CN101327057B - Ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle - Google Patents
Ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle Download PDFInfo
- Publication number
- CN101327057B CN101327057B CN2007100696569A CN200710069656A CN101327057B CN 101327057 B CN101327057 B CN 101327057B CN 2007100696569 A CN2007100696569 A CN 2007100696569A CN 200710069656 A CN200710069656 A CN 200710069656A CN 101327057 B CN101327057 B CN 101327057B
- Authority
- CN
- China
- Prior art keywords
- ultraviolet
- lens
- vehicle
- water
- eyeglass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to an anti-ultraviolet wear-resistant helmet lens provided with gradually changed colors and used for the vehicle. Plastics is adopted as the raw material, and produced into the lens through injection molding. The helmet lens is characterized in that anti-ultraviolet (UV) agent with the weight ratio of 0.3-0.5 percent is added into the plastic raw material, and the plastics is produced into the transparent lens through uniform mixing and injection molding; the lens is washed through water and dried, water-soluble dye powder is adopted to be dissolved in water according to the water-dye powder proportion of 100: 0.01-1.0, stirred uniformly and heated to 80 to 100 DEG C, the lens is fixed on a rack or held in the hand, immerged into dyeing solution and moved vertically, gradient dying and overlapping are then performed for one to two minutes, and the lens is respectively cleaned through cleaning agent and water, and then the lens with gradually changed colors can be obtained. The anti-ultraviolet wear-resistant helmet lens has the advantages of anti-ultraviolet function, through which the radiant heat of harmful ultraviolet and infrared rays emitted from the sun can be prevented and certain skin protection function can be achieved; the effect of gradually changed colors, which can protect the eyes from fatigue, and can provide the product with colorful and beautiful appearance.
Description
Technical field
The present invention relates to the helmet of motorcycle, electric motor car, particularly relate to a kind of ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle.
Background technology
It is raw material that the helmet glasses lens of existing motorcycle, electric motor car is selected PET or PS mostly for use, make transparent whites or whole eyeglass for light/dark balance, sky-blue, antiultraviolet and do not contain the gradual change look not, therefore, the one, the harmful ultraviolet ray penetrated in the sunshine and infrared radiation heat etc. impinge upon human body on the face, easily to skin damage, aging.The 2nd, because eyeglass is unified color, particularly transparent whites, eyes are subjected to strong illumination tired easily, dull coloring, and aesthetic property is poor.The 3rd, the glass lens surface is subjected to foreign object to scratch, wear and tear easily, causes the perspective rate to descend, and blurred vision causes traffic accident easily.Also have a small amount of reflective color sheet (antiultraviolet) of electroplating simultaneously, it is easily broken to electroplate the back eyeglass, injures human body, face easily.
Summary of the invention
The objective of the invention is in order to overcome the shortcoming of prior art, a kind of energy antiultraviolet is provided, avoid sunlight to the human injury, specular color from depth to shallow from top to bottom, rationally select suitable colourity for use by the user, alleviate eye fatigue, and eyeglass is carried out intensive treatment, improve ultraviolet-resistance gradient color abrasion-proof motorcycle, the electric vehicle helmet glasses lens of anti-wear performance.
The technical scheme of ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle of the present invention is: be raw material with plastics, make eyeglass through injection moulding, it is characterized in that in the plastic raw materials adding weight ratio and be 0.3%～0.5% antiultraviolet UV agent, described antiultraviolet UV agent be 2-(3 '-tert-butyl group-2 '-hydroxyl-5 '-aminomethyl phenyl)-5-chlorinated benzotriazole or 2-(2H-BTA-2-yl)-4,6-two (1,-methyl isophthalic acid-phenylethyl) phenol is made transparent glasses lens through mixing the back injection moulding; To the eyeglass water clean, the dry processing, water intaking soluble dye powder, described water-soluble dye are AC-E days golden yellow dyestuffs of the precious red or dispersed sun-proof type E-3RL of blue or dispersed sun-proof type AC-3R of dispersed sun-proof type.In water and dyestuff powder ratio is 100: in the 0.01-1.0 dissolving water, stir, be heated to 80 ℃～100 ℃, eyeglass is fixed on frame or takes, immerse in the staining solution and move up and down, gradient dyeing is stacked, and the time is taking-up in 1～2 minute, and front and back get gradual change look eyeglass after washing eyeglass respectively with cleaning agent and water.
Ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle of the present invention; compared with the prior art; have following advantage: the one, anti-ultraviolet function is arranged; intercept the harmful ultraviolet ray and the infrared radiation heat that penetrate in the sunshine; prevent that summer, the sun injured human body skin; protection is facial anti-aging, plays certain skin care effect.The 2nd, the gradual change chromatic effect is arranged, eyeglass from top to bottom, color changes to light color or colourless gradually by dark color, reduces eyeglass and dazzles the eyes high light, the protection eyes are anti-tired, and product color enriches attractive in appearance.
Ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle of the present invention, it gets the silica glass resin is forced fluid, gradual change look eyeglass is put into the forced fluid soak time to be taken out after the kind in 30～90 seconds, placed 2-5 minute, after the drying, the baking oven of putting into temperature and be 100 ℃ dries by the fire, and keeps constant temperature 30～90 minutes, naturally cools to 30 ℃ of-50 ℃ of taking-ups then.Gradual change look helmet glasses lens is after intensive treatment, and surface abrasion resistance, anti-zoned performance strengthen, and weather-resistant is good, not embrittlement of low temperature (20 ℃), and hydrophobic, light transmittance (visible light) reaches more than 90%.Perhaps getting the silica glass resin is that forced fluid is coated in gradual change look lens surface, places 2-5 minute, and after the drying, the baking oven of putting into temperature and be 100 ℃ dries by the fire, and keeps constant temperature 30～90 minutes, naturally cools to 30 ℃ of-50 ℃ of taking-ups then.Its described silica glass resin is a MTES.Its described plastic raw materials is poly-carbon PC or PET polyester, and the PC material is made eyeglass, and the transparency reaches 90%, has high refraction, birefringence is low, and tough is good.Its plastic raw materials and UV agent are 0.4% by weight proportion.Its gradual change look eyeglass soak time in forced fluid is to take out after 1 minute, places 3 minutes, keeps constant temperature 60 minutes in baking oven, naturally cools to 40 ℃ of taking-ups.Its forced fluid was placed 3 minutes after applying gradual change look eyeglass, kept constant temperature 60 minutes in baking oven, naturally cooled to 40 ℃ of taking-ups.
Description of drawings
Fig. 1 is a ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle schematic diagram of the present invention.
The specific embodiment
The present invention relates to a kind of ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle, as shown in Figure 1, be raw material with plastics, make eyeglass through injection moulding, it is characterized in that in the plastic raw materials adding weight ratio and be 0.3%～0.5% antiultraviolet UV agent, make transparent glasses lens through mixing the back injection moulding; To the eyeglass water clean, the dry processing, water intaking soluble dye powder, in water and dyestuff powder ratio is in the 100:0.01-1.0 dissolving water, the best is water and the dyestuff powder ratio of 100:0.2-0.4, stir, be heated to 80 ℃～100 ℃, eyeglass is fixed on frame or takes, immerse in the staining solution and move up and down, gradient dyeing is stacked, and the time is taking-up in 1～2 minute, and front and back get gradual change look eyeglass after washing eyeglass respectively with cleaning agent (available acetone or cleaning essence etc.) and water, eyeglass is A → B direction from top to bottom, by dark 1 look 2 that shoals.Compared with the prior art this programme has following advantage: the one, anti-ultraviolet function is arranged, and intercept the harmful ultraviolet ray and the infrared radiation heat that penetrate in the sunshine, prevent that summer, the sun injured human body skin, protection is facial anti-aging, plays certain skin care effect.The 2nd, the gradual change chromatic effect is arranged, eyeglass from top to bottom, color changes to light color or colourless gradually by dark color, reduces eyeglass and dazzles the eyes high light, the protection eyes are anti-tired, and product color enriches attractive in appearance.In actual product is produced, comprised all size of helmet glasses lens, dyestuff is various colors, is that Essential colour is allocated with the red, orange, yellow, green, indigo, azure, purple.Can be raw material also with PC or PET, painted after the interpolation antiultraviolet UV agent with plastic pigment (toner or look mother), mix, injection moulding then becomes transparent color antiultraviolet eyeglass.Its described antiultraviolet UV agent is 2-(3 '-tert-butyl group-2 '-hydroxyl-5 '-aminomethyl phenyl)-5-chlorinated benzotriazole or 2-(2H-BTA-2-yl)-4,6-two (1 ,-methyl-1-phenylethyl) phenol.Its described water-soluble dye is AC-E days blue or golden yellow dyestuffs of the precious red or dispersed sun-proof type E-3RL of dispersed sun-proof type AC-3R of dispersed sun-proof type.When actual production, dyeing water preparation: earlier 100 kilograms of clean waters are heated to 50 ℃ of temperature, add (xanthate water) active dye leveller-decentralized BOF1000g, after stirring, (producer: German De Sida Co., Ltd (Wuxi) produces disperse dyes BlueAC-E (indigo plant) 300～500g to add the dyestuff toner, YellowAC-E (Huang) 300～500g, three Essential colour of RedAC-E01 (red) 300～500g, requirement of all kinds is allotment separately, concoct the various colors that form then, quicken to stir 30 minutes, evenly, 65 ℃-70 ℃ of temperature add (black powder water) diffusant