CN101372615A

CN101372615A - organic electroluminescent device

Info

Publication number: CN101372615A
Application number: CN 200810145319
Authority: CN
Inventors: 细川地潮; 舟桥正和; 川村久幸; 新井宏昌; 古贺英俊; 池田秀嗣
Original assignee: Idemitsu Kosan Co Ltd
Current assignee: Idemitsu Kosan Co Ltd
Priority date: 1998-12-28
Filing date: 1999-12-28
Publication date: 2009-02-25
Also published as: CN1721499A; CN100482634C

Abstract

The present invention provides a material for an organic electroluminescent device having high luminous efficiency, a long life and excellent heat resistance, and a method for producing the same. The material is represented by general formula (1). In the formula, A represents optionally substituted C_22－60An arylene group; x¹－X⁴Each independently represents C which may be optionally substituted_6－30An arylene group; y is¹－Y⁴Each independently represents an organic group represented by the general formula (2); and a to d each represent an integer of 0 to 2. In the general formula (2), R¹－R⁴Each independently represents a hydrogen atom, an optionally substituted alkyl or aryl group, or a cyano group, or¹And R²Or R³And R⁴Is linked to form a triple bond, Z represents an optionally substituted aryl group, and n represents 0 or 1.

Description

Organnic electroluminescent device

The application is that application number is dividing an application of 200510084528.2 Chinese invention patent application, and its applying date is on December 28th, 1999, and priority date the earliest is on December 28th, 1998.

Technical field

The present invention relates to can be used as the method that light source such as televisor planar light-emitting element and indicating meter back of the body irradiation, the material with long Organnic electroluminescent device of high-luminous-efficiency, excellent heat resistance and life-span, the Organnic electroluminescent device that uses this material, novel cpd and production are used for the material of el light emitting device.

Background technology

Use electroluminescent (EL) the device expection of organic compound to can be used for the cheap solid luminescence type full color display that can big area shows, therefore carried out development energetically it.In general, the EL device is made up of luminescent layer and a pair of comparative electrode that is positioned at these luminescent layer both sides.If apply voltage between electrode, electronics just injects in anode side in cathode side injection and hole.Electronics and hole are compound at luminescent layer, form excited state.If this excited state turns back to normality, energy just discharges with the form of light.

Up to now, organic El device needs higher driving voltage, and compares with inorganic device, and luminosity is low and luminous efficiency is poor.In addition, the degradation of organic El device is very fast.Therefore, organic El device is unactual as yet so far uses.Although the performance of organic El device is improved, does not obtain having efficient luminous as yet and have the organic El device in enough thermotolerances and life-span.For example, Japanese Patent Application Publication Heisei 8 (1996)-12600 discloses a kind of phenylanthracene derivative of the EL of can be used for device.But the luminous efficiency of using the organic El device of this compound is low to moderate about 2-4cd/A, therefore need raise the efficiency.In Japanese Patent Application Publication Heisei 8 (1996)-199162, a kind of EL device is disclosed, it has and comprises amine or the diamine derivative luminescent layer as fluorescent dopants.But this EL device is at 300cd/m ²Life-span under the initial brightness is as short as 700 hours, although its luminous efficiency is 4-6dc/A, therefore needs to improve the life-span.In Japanese Patent Application Publication Heisei 9 (1997)-268284, a kind of material that is used for the EL device with phenylanthracene group is disclosed.If this material is life-time service at high temperature, it can obviously reduce luminosity so its thermotolerance deficiency.In addition, these devices can not send orange light to red color area.Because indispensable when sending redness and be the EL device and carrying out panchromatic demonstration, so claimed apparatus can be orange luminous to red color area.If these materials are used as dopant material as material of main part and other compound, can not realize the long lifetime.Application request can produce 10000d/m ²Or higher initial brightness.But this value still is unrealized.In Japanese Patent Application Publication Heisei 11 (1999)-152253, such example is disclosed, the material that is used for organic El device that wherein will have two naphthalene structures adds the luminescent layer that can transmit electronics, for example in layer of aluminum title complex or the analogue.But in this example, aluminum complex or analogue are luminous, and this material that is used for organic El device does not then play luminescence center, because the energy gap of aluminum complex or analogue luminescent layer is less than the energy gap of this material that is used for organic El device.

Arylamines as the organic El device material reacts by Ullmann, utilizes amine and phenyl-iodide to synthesize.For example, " chemical communication " (Chem.Lett.) the 1145th page-1148 pages, 1989, in the specification sheets of United States Patent (USP) 4764625 and Japanese Patent Application Publication Heisei8 (1996)-48974, described in unreactive hydrocarbons solvent such as perhydronaphthalene as exemplary, under 150 ℃ or higher temperature, in the presence of monovalent or more copper powders and potassium hydroxide and so on alkali, the reaction by corresponding phenyl-iodide and diarylamine obtains triarylamine.

But utilize the defective of the method for Ullmann reaction to be, must use expensive iodide as reaction reagent, this reaction can not be applied to the compound of many types, reaction yield is not high enough, reaction needed temperature height to 150 ℃ and time are long, and owing to a large amount of copper powders that use produce the waste liquid that comprises a large amount of copper, therefore environmental problem appears.

Disclosure of the present invention

The present invention has overcome above problem, therefore its objective is provide a kind of material that is used for Organnic electroluminescent device, can be efficiently luminous and have the Organnic electroluminescent device and the novel cpd of long lifetime and excellent heat resistance and produce this method that is used for the material of Organnic electroluminescent device.

In order to develop material that is used for organic El device with above-mentioned advantageous property and the organic El device that uses this material, the inventor finds that after further investigation this purpose can realize by using by the compound of following general formula that provides [1] and [3]-[10] expression.The present invention is accomplished on the basis of this understanding.

The inventor finds that also above purpose can realize as dopant material or luminescence center by using by the compound of general formula [11] and [11 '] expression.

The inventor further finds, can be in the presence of catalyzer that comprises phosphine compound and palladium compound and alkali as uncle's arylamines of organic El device material, and high reactivity ground synthesizes by the reaction of amine and aryl halide.The present invention is accomplished on the basis of above understanding.

The material (being called the material that is used for organic El device) that is used for Organnic electroluminescent device of the present invention is the compound by following general formula [1] expression:

General formula [1]

Wherein A represents to have the replacement of 22-60 carbon atom or does not replace arylidene, X ¹-X ⁴Expression has the replacement of 6-30 carbon atom or does not replace arylidene, X independently respectively ¹And X ²Key connects mutually, X ³And X ⁴Key connects mutually, Y ¹-Y ⁴Represent independently that respectively a-d represents the integer of 0-2 respectively by the organic group shown in the general formula [2], and have 26 or still less during carbon atom, a+b+c+d when arylidene shown in the A〉0 and this arylidene do not contain two or more anthracenes nuclears;

General formula [2] is:

General formula [2]

R wherein ¹-R ⁴Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting aromatic yl or cyano group, or pass through R with 6-20 carbon atom ¹And R ²Or R ³And R ⁴Key connect and form triple bond; Z represents to have the replacement or the unsubstituting aromatic yl of 6-20 carbon atom, and n represents 0 or 1.

The material that is used for Organnic electroluminescent device of the present invention can also be the compound by following general formula [3] expression:

General formula [3]

Wherein B represents to have the replacement of 6-60 carbon atom or does not replace arylidene, X ¹-X ⁴Expression has the replacement of 6-30 carbon atom or does not replace arylidene, X independently respectively ¹And X ²Key connects mutually, X ³And X ⁴Key connects mutually, Y ¹-Y ⁴Represent independently that respectively a-d represents the integer of 0-2 respectively, and at least one is by B, X by the organic group shown in the above-mentioned general formula [2] ¹, X ², X ³And X ⁴The group of expression has

Nuclear.

General formula [3] preferably refers to following general formula [4], general formula [5] or general formula [6].

General formula [4]:

X wherein ¹-X ⁴, Y ¹-Y ⁴With a-d respectively independently with general formula [3] in identical.

General formula [5]:

Wherein B, X ¹, X ², Y ¹, Y ², a and b respectively independently with general formula [3] in identical.

General formula [6]:

The material that is used for Organnic electroluminescent device of the present invention can also be the compound by following general formula [7] expression:

General formula [7]

Wherein D represents to have the divalent group of tetracene nuclear or pentacene nuclear, X ¹-X ⁴Expression comprises the replacement of 6-30 carbon atom or does not replace arylidene, X independently respectively ¹And X ²Key connects mutually, X ³And X ⁴Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the above-mentioned general formula [2] respectively independently, and a-d represents the integer of 0-2 respectively.

General formula [7] preferably refers to following general formula [8].

General formula [8]:

X wherein ¹-X ⁴, Y ¹-Y ⁴With a-d respectively independently with general formula [7] in identical, R ⁵¹-R ⁶⁰Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting alkoxy, replacement or unsubstituting aromatic yl or cyano group with 6-20 carbon atom with 1-20 carbon atom, and R ⁵¹-R ⁶⁰Shown in the group adjacent group mutually key connect, thereby form saturated or unsaturated and replacement or unsubstituted carbocyclic ring.

The material that is used for Organnic electroluminescent device of the present invention can also be the compound by following general formula [9] expression:

General formula [9]

Wherein E represents to comprise and is replaced or the divalent group of unsubstituted anthracene nuclear X by aryl ⁵-X ⁸Expression has the replacement of 6-20 carbon atom or does not replace arylidene, X independently respectively ⁵And X ⁶Key connects mutually, X ⁷And X ⁸Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the above-mentioned general formula [2] respectively independently, a-d represents the integer of 0-2 respectively, and group is substituted radical not shown in the E;

The time, X ⁵-X ⁸In at least two comprise and replace or substituted radical not:

Or

The material that is used for Organnic electroluminescent device of the present invention can also be the compound by following general formula [10] expression:

General formula [10]

Ar wherein ¹And Ar ³Represent divalent group respectively independently, be selected from and replace or unsubstituted phenylene, replacement or do not replace 1,3-naphthylidene, replacement or do not replace 1,8-naphthylidene, replacement or unsubstituted fluorenylidene and replacement or do not replace biphenylene, Ar ²The expression divalent group is selected from replacement or does not replace anthracene nuclear, replaces or do not replace pyrene and examines, replaces or do not replace phenanthrene nucleus, replacement or not replacement

Nuclear, replace or not substituted pentacenes nuclear, replace or do not replace tetracene nuclear and replace or substituted fluorene nuclear not X ⁵-X ⁸Expression has the replacement of 6-20 carbon atom or does not replace arylidene, X independently respectively ⁵And X ⁶Key connects mutually, X ⁷And X ⁸Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the above-mentioned general formula [2] respectively independently, a-d represents the integer of 0-2 respectively, a+b+c+d≤2, and e represents 0 or 1, f represents 1 or 2, works as Ar ²During expression anthracene nuclear, get rid of

And Ar ¹And Ar ³The situation of representing right-phenylene simultaneously.

The material that is used for Organnic electroluminescent device of the present invention can also be the compound by following general formula [11] expression:

General formula [11]

Wherein F represents to have the replacement of 6-21 carbon atom or does not replace arylidene, X ¹-X ⁴Expression has the replacement of 6-30 carbon atom or does not replace arylidene, X independently respectively ¹And X ²Key connects mutually, X ³And X ⁴Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the above-mentioned general formula [2] respectively independently, a-d represents the integer of 0-2, a+b+c+d respectively〉0.

In general formula [11], the group of being represented by F is preferably the group of being represented by following general formula [12], general formula [13] or general formula [14]:

General formula [12]

General formula [13]

R wherein ^{5 '}-R ^{24 '}Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting aromatic yl or cyano group with 6-20 carbon atom, and by R ^{5 '}-R ^{24 '}Adjacent group in the group of expression key mutually even forms saturated or unsaturated carbocyclic;

General formula [14]

R wherein ^{25 '}-R ^{34 '}Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting aromatic yl or cyano group with 6-20 carbon atom, and by R ^{5 '}-R ^{24 '}Adjacent group in the group of expression key mutually even forms saturated or unsaturated carbocyclic.

The luminescent material that also can be used as Organnic electroluminescent device by the material of the present invention that is used for organic El device of arbitrary general formula [1], [3]-[11] and [11 '] expression.

Organic electroluminescent of the present invention (EL) device comprises the luminescent layer between pair of electrodes or comprises the multilayer organic compound thin film of luminescent layer, and wherein one deck organic compound thin film comprises the material that is used for organic El device by arbitrary general formula [1], [3]-[11] and [11 '] expression at least.

Preferably in above organic El device, comprise by the material that is used for organic El device of arbitrary general formula [1], [3]-[11] and [11 '] expression as the layer of at least a material that is selected from hole-injecting material, hole-transfer material and dopant material between this electrode pair.

Preferably in above organic El device, luminescent layer comprises the organic El device material by arbitrary general formula [1], [3]-[11] and [11 '] expression of 0.1-20% weight.

Preferably in above Organnic electroluminescent device, one or more materials that are selected from hole-injecting material, hole-transfer material and dopant material comprise the organic El device material by arbitrary general formula [1], [3]-[11] and [11 '] expression of 0.1-20% weight independently of one another.

Preferably in above organic El device, luminescent layer is to comprise stilbene derivative and by the layer of the organic El device material of arbitrary general formula [1], [3]-[11] and [11 '] expression.

In above organic El device, the layer that comprises aromatic uncle amine derivative and/or phthalocyanine derivates is between luminescent layer and anode.

Preferably in above organic El device, by the energy gap of the organic El device material of general formula [11] expression than the little 0.07ev of material of main part energy gap or more.

Novel cpd of the present invention is represented by following general formula [11 ']:

General formula [11]

Wherein F represents group shown in the general formula [14], X ¹-X ⁴Expression has the replacement of 6-30 carbon atom or does not replace arylidene, X independently respectively ¹And X ²Key connects mutually, X ³And X ⁴Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the general formula [2] respectively independently, a-d represents the integer of 0-2 respectively, and a+b+c+d〉0;

General formula [14] is:

General formula [14]

The method of production organic El device material of the present invention comprises: in the presence of catalyzer that comprises phosphine compound and palladium compound and alkali, with primary amine or the secondary amine shown in the following general formula [15]:

R(NR’H) _k [15]

Wherein k represents the integer of 1-3; When k represents 1, R and R ' expression hydrogen atom, alkyl or replacement or unsubstituting aromatic yl; And when k represented 2 or 3, R represented alkylidene group or replacement or does not replace arylidene, and R ' expression hydrogen atom, alkyl or replacement or unsubstituting aromatic yl,

React with the aryl halide shown in the following general formula [16]:

Ar(X) _m [16]

Wherein Ar represents to replace or unsubstituting aromatic yl, and X represents F, Cl, Br or I, and m represents the integer of 1-3, thereby produces the material that is used for Organnic electroluminescent device that comprises arylamines.

Above-mentioned arylamines is preferably the compound by following general formula [17] expression:

Wherein F represents to have the replacement of 6-60 carbon atom or does not replace arylidene, X ¹-X ⁴Expression has the replacement of 6-30 carbon atom or does not replace arylidene, X independently respectively ¹And X ²Key connects mutually, X ³And X ⁴Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the general formula [2] respectively independently, a-d represents the integer of 0-2 respectively, and a+b+c+d〉0.

Described phosphine compound is preferably trialkyl phosphine compound, triaryl phosphine compound or diphosphine compound.

Brief description of the drawings

Fig. 1 has provided according to the inventive method synthetic compound a ¹H NMR figure.

Fig. 2 has provided according to the inventive method synthetic compound b ¹H NMR figure.

Fig. 3 has provided according to the inventive method synthetic Verbindung ¹H NMR figure.

Implement most preferred embodiment of the present invention

In general formula of the present invention [1], A represents to have the replacement of 22-60 carbon atom or does not replace arylidene.The example of arylidene comprises by biphenyl, terphenyl, naphthalene, anthracene, phenanthrene, pyrene, fluorenes, thiophene, cool and divalent group that fluoranthene forms and the divalent group by will the mutual key of a plurality of these groups company forming.X in the general formula [1] ¹-X ⁴Expression has the replacement of 6-30 carbon atom or does not replace arylidene independently respectively.By X ¹-X ⁴The example of group of expression comprise contain phenyl, biphenyl, terphenyl, naphthalene, anthracene, phenanthrene, pyrene, fluorenes, thiophene, cool and

The monovalence of skeleton structure or divalent group.X ¹And X ²Key connects and X mutually ³And X ⁴Key connects mutually.

As X ¹-X ⁴Shown in group substituent group respectively independently for alkyl with 1-20 carbon atom, have the alkoxyl group of 1-20 carbon atom or have the aryl of 6-20 carbon atom.Aryloxy, artyl sulfo, arylalkyl and aryl ketones group are got rid of from above substituting group, because the decomposes when gas deposition often of the compound with above eliminating group, so the life-span of gained device is short.

In general formula [1], a-d represents the integer of 0-2 respectively.If but have 26 or still less during carbon atom by the group that A represents, a+b+c+d so〉0 and do not comprise 2 or more anthracenes nuclear by the group that A represents.

In general formula of the present invention [2], R ¹-R ⁴Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting aromatic yl or cyano group with 6-20 carbon atom.By R ¹-R ⁴The example of group of expression comprises and replacing or not substituted alkyl such as methyl, ethyl, propyl group, butyl, sec-butyl, the tertiary butyl, amyl group, hexyl, heptyl, octyl group, stearyl, 2-propyloxy phenyl base, trichloromethyl, trifluoromethyl, benzyl, α-phenoxy benzyl, α, α-Er Jiajibianji, α, Alpha-Methyl phenylbenzyl, α, α-two (trifluoromethyl) benzyl, trityl and α-benzyloxy benzyl; With replacement or unsubstituting aromatic yl such as phenyl, 2-aminomethyl phenyl, 3-aminomethyl phenyl, 4-aminomethyl phenyl, 4-ethylphenyl, xenyl, 4-methyl biphenyl, 4-ethyl biphenyl base, 4-cyclohexyl biphenyl base, terphenyl, 3,5-dichlorophenyl, naphthyl, 5-methyl naphthyl, anthryl and pyrenyl.

