CN101210387A - Method for manufacturing wearing article surface layer coated glue line - Google Patents
Method for manufacturing wearing article surface layer coated glue line Download PDFInfo
- Publication number
- CN101210387A CN101210387A CNA2006101673095A CN200610167309A CN101210387A CN 101210387 A CN101210387 A CN 101210387A CN A2006101673095 A CNA2006101673095 A CN A2006101673095A CN 200610167309 A CN200610167309 A CN 200610167309A CN 101210387 A CN101210387 A CN 101210387A
- Authority
- CN
- China
- Prior art keywords
- line
- glue
- wear
- synthetic
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A preparation method of a surface coating adhesive layer on clothing comprises the following steps of: pre-mixing a base material containing components of predetermined ratios, adding a polymer, mixing, stirring uniformly so that the polymer completely absorbs the components of the base material to form a coagulated combination, heating the combination to a molten temperature to molt the combination to a liquid state, uniformly applying the molten combination on the base surface of the clothing, cooling to form an adhesive layer, and uniformly applying a powdery solid particle barrier layer on the surface of the adhesive layer to make the powder of the barrier layer attached on the surface of the adhesive layer to obtain the final product.
Description
Technical field
The present invention is relevant with a kind of wearing article surface layer coated glue line, more detailed it, be meant especially and a kind of base material and high molecular polymerization material mixed stirring, insert a heating tank hot melt, coat a wearing article surface layer again, with cooling forming is a glue-line, follows in the manufacture method of the wearing article surface layer coated glue line of this glue-line surface coated one barrier layer.
Background technology
Press; the known knitted thing; as socks; gloves; protector; tippet; goods such as fingerstall or cap; be to be worn on one's body the user; make knitted fabric have a warming and attractive in appearance effect; in addition; because modern's standard of living promotes; health care for daily life is paid attention to relatively, therefore, has the interpolation far infrared on the market; the knitted fabric of composition such as magnetite or activated carbon material; so that the user is when dressing knitted fabric; not only have thermal effect, and human body is had the effect of health care, only; the known knitted thing is to add far infrared; composition such as magnetite or activated carbon material is in the fiber of knitted fabric; but when additive is the liquid state health treatment; powder particle or when being difficult for being placed in the composition of knitted fabric fiber, it is can't make an addition to make knitted fabric in the fiber, makes this knitted fabric health-care effect limited.
Summary of the invention
The invention provides a kind of manufacture method of wearing article surface layer coated glue line, it is the base material premix that will contain the predetermined ratio composition earlier, add the high molecular polymerization material again and mix stirring, make the high molecular polymerization material absorb the composition of base material fully, and become a synthetic that condenses shape, and will mix completely that synthetic is heated to melt temperature, make it be fused solution, again with the even fusion synthetic that is coated with in the basic unit top layer of a wear, with cooling forming is a glue-line, last, evenly is coated with a Powdered solid granulates barrier layer in this glue-line surface, make the powder of this barrier layer be attached at the glue-line top layer, can finish finished product.
The manufacture method of wearing article surface layer coated glue line provided by the present invention, this glue-line be can add have the preserving moisture of different efficacies, whiten, the liquid object or the powder particle of curative effect or Chinese medicinal ingredients, in order to do making the user when dressing this wear, also has multiple different health-care effect, in addition, this barrier layer is to be coated in the glue-line surface, and the powder of this barrier layer is attached at this glue-line top layer, can make this glue-line surface can not produce the viscous sense, the user can dress use after buying immediately, dresses this wear to make things convenient for the user.
The manufacture method of a kind of wearing article surface layer coated glue line of the present invention is characterized in that, its step comprises:
(1) base material premix:
The base material that will contain the predetermined ratio composition mixes stirring, and it is evenly mixed fully;
(2) synthetic:
Predetermined high molecular polymerization material added in the base material mix stirring, make the high molecular polymerization material can absorb the predetermined composition of base material fully, and become a synthetic that condenses shape;
(3) hot melt:
Be heated to the melt temperature of synthetic with mixing synthetic completely, make it be fused solution;
(4) coating:
With a synthetic by precalculated position, the wear basic unit top layer coating fusion that basic unit constituted, make this basic unit top layer evenly be coated with the synthetic of fusion;
(5) cooling forming:
After treating that this basic unit top layer is coated with the wear cooling of fusion synthetic, this synthetic directly is condensed in this basic unit's top layer moulding one glue-line, this glue-line directly is posted solid in this basic unit top layer, and this glue-line is partly to permeate in this basic unit, makes this glue-line and basic unit's close adhesion;
(6) coating barrier layer:
Evenly be coated with the barrier layer of a Powdered solid granulates in the glue-line surface of this wear, and the powder of this barrier layer is to be attached at this glue-line top layer.
