CN101215700A - Magnesium alloy chemical synthesis treatment liquid - Google Patents
Magnesium alloy chemical synthesis treatment liquid Download PDFInfo
- Publication number
- CN101215700A CN101215700A CNA2007100195137A CN200710019513A CN101215700A CN 101215700 A CN101215700 A CN 101215700A CN A2007100195137 A CNA2007100195137 A CN A2007100195137A CN 200710019513 A CN200710019513 A CN 200710019513A CN 101215700 A CN101215700 A CN 101215700A
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- treatment liquid
- chemical synthesis
- synthesis treatment
- alloy chemical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to magnesium alloy formation treatment solution, wherein one liter of magnesium alloy formation treatment solution comprises the following materials which are dissolved in water: 10-30g molybdate ion compounds, 2-10 ml phosphoric acid, 0.1-5g tungsten acid compounds and 0.1-5g vanadate radical compounds. The using steps are that magnesium alloy which is regulated on surface is soaked in the magnesium alloy formation treatment solution for 45 seconds-5minutes, the working temperature is 35-45 DEG C, after being taken out, the magnesium alloy is cleaned by second pure water and is baked one time, and the surface of the alloy is formed with a protecting film which is corrosion resistance and has low impedance. The formula has small pollution for environment and has no toxicity for production personnel, and the cost is low.
Description
[technical field]
The invention belongs to field of metal surface treatment, be specifically related to the phosphatization protective treatment field of Mg alloy surface, on magnesium alloy, produce chemical protection film thus with splendid solidity to corrosion and rust-preventing characteristic.
[background technology]
Magnesium alloy is because proportion is low; intensity is enough and be suitable for reclaiming and use; so be widely used in automobile and electrical equipment; but because magnesium alloy chemical is reactive high; its surface forms one deck oxide compound rapidly in atmosphere; cause corrosion; therefore needing before use that this magnesium alloy is carried out protective handles; wherein change into and adopt chromic salt or phosphoric acid salt in the treatment process usually; to form the protective membrane that one deck strengthens corrosion stability of magnesium alloy: because the use of chromium compounds can cause water source and soil pollution; do not meet environmental protection requirement; therefore this area mostly adopts phosphate system to handle at present; but; use phosphoric acid salt is second-rate the formed protective membrane of Mg alloy surface; strengthen the limited in one's ability of magnesium alloy rotproofness; therefore, the Chrome-free of magnesium alloy and the research and development that change into treatment technology that do not reduce the protective membrane quality have become the important directions and the problem demanding prompt solution of magnesium alloy surface protective technical development.
Therefore, in fact be necessary to propose a kind of magnesium alloy chemical synthesis treatment liquid, that neither weakens magnesium alloy changes into the less again contaminate environment of treatment effect.
[summary of the invention]
Therefore, the object of the present invention is to provide a kind of magnesium alloy chemical synthesis treatment liquid, can form the measured protective film of one deck matter at Mg alloy surface, and less contaminate environment.
For reaching above-mentioned purpose, magnesium alloy chemical synthesis treatment liquid of the present invention, comprise molybdenum acid ion, phosphoric acid, tungstate ion and metavanadic acid radical ion, and the concentration as the water-soluble cpds in molybdenum acid ion source is 10-30g/L, the concentration of phosphoric acid solution is 2-10ml/L, is 0.1-5g/L and is 0.1-5g/L as the concentration of the water-soluble cpds in metavanadic acid radical ion source as the concentration of the water-soluble cpds in tungstate ion source.
Use the step of this chemical synthesis treatment liquid as follows:
Magnesium alloy after table transferred soaked 45 seconds-5 minutes in the solution of the metavanadate of the tungstate of the phosphoric acid that comprises the molybdate of 10-30g/L, 2-10ml/L, 0.1-5g/L and 0.1-5g/L, working temperature is 35-45 ℃, take out after second pure water cleans and once baking, then this alloy surface formation one deck outward appearance is linen protective film.
From the film forming properties test result as can be known, magnesium alloy does not after treatment still have obvious corrosion through 8 hours surfaces of neutral salt spray test, and measure two test point of distance≤5cm on this protective film, the impedance between them＜2 ohm meet the corrosion-resistant and low-impedance requirement of magnesium alloy fully.