In general formula of the present invention [2], Z represents to have the replacement or the unsubstituting aromatic yl of 6-20 carbon atom.The example of the group of being represented by Z comprises aryl such as phenyl, xenyl, terphenyl, naphthyl, anthryl, phenanthryl, fluorenyl, pyrenyl and thienyl.Above aryl can have substituting group.Substituent example comprises above as R ¹-R ⁴Shown in alkyl and aryl, alkoxyl group, amino, cyano group, hydroxyl, carboxylic acid, ether and the ester group described during the example of group.In general formula [2], n represents 0 or 1.

As mentioned above, because compound has two amine structures that are positioned at centre portions and the styryl amine structure that is positioned at the end shown in the general formula of the present invention [1], ionization energy is 5.6ev or lower, therefore easy injected hole.The mobility in hole is 10 ^-4m ²/ Vs or higher.Therefore, this compound has excellent performance as hole-injecting material and hole-transfer material.Because many phenyl structure at center, electron affinity is 2.5ev or higher, therefore injects electronics easily.

In addition, because structure has 22 or more carbon atoms shown in the A, therefore form amorphous thin film easily.Its second-order transition temperature rises to 100 ℃ or higher, so thermotolerance is improved.If comprise two or more anthryls shown in the A in the structure, the compound shown in the general formula [1] may thermolysis so.

X in its structure ¹And X ²Or X ³And X ⁴The compound that connects by singly-bound or the mutual key of carbocyclic ring key has high glass transition, so thermotolerance is higher.

In compound shown in general formula of the present invention [3]-[6], B represents to have the replacement of 6-60 carbon atom or does not replace arylidene.The example of the group of being represented by B comprises by biphenyl, terphenyl, naphthalene, anthracene, phenanthrene, pyrene, fluorenes, thiophene, cool and divalent group that fluoranthene forms and the divalent group by will the mutual key of a plurality of these groups company forming.X ¹-X ⁴, Y ¹-Y ⁴With a-d identical with described in the general formula [1], wherein by B, X ¹, X ², X ³And X ⁴At least one group of expression has Nuclear.

As mentioned above, because compound has two amine structures that are positioned at centre portions and the styryl amine structure that is positioned at the end shown in general formula of the present invention [3]-[6], ionization energy is 5.6ev or lower, therefore easy injected hole.The mobility in hole is 10 ^-4m ²/ Vs or higher.Therefore, this compound has excellent performance as hole-injecting material and hole-transfer material.Because by B, X ¹, X ², X ³And X ⁴Comprise at least one group of expression Nuclear, so weather resistance and thermotolerance can be improved.Therefore, can drive and can obtain the organic El device that can at high temperature store or drive for a long time.

In addition, the life-span of organic El device can prolong as dopant material by compound shown in use general formula [3]-[6], and luminous efficiency can improve as the material of luminescent layer by using described compound.

In the compound by general formula of the present invention [7] expression, D represents to comprise the divalent group that replaces or do not replace tetracene nuclear or pentacene nuclear.The example of the group of being represented by D comprises by connecting the divalent groups that a plurality of at least one group that is selected from biphenyl, naphthalene, anthracene, phenanthrene, fluorenes and thiophene and tetracene nuclear or pentacene nuclear form.X ¹-X ⁴, Y ¹-Y ⁴With a-d identical with described in the general formula [1], wherein X ¹And X ²Key connects and X mutually ³And X ⁴Key connects mutually.

In compound by general formula of the present invention [8] expression, X ¹-X ⁴, Y ¹-Y ⁴Represent with above at identical atom and group described in the general formula [1] independently respectively with a-d.R ⁵¹-R ⁶⁰Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting alkoxy, replacement or unsubstituting aromatic yl or cyano group with 6-20 carbon atom with 1-20 carbon atom, and by R ⁵¹-R ⁶⁰Adjacent group in the group of expression key mutually even forms saturated or unsaturated and replacement or unsubstituted carbocyclic ring.

In general formula [7] and [8], be used as substituent group respectively independently for alkyl with 1-20 magnetic atom, have the alkoxyl group of 1-20 carbon atom or have the aryl of 6-20 carbon atom.Aryloxy, arylthio, aralkyl and aryl ketones group are got rid of from above substituting group, because the decomposes when gas deposition often of the compound with above eliminating group, so the life-span of gained device is short.

As mentioned above, by the compound of general formula of the present invention [7] expression because tetracene or pentacene structure and have hyperfluorescence to red color area orange.The hole is injected easily owing to two amine structures.If this compound is included in the luminescent layer, the hole just is captured easily, and this has promoted the compound of electronics and hole.Therefore, can obtain efficiently to send the light-emitting device of yellow, orange and red light.

Especially, if will be used as dopant material by the compound of general formula [7] expression, the gained light-emitting device has more excellent stability with regard to life-span length and compared with any conventional equipment so.

In the compound by general formula of the present invention [9] expression, E represents to comprise and is replaced by aryl or the divalent group of unsubstituted anthracene nuclear.X ⁵-X ⁸Expression has the replacement of 6-20 carbon atom or does not replace arylidene independently respectively.By X ⁵-X ⁸The example of the group of expression comprises monovalence and the divalent group that contains phenylene, biphenyl, terphenyl, naphthalene, anthracene, phenanthrene, fluorenes and thiophene skeleton structure.X ⁵And X ⁶Key connects and X mutually ⁷And X ⁸Key connects mutually.Y ¹-Y ⁴With a-d identical with described in the general formula [1].

If but E represents not substituted radical:

X so ⁵-X ⁸In at least two comprise and replace or substituted radical not;

As mentioned above, because compound has two amine structures shown in the general formula of the present invention [9], ionization energy is 5.6ev or lower, therefore easy injected hole.The mobility in hole is 10 ^-4m ²/ Vs or higher.Therefore, this compound has excellent performance as hole-injecting material and hole-transfer material.Because electronics is injected in the replacement at center or do not replace anthracene nuclear easily.

If the anthracene nuclear of being represented by E is not substituted, second-order transition temperature is low to moderate 100 ℃ or lower so.This second-order transition temperature can be by with at least two substituting groups, and preferred 2-4 replacement base key linked on the above-mentioned nuclear and improved.Above-mentioned specific biphenyl structural has improved the solvability of compound shown in the general formula [9], and this helps purifying.If phenyl is on the position of non-above position, promptly key connects in contraposition, and the content of impurity can increase owing to being difficult to purifying so, so gained organic El device degradation.By the replacement of above-mentioned aryl, it is right to suppress to form molecule by association, has therefore improved the quantum yield of fluorescent emission.So just improved organic El device luminous efficiency.

In compound by general formula of the present invention [10] expression, Ar ¹And Ar ³Represent divalent group respectively independently, be selected from and replace or not substituted phenylene, replacement or do not replace 1,3-naphthylidene, replacement or do not replace 1,8-naphthylidene, replacement or unsubstituted fluorenylidene and replacement or substituted biphenyl base not, Ar ²The expression divalent group is selected from replacement or does not replace anthracene nuclear, replaces or do not replace pyrene and examines, replaces or do not replace phenanthrene nucleus, replacement or not replacement Nuclear, replace or not substituted pentacenes nuclear, replace or do not replace tetracene nuclear and replace or substituted fluorene nuclear not.

The example of described divalent group comprises:

X ⁵-X ⁸And Y ¹-Y ⁴Expression and identical group described in the general formula [9] independently respectively.A-d represents the integer of 0-2 respectively, a+b+c+d≤2, and e represents 0 or 1, and f represents 1 or 2, wherein: work as Ar ²During expression anthracene nuclear, get rid of a=b=b=d and Ar ¹And Ar ³The situation of representing right-phenylene simultaneously.

As mentioned above, because compound has two amine structures shown in the general formula of the present invention [10], ionization energy is 5.6ev or lower, therefore easy injected hole.The mobility in hole is 10 ^-4m ²/ Vs or higher.Therefore, this compound especially has excellent performance as luminescent material as hole-injecting material and hole-transfer material.Owing to have many phenyl structure of the compound of condensed ring at the center, inject electronics easily.

Because this compound has many phenyl structure and two amine structures simultaneously, therefore can form stable amorphous thin film, and owing to second-order transition temperature is 100 ℃ or higher thermotolerance with excellence.If this compound comprises two or more structures by general formula [2] expression, a+b+c+d≤2 that need satisfy condition are because this compound decomposes when gas deposition forms film.If Ar ²Expression anthracene nuclear can pass through Ar ¹And Ar ³Above-mentioned ad hoc structure prevent decomposes and oxidation when gas deposition.

At material that is used for organic El device and the novel cpd that is used for organic El device of the present invention, in the compound by general formula [11] and [11 '] expression, F represents to have the replacement of 6-21 carbon atom or does not replace arylidene.The example of the group of being represented by F comprises the divalent group that is formed by biphenyl, terphenyl, naphthalene, anthracene, phenanthrene, pyrene, fluorenes, thiophene and fluoranthene.

At general formula [11] with in [11 '], a-d represents the integer of 0-2, wherein a+b+c+d respectively〉0.

As mentioned above, because compound has two amine structures that are positioned at the center and the styryl amine structure that is positioned at the end shown in general formula of the present invention [11] and [11 '], ionization energy is 5.6ev or lower.Therefore, the hole is injected into the performance of luminescent layer by improving in this compound adding luminescent layer.In addition, electronics and the hole balance in luminescent layer can be improved by catching the hole, has therefore improved luminous efficiency and life-span.Luminous efficiency is compared with following situation with the life-span and is improved, and wherein: luminescent layer only is made up of compound shown in above general formula [11] and [11 ,], as the unique material that is used for organic EL Material.Compound with following structure has high glass transition and higher thermotolerance, wherein by singly-bound or by carbocyclic ring key, X ¹And X ²Key connects and X mutually ³And X ⁴Key connects mutually.

In by the group shown in general formula of the present invention [12]-[14], R wherein ^{5 '}-R ^{34 '}Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting aromatic yl or cyano group with 6-20 carbon atom, and by R ^{5 '}-R ^{24 '}Adjacent group in the group of expression key mutually even forms saturated or unsaturated carbocyclic.By R ^{5 '}-R ^{34 '}The example of group of expression comprises and replacing or not substituted alkyl such as methyl, ethyl, propyl group, butyl, sec-butyl, the tertiary butyl, amyl group, hexyl, heptyl, octyl group, stearyl, 2-propyloxy phenyl base, trichloromethyl, trifluoromethyl, benzyl, α-phenoxy benzyl, α, α-Er Jiajibianji, α, Alpha-Methyl phenylbenzyl, α, α-two (trifluoromethyl) benzyl, trityl and α-benzyloxy benzyl; With replacement or unsubstituting aromatic yl such as phenyl, 2-aminomethyl phenyl, 3-aminomethyl phenyl, 4-aminomethyl phenyl, 4-ethylphenyl, xenyl, 4-methyl biphenyl, 4-ethyl biphenyl base, 4-cyclohexyl biphenyl base, terphenyl, 3,5-dichlorophenyl, naphthyl, 5-methyl naphthyl, anthryl and pyrenyl.

Below provided compound (1)-(28) as compound exemplary shown in the general formula [1], as compound (29)-(56) of compound exemplary shown in general formula [3]-[6], as general formula

Shown in the compound exemplary compound (57)-(74), as compound (75)-(86) of compound exemplary shown in the general formula [8], as compound (87)-(104) of compound exemplary shown in the general formula [9], as compound (105)-(126) of compound exemplary shown in the general formula [10] and as compound (127)-(141) of compound exemplary shown in general formula [11] and [11 '].But the present invention is not limited to these exemplary.

Compound b

Compound a

Compound f

Compound by general formula of the present invention [1], [3]-[10] expression has hyperfluorescence when solid-state, in electric field, has excellent luminescent properties, and have 0.3 or higher fluorescent emission quantum yield, because many phenyl structure and the amine structure represented by A or B interconnect at the center of compound.Have hyperfluorescence at yellow, orange or red phosphor region by the compound of general formula [7] and [8] expression when solid-state or the dispersed, and in electric field, have excellent luminescent properties, interconnect because comprise the structure and the amine structure of tetracene nuclear or pentacene nuclear.

Compound by general formula of the present invention [1], [3]-[10] expression can be used as luminescent material effectively, but also can be used as hole-transfer material, electron transport material and dopant material because these compounds have all hole injection efficiencies from metal electrode or organic thin film layer, hole-transfer performance, from the electronics injection efficiency and the electron transport performance of metal electrode or organic thin film layer.Especially, if by the compound of general formula [7] and [8] expression as dopant material, can realize efficient red emission, because the center of these compounds during as electronics and hole-recombination.

Compound by general formula [8] expression has excellent especially performance, because arylamines and tetracene key on specific position connects.

Organic El device of the present invention is a kind of like this device: wherein one or more layers organic film is placed between anode and the negative electrode.If this device is an individual layer, luminescent layer is located between anode and the negative electrode.Luminescent layer comprises luminescent material, but also can comprise hole-injecting material or electronics injecting material being delivered to luminescent material at the anode injected holes or at the negative electrode injected electrons.But luminescent layer can only be formed by luminescent material of the present invention, because luminescent material of the present invention has the transmission hole ability and the excellent transmission electronic capability of very high fluorescent emission quantum yield, excellence, and can form uniform film.Organic El device of the present invention with multilayered structure has rhythmo structure, for example: (anode/hole injection layer/luminescent layer/negative electrode), (anode/luminescent layer/electron injecting layer/negative electrode) and (anode/hole injection layer/luminescent layer/electron injecting layer/negative electrode).Because compound has excellent luminescent properties shown in general formula [1], [3]-[11], [11 '] and [17], and excellent hole injection efficiency, hole-transfer performance, electronics injection efficiency and electron transport performance, these compounds can be used as luminescent material and are used for luminescent layer.

In luminescent layer, if desired, except compound shown in general formula [1], [3]-[11], [11 '] and [17], can also use conventional luminescent material, dopant material, hole-injecting material and electronics injecting material.Can prevent by the multilayered structure of described organic EL because the brightness that quencher causes and the reduction in life-span.If desired, can be used in combination luminescent material, dopant material, hole-injecting material and electronics injecting material.By using dopant material, can improve luminosity and luminous efficiency, and can launch blue light and ruddiness.Hole injection layer, luminescent layer and electron injecting layer can be respectively to have two-layer or the multiwalled multilayered structure.If hole injection layer has multilayered structure, the hole is called hole injection layer by the layer that electrode injects so, and is accepted the hole and the hole is called hole transport layer by the layer that hole injection layer is delivered to luminescent layer by hole injection layer.If electron injecting layer has multilayered structure, electronics is called electron injecting layer by the layer that electrode injects so, and is accepted electronics and electronics is called electron transfer layer by the layer that electron injecting layer is delivered to luminescent layer by electron injecting layer.These layers are selected to use according to the energy gap level of material and thermotolerance and with the adhesivity of organic layer or metal electrode respectively.

Can comprise with the examples of material that compound shown in general formula [1], [3]-[11], [11 '] and [17] is used for luminescent layer as luminescent material or dopant material anthracene, naphthalene, phenanthrene, pyrene, tetracene, cool,

Fluorescein perylene Tai Bing perylene (phthaloperylene) Nai Bing perylene (naphthaloperylene), Naphtocyclinon (perynone), phthalein and Naphtocyclinon (phthaloperynone), naphthacene cyclic ketones (naphthaloperynone), diphenyl diethylene, tetraphenylbutadiene, tonka bean camphor oxadiazole, aldazine, Er benzoxazole quinoline, distyryl, pyrazine, cyclopentadiene, the metal complexes of quinoline, the metal complexes of quinolylamine, the metal complexes of benzoquinoline, imines, diphenylethlene, vinyl anthracene, the diamino carbazole, pyrans, thiapyran, polymethine (polymethine), merocyanine, hydroxyquinoline class (oxinoid) compound with the imidazoles chelating, quinacridone, rubrene, stilbene derivative and fluorescence dye.But above examples of material is not limited to above compound.

Especially, the metal complexes of quinoline and stilbene derivative can combine as luminescent material or dopant material with compound shown in general formula [7] and [8] in luminescent layer.

Importantly, the content of the dopant material in the luminescent layer is greater than the content of compound shown in general formula [11] or [11 '].This content is preferably 80-99.9% weight.

Annotate material as the hole, preferably a kind of like this compound, it can transmit the hole, have excellent effect and the excellent effect that the hole is injected into luminescent layer or luminescent material by the anode injected hole, can prevent to excite transfer components in electron injecting layer or electronics injecting material, and have excellent film forming ability what luminescent layer formed.The example of this compound comprises phthalocyanine derivates; naphthalene cyanines (naphthalocyanine) derivative; derivatives of porphyrin oxazole (oxaozole) oxadiazole; triazole; imidazoles; imidazolone; imidazole thione; pyrazoline; pyrazolone; imidazolidine oxazole oxadiazole; hydrazone; the acyl group hydrazone; polyaryl alkane; Stilbene; divinyl; p-diaminodiphenyl-type triphenylamine; styryl amine type triphenylamine; diamines type triphenylamine; the derivative of these compounds and macromolecular cpd such as Polyvinyl carbazole; polysilane and conduction macromole.But the example of these compounds is not limited to above-mentioned compound.

In can be used for the hole-injecting material of organic El device of the present invention, more effective hole-injecting material is aromatic uncle amine derivative and phthalocyanine derivates.

The example of aromatic uncle amine derivative comprises triphenylamine, trimethylphenyl amine, the tolyl diphenylamine, N, N '-phenylbenzene-N, N '-(3-aminomethyl phenyl)-1,1 '-xenyl-4,4 '-diamines, N, N, N ', N '-(4-aminomethyl phenyl)-1,1 '-phenyl-4,4 '-diamines, N, N, N ', N '-(4-aminomethyl phenyl)-1,1 '-xenyl-4,4 '-diamines, N, N '-phenylbenzene-N, N '-dinaphthyl-1,1 '-xenyl-4,4 '-diamines, N, N '-(aminomethyl phenyl)-N, N '-(4-n-butylphenyl) luxuriant and rich with fragrance-9, the 10-diamines, N, two (4-two-4-tolyl aminophenyl)-4-Santosol 360s of N-, and oligopolymer and polymkeric substance with these aromatic uncle amine skeleton structures.But the example of aromatic uncle amine derivative is not limited to above-mentioned compound.

