CN101343523A - Adhesive, reflecting film, pad pasting glass or slice brick containing the adhesive - Google Patents
Adhesive, reflecting film, pad pasting glass or slice brick containing the adhesive Download PDFInfo
- Publication number
- CN101343523A CN101343523A CNA2008100625426A CN200810062542A CN101343523A CN 101343523 A CN101343523 A CN 101343523A CN A2008100625426 A CNA2008100625426 A CN A2008100625426A CN 200810062542 A CN200810062542 A CN 200810062542A CN 101343523 A CN101343523 A CN 101343523A
- Authority
- CN
- China
- Prior art keywords
- glass
- gum
- adhesive
- parts
- tapetum lucidum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses adhesive and reflective film, filmed glass and a split brick containing the adhesive. According to the weight parts, the adhesive comprises 100 parts of epoxy resin, 50 parts of anti-yellowing epoxy resin, 75 parts to 120 parts of rock powder higher than 600 meshes and 1 part to 6 parts of cellulose (HPMC). The reflective film is formed by scratching the adhesive on the back surface of the reflective film without gum. The filmed glass provided by the invention comprises glass and the reflective film without gum, wherein, the front face of the reflective film without gum is pasted on the glass, and the back surface of the reflective film without gum is scratched with the adhesive. The adhesive has the advantages of strong cohesive force, strong density, aging resistant and good barrier property, simultaneously, the adhesive has good repairing and leveling functions which can effectively make up for the defects of the pressure-sensitive adhesive.
Description
Technical field
The present invention relates to a kind of security warning material and finishing material, relate in particular to a kind of tapetum lucidum, pad pasting glass or tile, and be used for the adhesive glue on retroreflective marking glass, tapetum lucidum or the tile.
Background technology
Tapetum lucidum is a principal item of popular reflecting material in the market, tapetum lucidum plays an important role in the traffic safety facilities alarming sign, this class tapetum lucidum is a carrier with plastic film mainly, on plastic film, be coated with the mixture of last layer glue and aluminium base silver powder, form reflective material layer, be coated with last layer then and have the glass microballon of refraction effect and cover with paint, lacquer, colour wash, etc. various color and lusters, thereby form tapetum lucidum.According to the reflex reflection performance of product, divide one-level, secondary, three grades, level Four, Pyatyi to the tapetum lucidum performance among the GB/T 18833-2002 of the People's Republic of China (PRC) " highway traffic sign tapetum lucidum ".But be subjected to the constraint of plastic film ageing-resistant performance, and the constraint of pressure sensitive adhesive use properties, the Application Areas of tapetum lucidum is restricted.
The common engineering reflecting film is 2. planted the pearl resin layer by 1. weathering resistance resin layers, 3. soot layer, and 4. focus layer, 5. metallic reflector, 6. pressure-sensitive adhesive layer, 7. antiseized protection ply of paper is formed;
General high-strength reflecting film is 2. planted the pearl resin layer by 1. weathering resistance resin layers, 3. soot layer, and 4. adhesive linkage, 5. supporting layer, 6. pressure-sensitive adhesive layer, 7. antiseized protection ply of paper is formed.
Have the tapetum lucidum of pressure-sensitive glue to have following some shortcomings: pressure sensitive adhesive can not solidify within a certain period of time, realizes bonding by pressure.At present, work-ing life short (better slightly when on exsiccant cement mortar matrix, using) when gum-----pressure sensitive adhesive that tapetum lucidum uses is used on the outdoor naked cement mortar matrix of solidified, major cause is that the water resistance or perhaps the anti-permeability performance of pressure sensitive adhesive is bad, simultaneously, pressure sensitive adhesive also can't be pasted or be pasted not strongly on uneven whole or shaggy matrix.
Summary of the invention
In order to overcome deficiency of the prior art; the present invention is in the making processes of tapetum lucidum; omitted the last glue process of pressure-sensitive adhesive layer and the bonding process of antiseized protection sheet, formed the finished product of no gum tapetum lucidum, provide a kind of can the adhesive glue of blade coating on no gum tapetum lucidum.
Second purpose of the present invention the provided a kind of blade coating tapetum lucidum of adhesive glue of the present invention.
The 3rd purpose of the present invention provide a kind of at the no gum tapetum lucidum back side blade coating pad pasting glass made of the tapetum lucidum of adhesive glue of the present invention and glass.
The 4th purpose of the present invention provides a kind of tile that is made of the present invention the 3rd the described pad pasting glass of purpose, ceramics.
The 5th purpose of the present invention provides a kind of tile that is made of the present invention second the described tapetum lucidum of purpose, ceramics.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions:
A kind of adhesive glue, form by following components in weight percentage:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
The above rock powder of 600 orders 75-120 part Mierocrystalline cellulose (HPMC) 1-6 part.
The best composition weight proportion of above-mentioned adhesive glue is:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
4 parts of 600 orders, 120 parts of Mierocrystalline celluloses of above rock powder (HPMC).
