CN101210127A - Plastic surface color coating agent and preparing method thereof - Google Patents
Plastic surface color coating agent and preparing method thereof Download PDFInfo
- Publication number
- CN101210127A CN101210127A CNA2006101556284A CN200610155628A CN101210127A CN 101210127 A CN101210127 A CN 101210127A CN A2006101556284 A CNA2006101556284 A CN A2006101556284A CN 200610155628 A CN200610155628 A CN 200610155628A CN 101210127 A CN101210127 A CN 101210127A
- Authority
- CN
- China
- Prior art keywords
- coating agent
- plastic surface
- color coating
- surface color
- aluminium powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a colorful coating agent of the surface of plastic and a preparation method thereof. The coating agent consists of acetone, CDA, o-benzoic acid dibutyl ester, pear powder, powdered aluminum and paint. Under the processing temperature, the coating agent has good stability, light resistance, chemicals resistance and small toxicity and color does not bleed as well as the plastic does not become old; if the coating agent is painted on an object, the film forming performance is good and quick and the color is not changed.
Description
Technical field
The present invention relates to a kind of chemical agent and preparation method thereof, more particularly, relate to a kind of plastic surface color coating agent and preparation method thereof.
Background technology
Along with the raising of people's living standard, people also constantly increase the demand of plastics, and the plastics with special efficacy are also had specific demand, particularly have colorful plastics.
Summary of the invention
The purpose of this invention is to provide a kind of plastic surface color coating agent, so that color is scattered in the plastics equably.
Another object of the present invention provides a kind of preparation method of above-mentioned composition.
A kind of plastic surface color coating agent of the present invention, this plastic surface color coating agent is composed of the following components by weight percentage: acetone 10%～20% Cellulose diacetate 60%～70% dibutyl phthalate 10%～20% pearlescence 1%～10% aluminium powder 10%～20% pigment 1%～10%.
Prepare method of the present invention, this method may further comprise the steps: by the prescription requirement acetone is contained in container, at room temperature added aluminium powder, make the aluminium powder homodisperse through stirring; Add dibutyl phthalate then, then add pearlescence and mineral dye, restir mixing after the stirring; Exist side by side soon that Cellulose diacetate adds in the above-mentioned solution, the limit edged stirs, till dissolving fully; Continue again to stir 8 to 10 hours, left standstill then 24 hours, bubble is removed finish.
Embodiment
Further specify the present invention below by embodiment.
Embodiment 1, and the proportioning of this plastic surface color coating agent is as follows: acetone 100L, Cellulose diacetate 4kg, dibutyl phthalate 1kg, pearlescence 0.05kg, aluminium powder 1kg, pigment 0.05kg.
This acetone is as solvent.
This Cellulose diacetate, loose white granule or fiber particle meal, odorless, tasteless is nontoxic, dissolves in Glacial acetic acid, chloroform, acetone, and its solution has film-forming properties and spinning property.Thermoplasticity is good, and is nonflammable.Stable in weak acid and grease, easily be reduced into Mierocrystalline cellulose but meet soda acid.
This dibutyl phthalate is as softening agent.
This pearlescence can be given the material of the equally sparkling and crystal-clear flash of light of plastics pearl.Natural and synthetic two series products are arranged.Natural pearlescence is made by the fish scale of hairtail etc., and synthetic pearl essence has white lead carbonate etc. multiple, and good heat-resisting fast light solvent resistance is arranged.
This aluminium powder, silvery white powdery light metal, in damp atmosphere the utmost point lentamente oxidation become dead color.Be easy to acid, water insoluble, in air, add heat energy and fiercely burn, and send dazzling light, as filler.
This pigment is selected titanium dioxide for use.
By the prescription requirement acetone is contained in container, at room temperature added aluminium powder, make the aluminium powder homodisperse through stirring; Add dibutyl phthalate then, then add pearlescence and mineral dye, restir mixing after the stirring; Exist side by side soon that Cellulose diacetate adds in the above-mentioned solution, the limit edged stirs, till dissolving fully; Continue again to stir 8 to 10 hours, left standstill then 24 hours, bubble is removed finish.
The present invention is good stability under processing temperature, and is fast light, and chemicals-resistant, nonbleeding do not make ageing of plastics, and toxicity is little, and on article, film forming properties is good with its brushing, and film forming is fast, nondiscoloration.
Be mainly used in that carton surface coatings, paper inner surface of container are filmed, article surface is filmed, soft packaging is filmed etc.
Using method can adopt spraying or brush.
Claims (2)
1. plastic surface color coating agent, this plastic surface color coating agent is composed of the following components by weight percentage:
Acetone 10%～20%
Cellulose diacetate 60%～70%
Dibutyl phthalate 10%～20%
Pearlescence 1%～10%
Aluminium powder 10%～20%
Pigment 1%～10%
2. the method for preparing the described plastic surface color coating agent of claim 1 is characterized in that this method may further comprise the steps:
(1) by the prescription requirement acetone is contained in container, at room temperature added aluminium powder, make the aluminium powder homodisperse through stirring;
(2) add dibutyl phthalate then, then add pearlescence and mineral dye, restir mixing after the stirring;
(3) exist side by side soon that Cellulose diacetate adds in the above-mentioned solution, the limit edged stirs, till dissolving fully;
(4) continue again to stir 8 to 10 hours, left standstill then 24 hours, bubble is removed finish.