The example of phthalocyanine (PC) derivative comprises H ₂Pc, CuPc, CoPC, NiPc, ZnPc, PdPc, FePc, MnPc, ClAlPc, ClGaPc, ClInPc, ClSnPc, Cl ₂The corresponding derivative of SiPc, (HO) AlPc, (HO) GaPc, VOPc, TiOPc, MoOPc, GaPc-O-GaPc and naphthalene cyanines.But the example of the derivative of phthalocyanine and naphthalene cyanines is not limited to above-mentioned compound.

As the electronics injecting material, preferably a kind of like this compound, it can transmit electronics, have excellent effect and the excellent effect that electronics is injected into luminescent layer or luminescent material by negative electrode injection electronics, can prevent to arrive hole injection layer or hole-injecting material, and have excellent film forming ability in the transfer components that excites that luminescent layer forms.The example of this compound comprises the derivative of Fluorenone, anthraquinone bismethane, two benzoquinones, thiapyran dioxide, oxazole, oxadiazole, triazole, imidazoles, perylene tetracarboxylic acid, fluorenylidene methane, anthraquinone bismethane, anthrone and these compounds thereof.But this compound is not limited to above-claimed cpd.The electronics injection efficiency can be by accepting electronics material adding hole-injecting material or electronation material adding electronics injecting material being improved.

In organic El device of the present invention, more effective electronics injecting material is metal complexes and five yuan of nitrogenous derivatives.

The example of metal complexes comprises that the oxine root closes lithium, two (oxine roots) close zinc, two (oxine roots) close copper, two (oxine roots) close manganese, three (oxine roots) close aluminium, three (2-methyl-oxine root) close aluminium, three (oxine roots) close gallium, two (10-hydroxy benzo [h] quinoline roots) close beryllium, two (10-hydroxy benzo [h] quinoline roots) close zinc, chlorine two (2-methyl-8-quinoline root) closes gallium, two (2-methyl-8-quinophenol (oxine) root) (neighbours-cresols root) close gallium, two (2-methyl-8-quinoline root) (beta naphthal roots) close aluminium and two (2-methyl-8-quinophenol (oxine) root) (beta naphthal root) and close gallium.But the example of metal complexes is not limited to above compound.

The derivative of preferred example Bao Kuo oxazole, thiazole, thiadiazoles and the triazole of five yuan of nitrogenous derivatives.Object lesson comprises 2,5-two (1-phenyl)-1,3, the 4-oxazole, dimethyl POPOP, 2,5-two (1-phenyl)-1,3, the 4-thiazole, 2,5-two (1-phenyl)-1,3, the 4-oxadiazole, 2-(4 '-tert-butyl-phenyl)-5-(4 ' '-binaphthylyl)-1,3, the 4-oxadiazole, 2,5-two (1-naphthyl)-1,3, the 4-oxadiazole, 1,4-two [2-(5-Ben oxadiazole base)] benzene, 1,4-two [2-(5-Ben oxadiazole base)-4-tert.-butylbenzene], 2-(4 '-tert-butyl-phenyl)-5-(4 ' '-xenyl)-1,3, the 4-thiadiazoles, 2,5-two (1-naphthyl)-1,3, the 4-thiadiazoles, 1,4-two [2-(5-phenyl thiadiazolyl group)] benzene, 2-(4 '-tert-butyl-phenyl)-5-(4 ' '-xenyl)-1,3, the 4-triazole, 2,5-two (1-naphthyl)-1,3,4-triazole and 1,4-two [2-(5-Phenyltriazole base)] benzene.But the example of nitrogenous five yuan of derivatives is not limited to above compound.

In organic El device of the present invention, except the compound by general formula [1] and [3]-[8] expression, at least a luminescent material, dopant material, hole-injecting material and electronics injecting material can be included in the same luminescent layer.In order to improve the stability of organic El device of the present invention, can on the whole surface of this device, form protective layer, or available silicone oil or resin are protected whole device to temperature, humidity and oxygen.

As the anodic electro-conductive material as organic El device, work function is that 4ev or higher material are suitable.This examples of material comprises the alloy of carbon, aluminium, vanadium, iron, cobalt, nickel, tungsten, silver, gold, platinum, palladium, these metals, the metal oxide that is used for ITO substrate (Substrate) and NESA substrate such as stannic oxide and Indium sesquioxide and organic conductive resin such as Polythiophene and polypyrrole.As the electro-conductive material that is used for negative electrode, work function is suitable less than the material of 4ev.This examples of material comprises the alloy of magnesium, calcium, tin, lead, titanium, yttrium, lithium, ruthenium, manganese, aluminium and these metals.But be used for negative electrode and the anodic examples of material is not limited to above example.Usually, the example of alloy comprises magnesium and the alloy of alloy, magnesium and the indium of silver and the alloy of lithium and aluminium.But the example of alloy is not limited to these alloys.The composition of alloy is selected suitable composition then by temperature, atmosphere and the vacuum tightness decision of vapor deposition source.Anode and negative electrode can be as required for having two-layer or the multiwalled multilayered structure.

In organic El device, preferably, the one side at least of this device is enough transparent effectively luminous to realize in the emission wavelength district.This substrate preferably also is transparent.When the preparation transparency electrode, use above electro-conductive material and carry out gas deposition or sputter, like this transparency that can obtain stipulating.Preferably, be placed on electrode on the light-emitting area and have 10% or higher transmittance.This substrate is not particularly limited, as long as this substrate has physical strength and hot strength and transparent.Can use glass substrate or transparent resin film.The example of transparent resin film comprises polyethylene, vinyl-vinyl acetate copolymer, ethylene-vinyl alcohol copolymer, polypropylene, polystyrene, polymethylmethacrylate, polyvinyl chloride, polyvinyl alcohol, polyvinyl butyral acetal, nylon, polyether-ether-ketone, polysulfones, polyethersulfone, tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, fluorinated ethylene propylene, tetrafluoroethylene-ethylene copolymer, tetrafluoraoethylene-hexafluoropropylene copolymer, voltalef, polyvinylidene difluoride (PVDF), polyester, polycarbonate, urethane, polyimide, polyetherimide, polyimide and polyacrylic film.

Every layer of organic El device of the present invention can be suitably according to film forming dry method such as vacuum gas deposition, sputter and plasma body and ion plating or film forming wet method such as spin coating, dip-coating and flow coat are produced, the thickness of film is not particularly limited.But this thickness must be set at desired value.If thickness, must apply light output and decrease in efficiency that high voltage just can reach regulation greater than this desired value.If thickness is lower than this desired value, can form pin hole, even and apply electric field and can not obtain enough brightness.In general, the desired value of thickness is 5 nanometer to 10 μ m.Preferred thickness is 10 nanometer to 0.2 μ m.

If produce this device according to wet method, with form every layer material dissolves or be dispersed in suitable solvent such as ethanol, chloroform, tetrahydrofuran (THF) and diox in, form film by this solution or suspension then.Solvent is not particularly limited.In any organic thin layer, can use appropriate resin and additive to improve film forming properties and to prevent to form pin hole.The example of operable this resin comprises insulative resin such as polystyrene, polycarbonate, polyarylester (polyarylates), polyester, polymeric amide, urethane, polysulfones, polymethylmethacrylate, polymethyl acrylate and Mierocrystalline cellulose, the multipolymer derived from these resins, photoconduction electricity resin such as poly N-vinyl carbazole and polysilane and electroconductive resin such as Polythiophene and polypyrrole.The example of additive comprises antioxidant, UV light absorber and softening agent.

As mentioned above, by compound of the present invention being used for the luminescent layer of organic El device, can when applying low pressure, produce actual enough brightness.Therefore, can obtain having efficient luminous efficiency and have the long lifetime (owing to suppress degraded) and stable on heating organic El device.

Organic El device of the present invention can be used for the flat-panel monitor of planar light-emitting element such as wall hanging TV set; The back of the body irradiation of duplicating machine, printer and liquid-crystal display; The light source of instrument, display panel and mark lamp.

Material of the present invention not only can be used for organic El device, but also can be used in electronics photochromics, photoelectric conversion device, solar cell and the field of image sensors.

The example of primary amine comprises primary alkyl amine such as methylamine shown in the used general formula [15] in the method for production organic El device material of the present invention, ethamine, Tri N-Propyl Amine, Isopropylamine, n-Butyl Amine 99, isobutylamine, sec-butylamine, TERTIARY BUTYL AMINE, n-amylamine, isobutylcarbylamine, uncle's amylamine, hexahydroaniline, normal hexyl Amine, heptyl amice, 2-aminoheptane, the amino heptane of 3-, octylame, nonyl amine, decyl amine, undecyl amine, lauryl amine, tridecyl amine, the 1-tetradecylamine, pentadecyl amine, 1-hexadecylamine and octadecylamine; Primary alkyl diamines such as quadrol, 1,1,3-diaminopropanes and 1,4-diaminobutane; Arylamines such as aniline, ortho-fluorophenyl amine ,-fluoroaniline, right-fluoroaniline, neighbour-Tolylamine ,-Tolylamine, right-Tolylamine, neighbour-methyl oxyaniline ,-methyl oxyaniline, right-methyl oxyaniline, naphthalidine, 2-naphthylamines, 1-amino anthracene, 2-amino anthracene, 2-phenylaniline, 4-phenylaniline, the amino phenanthrene of 9-, 2-trifluoromethyl toluene amine, 3-trifluoromethyl toluene amine and 4-trifluoromethyl toluene amine; Aryl diamine such as ortho-phenylene diamine ,-phenylenediamine, p-phenylenediamine, fluorenediamine and 1, the 8-naphthylene diamine; And following compound:

Example by the secondary amine of general formula [15] expression comprises following compound:

Aryl halide by general formula [16] expression is not particularly limited.The group of being represented by Ar is generally the alkyl with 1-18 carbon atom or has the replacement or the unsubstituting aromatic yl of 6-22 carbon atom.Aromatic ring can have substituting group.In the present invention, aromatic group comprises the alkyl with condensed ring.

The example of aryl halide comprises aryl bromide such as bromobenzene, neighbour-bromine phenylmethylether, between-the bromine phenylmethylether, right-the bromine phenylmethylether, neighbour-toluene bromide, between-toluene bromide, right-toluene bromide, neighbour-bromophenol, between-bromophenol, right-bromophenol, the 2-5 bromine benzotrifluoride, the 3-5 bromine benzotrifluoride, the 4-5 bromine benzotrifluoride, 1-bromo-2, the 4-dimethoxy benzene, 1-bromo-2, the 5-dimethoxy benzene, 2-bromine phenelyl alcohol, 3-bromine phenelyl alcohol, 4-bromine phenelyl alcohol, 5-bromo-1,2, the 4-Three methyl Benzene, between the 2-bromo--dimethylbenzene, the 2-bromo-is right-dimethylbenzene, 3-bromo-ortho-xylene, 4-bromo-ortho-xylene, between the 4-bromo--dimethylbenzene, between the 5-bromo--dimethylbenzene, 1-bromo-3-(trifluoromethoxy) benzene, 1-bromo-4-(trifluoromethoxy) benzene, the 2-bromo biphenyl, the 3-bromo biphenyl, the 4-bromo biphenyl, 4-bromo-1,2-(methylene radical dioxy base) benzene, 1-bromo-naphthalene, the 2-bromonaphthalene, 1-bromo-2-methylnaphthalene and 1-bromo-4-methylnaphthalene; Aryl chloride such as chlorobenzene, neighbour-chlorine phenylmethylether, between-the chlorine phenylmethylether, right-the chlorine phenylmethylether, adjoin-chlorotoluene, between-toluene(mono)chloride, right-toluene(mono)chloride, neighbour-chlorophenol, between-chlorophenol, right-chlorophenol, the 2-chlorobenzotrifluoride, the 3-chlorobenzotrifluoride, the 4-chlorobenzotrifluoride, 1-chloro-2, the 4-dimethoxy benzene, 1-chloro-2, the 5-dimethoxy benzene, 2-chloroethene oxygen phenyl alcohol, 3-chloroethene oxygen phenyl alcohol, 4-chloroethene oxygen phenyl alcohol, 5-chloro-1,2, the 4-Three methyl Benzene, between the 2-chloro--dimethylbenzene, the 2-chloro-is right-dimethylbenzene, 3-chloro-ortho-xylene, 4-chloro-ortho-xylene, between the 4-chloro--dimethylbenzene, between the 5-chloro--dimethylbenzene, 1-chloro-3-(trifluoromethoxy) benzene, 1-chloro-4-(trifluoromethoxy) benzene, the 2-chlordiphenyl, the 3-chlordiphenyl, the 4-chlordiphenyl, 1-chloro-naphthalene, the 2-chloronaphthalene, 1-chloro-2-methylnaphthalene and 1-chloro-4-methylnaphthalene; Aryl iodide such as iodobenzene, neighbour-iodoanisole, between-iodoanisole, right-iodoanisole, neighbour-toluene iodide, between-toluene iodide, right-toluene iodide, neighbour-iodophenol, between-iodophenol, right-iodophenol, 2-iodine phenylfluoroform, 3-iodine phenylfluoroform, 4-iodine phenylfluoroform, 1-iodo-2, the 4-dimethoxy benzene, 1-iodo-2, the 5-dimethoxy benzene, 2-iodine phenelyl alcohol, 3-iodine phenelyl alcohol, 4-iodine phenelyl alcohol, 5-iodo-1,2, the 4-Three methyl Benzene, between the 2-iodo--dimethylbenzene, the 2-iodo-is right-dimethylbenzene, 3-iodo-ortho-xylene, 4-iodo-ortho-xylene, between the 4-iodo--dimethylbenzene, between the 5-iodo--dimethylbenzene, 1-iodo-3-(trifluoromethoxy) benzene, 1-iodo-4-(trifluoromethoxy) benzene, 2-iodine biphenyl, 3-iodine biphenyl, 4-iodine biphenyl, 1-iodo-naphthalene, 2-iodine naphthalene, 1-iodo-2-methylnaphthalene and 1-iodo-4-methylnaphthalene; Aryl fluoride such as fluorobenzene, neighbour-fluoroanisole, between-fluoroanisole, right-fluoroanisole, neighbour-toluene fluoride, between-toluene fluoride, right-toluene fluoride, ortho-fluorophenyl phenol, between-fluorophenol, right-fluorophenol, the 2-fluoride trifluoro toluene, the 3-fluoride trifluoro toluene, the 4-fluoride trifluoro toluene, 1-fluoro-2, the 4-dimethoxy benzene, 1-fluoro-2, the 5-dimethoxy benzene, 2-fluorine phenelyl alcohol, 3-fluorine phenelyl alcohol, 4-fluorine phenelyl alcohol, 5-fluoro-1,2, the 4-Three methyl Benzene, between the 2-fluoro--dimethylbenzene, the 2-fluoro-is right-dimethylbenzene, 3-fluoro-ortho-xylene, 4-fluoro-ortho-xylene, between the 4-fluoro--dimethylbenzene, between the 5-fluoro--dimethylbenzene, 1-fluoro-3-(trifluoromethoxy) benzene, 1-fluoro-4-(trifluoromethoxy) benzene, 2-fluorine biphenyl, 3-fluorine biphenyl, 4-fluorine biphenyl, 4-fluoro-1,2-(methylene radical dioxy base) benzene, the 1-fluoronaphthalene, the 2-fluoronaphthalene, 1-fluoro-2-methylnaphthalene and 1-fluoro-4-methylnaphthalene; And following compound:

Can use to have 2 or more halogen atoms, the aryl halide of preferred 2 or 3 halogen atoms is not as long as purpose of the present invention affects adversely yet.Example with aryl halide of 2 or more halogen atoms comprises 1, the 2-dibromobenzene, 1, the 3-dibromobenzene, 1, the 4-dibromobenzene, 9, the 10-dibromoanthracene, 9,10-two chrloroanthracenes, 4,4 '-'-dibromobiphenyl, 4,4 '-DCBP, 4,4 '-diiodobiphenyl, 1-bromo-2-fluorobenzene, 1-bromo-3-fluorobenzene, 1-bromo-4-fluorobenzene, the 2-bromochlorophene, the 3-bromochlorophene, the 4-bromochlorophene, 2-bromo-5-toluene(mono)chloride, 3-bromo-4-chlorobenzotrifluoride, 5-bromo-2-chlorobenzotrifluoride, 1-bromo-2, the 3-dichlorobenzene, 1-bromo-2, the 6-dichlorobenzene, 1-bromo-3, the 5-dichlorobenzene, 2-bromo-4-toluene fluoride, 2-bromo-5-toluene fluoride, 3-bromo-4-toluene fluoride, 4-bromo-2-toluene fluoride, 4-bromo-3-toluene fluoride, three (4-bromophenyl) amine, 1,3,5-tribromo-benzene and following compound:

Be used for the method for the material of organic El device of the present invention in production, be not particularly limited the method that adds aryl halide.For example, can before the reaction beginning, two kinds of different aryl halides be mixed with primary amine, use the gained mixture to react then.In addition, one of primary amine and two kinds of aryl halides can be reacted.Then, add gained secondary amine in another aryl halide and react.A back method that wherein adds different aryl halides in proper order is preferred, because can more optionally produce tertiary amine.

The add-on of aryl halide is not particularly limited.If two kinds of aryl halides are added primary amine simultaneously, the appropriate amount of aryl halide is 0.5-10 mole/1 a mole primary amine so.Consider economic factors and be easier to carry out post-reaction treatment as isolating unreacted aryl halide, the amount of aryl halide is preferably 0.75-5 mole/1 mole primary amine.If two kinds of aryl halides add primary amine in proper order, the amount that at first adds the aryl halide of reaction system is the amino in mole primary amine of 0.5-1.5 mole/1.In order to improve the selectivity of target compound tertiary amine, the amount of the above aryl halide of adding reaction system is preferably the amino in mole primary amine of 0.9-1.1 mole/1.

The amount of the aryl halide that adds after preparing secondary amine is the 0.1-10 mole/1 mole amino as the primary amine of starting raw material.For fear of the complex operations when separating unreacted aryl halide and unreacted secondary amine after reaction, the add-on of this aryl halide is preferably the amino that 0.9-5 mole/1 mole is used as the primary amine of starting raw material.