Wherein, this wear is to be knitted fabric, Nonwovens or leather material wherein a kind of goods of more than one the socks that basic unit constituted, gloves, protector, tippet, fingerstall, cap, clothes, trousers or facial mask wherein.
Wherein, this base material is plasticiser, softening oil, Chinese wax oil, maintenance oil, the essential oil by liquid state or ties up wherein more than one of its life and the flavor powder of solubility solid state powder or dolomol and contain liquid uniform ingredients and mix and constituted, in addition, be the insoluble additive that can mix at this moment, this additive be preserve moisture for far infrared ceramic powder and other have, whiten, curative effect or Chinese medicinal ingredients constitute.
Wherein, this high molecular polymer powder be for TPR, TPE, TPU, silica gel and rubber wherein more than one one-tenth branch constitute.
Wherein, when this synthetic hot melt state, but Dope Additive, this additive are for the far infrared ceramic powder of insoluble solid state powder or Chinese medicine and dissolve in the flavor powder of solid state powder of synthetic or dolomol more than one materials that are not added into wherein in base materials.
Wherein, this wear is to be placed on the mould of being scheduled to, and it is strutted fully, impregnated in the heating tank, does the operation of comprehensive even coated glue line for this wearing article surface layer.
Wherein, one heating tank is to be shaped to reservation shape, and is arranged on the substrate and heats, and this wear part be impregnated in this heating tank, supply this wearing article surface layer to do the operation of the even coated glue line of locality, also cool off this wear and this heating tank synchronously the coating back.
Wherein, this wear is to be placed on a predetermined mould earlier, again this wear is arranged in the heating tank, this heating tank is to be arranged with the perfusion groove that has the space between moulding one relative this wear in its inside, and this heating tank is to offer a fill orifice and a relative steam vent, filling out the space that is distributed between this depressed part and wear for the synthetic that injects fusion, is glue-line with the cooling forming.
Wherein, this barrier layer is constituted by talcum powder, talcum powder, Supermicron pearl powder, zinc oxide, zinc stearate, salicylic acid, stephanotis powder or glycyrrhizic acid amine component, its be also can be have the preserving moisture of different efficacies, whiten, the Powdered solid granulates of curative effect or Chinese medicinal ingredients constitutes.
Wherein, be to be installed with a heater element between this basic unit and this glue-line.
Description of drawings
For further specifying concrete technology contents of the present invention, below in conjunction with embodiment and accompanying drawing describes in detail as after, wherein:
Fig. 1 is the block schematic diagram of the manufacture method of wearing article surface layer coated glue line of the present invention.
Fig. 2 is the manufacture method schematic flow sheet of preferred embodiment of the present invention.
Fig. 3 is the finished product appearing diagram of preferred embodiment of the present invention.
Fig. 4 is the local amplification view of the finished product of preferred embodiment of the present invention.
Fig. 5 is the mould coating schematic diagram of another embodiment of the present invention.
Fig. 6 is the finished product appearing diagram of another embodiment of the present invention.
Fig. 7 is the mould coating cutaway view of further embodiment of this invention.
Fig. 8 is the finished product appearing diagram of further embodiment of this invention.
Fig. 9 is the finished product cutaway view of yet another embodiment of the invention.
