeroion was just affirmed by scientific circles.At the end of last century, Kubo studies the behavior of Verdelite electrolyzed water release air negative ion, has caused global extensive concern.In recent years, just in the ascendant for the research of negative aeroion both at home and abroad, and obtained a series of achievement.In today that the health environment-friendly idea has been rooted in the hearts of the people, discharge anion material with its health, environmental protection, energy-saving advantages, attract people's eyeball just day by day.Its development prospect at aspects such as indoor hardware fitting, daily necessities, sanitary ware, upholstery materials is inestimable.
Summary of the invention
The purpose of this invention is to provide a kind of ABS/ acrylonitrile styrene resin (AS) matrix material that produces negative ion, far infrared rays or antibacterial and antimildew function certainly that has.
Another object of the present invention provides the preparation method of above-mentioned matrix material.
Further purpose of the present invention provides above-mentioned matrix material and can produce negative ion, far infrared rays or have application in the antibacterial and mouldproof article in preparation.
To achieve these goals, the present invention adopts following technical scheme:
ABS/ acrylonitrile styrene resin (AS) matrix material with generation negative ion, far infrared rays or antibacterial and antimildew function of the present invention, form by the component of following weight percentage:
ABS and acrylonitrile styrene resin (AS) mixture 70-90%, inorganic functional additive 1-18%, coupling agent 0.5-1%, compatilizer 1-10%, oxidation inhibitor 0.1-1%;
Described inorganic functional additive is made up of following component: rare earth oxide 1-30%, zirconium silicate 10-45%, potassium felspar sand 20-75%, high temperature bamboo charcoal powder 1-20%, nano titanium oxide 0.5-5%.
In above-mentioned matrix material, described compatilizer is preferably toxilic acid bar grafting PS.
In above-mentioned matrix material, described oxidation inhibitor is preferably antioxidant 1076 or oxidation inhibitor 168.
In above-mentioned matrix material, described coupling agent is preferably KH570.
In above-mentioned matrix material, the mixed ratio of ABS and acrylonitrile styrene resin (AS) need not special qualification, arbitrary proportion all can, concrete required ratio can decide according to the performance requriements of product.
The preparation method of above-mentioned matrix material: mixing after each component is mixed in proportion through the twin screw extrusion equipment, extrude, after the granulation, again by injection moulding.
Compared with prior art, the present invention has following beneficial effect: matrix material of the present invention can produce negative ion, far infrared rays certainly and have antibacterial and antimildew function, can be used to prepare air purifier, bangle, necklace, Shui nationality articles for use, shoe-pad.The negative ion burst size of products obtained therefrom reaches more than 1000/second/cubic centimetres; Intestinal bacteria antibacterium rate〉90%, intestinal bacteria and streptococcus aureus antibacterium rate〉90%; 0 grade of mildew-resistant grade; Sample normal direction emissivity〉0.8.
Embodiment
The preparation method: mixing after each component mixed through the twin screw extrusion equipment, extrude, after the granulation, again by being injection molded into air purifier.Machined parameters is as follows: screw speed is 280r/min; One district's temperature control is 220 ℃; Two district's temperature controls are 220 ℃; Three district's temperature controls are 210 ℃; Four district's temperature controls are 215 ℃; Five district's temperature controls are 215 ℃; Six district's temperature controls are 215 ℃; The head temperature control is 220 ℃; Melt pressure is 35.00MPa.
The prescription of each embodiment is as shown in table 1.
Contained each weight percentages of components of each embodiment of table 1
| ABS and acrylonitrile styrene resin (AS) | Coupling agent | Compatilizer | The inorganic functional additive | Oxidation inhibitor | |
| Embodiment 1 | ABS 20% acrylonitrile styrene resin (AS) 70% | 0.5％ | 6％ | 3％ | 0.5％ |
| Embodiment 2 | ABS 40% acrylonitrile styrene resin (AS) 40% | 0.5％ | 9％ | 10％ | 0.5％ |
| Embodiment 3 | ABS?78％ | 0.5％ | 10％ | 11％ | 0.5％ |
| Embodiment 4 | ABS 5% acrylonitrile styrene resin (AS) 70% | 0.5％ | 5％ | 19％ | 0.5％ |
| Embodiment 5 | ABS 80% acrylonitrile styrene resin (AS) 5% | 0.5％ | 1％ | 13％ | 0.5％ |
The inorganic functional additive is made up of following components in weight percentage described in the embodiment 1: lanthanum trioxide 10%, zirconium silicate 10%, potassium felspar sand 65%, high temperature bamboo charcoal powder 10%, nano titanium oxide 5%.
The inorganic functional additive is made up of following components in weight percentage described in the embodiment 2: yttrium oxide 5%, zirconium silicate 20%, potassium felspar sand 60%, high temperature bamboo charcoal powder 10%, nano titanium oxide 5%.
The inorganic functional additive is made up of following components in weight percentage described in the embodiment 3: europium sesquioxide 30%, zirconium silicate 35%, potassium felspar sand 20%, high temperature bamboo charcoal powder 10%, nano titanium oxide 5%.
The inorganic functional additive is made up of following components in weight percentage described in the embodiment 4: europium sesquioxide 20%, zirconium silicate 29%, potassium felspar sand 40%, high temperature bamboo charcoal powder 10%, nano titanium oxide 1%.
The inorganic functional additive is made up of following components in weight percentage described in the embodiment 5: europium sesquioxide 20%, zirconium silicate 38%, potassium felspar sand 30%, high temperature bamboo charcoal powder 10%, nano titanium oxide 2%.
The above-mentioned matrix material that makes is tested made sample to be reached from discharging negative ion concentration through Chinese architecture material industry environmental monitoring center: more than 1000/second/square centimeters.
Through the test of Guangdong Province's microbiological analysis inspection center, made sample mildew-resistant grade reaches 0 grade, the intestinal bacteria antibiotic rate:〉90%, the streptococcus aureus antibiotic rate: 90%
Infrared and the industrial electroheat product quality supervision and inspection center test through country, made sample normal direction emissivity〉0.8.
Concrete outcome sees Table 2.
The mechanical property of each embodiment plastics of table 2 and surperficial negative ion concentration antibacterial and mouldproof test result
Claims (5)
1. have the ABS/ acrylonitrile styrene resin (AS) matrix material that produces negative ion, far infrared rays and antibacterial and antimildew function, it is characterized in that forming by the component of following weight percentage:
ABS and acrylonitrile styrene resin (AS) mixture 70-90%, inorganic functional additive 1-18%, coupling agent 0.5-1%, compatilizer 1-10%, oxidation inhibitor 0.1-1%;
Described inorganic functional additive is made up of the component of following weight percentage: rare earth oxide 1-30%, zirconium silicate 10-45%, potassium felspar sand 20-75%, high temperature bamboo charcoal powder 1-20%, nano titanium oxide 0.5-5%; Described compatilizer is maleic anhydride graft PS; Described coupling agent is KH570.
2. matrix material as claimed in claim 1 is characterized in that described oxidation inhibitor is antioxidant 1076 or oxidation inhibitor 168.
3. the preparation method of the described matrix material of claim 1 is characterized in that comprising the steps:
Mixing after each component is mixed in proportion through the twin screw extrusion equipment, extrude, after the granulation, again by injection moulding.
4. the described matrix material of claim 1 can produce negative ion, far infrared rays and have application in the antibacterial and mouldproof article in preparation.
5. application as claimed in claim 4 is characterized in that described article are air purifier, bangle, necklace, Shui nationality articles for use or shoe-pad.