Palladium catalyst as catalyst component is not particularly limited in the present invention, as long as it is a kind of palladium compound.The example of palladium compound comprises that the tetravalence palladium is as sour sodium of four hydration chlordene palladiums (IV) (sodium hexachloropalladate) and the sour potassium of chlordene palladium (IV); The compound of divalence palladium such as Palladous chloride (II), palladium bromide (II), acid chloride (II), palladium acetylacetonate (II), dichloro two (cyanobenzene) close palladium (II), dichloro two (acetonitrile) and close palladium (II), dichloro (two (diphenylphosphino) ethane) and close palladium (II), dichloro two (triphenylphosphine) and close palladium (II), dichloro tetramine and close palladium (II), dichloro (ring hot-1,5-diene) and close palladium (II) and palladium trifluoroacetate (II); And the compound of zeroth order palladium is as three (dibenzalacetones), two palladiums (0) (Pd ₂(dba) ₃) chloroform complex, four (triphenylphosphine) of (tris (dibenzyl ideneacetone) dipalladium), three (dibenzalacetones), two palladiums (0) closes palladium (0) and two (two (diphenylphosphino) ethane) and close palladium (0).In the method for the invention, the amount of palladium compound is not particularly limited.The amount of palladium compound is 0.00001-20.0% mole palladium/1 mole of primary amine.If the amount of palladium compound is in above scope, but the tertiary amine highly selective is synthetic.Because the palladium compound costliness, the amount of palladium compound is preferably 0.001-5.0 mole palladium/1 mole of primary amine.

In the method for the invention, the trialkyl phosphine compound as catalyst component is not particularly limited.The example of trialkyl phosphine compound comprises triethyl phosphine, tricyclohexyl phosphine, tri isopropyl phosphine, tri-n-butyl phosphine, tri isobutyl phosphine, three sec-butyl phosphine and tri-butyl phosphines.In these compounds, tri-butyl phosphine is because high reaction activity and preferred.The triaryl phosphine compound is not particularly limited.The example of triaryl phosphine compound comprise triphenylphosphine, benzyl diphenylphosphine, three-neighbour-tolylphosphine, three--tolylphosphine and three-right-tolylphosphine.In these compounds, triphenylphosphine and three-neighbour-tolylphosphine is preferred.Diphosphine compound is not particularly limited.The example of diphosphine compound comprises two (dimethyl phosphino-) methane, two (dimethyl phosphino-) ethane, two (dicyclohexyl phosphino-) methane, two (dicyclohexyl phosphino-) ethane, two (diphenylphosphino) ethane, 1, two (diphenylphosphino) propane of 3-, 1, two (diphenylphosphino) butane of 4-, two (diphenylphosphino) ferrocene, (R)-2,2 '-two (diphenylphosphino)-1,1 '-dinaphthalene ((R)-BINAP), (S)-2,2 '-two (diphenylphosphino)-1,1 '-dinaphthalene-((S)-BINAP), (R)-2,2 '-two (diphenylphosphino)-1,1 '-dinaphthalene ((±)-BINAP), 2S, two (diphenylphosphino) butane ((S of 3S-, S)-CHIRAPHOS), 2R, two (diphenylphosphino) butane ((R of 3R-, R)-CHIRAPHOS), 2, two (diphenylphosphino) butane ((±)-CHIRAPHOS) of 3-, (R)-2,2 '-two (two-right-tolyl phosphino-s)-1,1-dinaphthalene ((R)-Tol-BINAP), (S)-2,2 '-two (two-right-tolyl phosphino-s)-1,1 '-dinaphthalene ((S)-Tol-BINAP), 2,2 '-two (two-right-tolyl phosphino-s)-1,1 '-dinaphthalene ((±)-Tol-BINAP), 4R, two (the diphenylphosphine ylmethyls)-2 of 5R-, 2-dimethyl-1,3-dioxolane (dioxorane) ((S, S)-DIOP), 4, two (the diphenylphosphine ylmethyls)-2 of 5-, 2-dimethyl-1,3-dioxolane ((±)-DIOP), N, N '-dimethyl-(S)-1-[(R)-1 ', two (diphenylphosphino) ferrocenyls of 2-] ethylamine ((S), (R)-BPPFA), N, N '-dimethyl-(R)-1-[(S)-1 ', two (diphenylphosphino) ferrocenyls of 2-] ethylamine ((R), and N (S)-BPPFA), N '-dimethyl-1-[1 ', two (diphenylphosphino) ferrocenyls of 2-] ethylamine ((±)-BPPFA).In these compounds, two (diphenylphosphino) ethane, 1, two (diphenylphosphino) propane of 3-, two (diphenylphosphino) ferrocene and various BINAP are preferred.Described BINAP can be optically active compound or racemic compound.

The amount of trialkyl phosphine compound, triphenylphosphine compound and diphosphine compound is 0.01-10000 mole/1 a mole palladium compound.As long as amount is in this scope, the selectivity of arylamines just can not change.But this amount is preferably 0.1-10 mole/1 mole palladium compound, because phosphine compound costliness.

In the method for the invention, palladium compound and phosphine compound are the basal components of catalyzer.The composition that adds these components is as catalyzer.As the method that adds these components, two kinds of components separately or with the complex form of making in advance can be added in the reaction system.

The alkali that can be used for the present invention's reaction is not particularly limited, and therefore can be selected from mineral alkali such as yellow soda ash and salt of wormwood and alkali metal alcoholates and organic bases such as tertiary amine.The preferred example of alkali comprises alkali metal alcoholates such as sodium methylate, sodium ethylate, potassium methylate, potassium ethylate, trimethyl carbinol lithium, sodium tert-butoxide, potassium tert.-butoxide and cesium carbonate (Cs ₂CO ₃).Alkali can add reaction zone and need not any processing.In addition, alkali can be made and is used for reaction zone in reacting environment by basic metal, hydrogenated alkali metal or alkali metal hydroxide and alcohol.

The amount of alkali is not particularly limited.This amount is preferably the halogen atom in per 1 mole of two kinds of different aryl halide that add this reaction system, 0.5 mole or higher.If the amount of alkali is lower than 0.5 mole, reactive behavior descends and the arylamines productive rate reduces.Therefore, this amount is not preferred.If a large amount of excessive adding alkali, the productive rate of arylamines does not change, and but then, it is complicated that post-reaction treatment becomes.Therefore, the more preferably per 1 mole of halogen atom of described amount, 1.0 moles or higher and be lower than 5 moles.

Reaction in the inventive method generally is to carry out in the presence of inert solvent.Solvent is not particularly limited, as long as this solvent can not produce too much disadvantageous effect to reaction.The example of solvent comprises aromatic solvent such as benzene, toluene and dimethylbenzene, ether solvents such as diethyl ether, tetrahydrofuran (THF) He diox, acetonitrile, dimethyl formamide, methyl-sulphoxide and HMPA.Aromatic solvent such as benzene, toluene and dimethylbenzene are preferred.

The inventive method preferably under the atmosphere of rare gas element such as nitrogen and argon gas, is carried out under normal pressure.This method also can be carried out adding to depress.

In the method for the invention, temperature of reaction can be chosen in 20-300 ℃, preferred 50-200 ℃.Reaction times can be chosen in several minutes to 72 hour.

Synthetic embodiment 12,13,14,17 and 20 has specifically described the inventive method, and wherein novel arylamine compound obtains in the presence of catalyzer that comprises phosphine compound and palladium compound and alkali.

The present invention more specifically is described by reference following examples.But the present invention is not limited to these embodiment.

Synthetic embodiment 1 (compound (2))

Midbody compound A's is synthetic

In 200 milliliters of round-bottomed flasks, 0.38 gram (2.04 mmole) 4-bromobenzaldehyde and 0.98 gram (4.29 mmole) benzylphosphonic acid ethyl ester are dissolved in 40 milliliters of methyl-sulphoxides.At room temperature, to wherein add 0.5 gram (4.49 mmole) potassium tert.-butoxide on a small quantity in batches, stirred the gained mixture then 18 hours.This reaction mixture is poured in 500 ml waters, filtered out solid, obtain a kind of yellow solid (0.5 gram).

In 100 milliliters of round-bottomed flasks, the above crystal that obtains, 2.0 gram (12.0 mmole) potassiumiodides and 11.4 gram (6.0 mmole) cupric iodides are dissolved in 10 milliliters of hexamethylphosphoramides, under 150 ℃ of heating conditions, stirred the gained mixture 6 hours then.Reaction adds 10 milliliters of 1N spirit of salt aqueous solution in this reaction mixture after finishing, and extracts organic layer with toluene then.After extraction liquid concentrated, come this reaction product of purifying by in ether and methanol mixture, carrying out recrystallization, obtain 0.28 restraining (productive rate: following midbody compound A 45%):

(midbody compound A)

Midbody compound B's is synthetic

In 50 milliliters of round-bottomed flasks, be suspended in 10 milliliters of 6N spirit of salt 3 gram (17.4 mmole) right-bromanilines and cooling.In 4 ℃, under the temperature, in this refrigerative suspension, slowly drip by 1.25 gram (18.1 mmole) S-WATs are dissolved in the solution that obtains in 5.3 ml waters.The gained mixture was stirred 1 hour under this temperature, obtain the aqueous solution of diazonium compound then.

In addition, in 100 milliliters of round-bottomed flasks, 0.3 gram (1.7 mmole) anthracene is dissolved in 5 milliliters of acetone.A kind of to wherein adding by 0.46 gram Copper dichloride dihydrate (II) is dissolved in the solution that obtains in 5.7 ml waters, then this mixture is cooled to 4 ℃.In this cooling mixture, the aqueous solution of the diazonium compound that obtains more than adding under the same temperature at room temperature stirs the gained mixture overnight then.Reaction filters out the precipitation crystal after finishing, with methanol wash and dry, obtain 0.2 gram (productive rate: following midbody compound B 24%):

(midbody compound B)

Synthesizing of compound (2)

In 100 milliliters of round-bottomed flasks, 0.018 gram (0.2 mmole) aniline is dissolved in 5 milliliters of methylene dichloride.To wherein adding 0.05 gram (0.5 mmole) diacetyl oxide, then the gained mixture was at room temperature stirred 1 hour.Then, reaction solvent is removed in distillation, obtains a kind of oily compound.In this oily compound, add 0.56 gram (1.8 mmole) midbody compound A, 5 gram salt of wormwood, 0.3 gram copper powder and 20 milliliters of oil of mirbane, stirred the gained mixture 2 days down at 210 ℃ then.Then, solvent is removed in distillation, adds 10 milliliters of glycol ethers then and is dissolved in the solution that obtains in 10 ml waters by restraining potassium hydroxide with 3.The gained mixture is stirred a night down at 110 ℃.After reaction is finished, the mixture of ethyl acetate and water is added in this reaction mixture, isolate organic layer then.Distillation is removed after the solvent, obtains coarse crystal.

Subsequently, in 100 milliliters of round-bottomed flasks, the above coarse crystal that obtains of packing into, 0.05 gram (0.1 mmole) midbody compound B, 5 gram salt of wormwood, 0.3 gram copper powder and 20 milliliters of oil of mirbane stirred the gained mixture 2 days down at 220 ℃ then.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, and dry column chromatography (silica gel, the hexane/toluene=1/1) method of also passing through is carried out purifying, obtains 0.017 gram yellow powder.This powder is measured by NMR, IR and FD-MS (field desorption(FD) mass spectrum) and is confirmed as compound (2) (productive rate: 20%).

Synthetic embodiment 2 (compound (9))

Midbody compound C's is synthetic

In 200 milliliters of round-bottomed flasks, with 51.2 gram (0.3 mole) diphenylamines, 71.4 grams

Mole) 1,4-dibromobenzene, 34.6 gram (0.36 mole) potassium tert.-butoxides, 4.2 gram (5.9 mmole) PdCl ₂(PPh ₃) ₂Mix with 1.2 liters of dimethylbenzene, then the gained mixture is existed

Stir a night under ℃.

After reaction is finished, organic layer is concentrated, obtain the brown crystal of about 100 grams.By column chromatography (silica gel, hexane/toluene=10/1) this crystal of method purifying, obtain 28 the gram (productive rate: following midbody compound C 29%):

(midbody compound C)

Synthesizing of compound (9)

In 100 milliliters of round-bottomed flasks, 0.48 gram (1 mmole) midbody compound B is dissolved in 10 milliliters of ether, this mixture is cooled to-78 ℃ then.In this cooling mixture, add 2 milliliters of (1.5M, 3 mmoles) n-Butyl Lithiums, stirred the gained mixture then 1 hour.In this mixture, drip then by 0.3g (3 mmole) trimethyl borate is dissolved in the solution that obtains in 5 milliliters of ether.After reinforced the finishing, the gained mixture was stirred 1 hour down at-78 ℃.At room temperature add 10 milliliters of 1N spirit of salt aqueous solution then.Isolate after the organic layer, solvent is removed in distillation, obtains coarse crystal.

In 100 milliliters of round-bottomed flasks, with the above coarse crystal that obtains, 0.97 gram (3 mmole) midbody compound C, 12 milligrams of Pd (PPh ₃) ₄Be dissolved in 10 milliliters of dimethyl formamides with 0.32 gram (1.5 mmole) potassiumphosphate, stirred the gained mixture 4 hours down at 100 ℃ then.Isolate after the organic layer, solvent is removed in distillation, obtains coarse crystal.By column chromatography (silica gel, benzene/ethyl acetate=50/1) this crystal of method purifying, obtain 0.13 gram yellow powder.This powder is measured by NMR, IR and FD-MS and is confirmed as compound (9) (productive rate: 14%).

Synthetic embodiment 3 (compound (18))

Midbody compound D's is synthetic

Magnesium and ether are added 0.48 gram (2.0 mmole) 1, in the 4-dibromobenzene, prepare Grignard reagent.In addition, in 100 milliliters of round-bottomed flasks, with 5.7 gram (20.0 mmoles) 1,4-dibromine naphthalene and 10 milligrams of NiCl ₂(dppp) be dissolved in 20 milliliters of ether, then the gained mixture cooled off in ice bath.The Grignard reagent of preparation stirs the gained mixture 6 hours under refluxing then more than adding in this cooling mixture.Reaction adds 10 milliliters after finishing The spirit of salt aqueous solution.Isolate after the organic layer, solvent is removed in distillation, obtain 0.30 gram (productive rate: following Compound D 30%):

(midbody compound D)

Synthesizing of compound (18)

In 100 milliliters of round-bottomed flasks, 0.09 gram (1.0 mmole) aniline and 0.25 gram (2.5 mmole) diacetyl oxide are dissolved in 5 milliliters of methylene dichloride.The gained mixture was at room temperature stirred 1 hour.Then, reaction solvent is removed in distillation, obtains a kind of oily compound.To wherein adding 0.4 gram (4.5 mmole) midbody compound A, 5 gram salt of wormwood, 0.3 gram copper powder and 20 milliliters of oil of mirbane, stirred the gained mixture 2 days down at 210 ℃ then.Then, solvent is removed in distillation, adds 10 milliliters of glycol ethers afterwards and is dissolved in the solution that obtains in 10 ml waters by restraining potassium hydroxide with 3.The gained mixture is stirred a night down at 110 ℃.After reaction is finished, the mixture of ethyl acetate and water is added in this reaction mixture.After isolating organic layer,, obtain coarse crystal except that after desolvating.

Subsequently, in 100 milliliters of round-bottomed flasks, the above coarse crystal that obtains, 0.5 gram (1.0 mmole) midbody compound D, 5 gram salt of wormwood and 0.3 gram copper powder are dissolved in 20 milliliters of oil of mirbane, stirred the gained mixture 2 days down at 220 ℃ then.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, and dry column chromatography (silica gel, the hexane/toluene=1/1) method of also passing through is carried out purifying, obtains 0.1 gram yellow powder.This powder is confirmed as compound (18) (productive rate: 10%) by measuring according to NMR, IR and FD-MS.

Embodiment 1

According to spin-coating method, the cleaning panes that will have the ITO electrode is coated with to comprise the above gained compound (2), 2 as luminescent material that weight ratio is 5:3:2, two (the 1-naphthyls)-1,3 of 5-, (by TEIJIN KASEI Co., Ltd. makes for 4-oxadiazole and polycarbonate resin; PANLITE K-1300) and be dissolved in composition in the tetrahydrofuran (THF), obtain the luminescent layer that thickness is 100 nanometers.On the gained luminescent layer, use alloy to make the electrode of thickness 150 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.The luminosity of this organic El device is 200 (cd/m ²), high-high brightness is 14000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 2.1 (lm/W).

Embodiment 2

On cleaning panes with ITO electrode, the above compound that obtains (9) vacuum gas deposition is become luminescent material, form the luminescent layer of thickness 100 nanometers.On the layer of above formation, use alloy to make the electrode of thickness 100 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.This luminescent layer is 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminosity of this organic El device is about 110 (cd/m ²), high-high brightness is 20000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 2.1 (lm/W).

Embodiment 3

On cleaning panes with ITO electrode, the above compound that obtains (2) vacuum gas deposition is become luminescent material, form the luminescent layer of thickness 50 nanometers.Then, by the following compound of gas deposition (Alq), form the electron injecting layer of thickness 10 nanometers:

On the layer of above formation, use alloy to make the electrode of thickness 100 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.This luminescent layer and electron injecting layer are 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.This organic El device sends blue green light, and luminosity is about 600 (cd/m ²), high-high brightness is 30000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 3.0 (lm/W).If this organic El device is at 600cd/m ²Initial luminosity under by constant current driven, its half-life is grown to 2000 hours so.

Embodiment 4-16

On cleaning panes with ITO electrode, luminescent material shown in the table 1 is carried out gas deposition, form the luminescent layer of thickness 80 nanometers.Then, above-claimed cpd (Alq) vacuum gas deposition is become the electronics injecting material, form the electron injecting layer of thickness 20 nanometers.On the layer of above formation, use alloy to make the electrode of thickness 150 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.With the upper strata 10 ^-Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminescent properties of gained device provides in table 1.Organic El device among all these embodiment has excellent luminance, and for example high-high brightness is 10000 (cd/m ²) or higher.