The specific embodiment
See also Fig. 1 to shown in Figure 4, the invention provides a kind of preferred embodiment of manufacture method of wearing article surface layer coated glue line, wherein, one wear 1 is to be shaped to gloves, it also can be socks, tippet, fingerstall, cap, clothes, trousers or facial mask etc. wearable in human body and with the goods of contact skin, this wear 1 is to include a basic unit 10, members such as one glue-line 20 and a barrier layer 30 are formed, and this basic unit 10 is the primary structures for this wear 1, and this wear 1 is to can be knitted fabric, material such as Nonwovens or leather constitutes, therefore, the manufacture method step of this wear 1 surface layer coated glue line 20 is to include:
(1) base material premix:
The composition that will contain predetermined ratio composition liquid state, as plasticiser, softening oil, Chinese wax oil, maintenance oil, essential oil, tie up its life, sweet apricot oil, aloe, avocado oil, carrot oil, evening primrose oil, grape seed oil, hazelnut oil, lotus lotus flower oil, Hawaii drupe oil, olive oil, rose hip oil, Squalene, other the pre-liquid parts that adds of nut oil or wheat embryo wet goods and the composition of solubility solid state powder, other has maintenance as flavor powder or dolomol etc., the composition of fragrance or curative effect, choose required composition and after constituting base material 21, mix and stir, it is evenly mixed fully, in addition, be the insoluble additive 23 that can mix at this moment, this additive 23 is to preserve moisture for far infrared ceramic powder and other have, whiten, curative effect or Chinese medicinal ingredients constitute;
(2) synthetic:
To mix stirring in the predetermined high molecular polymerization material 22 adding base materials 21, this high molecular polymerization material 22 is to be TPR powder institute constitutor, it is that the material that also can be compositions such as TPE, TPU, silica gel and rubber constitutes, after this high molecular polymerization material 22 dissolves in base material 21, can absorb the composition of base material 21 fully, and become a synthetic 24 that condenses shape;
(3) hot melt:
To mix completely synthetic 24 and insert in the heating tank 40 and be heated to its melt temperature, and make this synthetic 24 be molten condition;
(4) Dope Additive:
When the molten condition of synthetic 24, also but Dope Additive 23, and the fusing point of this additive 23 is the melt temperatures that can be higher than synthetic 24, as far infrared ceramic powder or Chinese medicine, making this additive 23 is to keep solid-state state in this synthetic 24, can not be melted in this synthetic 24, in addition, this additive 23 also is to can be the fusible fusible one-tenth branch that is melted in this synthetic 24 to constitute, in the synthetic 24 of the state of dissolving, add, it is evenly dissolved in the synthetic 24, so that this synthetic 24 can be according to different demands, the interpolation of heterogeneity is arranged, increase its variability;
(5) coating:
This wear 1 is placed on the mould 50, this mould 50 is to be shaped to the shape of this wear 1 relatively, state for strutting fully when making this wear 1 be sheathed on the mould 50, then, this wear 1 be impregnated in the heating tank 40, make the synthetic 24 of comprehensive even coating one fusion in basic unit 10 top layers of this wear 1;
(6) cooling forming:
Treat that the top layer is coated with wear 1 cooling of fusion synthetic 24, at this moment, this wear 1 is to do a spinning movement with mould 50, make the synthetic 24 of fusion be uniformly distributed in basic unit 10 top layers of this wear 1, in addition, this wear 1 can be put into cold water with mould 50, with accelerating cooling process, in order to do basic unit's 10 top layer moulding, one glue-line 20 that makes this wear 1, and this glue-line 20 is partly to permeate in this basic unit 10, makes this glue-line 20 and basic unit's 10 close adhesion;
(7) coating barrier layer:
Glue-line 20 surfaces in this wear 1 evenly are coated with a barrier layer 30, this barrier layer 30 is to constitute for talcum powder, talcum powder, Supermicron pearl powder, zinc oxide, zinc stearate, salicylic acid, stephanotis powder, Radix Glycyrrhizae acid amide etc. become branch, its be also can be have the preserving moisture of different efficacies, whiten, the Powdered solid granulates that composition constituted such as curative effect or Chinese medicine, and the powder of this barrier layer 30 is to be attached at this glue-line 20 top layers;
(8) finished product:
After treating glue-line 20 surface coated one barrier layer 30 of this wear 1, this mould 50 is removed, can finish finished product.