M-9 (700g) again, stir after 10 minutes, add phenmethylol 3600g, 75 ℃-80 ℃ of temperature stirred about 1 hour, finished.Getting the silica glass resin is forced fluid, gradual change look eyeglass is put into the forced fluid soak time took out after the kind in 30～90 seconds, places 2-5 minutes, after the drying, the baking oven of putting into temperature and be 100 ℃ dries by the fire, and keeps constant temperature 30～90 minutes, naturally cools to 30 ℃ of-50 ℃ of taking-ups then.Gradual change look helmet glasses lens is after intensive treatment, and surface abrasion resistance, anti-zoned performance strengthen, and weather-resistant is good, not embrittlement of low temperature (20 ℃), and hydrophobic, light transmittance (visible light) reaches more than 90%.Getting the silica glass resin is that forced fluid is coated in gradual change look lens surface, places 2-5 minutes, and after the drying, the baking oven of putting into temperature and be 100 ℃ dries by the fire, and keeps constant temperature 30～90 minutes, naturally cools to 30 ℃ of-50 ℃ of taking-ups then.Its described silica glass resin is a MTES.Its described plastic raw materials is poly-carbon PC (being Merlon) or PET polyester.The PC material is made eyeglass, and the transparency reaches 90%, has high refraction, birefringence is low, and tough is good.Its plastic raw materials and UV agent are 0.4% by weight proportion.Its gradual change look eyeglass soak time in forced fluid is to take out after 1 minute, places 3 minutes, keeps constant temperature 60 minutes in baking oven, naturally cools to 40 ℃ of taking-ups.Its forced fluid was placed 3 minutes after applying gradual change look eyeglass, kept constant temperature 60 minutes in baking oven, naturally cooled to 40 ℃ of taking-ups.
Claims (8)
1. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle, with plastics is raw material, make eyeglass through injection moulding, it is characterized in that in the plastic raw materials adding weight ratio and be 0.3%～0.5% antiultraviolet UV agent, described antiultraviolet UV agent be 2-(3 '-tert-butyl group-2 '-hydroxyl-5 '-aminomethyl phenyl)-5-chlorinated benzotriazole or 2-(2H-BTA-2-yl)-4,6-two (1 ,-methyl isophthalic acid-phenylethyl) phenol is made transparent glasses lens through mixing the back injection moulding; To the eyeglass water clean, the dry processing, water intaking soluble dye powder, described water-soluble dye is AC-E days golden yellow dyestuffs of the precious red or dispersed sun-proof type E-3RL of blue or dispersed sun-proof type AC-3R of dispersed sun-proof type, in water and dyestuff powder ratio is 100: in the 0.01-1.0 dissolving water, stir, be heated to 80 ℃～100 ℃, eyeglass is fixed on frame or takes, immerse in the staining solution and move up and down, gradient dyeing is stacked, time is taking-up in 1～2 minute, and front and back get gradual change look eyeglass after washing eyeglass respectively with cleaning agent and water.
2. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle as claimed in claim 1, it is characterized in that getting the silica glass resin is forced fluid, gradual change look eyeglass is put into the forced fluid soak time to be taken out after the kind in 30～90 seconds, placed 2-5 minute, after the drying, the baking oven of putting into temperature and be 100 ℃ dries by the fire, and keeps constant temperature 30～90 minutes, naturally cools to 30 ℃ of-50 ℃ of taking-ups then.
3. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle as claimed in claim 1, it is characterized in that getting the silica glass resin is that forced fluid is coated in gradual change look lens surface, placed 2-5 minute, after the drying, the baking oven of putting into temperature and be 100 ℃ dries by the fire, keep constant temperature 30～90 minutes, and naturally cooled to 30 ℃ of-50 ℃ of taking-ups then.
4. as claim 2 or 3 described ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle, it is characterized in that described silica glass resin is a MTES.
5. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle as claimed in claim 1 is characterized in that described plastic raw materials is poly-carbon PC or PET polyester.
6. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle as claimed in claim 1 is characterized in that plastic raw materials and UV agent are 0.4% by weight proportion.
7. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle as claimed in claim 2 is characterized in that gradual change look eyeglass soak time in forced fluid is to take out after 1 minute, places 3 minutes, keeps constant temperature 60 minutes in baking oven, naturally cools to 40 ℃ of taking-ups.
8. ultraviolet-resistance gradient color abrasion-proof helmet glasses lens for vehicle as claimed in claim 3 is characterized in that placing 3 minutes after forced fluid applies gradual change look eyeglass, keeps constant temperature 60 minutes in baking oven, naturally cools to 40 ℃ of taking-ups.