Table 1

Embodiment 17

On cleaning panes, with following compound (TPD74) with ITO electrode:

The vacuum gas deposition becomes hole-injecting material, forms the film of thickness 60 nanometers.Then, with following compound (NPD):

The vacuum gas deposition becomes the hole-transfer material on the film of above formation, forms the film of thickness 20 nanometers.Then, with 4,4 '-two (2, the 2-diphenylacetylene) biphenyl (DPVBi) and more than the compound (3) that obtains carry out gas deposition simultaneously, forming compound (3) content is that 5% weight and thickness are the layer of 40 nanometers.Compound (3) is as fluorescent dopants.Subsequently, compound (Alq) gas deposition is become the electronics injecting material, form the layer of thickness 20 nanometers.Then, LiF is carried out gas deposition, form the layer of thickness 0.5 nanometer.On with the upper strata, form electrode, form the layer of thickness 100 nanometers by gas deposition aluminium.Obtain a kind of organic El device like this.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminosity of this organic El device when applying the 5V volts DS is high to about 750 (cd/m ²).If this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 3000 hours.

Comparative Examples 1

Make organic El device according to the same steps as that embodiment 1 is carried out, only be to use the following compound of Comparative Examples 1:

(compound of Comparative Examples 1)

As luminescent material.The luminosity of gained organic El device when applying the 5V volts DS is 60 (cd/m ²) and luminous efficiency be 0.34 (lm/W).Can not reach enough performances.

Comparative Examples 2

Make organic El device according to the same steps as that embodiment 3 is carried out, only be to use the following compound of Comparative Examples 2:

(compound of Comparative Examples 2)

As luminescent material.The luminosity of gained organic El device when applying the 5V volts DS is 200 (cd/m ²) and luminous efficiency be 1.2 (lm/W).If but this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, the half-life is as short as 600 hours so.

The thermotolerance test

With embodiment 2 and 3 and Comparative Examples 1 and 2 in the organic El device that is used for measuring luminosity made be placed on the chamber that keeps 100 ℃ of constant temperature.After 500 hours, measure luminosity once more.Relatively this device calculates the brightness conservation rate before being positioned over this chamber and brightness value afterwards then.

Embodiment 2 and 3 and Comparative Examples 1 and 2 in the gained brightness conservation rate like this of the organic El device made be respectively 85%, 95%, 25% and 30%.This result shows that the compound that is used as luminescent material in Comparative Examples 1 and 2 can not keep brightness, because the second-order transition temperature of these compounds is lower than 100 ℃.On the contrary, the compound that is used as luminescent material in embodiment 2 and 3 has excellent thermotolerance and can keep brightness for a long time, because the second-order transition temperature of these compounds is higher than 110 ℃.

Synthetic embodiment 4 (compound (30))

Midbody compound E (6, the 12-diiodo- ) synthetic

In 300 milliliters of round-bottomed flasks, with 5 grams (22 mmole)

Be dissolved in 100 milliliters of tetracol phenixin.At room temperature, be dissolved in the gram of 16 in 100 milliliters of tetracol phenixin (64 mmole) iodine to wherein dripping.The gained mixture was stirred 5 hours under heating, filter to isolate the precipitation crystal, wash this crystal with 100 milliliters of tetracol phenixin then.With coarse crystal recrystallization from 200 milliliters of toluene, obtain midbody compound E (productive rate: 35%).

Synthesizing of compound (30)

In 100 milliliter of 2 neck flask, the amino Stilbene of 2 gram (10 mmole) 4-are dissolved in 20 milliliters of methylene dichloride.To wherein adding 2.5 gram (25 mmole) diacetyl oxides.The gained mixture was at room temperature stirred 1 hour.Then, reaction solvent is removed in distillation, obtains a kind of oily compound.In 300 milliliter of two neck round-bottomed flask, 4.1 gram (20 mmole) phenyl-iodides, 3 gram (30 mmole) salt of wormwood, 0.06 gram (1 mmole) copper powder and 100 milliliters of oil of mirbane are added in the gained oily compound, then the gained mixture was stirred 2 days under 220 ℃ of heating.Then, solvent is removed in distillation, adds in the resistates with 10 milliliters of glycol ethers with by 30 gram potassium hydroxide are dissolved in the solution that obtains in 100 ml waters.Be reflected under 110 ℃ and carry out a night.After reaction is finished, in the mixture adding reaction mixture with ethyl acetate and water.Isolate after the organic layer, solvent is removed in distillation, obtains coarse crystal.

Subsequently, in 300 milliliter of 2 neck flask, above coarse crystal, 2.4 gram (5 mmole) midbody compound E, 3 gram (20 mmole) salt of wormwood and 0.06 gram (1 mmole) copper powder are dissolved in 100 milliliters of oil of mirbane, then the gained mixture were stirred 2 days under 230 ℃ of heating, after reaction is finished, filter to isolate the precipitation crystal, use methanol wash, drying is then by column chromatography (silica gel, hexane/toluene=1/1) method is carried out purifying, obtains 1.0 gram yellow powders.This powder is confirmed as compound (30) (productive rate: 25%) by measuring according to NMR, IR and FD-MS.

Synthetic embodiment 5 (compound (36))

Synthesizing of compound (36)

In 100 milliliters of round-bottomed flasks, 3.4 gram (20 mmole) diphenylamines, 4.8 gram (10 mmole) midbody compound E, 3 gram (30 mmole) salt of wormwood and 0.06 gram (1 mmole) copper powder are dissolved in 100 milliliters of oil of mirbane, then the gained mixture were stirred 2 days under 210 ℃ of heating.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, and drying is carried out purifying by column chromatography (silica gel, hexane/toluene=1/1) method then, obtains 2.8 gram yellow powders.This powder is confirmed as compound (36) (productive rate: 50%) by measuring according to NMR, IR and FD-MS.

Synthetic embodiment 6 (compound (38))

Synthesizing of compound (38)

Under argon atmospher, 1.0 gram (41 mmole) magnesium, 1 milliliter of tetrahydrofuran (THF) and small pieces iodine are joined in 100 milliliter of 4 neck flask.At room temperature, in this mixture, slowly drip and be dissolved in the gram of 9.7 in 100 milliliters of tetrahydrofuran (THF)s (30 mmole) 4-bromine triphenylamine.After reinforced the finishing, this reaction mixture was stirred 1 hour under 60 ℃ of heating, prepare Grignard reagent.

In 300 milliliter of 4 neck flask, with 4.8 gram (10 mmole) midbody compound E, 0.28 gram (0.4 mmole) PdCl ₂(PPh ₃) ₂AlH (iso-Bu) with 1.0 milliliters of (1 mmole) 1.0M ₂Toluene solution is dissolved under argon atmospher in 50 milliliters of tetrahydrofuran (THF)s.At room temperature, the Grignard reagent of preparation more than wherein dripping.Temperature is raise, and this reaction mixture of heating spends the night under refluxing then.Reaction is cooled off this reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, use washing with acetone then.With gained coarse crystal recrystallization from 100 milliliters of acetone, obtain 4.3 gram yellow powders.This powder is confirmed as compound (38) (productive rate: 60%) by measuring according to NMR, IR and FD-MS.

Synthetic embodiment 7 (compound (47))

Synthesizing of compound (47)

In 100 milliliter of 2 neck flask, with 2.4 gram (10 mmole) 6-amino

Be dissolved in 20 milliliters of methylene dichloride.To wherein adding 2.5 gram (25 mmole) diacetyl oxides, then the gained mixture was at room temperature stirred 1 hour.Then, reaction solvent is removed in distillation, obtains a kind of oily compound.In 300 milliliter of 2 neck flask, 4.1 gram (20 mmole) phenyl-iodides, 3 gram (30 mmole) salt of wormwood and 0.06 gram (1 mmole) copper powder are dissolved in 100 milliliters of oil of mirbane.To wherein adding described oily compound, then with the gained mixture 220 ℃ of following heated and stirred 2 days.Then, solvent is removed in distillation, adds in the resistates 10 milliliters of glycol ethers with by 30 gram potassium hydroxide are dissolved in the solution that obtains in 100 ml waters then.Be reflected under 110 ℃ and carry out a night.After reaction is finished, the mixture of ethyl acetate and water is added in this reaction mixture.Isolate after the organic layer, solvent is removed in distillation, obtains coarse crystal.

Subsequently, in 300 milliliter of 2 neck flask, with the above coarse crystal that obtains, 2 the gram (5 mmoles) 4,4 '-diiodobiphenyl, 3 the gram (30 mmole) salt of wormwood and 0.06 the gram (1 mmole) copper powder be dissolved in 100 milliliters of oil of mirbane, then with the gained mixture 230 ℃ of following heated and stirred

My god.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, and drying is carried out purifying by column chromatography (silica gel, hexane/toluene=1/3) method then, obtains 0.8 gram yellow powder.This powder is confirmed as compound (47) (productive rate: 30%) by measuring according to NMR, IR and FD-MS.)

Embodiment 18

According to spin-coating method, the cleaning panes that will have the ITO electrode is coated with to comprise the above gained compound (30), 2 as luminescent material that weight ratio is 5:3:2, two (the 1-naphthyls)-1,3 of 5-, (by TEIJIN KASEI Co., Ltd. makes for 4-oxadiazole and polycarbonate resin; PANLITE K-1300) and be dissolved in composition in the tetrahydrofuran (THF), obtain the luminescent layer that thickness is 100 nanometers.On the gained luminescent layer, use alloy to make the electrode of thickness 150 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.The luminosity of this organic El device is 320 (cd/m ²), high-high brightness is 14000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 2.5 (lm/W).

Embodiment 19

On cleaning panes with ITO electrode, above gained compound (37) vacuum gas deposition is become luminescent material, form the luminescent layer of thickness 100 nanometers.On formed layer, use lithium fluoride to form the inorganic electronic input horizon of thickness 0.3 nanometer.Then, the electrode with aluminium formation thickness 100 nanometers obtains a kind of organic El device like this.This luminescent layer is 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminosity of this organic El device is about 110 (cd/m ²), high-high brightness is 20000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 1.2 (lm/W).

Embodiment 20

On cleaning panes with ITO electrode, CuPc vacuum gas deposition is become hole-injecting material, form the hole injection layer of thickness 40 nanometers.Then, the compound that obtains more than the use (47) is as the hole transport layer of hole-transfer material formation thickness 20 nanometers, then by above-claimed cpd (Alq) is carried out the luminescent layer that the vacuum gas deposition forms thickness 60 nanometers.The rubrene of 4% weight is added in the luminescent layer.On formed layer, use alloy to form the electrode of thickness 100 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminosity of this organic El device is about 700 (cd/m ²), high-high brightness is 80000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 6.0 (lm/W).If this organic El device is at 600 (cd/m ²) initial luminosity under by constant current driven, the half-life is grown to 4000 hours.

Embodiment 21-23

On cleaning panes,, form the hole injection layer of thickness 20 nanometers by the hole-injecting material shown in the vacuum gas deposition table 2 with ITO electrode.By above-claimed cpd (Alq) is carried out the luminescent layer that the vacuum gas deposition forms thickness 60 nanometers as luminescent material, the rubrene with 4% weight adds in the luminescent layer then.On formed layer, use alloy to form the electrode of thickness 150 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains.Obtain a kind of organic El device like this.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.Table 2 has provided the luminescent properties of gained device.The organic El device of all these embodiment all has excellent luminance, and for example high-high brightness is 10000 (cd/m ²) or higher.

Table 2

Embodiment 34

On cleaning panes, above-claimed cpd (TPD74) as hole-injecting material and the vacuum gas deposition, is formed the layer of thickness 60 nanometers with ITO electrode.Then, above-claimed cpd (NPD) vacuum gas deposition is become the hole-transfer material, form the layer of thickness 20 nanometers.

To carry out gas deposition simultaneously as 4,4 ' of luminescent material-two (2, the 2-diphenylacetylene) phenylanthracenes (DPVDPAN) with as the above-claimed cpd (36) of doping agent, forming compound (36) content is that 2% weight and thickness are the layer of 40 nanometers.Then, above-claimed cpd (Alq) gas deposition is become the electric charge injecting material, form the layer of thickness 20 nanometers.At depositing fluorinated lithium and after forming the layer of thickness 0.5 nanometer, aluminium is carried out gas deposition, form the electrode of 100 nanometer thickness.Obtain a kind of organic El device like this.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.Luminosity height to the 500 (cd/m of this organic El device when applying the 8V volts DS ²), and luminous be the blue light of purity excellence.If this organic El device is at 100 (cd/m ²) initial luminosity under by constant current driven, the half-life is grown to 7000 hours.

Measure the spectrum that sends of this device, found that, this spectrum is identical with the device that uses DPVBi.This shows that compound (36) does not influence luminous, but can prolong the life-span of this device.

Comparative Examples 3

Same procedure according to embodiment 34 is prepared organic El device, does not just add above-claimed cpd (36) as doping agent.If this organic El device is at 100 (cd/m ²) initial luminosity under by constant current driven, the half-life is than the weak point of embodiment 34, promptly 4000 hours.

Comparative Examples 4

Same procedure according to embodiment 20 is prepared organic El device, does not just use the compound of above-mentioned Comparative Examples 2 as the hole-transfer material.

The luminosity of gained organic El device is 300 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 4.2 (lm/W).If but this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, the half-life is as short as 300 hours.

The thermotolerance test

With embodiment 20 and 27 and Comparative Examples 4 in the organic El device that is used for measuring luminosity made be placed on the chamber that keeps 105 ℃ of constant temperature.After 500 hours, measure luminosity once more.Relatively this device calculates the brightness conservation rate before being positioned over this chamber and brightness value afterwards then.

Embodiment 20 and 27 and Comparative Examples 4 in the gained brightness conservation rate like this of the organic El device made be respectively 87%, 90% and 25%.This result shows that the compound that is used as luminescent material in Comparative Examples 4 can not keep brightness, because the second-order transition temperature of these compounds is lower than 105 ℃.On the contrary, the compound that is used as luminescent material in embodiment 20 and 27 has excellent thermotolerance and can keep brightness for a long time, because the second-order transition temperature of these compounds is higher than 110 ℃.

Synthetic embodiment 8 (compound (58))

Midbody compound F's (5,11-diiodo-tetracene) is synthetic

In 2 liters of round-bottomed flasks, 50 gram (0.19 mmoles) 5 of packing into, 12-tetracene, 108 gram (0.57 mmole) tin chloride (IV), 500 milliliters of acetate and 200 milliliters of concentrated hydrochloric acids.With gained compound stirring and refluxing 2 hours.Reaction filters to isolate the precipitation crystal after finishing, washing, and in the vacuum-drying chamber, carry out drying, obtain 48 gram coarse crystals.

Subsequently, in 2 liter of four neck flask, above coarse crystal and 50 gram (0.19 mmole) triphenylphosphines are dissolved under argon atmospher in 300 milliliters of dimethyl formamides.Be dissolved in the gram of 64 in 200 milliliters of dimethyl formamides (0.4 mmole) bromine to wherein slowly dripping, stir the gained mixture then at ambient temperature.After reinforced the finishing, with this mixture 200 ℃ of one nights of following heated and stirred.After reaction is finished, remove dimethyl formamide, then 200 ml waters are added in the resistates by vacuum distilling.Extract organic layer with toluene.Use the dried over mgso extraction liquid, use rotary evaporator to carry out vacuum concentration then, obtain a kind of oily compound.By column chromatography (silica gel, hexane/toluene=1/1) this oily compound of method purifying, obtain 30 gram yellow powders.This powder is confirmed as midbody compound F (productive rate: 40%) by measuring according to NMR, IR and FD-MS.

Synthesizing of compound (58)

In 100 milliliter of 2 neck flask, the amino Stilbene of 2 gram (10 mmole) 4-are dissolved in 20 milliliters of methylene dichloride.To wherein adding 2.5 gram (25 mmole) diacetyl oxides, then the gained mixture was at room temperature stirred 1 hour.Then, reaction solvent is removed in distillation, obtains a kind of oily compound.In 300 milliliter of 2 neck flask, in this oily compound, add 4.1 gram (20 mmole) phenyl-iodides, 3 gram (30 mmole) salt of wormwood, 0.06 gram (1 mmole) copper powder and 100 milliliters of oil of mirbane, then in 220 ℃ of following heated and stirred gained mixtures 2 days.Then, solvent is removed in distillation, adds 10 milliliters of glycol ethers then and is dissolved in the solution that obtains in 100 ml waters by restraining potassium hydroxide with 30.Be reflected under 110 ℃ and carry out a night.After reaction is finished, the mixture of ethyl acetate and water is added in this reaction mixture.Isolate after the organic layer, remove solvent, obtain coarse crystal.

Subsequently, in 100 milliliters of round-bottomed flasks, with the above coarse crystal that obtains, 1.9 gram (5 mmole) midbody compound F, 1.3 gram (12 mmole) potassium tert.-butoxide and 40 milligrams of (5% mole) PdCl ₂(PPh ₃) ₂Under argon atmospher, be dissolved in 30 milliliters of dimethylbenzene.Under 130 ℃ of heating, stir the gained mixture overnight.Reaction filters to isolate the precipitation crystal after finishing, and use methanol wash, and is dry and carry out purifying according to column chromatography (silica gel, hexane/toluene=1/1) method, obtains 0.9 and restrains yellow powder.This powder is confirmed as compound (58) (productive rate: 25%) by measuring according to NMR, IR and FD-MS.

Synthetic embodiment 9

Synthesizing of compound (59)

In 300 milliliter of four neck flask, under argon gas stream, 2 gram (10 mmole) 4-hydroxyl Stilbene and 5.2 are restrained (20 mmole) triphenylphosphine dissolved in 50 milliliters of dimethyl formamides.At room temperature, in this mixture, slowly drip and be dissolved in the gram of 5 in 50 milliliters of dimethyl formamides (20 mmole) iodine, react then.After reinforced the finishing, reaction mixture stirring under 200 ℃ is spent the night.After reaction was finished, dimethyl formamide was removed in vacuum distilling, then 200 ml waters was added in the resistates.Extract organic layer with toluene.Use the dried over mgso extraction liquid, use rotary evaporator to carry out vacuum concentration then, obtain a kind of oily compound.According to column chromatography (silica gel, hexane/toluene=1/1) this oily compound of method purifying, obtain 2.5 gram yellow powders.

In addition, in 100 milliliter of 2 neck flask, the amino Stilbene of 2 gram (10 mmole) 4-are dissolved in 20 milliliters of methylene dichloride.To wherein adding 2.5 gram (25 mmole) diacetyl oxides, then the gained mixture was at room temperature stirred 1 hour.Then, reaction solvent is removed in distillation, obtains a kind of oily compound.