After these glue-line 20 moulding; the maintenance composition in the base material 21 in it and the composition of additive 23; can absorb the effectiveness of reaching a maintenance when making the user dress; simultaneously; because of this glue-line 20 can intercept extraneous environment; human body is formed with a seal cavity when dressing; skin care products can be absorbed by the body fully; and there is the protection of a sealing take good care of by this glue-line 20; in addition; the base material 21 of this glue-line 20 and the composition of additive 23 can be with the need difference; and can have different compositions to add; can change at different demands; of many uses; in addition; this glue-line 20 is to be coated in this precalculated position, basic unit 10 inboard top layer; its surface coated has barrier layer 30; and the powder of this barrier layer 30 is evenly to be attached at this glue-line 20 top layers; make these glue-line 20 surfaces cover one deck barrier layer 30 fully; make the top layer of this glue-line 20 can not produce the viscous sense; so that the user is when dressing this wear 1; human body and this glue-line 20 contact-making surfaces are because of having barrier layer 30; dress with convenient; and when user's contact skin arrived this wear 1, the base material 21 in this glue-line 20 and the maintenance composition of additive 23 can produce effectiveness, simultaneously; the composition of this barrier layer 30 can be has curative effect; whiten or the powdery granule of function such as health care constitutes, also can produce favorable effects.
In addition; please cooperate and consult Fig. 5 to shown in Figure 6; the invention provides another embodiment of a kind of manufacture method of wearing article surface layer coated glue line; its major function is same with last embodiment; so repeat no more; wherein; this wear 1 is to be shaped to a protector; it is to can be used for knee-pad; purposes such as wrister or protection ankle; this wear 1 is to be placed on one to be shaped on the mould 60 of relative this wear 1 shape; one heating tank 70 is arranged on the substrate 80; at this moment; this heating tank 70 is the shapes that are shaped to these wear 1 desire coating synthetic 24 areas; then; after being heated to predetermined temperature in these substrate 80 belows; heating source with these substrate 80 belows removes again; the synthetic 24 of molten condition is added in this heating tank 70; local location with this wear 1 pre-coating is attached at this heating tank 70 tops again; make the synthetic 24 of even coating one fusion of basic unit's 10 top layer localities of this wear 1; in addition; this wear 1 is not to be placed on the mould 60; and directly be pressed on the heating tank 70; then; treat synthetic 24 coolings of fusion; again this wear 1 is peeled off this heating tank 70; in these glue-line 20 surface coated barrier layers 30, can finish the finished product of a wear 1 surface layer coated glue line 20 again, in addition; these heating tank 70 inner surfaces are coated with the material of a Teflon in advance; after making things convenient for this synthetic 24 to solidify, be easy to peel off this heating tank 70, in addition, because of this glue-line 20 is to be coated in basic unit's 10 outer skin; can be when base material 21 mixes stirring; adjust the component ratio of base material 21, make it be shaped to one and have the harder glue-line of hardness 20, the harder glue-line 20 of this hardness can produce a good buffering effect; can when being subjected to the impact of external force, produce a preferable protective effect.
In addition, please cooperate and consult Fig. 7 to shown in Figure 8, the invention provides a kind of another embodiment of manufacture method of wearing article surface layer coated glue line, its major function is same with last embodiment, so repeat no more, wherein, this wear 1 is to be shaped to socks, this wear 1 is to be placed on one earlier to be shaped to the mould 90 of this wear 1 shape relatively, again this wear 1 is arranged in the heating tank 100, this heating tank 100 is to be arranged with a perfusion groove 101 in its inside, make this wear 1 and 101 of grooves of perfusion have one by the space of desire moulding glue-line 20 thickness, this heating tank 100 is to be convexly equipped with predetermined several projections 102 in these perfusion groove 101 bottoms, when making this wear 1 be arranged in this perfusion groove 101, be to join with these projections 102, this mould 100 is that one side is offered a fill orifice 103 in the top, also offer a steam vent 104 relatively in the below opposite side, this heating tank 100 is heated to predetermined temperature simultaneously, with synthetic 24 be heated to be molten condition after, again the synthetic 24 of fusion is injected the perfusion groove 101 of this heating tank 100 via these fill orifice 103 pressurizations, it is mobile to make the synthetic 24 of these fusions inject the space of 1 of these perfusion grooves 101 and this wear, to fill up the space, and this steam vent 104 is can discharge the air that exists originally in these heating tank 100 perfusion grooves 101 to go out, make the synthetic 24 of basic unit's even coating fusion in 10 top layers of this wear 1, after treating glue-line 20 moulding, this wear 1 bottom and this heating tank 100 projections 102 position contacting places are because of the synthetic 24 of no coating fusion, so be shaped to predetermined several air-vents 11, this wear 1 is broken away from this heating tank 100, again in these glue-line 20 surface coated barrier layers 30, when the user dresses this wear 1, because of this wear 1 top layer has glue-line 20, can intercept extraneous air, can provide a warming effect to human body, and because of human body perspire meeting produces aqueous vapor, these air-vents 11 are the basic units 10 that the aqueous vapor that produces can be disposed to this wear 1, make this basic unit 10 can absorb the aqueous vapor that the human body perspire produces, so that these air-vents 11 have perspire, regulate the effect of aqueous vapor, and move in cold climate, as climb the mountain, when skiing or walking, can have the effect of warming perspire.
