CN101352724B - 一种含硼非调质塑料模具钢的制造方法 - Google Patents

一种含硼非调质塑料模具钢的制造方法 Download PDF

Info

Publication number
CN101352724B
CN101352724B CN2008101194992A CN200810119499A CN101352724B CN 101352724 B CN101352724 B CN 101352724B CN 2008101194992 A CN2008101194992 A CN 2008101194992A CN 200810119499 A CN200810119499 A CN 200810119499A CN 101352724 B CN101352724 B CN 101352724B
Authority
CN
China
Prior art keywords
rolling
steel plate
steel
controlled
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008101194992A
Other languages
English (en)
Other versions
CN101352724A (zh
Inventor
金茹
麻庆申
张炜星
高彩茹
陈松林
宋增强
吕延春
郑会平
田士平
闫治平
王臻明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Group Co Ltd
Original Assignee
Shougang Corp
Qinhuangdao Shouqin Metal Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Corp, Qinhuangdao Shouqin Metal Materials Co Ltd filed Critical Shougang Corp
Priority to CN2008101194992A priority Critical patent/CN101352724B/zh
Publication of CN101352724A publication Critical patent/CN101352724A/zh
Application granted granted Critical
Publication of CN101352724B publication Critical patent/CN101352724B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种含硼非调质塑料模具钢的制造方法。属于中厚板钢板制造技术领域。工艺为：将连铸坯均热，温度为1150～1250℃；控制热轧温度，精轧开轧温度在900～950℃，终轧温度在840～880℃；钢板热轧后控冷，冷却速度控制在1～5℃/s；在轧制后需要进行回火处理。采用控制轧制和控制冷却方法获得20-80mm的贝氏体组织钢板，轧后进行消应力回火，钢板综合性能达到预硬型P20的工艺要求。钢板的屈服强度≥650MPa，抗拉强度≥900MPa，横截面硬度在280-330HV，抛光性均达到P20预硬型钢板的要求。