In 300 milliliter of 2 neck flask, in this oily compound, add yellow powder, 3 gram (30 mmole) salt of wormwood, 0.06 gram (1 mmole) copper powder and 100 milliliters of oil of mirbane of obtaining more than 2.5 grams.Under 220 ℃ of heating, stirred the gained mixture 2 days.In by the resistates that distillation removal solvent obtains from above mixture, add 10 milliliters of glycol ethers and be dissolved in the solution that obtains in 100 ml waters by restraining potassium hydroxide with 30.Be reflected under 110 ℃ and spend the night.After reaction is finished, the mixture of ethyl acetate and water is added in this reaction mixture.Isolate after the organic layer, solvent is removed in distillation, obtains coarse crystal.

Subsequently, in 300 milliliter of 2 neck round-bottomed flask, with the above coarse crystal that obtains, 2.4 gram (5 mmole) midbody compound F, 1.3 gram (12 mmole) potassium tert.-butoxide and 40 milligrams of (5% mole) PdCl ₂(PPh ₃) ₂Under argon gas stream, be dissolved in 30 milliliters of dimethylbenzene.Stir the gained mixture under 130 ℃ of heating, reaction is spent the night then.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, and dry column chromatography (silica gel, the hexane/toluene=1/1) method of also passing through is carried out purifying, obtains 0.2 gram yellow powder.This powder is confirmed as compound (59) (productive rate: 5%) by measuring according to NMR, IR and FD-MS.

Synthetic embodiment 10 (compound (61))

Synthesizing of compound (61)

In 300 milliliter of four neck flask, under argon gas stream, pack into 9.7 gram (30 mmole) 4-bromine triphenylamines, 50 milliliters of toluene and 50 milliliters of ether are then with frozen water cooling gained mixture.At room temperature, in this cooling mixture, slowly drip the hexane solution (1.52 mol) of 22 milliliters of (33 mmole) n-Butyl Lithiums and the mixture of 100 milliliters of tetrahydrofuran (THF)s, stir the gained mixture then.With 4.3 gram (10 mmoles) 6, (penthacene adds after the reaction mixture 13-dibromo pentacene, and the gained mixture is stirred a night under same temperature.After reaction is finished, 500 ml waters are added in the reaction mixture, use the extracted with diethyl ether organic layer then.Use the dried over mgso extraction liquid, use rotary evaporator to carry out vacuum concentration then, obtain 7.4 gram oily compounds.

In 300 milliliter of 4 neck flask, the above compound of packing into, 6.6 gram (40 mmole) potassiumiodide and 100 milliliters of acetate are then with the heating 1 hour under refluxing of gained mixture.Reaction is cooled to room temperature with reaction mixture after finishing, and filters to isolate the precipitation crystal then.Water and washing with acetone gained crystal obtain 2.7 gram orange solids.This orange solids is confirmed as compound (61) (productive rate: 35%) by measuring according to NMR, IR and FD-MS.

Synthetic embodiment 10 (compound (62))

Midbody compound G's (5,11-diiodo-tetracene) is synthetic

In 500 milliliters of round-bottomed flasks, 50 gram (0.22 mmole) tetracene and the 200 milliliters of tetrachloroethane of packing into.At room temperature, be dissolved in the gram of 160 in 200 milliliters of tetracol phenixin (0.64 mole) iodine, then the gained mixture stirred 5 hours under heating to wherein slowly dripping.Filter to isolate the precipitation crystal, wash with 500 ml methanol then.With gained coarse crystal recrystallization from 200 milliliters of toluene, obtain 34 gram midbody compound G (productive rates: 40%).

Synthesizing of compound (62)

In 100 milliliter of four neck flask, under argon gas stream, the iodine of pack into 1.0 gram (41 mmole) magnesium, 1 milliliter of tetrahydrofuran (THF) and small pieces.Under the room temperature, be dissolved in the gram of 9.7 in 100 milliliters of tetrahydrofuran (THF)s (30 mmole) 4-bromine triphenylamine to wherein slowly dripping.After reinforced the finishing, the gained mixture was stirred 1 hour under 60 ℃ of heating, prepare Grignard reagent.

In 300 milliliter of 4 neck flask, under argon gas stream, with 4.8 gram (10 mmole) midbody compound G, 0.28 gram (0.4 mmole) PdCl ₂(PPh ₃) ₂AlH (iso-Bu) with 1.0 milliliters of (1 mmole) 1.0M ₂Toluene solution is dissolved in 50 milliliters of tetrahydrofuran (THF)s.At room temperature, the Grignard reagent that in this mixture, prepares more than the dropping.Temperature is raise, then one night of this reaction mixture of heating under refluxing.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, use washing with acetone then.With gained coarse crystal recrystallization from 100 milliliters of acetone, obtain 3.6 gram yellow powders.This powder is confirmed as compound (62) (productive rate: 50%) by measuring according to NMR, IR and FD-MS.

Embodiment 35

According to spin-coating method, the cleaning panes that will have the ITO electrode is coated with to comprise the above gained compound (58), 2 as luminescent material that weight ratio is 5:2:2, two (the 1-naphthyls)-1,3 of 5-, (by TEIJIN KASEI Co., Ltd. makes for 4-oxadiazole and polycarbonate resin; PANLITE K-1300) and be dissolved in composition in the tetrahydrofuran (THF), obtain the luminescent layer that thickness is 100 nanometers.On the gained luminescent layer, with the electrode of alloy formation thickness 150 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.This organic El device sends yellow orange coloured light, and luminosity is 130 (cd/m ²), high-high brightness is 14000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 1.2 (lm/W).

Embodiment 36

On cleaning panes with ITO electrode, the above compound that obtains (71) vacuum gas deposition is become luminescent material, make the luminescent layer of thickness 100 nanometers.On the gained luminescent layer, with the electrode of alloy formation thickness 100 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.This luminescent layer is 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.This organic El device sends orange-colored light and luminosity is 120 (cd/m ²), high-high brightness is 1800 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 0.3 (lm/W).

Embodiment 37

On cleaning panes with ITO electrode, the above compound that obtains (71) vacuum gas deposition is become luminescent material, form the luminescent layer of thickness 50 nanometers.Then, above-claimed cpd (Alq) gas deposition on the gained luminescent layer, is formed the electron injecting layer of thickness 10 nanometers.On formed layer, with the electrode of alloy formation thickness 100 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains, and obtains a kind of organic El device like this.Luminescent layer and electron injecting layer are 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.This organic El device sends orange-colored light, and luminosity is about 200 (cd/m ²), high-high brightness is 12000 (cd/m ²), and the luminous efficiency when applying the 5V volts DS is 1.0 (lm/W).

Embodiment 38-46

On cleaning panes with ITO electrode, luminescent material shown in the table 3 is carried out gas deposition, form the luminescent layer of thickness 80 nanometers.Then, above-claimed cpd (Alq) vacuum gas deposition to the luminescent layer of gained, is formed the electron injecting layer of thickness 20 nanometers.On formed layer, with the electrode of alloy formation thickness 150 nanometers, this alloy makes that by aluminum mixture and lithium lithium content is that 3% weight obtains.Obtain organic El device like this.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminescent properties of gained organic El device provides in table 3.Organic El device among all these embodiment all has excellent luminance, and for example high-high brightness is 5000 (cd/m ²) or higher.

Table 3

Embodiment 47

On cleaning panes with ITO electrode, above-claimed cpd (TPD74) vacuum gas deposition is become hole-injecting material, form the layer of thickness 60 nanometers.Then, above-claimed cpd (NPD) vacuum gas deposition is become the hole-transfer material, form the layer of thickness 20 nanometers.

Then, with 4,4 '-two (2, the 2-diphenylacetylene) biphenyl (DPVBi) and above-mentioned compound (58) carry out gas deposition simultaneously as luminescent material, and forming compound (58) content is that 5% weight and thickness are the layer of 40 nanometers.Compound (58) is also as fluorescent dopants.Then, above-claimed cpd (Alq) gas deposition is become the electronics injecting material, form the layer of thickness 20 nanometers.On formed layer,, form the layer of thickness 0.5 nanometer with the lithium fluoride gas deposition.Then, aluminium is carried out gas deposition, form the layer of thickness 100 nanometers.Like this, form a kind of electrode and obtain a kind of organic El device.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.This organic El device sends sodium yellow, and the luminosity when applying the 5V volts DS is about 600 (cd/m ²).If this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 2800 hours.

Embodiment 48

Same steps as according to embodiment 47 is made organic El device, just luminescent layer forms as the above-claimed cpd (Alq) of luminescent material with as the above-claimed cpd (61) of doping agent by same gas deposition constantly, and obtaining compound (61) content is the luminescent layer of 5% weight.This organic El device sends red light, and the luminosity when applying the 5V volts DS is about 240 (cd/m ²).If this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 3200 hours.

Comparative Examples 5

Make organic El device according to the same steps as that embodiment 35 is carried out, only be to use above-mentioned (compound of Comparative Examples 1) as luminescent material.

The luminosity of this organic El device when applying the 5V volts DS is about 60 (cd/m ²) and luminous efficiency be 0.34 (lm/W).Can not reach enough performances.The light that sends is blue light.

Comparative Examples 6

Make organic El device according to the same steps as that embodiment 37 is carried out, only be to use above-mentioned (compound of Comparative Examples 2) as luminescent material.

The luminosity of this organic El device when applying the 5V volts DS is 200 (cd/m ²) and luminous efficiency be 1.2 (lm/W).If but this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, the half-life is as short as 600 hours so.The light that sends is blue light.

Comparative Examples 7

Make organic El device according to the same steps as that embodiment 47 is carried out, only be to use above-mentioned (compound of Comparative Examples 1) alternative compounds (58).

The luminosity of this organic El device when applying the 5V volts DS is about 200 (cd/m ²).If but this organic El device is at 400 (cd/m ²) initial luminosity under by constant current driven, the half-life is as short as 700 hours so.The light that sends is blue light.

Synthetic embodiment 12 (compound (75))

Synthesizing of compound (75)

In 200 milliliters of three-necked flasks, with 2.16 gram (5.5 mmoles) 6,12-dibromo tetracene (40577-78-4), 0.06 gram (0.3 mmole) Pd (OAc) ₂, 0.23 the gram (1.1 mmole) P (tBu) ₃, 1.51g (15.7 mmole) NaOtBu and 1.89g (11.2 mmole)

Under argon gas stream, be dissolved in 25 milliliters of toluene.With the gained mixture 120 ℃ of following heated and stirred and reacted 7 hours.After reaction is finished, reaction mixture is placed cooling.Filter to isolate after the red crystals,, obtain 3.02 gram red powder with toluene and this crystal of water washing, vacuum-drying then.This powder is confirmed as compound (75) (productive rate: 96%) by measuring according to NMR, IR and FD-MS.NMR (CDCl ₃, the data that obtain in TMS) are as follows: 6.8-7.0 (m, 2H), 7.0-7.4 (m, 10H), 7.8-7.9 (m, 1H), 8.0-8.1 (m, 1H) and 8.85 (s, 1H).

Embodiment 49

Then, will carry out gas deposition simultaneously as the above-claimed cpd (Alq) of luminescent material with as the above-claimed cpd (75) of doping agent, forming compound (75) content is that 2% weight and thickness are the layer of 40 nanometers.Then, above-claimed cpd (Alq) gas deposition is become the electronics injecting material, form the layer of thickness 20 nanometers.At the gas deposition lithium fluoride and after forming the layer of thickness 20 nanometers, aluminium carried out gas deposition and form the layer of thickness 100 nanometers.Form electrode like this and obtained a kind of organic El device.With the upper strata 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.Luminosity height to the 500 (cd/m of this organic El device when applying the 8V volts DS ²), and the light that sends is orange-colored light.Luminosity height to the 500 (cd/m of this organic El device when applying the 8V volts DS ²), and the light that sends is orange-colored light.If this organic El device is at 500 (cd/m ²) initial luminosity under by constant current driven, the half-life of this organic El device was long especially, above 2000 hours.

Embodiment 50

Same steps as during according to embodiment 49 is made organic El device, only is to use above-claimed cpd (86) as doping agent alternative compounds (75).If this organic El device is at 500 (cd/m ²) initial luminosity under by constant current driven, the half-life of this organic El device is grown to 2000 hours.The light that sends is bright red coloured light.

Embodiment 51

Same steps as during according to embodiment 49 is made organic El device, only is to use above-claimed cpd (82) as doping agent alternative compounds (75).If this organic El device is by constant current driven, the initial luminosity of this organic El device is 500 (cd/m ²) and the half-life grow to 2800 hours or higher.The light that sends is red light.

Synthetic embodiment 13 (compound (100))

Midbody compound H's is synthetic

In 1 liter of three-necked flask of condenser is housed, with 22.7 gram (0.1 mole) 4-phthalate bromine acid anhydrides and 42.4 gram (0.4 mole) yellow soda ash at the argon gas stream low suspension in 300 ml waters, then 60 ℃ down heating to dissolve each component.After this mixture dissolving, the gained mixture is cooled to room temperature.In this cooling mixture, add 18.3 gram (0.15 mole) phenyl-boron dihydroxides and 0.7 gram (3% mole) acid chloride, then the gained mixture is at room temperature stirred a night.Reaction adds the crystal that entry goes out with separated and dissolved after finishing.Filter and remove after the catalyzer, add concentrated hydrochloric acid to be settled out crystal.Filter to isolate crystal and washing.The gained dissolution of crystals in ethyl acetate, is extracted organic layer then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then, obtain 23.7 gram (productive rates: target compound 98%), midbody compound H.

Midbody compound I's is synthetic

In 500 milliliters of eggplant type flasks of condenser were housed, 23.7 gram (98 mmole) midbody compound H and 200 ml acetic anhydride of packing into stirred the gained mixture 3 hours down at 80 ℃ then.After reaction was finished, excessive acetic anhydride via was removed in distillation, obtained 22 gram (productive rates: target compound 10%), midbody compound I.

Midbody compound J's is synthetic

In 500 milliliters of three-necked flasks of condenser are housed, 7.7 gram (50 mmole) biphenyl of under argon gas stream, packing into, 13.4 gram (0.1 mmole) Aluminum chloride anhydrouss and 200 milliliters 1, the 2-ethylene dichloride is cooled to 0 ℃ with the gained mixture then.In this cooling mixture, slowly add 22 gram (98 mmole) midbody compound I, then the gained mixture was stirred 2 hours down at 40 ℃.Reaction adds frozen water in this reaction mixture after finishing, and uses chloroform extraction gained mixture then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then, obtain 19.0 gram (productive rates: target compound 100%), midbody compound J.

Midbody compound K's is synthetic

In 500 milliliters of eggplant type flasks of condenser are housed, add 200 milliliters of Tripyrophosphoric acid and be heated to 150 ℃.Then, add 19 gram (50 mmole) midbody compound J on a small quantity in batches, then the gained mixture was stirred 3 hours under same temperature.Reaction adds frozen water in this reaction mixture after finishing, and uses chloroform extraction gained mixture then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then.The gained coarse crystal carries out purifying by column chromatography (silica gel, chloroform/methanol=99/1), obtains 19 gram (productive rates: target compound 55%), midbody compound K.

Midbody compound L's is synthetic

In 500 milliliters of eggplant type flasks of condenser are housed, under argon gas stream, add 19.0 gram (28 mmole) midbody compound K, 0.19 gram (1 mmole) tin chloride, 100 milliliters of acetate and 50 milliliters of concentrated hydrochloric acids, then the gained mixture heating up was refluxed 2 hours.Reaction is cooled off this reaction mixture with frozen water after finishing, and isolates the precipitation crystal, and washing obtains 19 gram (productive rates: target compound 100%), midbody compound L.

Midbody compound M's is synthetic

In 500 milliliters of three-necked flasks of condenser are housed, under argon gas stream, add 19.0 gram (28 mmole) midbody compound L, 16 gram (60 mmole) triphenylphosphine and 200 milliliters of dimethyl formamides.Be dissolved in the gram of 9.6 in 50 milliliters of dimethyl formamides (60 mmole) iodine to wherein slowly dripping, then the gained mixture stirred 8 hours under 200 ℃ of heating.Reaction is cooled off this reaction mixture with frozen water after finishing, and isolates the precipitation crystal then.Gained crystal water and methyl alcohol are washed, obtain 6.7 gram (productive rates: target compound 50%), midbody compound M.

Synthesizing of compound (100)

In 200 milliliters of three-necked flasks of condenser are housed, under argon gas stream, add 4.9 gram (10 mmole) midbody compound M, 5.1 gram (30 mmole) diphenylamines, 0.14 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.91 gram (3% mole) three-neighbour-tolylphosphine, 2.9 gram (30 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then, obtains 4.0 gram yellow powders.The gained powder by according to NMR,

Measure with FD-MS and confirm as compound (100) (productive rate: 60%).

The synthesis path of the chemical structure of midbody compound and compound (100) is as follows.

Synthetic embodiment 14 (compound (101))

Midbody compound N's is synthetic

In 500 milliliters of eggplant type flasks of condenser are housed, under argon gas stream, add 12 gram (50 mmoles) 2,6-dihydroxyanthraquinone, 42.5 gram (0.3 mole) methyl-iodides, 17 gram (0.3 mole) potassium hydroxide and 200 milliliters of methyl-sulphoxides at room temperature stirred the gained mixture 2 hours then.Reaction filters to isolate the precipitation crystal after finishing.With 100 ml methanol washing gained crystal, obtain 10.7 gram (productive rates: target compound 80%), midbody compound N.

Midbody compound O's is synthetic

In 500 milliliters of three-necked flasks of condenser are housed, under argon gas stream, add 10.7 gram (40 mmole) midbody compound N and 200 milliliters of anhydrous tetrahydro furans, the gained mixture is cooled to-40 ℃ then.The phenyl lithium hexane solution of 3 milliliters of (80 mmole) 1.5M of Dropwise 5 slowly in this cooling mixture.After reinforced the finishing, reaction mixture is at room temperature stirred a night.Reaction filters to isolate the precipitation crystal after finishing, and uses 100 ml methanol and 100 milliliters of washing with acetones then.The glycol coarse crystal of gained is used for following reaction and need not to be further purified.