Above-mentioned described rock powder is silica powder or talcum powder.
A kind of tapetum lucidum is at the above-mentioned described adhesive glue of the back side of no gum tapetum lucidum blade coating.
A kind of pad pasting glass comprises no gum tapetum lucidum and glass, and the front of described no gum tapetum lucidum sticks on glass, and the back side of described no gum tapetum lucidum is scraped and scribbled the above-mentioned described adhesive glue of the present invention.
A kind of tile comprises no gum tapetum lucidum, glass and ceramics, and the front of described no gum tapetum lucidum sticks on glass, and the back side of described no gum tapetum lucidum is scraped and scribbled the above-mentioned described adhesive glue of the present invention and bonding with ceramics.
A kind of tile comprises no gum tapetum lucidum and ceramics, and the described no gum tapetum lucidum back side is scraped and scribbled the above-mentioned described adhesive glue of the present invention and bonding with ceramics.
A kind of pad pasting glass, described glass the best are float glass or PE, PVC synthetic glass.
A kind of tile, described glass the best are float glass or PE, PVC synthetic glass.
Tapetum lucidum four limit cutting profiles described in the above-mentioned described tile and front give close and protect by the transparent adhesive glue or the coating of low water absorption, high bond strength, high-weatherability, to improve the weather resistance of original tapetum lucidum.
Mierocrystalline cellulose in the adhesive glue of the present invention (HPMC) can improve the following performance of colloid:
1, water-retentivity--strengthen water-retentivity, improve too fast drying of colloid and hydration and cause phenomenons such as sclerosis is bad, cracking inadequately; 2, operation--increased colloidal plasticity-, increased work efficiency; 3, cohesiveness--because colloid plasticity-improves, make its better bonding substrates and bonded thing; 4, antiskid moves--because its thickening power, so the appearance of colloid and bonded thing sliding phenomenon can prevent to construct the time.
The rock powder has viscosifying power and weather resistance preferably.Therefore, adhesive glue cohesive force height of the present invention, density is strong, and is ageing-resistant, impervious good, has good repairing levelling function simultaneously, effectively remedied the defective of pressure sensitive adhesive.
The present invention does not adopt the tapetum lucidum of pressure sensitive adhesive; in the making processes of tapetum lucidum; the last glue process of pressure-sensitive adhesive layer and the bonding process of antiseized protection sheet have been omitted; formed the finished product of no gum tapetum lucidum; saved the waste of pressure sensitive adhesive and protection sheet; simplify production process, reduced production cost.
No gum tapetum lucidum is directly pasted behind blade coating adhesive glue of the present invention on the outdoor naked cement mortar matrix, or with the colloid blade coating at the tapetum lucidum back side, matrix is handled the directly stickup of clean back.Its advantage is: reduced production cost and application cost significantly, easy construction, the maintaining expense is cheap, adhesive glue is because of the cohesive force height, and density is strong, and is ageing-resistant, impervious good, so expanded the Application Areas of tapetum lucidum effectively, reduce the waste of material, reduced construction costs, also had good social enviroment protection energy-saving effect simultaneously.
By compound to the science of no gum tapetum lucidum and glass, make by the building material industry standard JC 846-2007 of the People's Republic of China (PRC) " pad pasting glass " requirement, formation has the pad pasting glass of reflective function, gives original tapetum lucidum a kind of brand-new caution decorative applications function.
Description of drawings
Fig. 1 is the structural representation of seventh embodiment of the invention tapetum lucidum;
Fig. 2 is the structural representation of eighth embodiment of the invention pad pasting glass;
Fig. 3 is the structural representation of ninth embodiment of the invention tile;
Fig. 4 is the structural representation of tenth embodiment of the invention tile.
Among the figure: no gum tapetum lucidum 1 bonding glue-line 2 glass 3 tapetum lucidums 4 ceramics 5 pad pasting glass 6
Embodiment
The invention will be further described below in conjunction with accompanying drawing and embodiment, but they are not limitation of the invention.
Embodiment one
A kind of adhesive glue is mixed together by the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
1 part of 600 orders, 75 parts of Mierocrystalline cellulose of above china clay in powder (HPMC).
Embodiment two
A kind of adhesive glue is mixed together by the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
6 parts of 600 orders, 120 parts of Mierocrystalline celluloses of above silica powder (HPMC).
Embodiment three
A kind of adhesive glue is mixed together by the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
4 parts of 600 orders, 120 parts of Mierocrystalline celluloses of above silica powder (HPMC).
Embodiment four
A kind of adhesive glue is mixed together by the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
1 part of 600 orders, 75 parts of Mierocrystalline cellulose of above Feldspar Powder (HPMC).
Embodiment five
A kind of adhesive glue is mixed together by the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
6 parts of 600 orders, 120 parts of Mierocrystalline celluloses of above talcum powder (HPMC).
