CN101280138A - High-glaze silk-screen printing ink for plastic articles - Google Patents
High-glaze silk-screen printing ink for plastic articles Download PDFInfo
- Publication number
- CN101280138A CN101280138A CN 200810067627 CN200810067627A CN101280138A CN 101280138 A CN101280138 A CN 101280138A CN 200810067627 CN200810067627 CN 200810067627 CN 200810067627 A CN200810067627 A CN 200810067627A CN 101280138 A CN101280138 A CN 101280138A
- Authority
- CN
- China
- Prior art keywords
- printing ink
- screen printing
- acrylic resin
- ink
- high gloss
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention is high gloss silk-screen printing ink used for a plastic piece, containing aluminum paste pigment, UV curing photoinitiator, acrylic resin and oxidation resistance protective agent; the weight ratio that aluminum paste pigment : UV curing photoinitiator : acrylic resin : oxidation resistance protective agent equal to 1000 : (25-40) : (60-125) : (25-100); the ink of the high gloss silk-screen printing ink can maintain the effect of silvery white and gloss and for a long time.
Description
Technical field
The present invention relates to a kind of ink for screen printing that band on the plastic component surface that is used for.
Background technology
The ink for screen printing that is used on plastic component such as the cosmetic package plastic hose adopts conventional aluminium ink usually, and this aluminium ink is because of easy oxidized obfuscation of its main component " aluminium ", so printing ink is canescence.
Summary of the invention
The objective of the invention is to the problems referred to above of existing at existing ink for screen printing, the high gloss ink for screen printing on the plastic component of being used for of the silvery white effect of a kind of tool is provided.
The object of the present invention is achieved like this: the present invention is made up of aluminium paste pigment, UV photocuring light trigger, acrylic resin, the agent of resistance oxidation protection; their weight ratio is aluminium paste pigment: UV photocuring light trigger: acrylic resin: resistance oxidation protection agent=1000: (25-40): (60-125): (25-100).
Described UV photocuring light trigger is the ultraviolet light polymerization light trigger, can select 1-hydroxy-cyclohexyl phenyl-acetone for use.Described acrylic resin can be selected the 2-Hydroxylated acrylic resin for use.
Preparation method of the present invention is with reference to as follows: add UV photocuring light trigger, acrylic resin, the agent of resistance oxidation protection in aluminium paste pigment; be heated to 50 ℃; stir in the stirrer of 40000 rev/mins of rotating speeds, sealing is at room temperature preserved and is promptly got high gloss ink for screen printing of the present invention.
Using method of the present invention is as follows:
1, flame or corona treatment are adopted in the plastic component surface;
2, printing ink of the present invention is coated on the plastic component surface by screen process press;
3, with ink solidification.
Each component among the present invention all can be buied on market.
Technique effect of the present invention is: the present invention with the suitable agent of resistance oxidation protection, UV trigger for optical solidification, acrylic resin, can slow down aluminium paste pigment parcel " aluminium " oxidized speed in the printing ink, thereby reach silvery white effect.
Embodiment
Embodiment one:
The preparation of printing ink:
In 1 kilogram of aluminium paste pigment (model is Silver Paste EO), add 25 gram 1-hydroxy-cyclohexyl phenyl-acetones, 80 gram 2-Hydroxylated acrylic resins and 30 gram resistance oxidation protection agent (model is 1753); be heated to 50 ℃ outward; stir in the stirrer of 40000 rev/mins of rotating speeds, sealing is at room temperature preserved.
The use of printing ink:
Glossiness and viscosity are observed in the above-mentioned silvery white printing ink placement for preparing after 24 hours, with printing ink by screen process press on vinyon packaging tube surface (in advance through flame or corona treatment) print off the standard reference example edition, solidify by ultraviolet lamp box (being the UV lamp box) then, sealing is preserved.Printing ink through the following time period, is printed off example edition respectively and observes and contrast, and the result is as follows:
A. the color and luster through 7 days printing ink does not change;
B. the color and luster through 15 days printing ink does not change;
C. the color and luster through 30 days printing ink does not change.
Embodiment two:
The preparation of printing ink:
In 1 kilogram of aluminium paste pigment (model is Silver Paste EO), add 40 gram 1-hydroxy-cyclohexyl phenyl-acetones, 120 gram 2-Hydroxylated acrylic resins and 65 gram resistance oxidation protection agent (model is 1753); be heated to 50 ℃ outward; stir in the stirrer of 40000 rev/mins of rotating speeds, sealing is at room temperature preserved.