In 500 milliliters of eggplant type flasks of condenser were housed, the coarse crystal that obtains more than the adding, 100 milliliter of 57% aqueous solution of hydrogen iodide and 200 milliliters of acetate refluxed the gained mixture heating up 3 hours then.Reaction is cooled to room temperature, adds a spot of Hypophosporous Acid, 50 then to react away excessive hydrogen iodide.Filter to isolate the precipitation crystal, order is washed with 100 ml waters, 100 ml methanol and 100 milliliters of acetone then, obtains 10.1 gram (productive rates: target compound 70%), midbody compound 0.

Midbody compound P's is synthetic

In 500 milliliters of eggplant type flasks of condenser are housed, under argon gas stream, add 10.1 gram (28 mmole) midbody compounds, 0,7.9 gram (30 mmole) triphenylphosphine and 200 milliliters of dimethyl formamides.In the gained mixture, slowly drip and be dissolved in the gram of 4.8 in 50 milliliters of dimethyl formamides (30 mmole) bromine, then the gained mixture was stirred 8 hours under 200 ℃ of heating.Reaction is cooled off this reaction mixture with frozen water after finishing, and filters to isolate the precipitation crystal then.Gained crystal water and methyl alcohol are washed, obtain 8.2 gram (productive rates: target compound 60%), midbody compound P.

Synthesizing of compound (101)

In 200 milliliters of three-necked flasks of condenser are housed, under argon gas stream, add 4.9 gram (30 mmole) midbody compound P, 5.1 gram (30 mmole) diphenylamines, 0.14 gram (1.5% mole) three (dibenzalacetone)-two palladiums, 0.91 gram (3% mole) three-neighbour-tolylphosphine, 2.9 gram (30 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then, obtains 4.0 gram yellow powders.The gained powder by according to NMR,

Measure with FD-MS and confirm as compound (101) (productive rate: 60%).

The synthesis path of the chemical structure of midbody compound and compound (101) is as follows:

Synthetic embodiment 15 (compound (93))

Midbody compound Q's is synthetic

In being furnished with 300 milliliters of three-necked flasks of condenser, 11.7 gram (50 mmole) the 2-bromo biphenyls of under argon gas stream, packing into, 19 gram (0.2 mole) aniline, 0.69 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.46 gram (3% mole) three-neighbour-tolylphosphine, 7.2 gram (75 mmole) sodium tert-butoxide and 100 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 9.8 gram (productive rates: target compound 80%), midbody compound Q.

Synthesizing of compound (93)

In being furnished with 200 milliliters of three-necked flasks of condenser, 2.4 gram (10 mmoles) 9 of under argon gas stream, packing into, 10-dibromoanthracene, 7.4 gram (30 mmole) midbody compound Q, 0.14 gram (1.5% mole) three (dibenzalacetone) two palladiums, 0.91 gram (3% mole) three-neighbour-tolylphosphine, 2.9 gram (30 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then, obtains 4.3 gram yellow powders.The gained powder is confirmed as compound (93) (productive rate: 65%) by measuring according to NMR, IR and FD-MS.

The synthesis path of the chemical structure of midbody compound and compound (93) is as follows:

Synthetic embodiment 16 (compound (95))

Midbody compound R's is synthetic

In being furnished with 1 liter of three-necked flask of condenser, under argon gas stream, pack into 34 gram (0.2 mole) 3-phenylphenols, 58 gram (0.22 mmole) triphenylphosphine and 300 milliliters of dimethyl formamides.In the gained mixture, slowly drip and be dissolved in the gram of 35 in 100 milliliters of dimethyl formamides (0.22 mmole) bromine, then the gained mixture was stirred 8 hours down at 200 ℃.Reaction is cooled off this reaction mixture with frozen water after finishing, and filters to isolate the precipitation crystal then.Water and methanol wash gained crystal obtain 37 gram (productive rates: target compound 80%), midbody compound R.

Midbody compound S's is synthetic

In being furnished with 300 milliliters of three-necked flasks of condenser, 19 gram (0.2 mmole) aniline of under argon gas stream, packing into, 0.69 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.46 gram (3% mole) three-neighbour-tolylphosphine, 7.2 gram (75 mmole) sodium tert-butoxide and 100 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 9.8 gram (productive rates: target compound 80%), midbody compound S.

Synthesizing of compound (95)

In being furnished with 200 milliliters of three-necked flasks of condenser, 2.4 gram (10 mmoles) 9 of under argon gas stream, packing into, 10-dibromoanthracene, 7.4 gram (30 mmole) midbody compound S, 0.14 gram (1.5% mole) three (dibenzalacetone) two palladiums, 0.91 gram (3% mole) three-neighbour-tolylphosphine, 2.9 gram (30 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then, obtains 4.2 gram yellow powders.The gained powder by according to NMR,

Measure with FD-MS and confirm as compound (95) (productive rate: 70%).

The synthesis path of the chemical structure of midbody compound and compound (95) is as follows:

Synthetic embodiment 17 (compound (104))

Midbody compound T's is synthetic

In being furnished with 300 milliliters of three-necked flasks of condenser, 23 grams of under argon gas stream, packing into (

Mole) 4-bromo biphenyl, 9.8 gram (50 mmole) amino Stilbene, 0.69 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.46 gram (3% mole) three-neighbour-tolylphosphine, 7.2 gram (75 mmole) sodium tert-butoxide and 100 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 13.9 gram (productive rates: target compound 80%), midbody compound T.

Synthesizing of compound (104)

In being furnished with 200 milliliters of three-necked flasks of condenser, 2.4 gram (10 mmoles) 9 of under argon gas stream, packing into, 10-dibromoanthracene, 7.4 gram (30 mmole) midbody compound T, 0.14 gram (1.5% mole) three (dibenzalacetone) two palladiums, 0.91 gram (3% mole) three-neighbour-tolylphosphine, 2.9 gram (30 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then, obtains 4.5 gram yellow powders.The gained powder by according to NMR,

Measure with FD-MS and confirm as compound (104) (productive rate: 70%).

The synthesis path of the chemical structure of midbody compound and compound (104) is as follows:

Synthetic embodiment 18 (compound (105))

Midbody compound U's is synthetic

In being furnished with 500 milliliters of three-necked flasks of condenser, 25 gram (0.1 mole) triphenylamines of under argon gas stream, packing into, 18 gram (0.1 mole) N-bromosuccinimides, 0.82 gram (5% mole) 2,2 '-Diisopropyl azodicarboxylate and 200 milliliters of dimethyl formamides.The gained mixture was stirred 4 hours under 110 ℃ of heating.After reaction is finished, filter and remove impurity, use rotary evaporator that filtrate is carried out vacuum concentration then.The gained coarse crystal carries out purifying by column chromatography (silica gel, methylene dichloride), obtains 19 gram (productive rates: target compound 60%), midbody compound U.

Midbody compound V's is synthetic

In being furnished with 1 liter of three-necked flask of condenser, 1.6 gram (66 mmole) magnesium, small pieces iodine and the 100 milliliters of tetrahydrofuran (THF)s of under argon gas stream, packing into.At room temperature stirred the gained mixture 30 minutes, and dripped then and be dissolved in the gram of 19 in 300 milliliters of tetrahydrofuran (THF)s (60 moles) midbody compound U.After reinforced the finishing, reaction mixture was stirred 1 hour under 60 ℃ of heating, prepare Grignard reagent like this.

In being furnished with 1 liter of three-necked flask of condenser, 42 gram (0.18 mmoles) 1 of packing under argon gas stream, 3-dibromobenzene, 2.1 gram (5% mole) dichloros two (triphenylphosphine) close toluene solution and 200 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 6 milliliters of (6 mmole) 1M.The Grignard reagent of preparation stirs a night with the gained mixture heating up then more than dripping in this mixture.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, use washing with acetone then, obtain 14 gram (productive rates: target compound 60%), midbody compound V.

Synthesizing of compound (105)

In being furnished with 500 milliliters of three-necked flasks of condenser, 0.8 gram (33 mmole) magnesium, small pieces iodine and the 50 milliliters of tetrahydrofuran (THF)s of under argon gas stream, packing into.At room temperature stirred the gained mixture 30 minutes, and dripped then and be dissolved in the gram of 12 in 100 milliliters of tetrahydrofuran (THF)s (30 mmole) midbody compound V.After reinforced the finishing, reaction mixture was stirred 1 hour under 60 ℃ of heating, prepare Grignard reagent like this.

In being furnished with 500 milliliters of three-necked flasks of condenser, 3.4 gram (10 mmoles) 9 of packing under argon gas stream, 10-dibromoanthracene, 0.4 gram (5% mole) dichloro two (triphenylphosphine) close toluene solution and 100 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 0.46 gram (3% mole) three-neighbour-tolylphosphine, 1 milliliter of (1 mmole) 1M.At room temperature, the Grignard reagent of preparation more than dripping in the gained mixture refluxes the gained mixture then and spends the night.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, wash in proper order with 50 ml methanol and 50 milliliters of acetone then, obtain 4.1 gram yellow powders.The gained powder by according to NMR,

Measure with FD-MS and confirm as compound (105) (productive rate: 50%).

The synthesis path of the chemical structure of midbody compound and compound (105) is as follows:

Compound (105)

Synthetic embodiment 19 (compound (122))

Midbody compound W's is synthetic

In being furnished with 300 milliliters of three-necked flasks of condenser, 19 gram (80 mmoles) 1 of under argon gas stream, packing into, 3-dibromobenzene, 6.5 gram (20 mmole) diphenylamines, 0.27 gram (1.5% mole) three (dibenzalacetone) two palladiums, 0.18 gram (3% mole) three-neighbour-tolylphosphine, 2.9 gram (30 mmole) sodium tert-butoxide and 100 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 4.9 gram (productive rates: target compound 75%), midbody compound W.

Synthesizing of compound (122)

In being furnished with 300 milliliters of three-necked flasks of condenser, 0.5 gram (20 mmole) magnesium, small pieces iodine and the 50 milliliters of tetrahydrofuran (THF)s of under argon gas stream, packing into.At room temperature stirred the gained mixture 30 minutes, and dripped then and be dissolved in the gram of 4.9 in 100 milliliters of tetrahydrofuran (THF)s (15 mmole) midbody compound W.After reinforced the finishing, reaction mixture was stirred 1 hour under 60 ℃ of heating, prepare Grignard reagent like this.

In being furnished with 500 milliliters of three-necked flasks of condenser, 1.7 gram (5 mmoles) 9 of packing under argon gas stream, 10-dibromoanthracene, 0.2 gram (5% mole) dichloro two (triphenylphosphine) close toluene solution and 100 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 0.5 milliliter of (0.5 mmole) 1M.At room temperature, the Grignard reagent of preparation more than dripping in this mixture stirs the gained mixture heating up then and spends the night.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, wash in proper order with 50 ml methanol and 50 milliliters of acetone then, obtain 1.7 gram yellow powders.The gained powder is confirmed as compound (122) (productive rate: 50%) by measuring according to NMR, IR and FD-MS.

The synthesis path of the chemical structure of midbody compound and compound (122) is as follows:

Compound (122)

Synthetic embodiment 20 (compound (123))

Midbody compound X's is synthetic

In being furnished with 300 milliliters of three-necked flasks of condenser, 16 gram (0.1 mole) bromobenzenes of under argon gas stream, packing into, 9.8 gram (50 mmole) amino Stilbene, 0.69 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.46 gram (3% mole) three-neighbour-tolylphosphine, 7.2 gram (75 mmole) sodium tert-butoxide and 100 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 11 gram (productive rates: target compound 80%), midbody compound X.

Midbody compound Y's is synthetic

In being furnished with 500 milliliters of three-necked flasks of condenser, 38 gram (0.16 mole) bromobenzenes of under argon gas stream, packing into, 11 gram (40 mmole) midbody compound X, 0.55 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.37 gram (3% mole) three-neighbour-tolylphosphine, 5.8 gram (60 mmole) sodium tert-butoxide and 300 milliliters of dry toluenes.The gained mixture stirred under 120 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and washs with 100 ml methanol then.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 13 gram (productive rates: target compound 75%), midbody compound Y.

Synthesizing of compound (123)

In being furnished with 300 milliliters of three-necked flasks of condenser, 0.97 gram (40 mmole) magnesium, small pieces iodine and the 50 milliliters of tetrahydrofuran (THF)s of under argon gas stream, packing into.At room temperature stirred the gained mixture 30 minutes, and dripped then and be dissolved in the gram of 12 in 100 milliliters of tetrahydrofuran (THF)s (30 mmole) midbody compound Y.After reinforced the finishing, reaction mixture was stirred 1 hour under 60 ℃ of heating, prepare Grignard reagent like this.

In being furnished with 500 milliliters of three-necked flasks of condenser, 3.4 gram (10 mmoles) 9 of packing under argon gas stream, 10-dibromoanthracene, 0.4 gram (5% mole) dichloro two (triphenylphosphine) close toluene solution and 100 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 1 milliliter of (1 mmole) 1M.At room temperature, the Grignard reagent of preparation more than dripping in this mixture refluxes the gained mixture then and spends the night.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, wash in proper order with 50 ml methanol and 50 milliliters of acetone then, obtain 5.4 gram yellow powders.The gained powder is confirmed as compound (123) (productive rate: 50%) by measuring according to NMR, IR and FD-MS.

The synthesis path of the chemical structure of midbody compound and compound (123) is as follows:

Synthetic embodiment 21 (compound (124))

Synthesizing of compound (124)

In being furnished with 500 milliliters of three-necked flasks of condenser, under argon gas stream, pack into 2.5 the gram (5 mmoles) 10,10 '-two bromo-9,9 '-dianthranide, 0.2 gram (5% mole) dichloro two (triphenylphosphine) close toluene solution and 100 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 0.5 milliliter of (0.5 mmole) 1M.At room temperature, in this mixture, drip the Grignard reagent of preparation in synthetic embodiment 19, the gained mixture is refluxed spend the night then.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, wash in proper order with 50 ml methanol and 50 milliliters of acetone then, obtain 2.0 gram yellow powders.The gained powder is confirmed as compound (124) (productive rate: 60%) by measuring according to NMR, IR and FD-MS.

The synthesis path of compound (124) is as follows:

Compound (124)

Synthetic embodiment 22 (compound (125))

Synthesizing of compound (125)

In being furnished with 500 milliliters of three-necked flasks of condenser, 1.9 grams of under argon gas stream, packing into

Mmole) 6, the 12-dibromo

0.2 gram (5% mole) dichloro two (triphenylphosphine) closes toluene solution and 100 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 0.1 milliliter of (0.5 mmole) 1M.At room temperature, in this mixture, drip the Ge Shi examination of preparation in synthetic embodiment 19

Then the gained mixture heating up is stirred and spend the night.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, wash in proper order with 50 ml methanol and 50 milliliters of acetone then, obtain 2.1 gram yellow powders.The gained powder is confirmed as compound (125) (productive rate: 60%) by measuring according to NMR, IR and FD-MS.

The synthesis path of compound (125) is as follows:

Synthetic embodiment 23 (compound (126))

Synthesizing of compound (126)

Mmole) 5,12-dibromo tetracene, 0.2 gram (5% mole) dichloro two (triphenylphosphine) close toluene solution and 100 milliliters of tetrahydrofuran (THF)s of the diisobutylaluminium hydride of palladium, 0.5 milliliter of (0.5 mmole) 1M.At room temperature, in this mixture, drip the Grignard reagent of preparation in synthetic embodiment 19, the gained mixture heating up is stirred spend the night then.Reaction is cooled off reaction liquid with frozen water after finishing.Filter to isolate the precipitation crystal, use 50 ml methanol and 50 milliliter third then

The order washing obtains 2.1 gram yellow powders.The gained powder by according to NMR, IR and

Measure and confirm as compound (126) (productive rate: 60%).

The synthesis path of compound (126) provides as follows.

Embodiment 52

Being of a size of on 25 millimeters * 75 millimeters * 1.1 millimeters the glass substrate, form the transparent anode of the indium tin oxides film of thickness 10 nanometers, be used in combination ultraviolet ray and ozone then and cleaned 1 minute.

This glass substrate is placed in the device (by NIPPON SHINKUGIJUTU Co., Ltd. makes) that is used for the vacuum gas deposition, pressure is reduced to about 10 then ^-4Pa.Above-mentioned TPD7 is carried out gas deposition with the speed of 0.2 nm/sec, form the layer of thickness 60 nanometers.Then, the TPD78 that will have structure shown below carries out gas deposition with the speed of 0.2 nm/sec, forms the layer of thickness 20 nanometers.

On the layer of above formation, the DPVDPAN and the above-claimed cpd (100) that will have structure shown below carry out gas deposition simultaneously as luminescent material, form the luminescent layer of thickness 40 nanometers.The gas deposition speed of DPVDPAN is 0.4 nm/sec, and the gas deposition speed of compound (100) is 0.01 nm/sec.On the layer of above formation, above-mentioned Alq is carried out gas deposition with the speed of 0.2 nm/sec.At last, aluminium and lithium are carried out gas deposition simultaneously, form the negative electrode of thickness 150 nanometers.Obtain a kind of organic El device like this.The gas deposition speed of aluminium is 1 nm/sec, and the gas deposition speed of lithium is 0.004 nm/sec.

Estimate the performance of gained organic El device.The luminosity of measurement under voltage shown in the table 4, and calculate luminous efficiency.Observe glow color.Under nitrogen gas stream, at 500 (cd/m ²) initial luminosity under, by this organic El device of constant current driven, measure the half-life then, that is, 250 (cd/m are reduced in brightness ²) time.The results are shown in the table 4.

Embodiment 53-62

Same procedure according to embodiment 52 is made organic El device, only is to use compound shown in the table 4 as luminescent material alternative compounds (100), assess performance then.The result provides in table 4.

Comparative Examples 8

Same steps as according to embodiment 52 is made organic El device, only is to use diamine compound shown below as luminescent material alternative compounds (100), assess performance then.The result provides in table 4.

Table 4

As shown in table 4, compare with Comparative Examples 8 organic El devices that wherein use diamine compound, it is longer wherein to use compound shown in general formula of the present invention [9] and [10] to have a more excellent luminosity and luminous efficiency and life-span as the embodiment 52-62 organic El device of luminescent material or hole-transfer material.