Embodiment six
A kind of adhesive glue is mixed together by the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
4 parts of 600 orders, 120 parts of Mierocrystalline celluloses of above talcum powder (HPMC).
Embodiment seven
A kind of high weather-proof retroreflective marking tapetum lucidum 4; in the making processes of tapetum lucidum 4; the last glue process of pressure-sensitive adhesive layer and the bonding process of antiseized protection sheet have been omitted; formed the finished product of no gum tapetum lucidum 1; scrape at no gum tapetum lucidum 1 back side and to scribble one to six arbitrary prepared adhesive glue by embodiment; form bonding glue-line 2, promptly get tapetum lucidum 4 of the present invention.
The application of tapetum lucidum 4: press embodiment one to six arbitrary prepared adhesive glue at tapetum lucidum 4 back side blade coatings, form the close and protect layer of bonding glue-line 2; Maybe will not having gum tapetum lucidum 1 directly pastes after blade coating on the outdoor naked cement mortar matrix is pressed embodiment one to six arbitrary prepared adhesive glue, maybe will matrix be handled clean back directly paste by embodiment one to six arbitrary prepared adhesive glue blade coating at tapetum lucidum 4 back sides.
Embodiment eight
A kind of high weather-proof retroreflective marking pad pasting glass 6, comprise the no gum tapetum lucidum 1 and the glass 3 that get described in the embodiment seven, make by the building material industry standard JC 846-2007 of the People's Republic of China (PRC) " pad pasting glass " requirement, form pad pasting glass with reflective function; Press embodiment one to six arbitrary prepared adhesive glue at no gum tapetum lucidum 1 back side blade coating, form the close and protect layer of bonding glue-line 2, promptly make the high weather-proof retroreflective marking pad pasting glass 6 of the present invention.Also can high weather-proof retroreflective marking pad pasting glass 6 application base materials direct and that processing is clean that press embodiment one to six arbitrary prepared adhesive glue at no gum tapetum lucidum 1 back side blade coating are directly bonding.Glass 3 preferably adopts float glass or high-weatherability, high transparent PE, PVC synthetic glass.
Embodiment nine
A kind of high weather-proof retroreflective marking tile comprises obtained tapetum lucidum 4 and ceramics 5 bottoms among the embodiment seven; Tapetum lucidum 4 is positioned at above ceramics 5 bottoms, and ceramics 5 bottoms are positioned at below the tapetum lucidum 4, tapetum lucidum scrape scribble by embodiment one to six arbitrary prepared adhesive glue face and ceramics bottom bonding.
Embodiment ten
A kind of high weather-proof retroreflective marking tile comprises obtained pad pasting glass 6 and ceramics 5 bottoms formation among the embodiment eight; Pad pasting glass 6 is positioned at above ceramics 5 bottoms, and ceramics 5 bottoms are positioned at below the pad pasting glass 6, in the pad pasting glass 6 the tapetum lucidum back side scrape scribble by embodiment one to six arbitrary prepared adhesive glue face and ceramics 5 bottoms bonding.Glass 3 preferably adopts float glass or high-weatherability, high transparent PE, PVC synthetic glass.
Claims (9)
1, a kind of adhesive glue is characterized in that being made up of the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
The above rock powder of 600 orders 75-120 part Mierocrystalline cellulose (HPMC) 1-6 part.
2, adhesive glue according to claim 1 is characterized in that being made up of the component of following weight proportioning:
50 parts of 100 parts of Resins, epoxy of anti-xanthochromia of Resins, epoxy
4 parts of 600 orders, 120 parts of Mierocrystalline celluloses of above rock powder (HPMC).
3, adhesive glue according to claim 1 and 2 is characterized in that described rock powder is silica powder or talcum powder.
4, a kind of tapetum lucidum (4) is characterized in that described tapetum lucidum (4) is at the back side blade coating of no gum tapetum lucidum (1) the requirement 1 described adhesive glue of having the right.
5, a kind of pad pasting glass (6) comprises no gum tapetum lucidum (1) and glass (3), it is characterized in that the front of described no gum tapetum lucidum (1) sticks on the glass (3), the back side blade coating of described no gum tapetum lucidum (1) the requirement 1 described adhesive glue of having the right.
6, a kind of tile, comprise no gum tapetum lucidum (1), glass (3) and ceramics (5), the front that it is characterized in that described no gum tapetum lucidum (1) sticks on the glass (3), the back side blade coating of described no gum tapetum lucidum (1) the requirement 1 described adhesive glue and bonding with ceramics (5) of having the right.
7, a kind of tile comprises no gum tapetum lucidum (1) and ceramics (5), it is characterized in that described no gum tapetum lucidum (1) the back side blade coating requirement 1 described adhesive glue and bonding with ceramics (5) of having the right.
8, a kind of pad pasting glass according to claim 5 (6) is characterized in that described glass (3) is float glass or PE, PVC synthetic glass.
9, a kind of tile according to claim 6 is characterized in that described glass (3) is float glass or PE, PVC synthetic glass.