The use of printing ink:
Glossiness and viscosity are observed in the above-mentioned silvery white printing ink placement for preparing after 24 hours, with printing ink by screen process press on vinyon packaging tube surface (in advance through flame or corona treatment) print off the standard reference example edition, solidify by the UV lamp box then, sealing is preserved.Printing ink through the following time period, is printed off example edition respectively and observes and contrast, and the result is as follows:
A. the color and luster through 7 days printing ink does not change;
B. the color and luster through 15 days printing ink does not change;
C. the color and luster through 30 days printing ink does not change.
Embodiment three:
The preparation of printing ink:
In 1 kilogram of aluminium paste pigment (model is Silver Paste EO), add 30 gram 1-hydroxy-cyclohexyl phenyl-acetones, 60 gram 2-Hydroxylated acrylic resins and 100 gram resistance oxidation protection agent (model is 1753); be heated to 50 ℃ outward; stir in the stirrer of 40000 rev/mins of rotating speeds, sealing is at room temperature preserved.
The use of printing ink:
Glossiness and viscosity are observed in the above-mentioned silvery white printing ink placement for preparing after 24 hours, with printing ink by screen process press on vinyon packaging tube surface (in advance through flame or corona treatment) print off the standard reference example edition, solidify by the UV lamp box then, sealing is preserved.Printing ink through the following time period, is printed off example edition respectively and observes and contrast, and the result is as follows:
D. the color and luster through 7 days printing ink does not change;
E. the color and luster through 15 days printing ink does not change;
F. the color and luster through 30 days printing ink does not change.
Embodiment four:
The preparation of printing ink:
In 1 kilogram of aluminium paste pigment (model is Silver Paste EO), add 35 gram 1-hydroxy-cyclohexyl phenyl-acetones, 100 gram 2-Hydroxylated acrylic resins and 25 gram resistance oxidation protection agent (model is 1753); be heated to 50 ℃ outward; stir in the stirrer of 40000 rev/mins of rotating speeds, sealing is at room temperature preserved.
The use of printing ink:
Glossiness and viscosity are observed in the above-mentioned silvery white printing ink placement for preparing after 24 hours, with printing ink by screen process press on vinyon packaging tube surface (in advance through flame or corona treatment) print off the standard reference example edition, solidify by the UV lamp box then, sealing is preserved.Printing ink through the following time period, is printed off example edition respectively and observes and contrast, and the result is as follows:
G. the color and luster through 7 days printing ink does not change;
H. the color and luster through 15 days printing ink does not change;
I. the color and luster through 30 days printing ink does not change.
Aluminium paste pigment in the various embodiments described above (Silver Paste EO) is available from the Visprox company of Holland; resistance oxidation protection agent (1753) is available from the CIBA company of Switzerland, and 1-hydroxy-cyclohexyl phenyl-acetone and 2-Hydroxylated acrylic resin are available from the Schekolin AG company of Switzerland.
From the foregoing description as seen, printing ink of the present invention still can keep original silvery white gloss and effect through after the long period.
Claims (3)
1. high gloss ink for screen printing that is used on the plastic component; it is characterized in that: form by aluminium paste pigment, UV photocuring light trigger, acrylic resin, the agent of resistance oxidation protection; their weight ratio is aluminium paste pigment: UV photocuring light trigger: acrylic resin: resistance oxidation protection agent=1000: (25-40): (60-125): (25-100).
2. the high gloss ink for screen printing that is used on the plastic component according to claim 1 is characterized in that: described UV photocuring light trigger is a 1-hydroxy-cyclohexyl phenyl-acetone.
3. the high gloss ink for screen printing that is used on the plastic component according to claim 1 and 2 is characterized in that: described acrylic resin is the 2-Hydroxylated acrylic resin.