Synthetic embodiment 24 (compound a)

Midbody compound A's is synthetic

In 500 milliliters of three-necked flasks, right-bromobenzaldehyde, 50 gram (0.22 mmole) benzylphosphonic acid diethyl ester and the 200 milliliters of methyl-sulphoxides of 50 grams (0.27 mole) of under argon gas stream, packing into.To wherein add 30 gram (0.27 mole) potassium tert.-butoxides on a small quantity in batches.The gained mixture at room temperature stirred spend the night.Reaction is poured reaction liquid in 500 ml waters into after finishing, and uses ethyl acetate extraction then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then.With gained coarse crystal recrystallization from 100 milliliters of ethyl acetate, obtain 46 gram (productive rates: midbody compound A 81%).

Midbody compound B's is synthetic

In being furnished with 300 milliliters of three-necked flasks of condenser, 10 gram (38 mmole) the midbody compound A that under argon gas stream, pack into, 14 gram (150 mmole) aniline, 0.53 gram (1.5% mole) three (dibenzalacetone), two palladiums, 0.35 gram (3% mole) three-neighbour-tolylphosphine, 7.4 gram (77 mmole) sodium tert-butoxide and 100 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal, and washs with 100 ml methanol after finishing.With gained coarse crystal recrystallization from 50 milliliters of ethyl acetate, obtain 7.7 gram (productive rates: midbody compound B 73%).

Midbody compound C's is synthetic

In 100 milliliters of eggplant type flasks of condenser are housed, pack into 12.5 gram (50 mmole) 4-bromo benzyl bromos and 12.5 gram (75 mmole) triethyl-phosphites.The gained mixture was stirred 7 hours under 100 ℃ of heating.After reaction was finished, excessive triethyl-phosphite was removed in vacuum distilling, obtained 15.4 gram midbody compound C.Midbody compound C is used for following reaction and need not to be further purified.

Midbody compound D's is synthetic

In 300 milliliters of three-necked flasks, right-bromobenzaldehyde, 15.4 gram (50 mmole) midbody compound C and the 100 milliliters of methyl-sulphoxides of 9.2 grams (50 mmole) of under argon gas stream, packing into.To wherein add 6.7 gram (60 mmole) potassium tert.-butoxides on a small quantity in batches, the gained mixture is at room temperature stirred spend the night then.Reaction is poured reaction liquid in 200 ml waters into after finishing, and uses ethyl acetate extraction then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then.With 100 ml methanol washing gained crystal, obtain 13 gram (productive rates: midbody compound D 77%).

Synthesizing of compound a

In being furnished with 200 milliliters of three-necked flasks of condenser, 4 gram (15 mmole) the midbody compound B that under argon gas stream, pack into, 2 gram (6 mmole) midbody compound D, 0.16 gram (3% mole) three (dibenzalacetone) two palladiums, 0.22 gram (6% mole) (S)-BINAP, 1.4 gram (15 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, then 60 ℃ of one nights of following heat drying.The gained coarse crystal carries out purifying by column chromatography (silica gel, hexane/toluene=8/2), obtains 1.4 gram yellow powders.The gained powder by measure according to NMR, IR and FD-MS (field desorption(FD) mass spectrum) confirm as compound a (productive rate: 32%, ¹Among the H NMR (90Hz): δ 7.0-7.4ppm (42H, m)).The NMR figure of compound a provides in Fig. 1.

The chemical reaction that is used to obtain compound a is as follows:

Synthetic embodiment 25 (compound b)

Midbody compound E's is synthetic

In 300 milliliters of three-necked flasks, right-toluic aldehyde, 15.4 gram (50 mmole) midbody compound C and the 100 milliliters of methyl-sulphoxides of 6 grams (50 mmole) of under argon gas stream, packing into.To wherein add 6.7 gram (60 mmole) potassium tert.-butoxides on a small quantity in batches, the gained mixture is at room temperature stirred spend the night then.Reaction is poured reaction liquid in 200 ml waters into after finishing, and uses ethyl acetate extraction then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then.The gained crystal is washed with 100 ml methanol, obtain 9.2 gram (productive rates: midbody compound E 67%).

Synthesizing of compound b

In being furnished with 200 milliliters of three-necked flasks of condenser, under argon gas stream, pack into 4 gram (15 mmole) midbody compound E, 2 gram (6 mmole) N, N '-diphenylbenzidine, 0.16 gram (3% mole) three (dibenzalacetone) two palladiums, 0.22 gram (6% mole) (S)-BINAP, 1.4 gram (15 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, then 60 ℃ of one nights of following heat drying.The gained coarse crystal carries out purifying by column chromatography (silica gel, hexane/toluene=8/2), obtains 2.5 gram yellow powders.The gained powder by according to NMR,

Measure with FD-MS and confirm as compound b (productive rate: 58%, ¹Among the H NMR (90Hz): δ 7.0-7.4ppm (40H, m), the outer 2.34ppm (6H, s)) of δ.The NMR figure of compound b provides in Fig. 2.

The chemical reaction that is used to obtain compound b is as follows:

Compound b

Synthetic embodiment 26 (compound c)

Synthesizing of compound c

In being furnished with 200 milliliters of three-necked flasks of condenser, under argon gas stream, pack into 4 gram (15 mmole) midbody compound B, 1.7 gram (6 mmoles) 1,4-dibromine naphthalene, 0.16 gram (3% mole) three (dibenzalacetone) two palladiums, 0.22 gram (6% mole) (S)-BINAP, 1.4 gram (15 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, then 60 ℃ of one nights of following heat drying.The gained coarse crystal carries out purifying by column chromatography (silica gel, hexane/toluene=8/2), obtains 2.0 gram yellow powders.The gained powder by measure according to NMR, IR and FD-MS confirm as compound c (productive rate: 50%, ¹Among the H NMR (90Hz): δ 7.0-7.4ppm (68H, m)).

The chemical reaction that is used to obtain compound c is as follows:

Compound c

Synthetic embodiment 27 (compound d)

Synthesizing of compound d

In being furnished with 200 milliliters of three-necked flasks of condenser, 4 gram (15 mmole) the midbody compound B, 2 that pack under argon gas stream restrain (6 mmoles) 9,10-dibromoanthracene, 0.16 gram (3% mole) three (dibenzalacetone), two palladiums, 0.07 gram (6% mole) tri-butyl phosphine, 1.4 gram (15 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, then 60 ℃ of one nights of following heat drying.The gained coarse crystal carries out purifying by column chromatography (silica gel, hexane/toluene=8/2), obtains 1.9 gram yellow powders.The gained powder by measure according to NMR, IR and FD-MS confirm as compound d (productive rate: 44%, ¹Among the H NMR (90Hz): δ 7.0-7.4ppm (40H, m)).

The chemical reaction that is used to obtain compound d is as follows:

Compound d

Synthetic embodiment 28 (Verbindung)

Midbody compound E's is synthetic

In 300 milliliters of three-necked flasks, 10.4 grams (50 mmole) of packing under argon gas stream are trans-4-Stilbene formaldehyde, 15.4 gram (50 mmole) midbody compound C and 100 milliliters of methyl-sulphoxides.To wherein add 6.7 gram (60 mmole) potassium tert.-butoxides on a small quantity in batches, the gained mixture is at room temperature stirred spend the night then.Reaction is poured reaction liquid in 200 ml waters into after finishing, and uses ethyl acetate extraction then.With the extraction liquid dried over mgso, use rotary evaporator to carry out vacuum concentration then.With 100 ml methanol washing gained crystal, obtain 12.5 gram (productive rates: midbody compound F 69%).

Synthesizing of Verbindung

In being furnished with 200 milliliters of three-necked flasks of condenser, 5.4 gram (15 mmole) the midbody compound F, 2 that pack under argon gas stream restrain (6 mmole) N, N '-diphenylbenzidine, 0.16 gram (3% mole) three (dibenzalacetone), two palladiums, 0.11 gram (6% mole) three-neighbour-tolylphosphine, 1.4 gram (15 mmole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, then 60 ℃ of one nights of following heat drying.The gained coarse crystal carries out purifying by column chromatography (silica gel, hexane/toluene=6/4), obtains 1.0 gram yellow powders.The gained powder by measure according to NMR, IR and FD-MS confirm as Verbindung (productive rate: 19%, ¹H NMR is (among the 90Hz: δ 7.0-7.5ppm (52H, m)).The NMR figure of Verbindung as shown in Figure 3.

The chemical reaction that is used to obtain Verbindung is as follows:

Verbindung

Compound f's is synthetic

In being furnished with 200 milliliters of three-necked flasks of condenser, 7.8 grams (3 of under argon gas stream, packing into

Mmole) midbody compound A, 1.7 gram (6 mmoles) 4,4 '-diamino Stilbene carbonic acid gas (carbon dioxide), 0.16 gram (3% mole) three (dibenzalacetone) two palladiums (tris (dibenzylideneacetone) dipalladium), 0.22 gram (6% mole) (S)-BINAP, 9.6 gram (0.1 mole) sodium tert-butoxide and 50 milliliters of dry toluenes.The gained mixture stirred under 100 ℃ of heating spend the night.Reaction filters to isolate the precipitation crystal after finishing, and uses methanol wash, then 60 ℃ of one nights of following heat drying.The gained coarse crystal passes through

Chromatogram (silica gel, hexane/toluene=6/4) is carried out purifying, obtains 2.0 gram yellow powders.The gained powder by measure according to NMR, IR and FD-MS confirm as compound f (productive rate:

¹Among the H NMR (90Hz): δ is at ground 7.0-7.5ppm (54H, m)).

The chemical reaction that is used to obtain compound f is as follows:

Compound f

Embodiment 63

On cleaning panes, with above-claimed cpd TPD74 vacuum vapour phase with ITO electrode Amass into hole-injecting material, form the layer of thickness 60 nanometers.

Then, above-claimed cpd NPD vacuum gas deposition is become the hole-transfer material, form the layer of thickness 20 nanometers.

Then, as luminescent material, with stilbene derivative 4,4 '-two (2, the 2-diphenylacetylene) biphenyl (DPVBi) and above-claimed cpd a carry out gas deposition simultaneously, and forming compound a content is that 2% weight and thickness are the layer of 40 nanometers.Compound a is as fluorescent dopants or luminescence center.On formed layer, above-mentioned Alq gas deposition is become the electronics injecting material, and form the layer of thickness 20 nanometers.With the lithium fluoride gas deposition and after forming the layer of thickness 0.5 nanometer, aluminium carried out gas deposition and form the layer of thickness 100 nanometers.Like this, formed electrode and obtain a kind of organic El device.These layers are 10 ^-6Under the torr vacuum, when substrate temperature keeps room temperature, form by gas deposition.The luminosity of this organic El device when applying the 6V volts DS is 100 (cd/m ²) and luminous efficiency be 2.1 (lm/W).Color coordinates is (0.146,0.140), can send highly purified blue light.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 2000 hours.Luminescent properties is shown in Table 5.

The energy gap of compound a is that the energy gap of 2.78ev and DPVBi is 3.0ev.

Embodiment 64

Same steps as according to embodiment 63 is made organic El device, only is to use compound b as doping agent or luminescence center.The luminosity of this organic El device when applying the 6V volts DS is 110 (cd/m ²) and luminous efficiency be 1.3 (lm/W).Color coordinates is (0.152,0.163), can send highly purified blue light.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 1500 hours.Luminescent properties is shown in Table 5.

The energy gap of compound b is that the energy gap of 2.90ev and DPVBi is 3.0ev.

Embodiment 65

Same steps as according to embodiment 63 is made organic El device, only is to use compound c as doping agent or luminescence center.The luminosity of this device when applying the 6V volts DS is 130 (cd/m ²) and luminous efficiency be 2.1 (lm/W).Color coordinates is (0.162,0.181), can send highly purified blue light.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 2800 hours.Luminescent properties is shown in Table 5.

The energy gap of compound b is that the energy gap of 2.83ev and DPVBi is 3.0ev.

Embodiment 66

Same steps as according to embodiment 63 is made organic El device, only is to use compound d as doping agent or luminescence center.The luminosity of this organic El device when applying the 6V volts DS is 300 (cd/m ²) and luminous efficiency be 4.6 (lm/W).Can send highly purified green light efficiently.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is grown to 3400 hours.Luminescent properties is shown in Table 5.

The energy gap of compound d is that the energy gap of 2.78ev and DPVBi is 3.0ev.

Comparative Examples 9

Same steps as according to embodiment 63 is made organic El device, only is to use following compound (TPD):

As doping agent or luminescence center.The luminosity of this organic El device when applying the 5V volts DS is 60 (cd/m ²) and luminous efficiency be 0.7 (lm/W).Can not reach enough performances.TPD does not play luminescence center and what obtain is the light that is sent by DPVTP.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is as short as 100 hours.Luminescent properties is shown in Table 5.

The energy gap of compound d is that the energy gap of 3.10ev and DPVBi is 3.0ev.

Comparative Examples 10

Same steps as according to embodiment 63 is made organic El device, only is to use above-claimed cpd a as doping agent or luminescent material and use compd A lq as luminescent material.This is organic

The luminosity of device when applying the 6V volts DS is 210 (cd/m ²) and luminous efficiency be 1.3 (lm/W).But only obtain pink from Alq.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is as short as 200 hours.Luminescent properties is shown in Table 5.Compound a does not play the effect of luminescence center.

The energy gap of compound a is that the energy gap of 2.95ev and Alq is 2.7ev.

Comparative Examples 11

Same steps as according to embodiment 63 is made organic El device, does not just use any doping agent or luminescent material and only uses above-claimed cpd c as unique luminescent material.The luminosity of this organic El device when applying the 6V volts DS is 40 (cd/m ²) and luminous efficiency be 0.9 (lm/W).Can not reach enough performances.If this organic El device is at 200 (cd/m ²) initial luminosity under by constant current driven, its half-life is as short as 180 hours.Luminescent properties is shown in Table 5.

The luminescent properties that more than obtains is shown in Table 5.

Table 5

As shown in table 5, compare with the organic El device of Comparative Examples 9-11, wherein the embodiment 63-66 organic El device as doping agent or luminescence center in the material of main part of compound adding shown in a small amount of (1-20% weight) general formula [1] is had higher luminous efficiency and longer life-span.

Industrial applicibility

Wherein use and be used for the organic El device material shown in general formula [1], [3]-[6] and [9]-[10] Material is as the present invention of luminescent material, hole-injecting material, hole-transfer material or dopant material Organic El device has when applying low-voltage is enough to practical luminosity and high-luminous-efficiency, Owing to the hydraulic performance decline that has suppressed after the long-term use has the long life-span, and because it is excellent Different heat resistance and make its in hot environment without any hydraulic performance decline.

Yellow and orange to red color area, wherein use shown in general formula [7] and [8] for organic The EL device materials is as luminescent material, hole-injecting material, hole-transfer material or dopant material Above-mentioned organic El device when applying low-voltage, have and be enough to practical luminosity and high luminous Efficient, and owing to the hydraulic performance decline that has suppressed after the long-term use has the long life-span.

Wherein use and comprise novelization shown in compound shown in the general formula of the present invention [11] or the general formula [11 '] Existing for the organic El device of organic El device material as adulterant or the centre of luminescence of compound Having when applying low-voltage is enough to practical luminosity and high-luminous-efficiency, and owing to has suppressed Hydraulic performance decline after long-term use the and having the long life-span.

By produce being used for the material of organic El device according to the inventive method, but high productivity is given birth to Output has high-luminous-efficiency, long, active height of life-span and contains organic EL dress that is used for of few impurities The material of putting.

Claims

1. a material that is used for Organnic electroluminescent device is represented by following general formula [9]: general formula [9]

Wherein E represents to include and is replaced or the divalent group of unsubstituted anthracene nuclear X by aryl ⁵-X ⁸Expression has the replacement of 6-20 carbon atom or does not replace arylidene, X independently respectively ⁵And X ⁶Key connects mutually, X ⁷And X ⁸Key connects mutually, Y ¹-Y ⁴Represent the organic group shown in the general formula [2] respectively independently, a-d represents the integer of 0-2 respectively, and group is following not substituted radical shown in the E;

Or

General formula [2] is:

General formula [2]

R wherein ¹-R ⁴Represent hydrogen atom respectively independently, have the replacement of 1-20 carbon atom or not substituted alkyl, replacement or unsubstituting aromatic yl, cyano group, perhaps pass through R with 6-20 carbon atom ¹And R ²Or R ³And R ⁴Key connect and form triple bond, Z represents to have the replacement or the unsubstituting aromatic yl of 6-20 carbon atom, and n represents 0 or 1.

2. the material that is used for Organnic electroluminescent device of claim 1, it is the luminescent material that is used for Organnic electroluminescent device.

3. the described material that is used for Organnic electroluminescent device of claim 1, compound is to be selected from following compound shown in its formula of [9]:

4. Organnic electroluminescent device, comprise the luminescent layer between pair of electrodes or comprise the multilayer organic compound thin film of luminescent layer that wherein one deck organic compound thin film is included in the layer of the material that be used for Organnic electroluminescent device of claim 1-3 described in each at least.

5. Organnic electroluminescent device, comprise the luminescent layer between pair of electrodes or comprise the multilayer organic compound thin film of luminescent layer, wherein be included in the material that be used for Organnic electroluminescent device of claim 1-3 described in each as the layer of at least a material that is selected from hole-injecting material, hole-transfer material and dopant material between this electrode pair.

6. Organnic electroluminescent device, comprise the luminescent layer between pair of electrodes or comprise the multilayer organic compound thin film of luminescent layer, wherein said luminescent layer comprise 0.1-20% weight at the material that be used for Organnic electroluminescent device of claim 1-3 described in each.

7. Organnic electroluminescent device, comprise the luminescent layer between pair of electrodes or comprise the multilayer organic compound thin film of luminescent layer, one or more materials that wherein are selected from hole-injecting material, hole-transfer material and dopant material comprise independently of one another 0.1-20% weight at the material that be used for Organnic electroluminescent device of claim 1-3 described in each.

8. Organnic electroluminescent device, comprise the luminescent layer between pair of electrodes or comprise the multilayer organic compound thin film of luminescent layer that wherein said luminescent layer is to comprise stilbene derivative and at the layer that be used for Organnic electroluminescent device material of claim 1-3 described in each.

9. according to each Organnic electroluminescent device of claim 4-7, the layer that wherein comprises aromatic uncle amine derivative and/or phthalocyanine derivates is between luminescent layer and anode.