Description

一种含硼非调质塑料模具钢的制造方法
技术领域
本发明属中厚板钢板制造技术领域，特别是提供了一种含硼非调质塑料模具钢的制造方法，使其屈服强度≥660MPa，抗拉强度≥960MPa，硬度在HV280-320，金相组织为贝氏体。
背景技术
长久以来，塑料模具钢的生产几乎都是特钢厂以铸锭-开坯-轧制-预硬化热处理的模块方式生产，其生产环节多，生产周期长，成本高。本发明旨在中厚板轧机上利用控制轧制控制冷却的方法生产出符合性能要求的塑料模具钢厚板，提高生产效率，扩大生产规模。国内已有工厂利用厚板轧机生产P20等塑料模具钢的先例，但是在轧制后仍需进行调质处理；也有企业尝试采用连铸坯在中厚板轧机上用控轧控冷的方法生产厚度在100mm以下的塑料模具钢，但是鉴于厚板厚度方向的硬度均匀性的控制难题，一般都采用加入淬透性较好的Ni元素，但是Ni元素价格昂贵，生产成本高。
专利200410053281.3虽然也涉及到了一种免淬火的预硬型塑料模具钢，但其化学成份中添加了贵重的合金元素Ni，同时钢中不加B、Ti、V等元素，与本发明相比，合金成本较高。本发明在降低合金元素的前提下通过采用中厚板控轧控冷工艺生产了性能优良的合金塑料模具钢。
发明内容
本发明的目的在于提供一种含B非调质塑料模具钢的制造方法，解决了现有塑料模具钢生产上存在的生产环节多，生产周期长，成本高问题。
本发明所述的钢板为低碳含B不含Ni，化学成分按质量百分数为：C：0.06～0.20％，Si：0.10～0.50％，Mn：1.10～1.80％，P：≤0.015％，S≤0.010％，Cr：1.00～1.90％，B：0.001～0.010％，Mo：0.10～0.80％，余量为Fe。钢板化学成分中不添加贵重的Ni元素，极大地降低了生产成本。发明涉及的钢板厚度规格为20-80mm，沿横断面全部为粒状贝氏体组织。
本发明采用上述化学成分生产厚度为220-320mm的连铸坯，通过热轧和冷却工艺生产屈服强度≥660MPa，抗拉强度≥960MPa，硬度为HV280～320，硬度均匀、机加工性能良好的塑料模具钢厚板，具体按照以下步骤进行：
1)工艺路线：转炉+LF脱硫+RH真空脱气、夹杂物处理+连铸；钢水经LF、RH精炼后浇注成板坯，在中厚板轧机上采用控制轧制和控制冷却工艺轧制20-80mm厚的钢板；
2)采用上述成分冶炼的连铸坯均热温度为1150～1250℃；
3)控制热轧温度，精轧开轧温度在900～950℃，终轧温度在840～880℃。
4)钢板热轧后控冷，冷却速度控制在1～5℃/s。
5)为了消除在轧制过程中产生的残余应力，提高钢板的稳定性和综合性能，防止钢板的锯切开裂，在轧制后需要进行300～500℃的回火处理；钢板综合性能达到预硬型P20的工艺要求。
本发明所涉及的新型塑料模具钢即要满足强度、硬度及硬度均匀性的要求，还要满足与同类产品P20或718具有同等的抛光性能及耐磨性能等使用性能的要求。考虑到降低对资源和能源消耗的问题，本发明采用低碳路线，利用微合金元素V来保证其力学性能，加入适量的B元素及少量Mo元素来保证其淬透性及获得均匀的贝氏体组织，降低对冷却速度的敏感性，保证厚度方向不同区域的组织及硬度的均匀性。
附图说明
图1为本发明钢的静态CCT曲线。
图2为本发明钢的动态CCT曲线。
图3为本发明钢的金相显微组织。
图4为实施例1钢板横截面的硬度分布。
图5为实施例2钢板横截面的硬度分布。
附图说明：塑料模具钢的静态CCT曲线、动态CCT曲线和冷却后的组织。
具体实施方式
实施例1
钢板化学成分如表1中实施例1所示，浇注板坯尺寸为220mm×1700mm，成品板尺寸20×2000×L，按照表2中实施例1所示的生产工艺进行轧制，得到如表3所示的力学性能。钢板横截面的硬度分布见附图4，硬度相差值≤20HV，钢板的抛光性见表4。钢板性能均符合P20预硬型钢板的要求。
实施例2
钢板化学成分如表1中实施例2所示，浇注板坯尺寸为250mm×1700mm，成品板尺寸50×2000×L，按照表2中实施例2所示的生产工艺进行轧制，得到如表3所示的力学性能。钢板横截面的硬度分布见附图4，硬度相差值≤20HV。钢板抛光性见表4。钢板性能均符合P20预硬型钢板的要求。
表1实施例实测化学成分(质量分数％，余量为Fe)
表2实施例工艺参数
Figure G2008101194992D00031
表3实施例力学性能
Figure G2008101194992D00032
表4实施例钢板表面粗糙度
Figure G2008101194992D00033

Claims (1)

1.一种含硼非调质塑料模具钢的制造方法，其特征在于，工艺为：
(1)钢水经LF、RH精炼后浇注成板坯，在中厚板轧机上采用控制轧制和控制冷却工艺轧制20～80mm厚的钢板；
(2)将连铸坯均热，温度为1150～1250℃；
(3)控制热轧温度，精轧开轧温度在900～950℃，终轧温度在840～880℃；
(4)钢板热轧后控冷，冷却速度控制在1～5℃/s；
(5)在轧制后需要进行300～500℃的回火处理；
所述钢板化学成分按重量百分比计为：C：0.06～0.20％，Si：0.10～0.50％，Mn：1.10～1.80％，P：≤0.015％，S≤0.010％，Cr：1.00～1.90％，B：0.001～0.010％，Mo：0.10～0.80％，余量为Fe。
CN2008101194992A 2008-09-02 2008-09-02 一种含硼非调质塑料模具钢的制造方法 Active CN101352724B (zh)