In addition, please cooperate consult shown in Figure 9, the invention provides an a kind of embodiment again of manufacture method of wearing article surface layer coated glue line, its major function is same with last embodiment, so repeat no more, wherein, this wear 1 is to be shaped to a heating cushion, one heater element 110 is can be arranged in the basic unit 10 of this wear 1, pour into this glue-line 20 again in these heater element 110 tops, make the glue-line 20 of part can fill up the space of 110 of this heater elements, treat these glue-line 20 moulding after, can set firmly this heater element 110 in this basic unit 10, and this heater element 110 is constituted by other materials that can conduct heat energy such as carbon fiber electrothermal line or metallic plate materials, so that the user is when dressing, this wear 1 can provide a hot compress effect to human body, in addition, base material 21 in this glue-line 20 and additives 23 can improve temperature because of these heater element 110 heatings, and quicken to discharge the contained maintenance composition of this base material 21 and additive 23, and temperature improves, and can quicken the maintenance composition of this base material 21 of absorption of human body and additive 23.
Now, again feature of the present invention and attainable expection effect thereof are presented below:
1, the manufacture method of wearing article surface layer coated glue line of the present invention, this glue-line be can add have the preserving moisture of different efficacies, whiten, the liquid object or the powder particle of curative effect or Chinese medicinal ingredients, so that the user is when dressing, this glue-line can provide protection, and has multiple different health-care effect.
2, the manufacture method of wearing article surface layer coated glue line of the present invention, this barrier layer is the wear glue-line surface that can evenly coat Any shape easily, in order to do to reach the effect of handling ease, in addition, this barrier layer is to be coated in this glue-line surface, and this barrier layer can make the glue-line surface can not produce the viscous sense, to make things convenient for the user to be easy to dress this wear, and when dressing, can not experience the viscosity of this glue-line, and then promote the comfortableness of dressing when using.
3, the manufacture method of wearing article surface layer coated glue line of the present invention, the powder composition of this barrier layer be can be have the preserving moisture of different efficacies, whiten, composition such as curative effect or Chinese medicine, make it that effectiveness of maintenance can be arranged health.
4, the manufacture method of wearing article surface layer coated glue line of the present invention; the base material maintenance composition in this glue-line and the one-tenth branch of additive ooze gradually to the inboard; can absorb these compositions when making the user dress; this glue-line can intercept extraneous environment in addition; human body can have a confined space when dressing, and skin care products can be absorbed by the body fully, and has the protection of a sealing to take good care of by this glue-line; and be difficult for to improve the permanent effect that continues use because of wear and external world's friction are run off skin care products.
5, the manufacture method of wearing article surface layer coated glue line of the present invention, this glue-line has soft characteristic, the impulse force during the available buffer collision, the injury when colliding to reduce.
6, the manufacture method of wearing article surface layer coated glue line of the present invention, this glue can provide a warming effect to human body, and these air-vents can be disposed to the aqueous vapor that the human body perspire produces the basic unit of this wear, make this basic unit absorb the aqueous vapor that produces, so that these air-vents have the effect of perspire, adjusting aqueous vapor.