In addition, compared to prior art, magnesium alloy chemical synthesis treatment liquid of the present invention does not contain sexavalent chrome, environmental pollution is little, and the material in this chemical synthesis treatment liquid is all nontoxic or low toxicity material, when using this prescription to produce in enormous quantities, can not produce murder by poisoning to producers, and with low cost; Again, this chemical synthesis treatment liquid can use under mesophilic condition, and energy consumption is little.
[embodiment]
This magnesium alloy chemical synthesis treatment liquid comprises as the molybdenum acid ion of film forming host and phosphoric acid, and the compound concentration that molybdenum acid ion wherein is provided is 10-30g/L, and concentration of phosphoric acid is 2-10ml/L.
Preferably, comprise in every liter of this magnesium alloy chemical synthesis treatment liquid:
Molybdate compound 10-30g;
Phosphoric acid 2-10ml;
Wolframate radical compound 0.1-5g;
Metavanadic acid radical compound 0.1-5g.
Wherein, this molybdate compound, wolframate radical compound and metavanadic acid radical compound all water-soluble (being preferably pure water), and more preferably, this molybdate compound, wolframate radical compound and metavanadic acid radical compound comprise sodium ion or ammonium ion respectively.
The strength of solution of molybdate compound, phosphoric acid, wolframate radical compound and metavanadic acid radical compound is not limited in the above-mentioned scope, because it depends on that desire forms the thickness and the soak time of protective film.
Preferably, this magnesium alloy chemical synthesis treatment liquid pH value is mainly controlled the pH value by adding phosphoric acid solution between 2 to 3.5.If the pH value is lower than 2, the solvency action of magnesium alloy is too active, with its surface of induced damage resistive; If the pH value is higher than 3.5, then can't provide a free acid environment for molybdate.
Use two preferred embodiments of this magnesium alloy chemical synthesis treatment liquid as follows:
Embodiment 1:
To show to transfer (alloy process degreasing, after the pickling, re-using PS-F01 is that surface conditioner is handled, when alloy phosphating, can promote the phosphatize phosphate coat nucleus to produce, thereby shorten the formation time of alloy surface phosphatize phosphate coat, make phosphatize phosphate coat thin and even, fine and close, improve the rustless property of alloy, the compound method of this surface conditioner wherein: add 1-2 kilogram surface conditioner in the clear water per ton, can use after stirring, and this surface conditioner solution pH value is 7.5-9) after magnesium alloy comprising the 10g/L molybdate, 9ml/L phosphoric acid, 0.2g/L soaked 45 seconds in this magnesium alloy chemical synthesis treatment liquid of tungstate and 5g/L metavanadate, 35 ℃ of working temperatures, take out after 1 st pure water cleans and once baking, then this alloy surface adhesion one deck appearance is linen protective film.
Embodiment 2:
Magnesium alloy behind the table accent was soaked 5 minutes in this magnesium alloy chemical synthesis treatment liquid that comprises 30g/L molybdate, 2ml/L phosphoric acid, 5g/L tungstate and 0.1g/L metavanadate, 45 ℃ of working temperatures, take out after 1 st pure water cleans and once baking, then this alloy surface adhesion one deck appearance is linen protective film.
The working temperature of above magnesium alloy chemical synthesis treatment liquid and time are not limited in the above-mentioned scope, because it depends on that desire forms the thickness of protective film.
Claims (6)
1. magnesium alloy chemical synthesis treatment liquid, it is characterized in that: it is water-soluble to comprise following material in every liter of this magnesium alloy chemical synthesis treatment liquid:
Molybdate compound 10-30g;
Phosphoric acid 2-10ml;
Wolframate radical compound 0.1-5g;
Metavanadic acid radical compound 0.1-5g.
2. magnesium alloy chemical synthesis treatment liquid as claimed in claim 1 is characterized in that: this molybdate compound, wolframate radical compound and metavanadic acid radical compound also comprise sodium ion or ammonium ion.
3. magnesium alloy chemical synthesis treatment liquid as claimed in claim 2 is characterized in that: the pH value of this magnesium alloy chemical synthesis treatment liquid is between 2 and 3.5.
4. magnesium alloy chemical synthesis treatment liquid as claimed in claim 1 is characterized in that: the working hour of this magnesium alloy chemical synthesis treatment liquid is 45 seconds-5 minutes.
5. magnesium alloy chemical synthesis treatment liquid as claimed in claim 1 is characterized in that: the working temperature of this magnesium alloy chemical synthesis treatment liquid is 35-45 ℃.
6. magnesium alloy chemical synthesis treatment liquid as claimed in claim 1 is characterized in that: this solvent is a pure water.