7, the manufacture method of wearing article surface layer coated glue line of the present invention is to increase by a heater element between the basic unit of this wear and this glue-line, so that the user when dressing, can provide a hot compress comfortable effect to human body.
In sum, the present invention has its splendid progressive practicality in fact in like product, simultaneously all over looking into domestic and international technical data about this class formation, also finding no identical construction in the document exists formerly, be to have possessed the patent of invention condition, so file an application in accordance with the law so that, the present invention is real.
Only, above-described, only be of the present invention one preferable possible embodiments, so the equivalent structure that every application specification of the present invention and claim are done changes, ought to be included in the claim of the present invention.
Claims (10)
1. the manufacture method of a wearing article surface layer coated glue line is characterized in that, its step comprises:
(1) base material premix:
The base material that will contain the predetermined ratio composition mixes stirring, and it is evenly mixed fully;
(2) synthetic:
Predetermined high molecular polymerization material added in the base material mix stirring, make the high molecular polymerization material can absorb the predetermined composition of base material fully, and become a synthetic that condenses shape;
(3) hot melt:
Be heated to the melt temperature of synthetic with mixing synthetic completely, make it be fused solution;
(4) coating:
With a synthetic by precalculated position, the wear basic unit top layer coating fusion that basic unit constituted, make this basic unit top layer evenly be coated with the synthetic of fusion;
(5) cooling forming:
After treating that this basic unit top layer is coated with the wear cooling of fusion synthetic, this synthetic directly is condensed in this basic unit's top layer moulding one glue-line, this glue-line directly is posted solid in this basic unit top layer, and this glue-line is partly to permeate in this basic unit, makes this glue-line and basic unit's close adhesion;
(6) coating barrier layer:
Evenly be coated with the barrier layer of a Powdered solid granulates in the glue-line surface of this wear, and the powder of this barrier layer is to be attached at this glue-line top layer.
2. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, this wear is to be knitted fabric, Nonwovens or leather material wherein a kind of goods of more than one the socks that basic unit constituted, gloves, protector, tippet, fingerstall, cap, clothes, trousers or facial mask wherein.
3. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, this base material is plasticiser, softening oil, Chinese wax oil, maintenance oil, the essential oil by liquid state or ties up wherein more than one of its life and the flavor powder of solubility solid state powder or dolomol and contain liquid uniform ingredients and mix and constituted, in addition, be the insoluble additive that can mix at this moment, this additive be preserve moisture for far infrared ceramic powder and other have, whiten, curative effect or Chinese medicinal ingredients constitute.
4. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, this high molecular polymer powder be for TPR, TPE, TPU, silica gel and rubber wherein more than one one-tenth branch constitute.
5. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, when this synthetic hot melt state, but Dope Additive, this additive are for the far infrared ceramic powder of insoluble solid state powder or Chinese medicine and dissolve in the flavor powder of solid state powder of synthetic or dolomol more than one materials that are not added into wherein in base materials.
6. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, this wear is to be placed on the mould of being scheduled to, it is strutted fully,, do the operation of comprehensive even coated glue line for this wearing article surface layer impregnated in the heating tank.
7. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, one heating tank is to be shaped to reservation shape, and be arranged on the substrate and heat, this wear part be impregnated in this heating tank, supply this wearing article surface layer to do the operation of the even coated glue line of locality, also cool off this wear and this heating tank synchronously the coating back.
8. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, this wear is to be placed on a predetermined mould earlier, this wear is arranged in the heating tank, this heating tank is to be arranged with the perfusion groove that has the space between moulding one relative this wear in its inside, and this heating tank is to offer a fill orifice and a relative steam vent again, filling out the space that is distributed between this depressed part and wear for the synthetic that injects fusion, is glue-line with the cooling forming.
9. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, this barrier layer is constituted by talcum powder, talcum powder, Supermicron pearl powder, zinc oxide, zinc stearate, salicylic acid, stephanotis powder or glycyrrhizic acid amine component, its be also can be have the preserving moisture of different efficacies, whiten, the Powdered solid granulates of curative effect or Chinese medicinal ingredients constitutes.
10. as the manufacture method of claim 1 a described wearing article surface layer coated glue line, it is characterized in that, wherein, is to be installed with a heater element between this basic unit and this glue-line.