CN101205380A - Novel modified asphalt composition - Google Patents
Novel modified asphalt composition Download PDFInfo
- Publication number
- CN101205380A CN101205380A CNA200610147593XA CN200610147593A CN101205380A CN 101205380 A CN101205380 A CN 101205380A CN A200610147593X A CNA200610147593X A CN A200610147593XA CN 200610147593 A CN200610147593 A CN 200610147593A CN 101205380 A CN101205380 A CN 101205380A
- Authority
- CN
- China
- Prior art keywords
- modified asphalt
- rubber
- novel modified
- asphalt
- asphalt composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel modified asphalt composite, which is characterized in that the novel modified asphalt composite comprises the following compositions by weight portion: 100 weight portions of asphalt, 25 to 35 weigh portions of rubber, 1 to 6 weight portions of fiber, 1 to 3 weight portions of thinner and 0.2 to 2 weight portions of coupling agents. The novel modified asphalt composite of the invention, which is effectively improved in terms of asphalt property, is suited to paving road surfaces, with long service life and less further maintenance cost. In addition, the novel rubber asphalt is simple in production process, easy to operate and low in cost, with the capacity of reusing waste tyre rubber.
Description
Technical field
The present invention relates to a kind of novel modified asphalt composition.
Background technology
Bituminous pavement generally is made up of with gathering materials pitch.The use on oxidation, weather condition and the road surface of bituminous cement between its usage period is particularly used through heavy load, has caused the road surface to be degenerated along with the past of time.For example, the road surface is shunk repeatedly owing to temperature variation and has been caused the road surface to form vertical crackle during the night in winter of cold, is called as cold fracture.Bituminous cement becomes too soft during the summer of sweltering heat, caused road surface tension set under heavy loading repeatedly, is called " rut ".In addition, it is tired that the result of successive mechanical stress is that the road surface becomes, and caused forming the crackle as crocodile skin, is called as repeated stress failure.
But the bituminous wax content is higher, and the road surface of causing asphalt paving is easily softening when high temperature, produce pile-up, permeable, form phenomenons such as reflection crack, surface deformation, a large amount of maintenance of surface expenses is had to drop in the havoc road surface therefore.Proposed multiple in the prior art to the pitch method of modification in addition.Chinese patent application 90104833.X (publication number is CN1058412A) has disclosed a kind of modifying asphalt that machinery is extruded the clad metal pipeline that is used for, and its main component is byerlyte, Atactic Polypropelene, short glass fiber, regenerated rubber, talcum powder and linking agent etc.Make miscible crosslinked this modifying asphalt that obtains of above-mentioned substance by physics, chemical process.Do not provide the performance of this modifying asphalt in the document.The softening temperature of modifying asphalt of the prior art still remains to be improved, to satisfy the needs of pavement asphalt better.
The method of polymer-modified asphalt and production polymer-modified asphalt is known in the present technique field.Polymer, for example thermoplastic elastomer in conjunction with very extensive, is used to improve its intensity and performance in pitch.It also is known adding the stability that sulphur can improve it in polymer one bituminous composition.It is generally acknowledged, with sulfide and polysulfide key Chemical bond, can strengthen and quicken polymer one bituminous Cheng Jian and sulfidation like this between sulphur and polymer and the pitch.Promotor, for example sulphur can add Cheng Jian and the sulfuration that is used to strengthen in the polymer one pitch system between polymer and the pitch to.Multi-form sulphur promotor, for example elementary sulfur comprises alkyl polysulfide with the coupling agent that provides sulphur, dithiocar-bamate, thiophosphoric anhydride, thiuram, thiazole derivative, 4,4 ' one dithiomorpholine may be used to polymer pitch system.Sulphur can combine with polymer and pitch by variety of way, typically comprises behind polymer and the bituminous miscellany stirring certain hour, and sulphur is added in polymer and the bituminous miscellany with the form of simple substance or the form of coupling agent.Perhaps, also can carry out pre-treatment with sulphur to polymer earlier, then the polymer of sulphuring treatment be added in the pitch of fusing.
Summary of the invention
The objective of the invention is provides a kind of novel modified asphalt composition in order to solve shortcoming of the prior art.
For realizing above purpose, the present invention is achieved through the following technical solutions:
A kind of novel modified asphalt composition is characterized in that, comprises following component, pitch 100 weight parts; Rubber 25-35 weight part, fiber 1-6 weight part, thinner 1-3 weight part, coupling agent 0.2-2 weight part.
Wherein, described pitch is petroleum pitch.
Wherein, described rubber is rubber for tire.
Wherein, also include 10-30 part SBS rubber.
Novel modified asphalt composition among the present invention can effectively improve the bituminous performance, is fit to the laying road road surface, and long service life has reduced follow-up maintenance cost.And this modified asphalt composite production technique is simple, easy handling, and cost is low.And can use rubber for tire, realize refuse reclamation.
Embodiment
Below in conjunction with specific embodiment component of the present invention is described further:
Embodiment 1, and a kind of novel modified asphalt composition comprises pitch 100 weight parts; Rubber 25 weight parts, fiber 1 weight part, thinner 1 weight part, coupling agent 0.2 weight part.
Pitch is added in the stirred pot, add the rubber powder resin down, fully mix, leave standstill, add fiber, thinner and coupling agent, continue to stir, be warmed up to 220 ℃ and continue to stir 1 hour at 220 ℃.
Embodiment 2, are made of petroleum pitch 100 weight parts by weight following component; Rubber for tire 30 weight parts, fiber 3 weight parts, thinner 2 weight parts, coupling agent 0.8 weight part.
Production method is identical with embodiment 1.
Embodiment 3, are made of rock asphalt 100 weight parts by weight following component; Rubber for tire 35 weight parts, fiber 6 weight parts, thinner 2.5 weight parts, coupling agent 2 weight parts, SBS rubber 10 weight parts.
Production method is identical with embodiment 1.
Embodiment 4, are made of rock asphalt 100 weight parts by weight following component; Rubber for tire 35 weight parts, fiber 4 weight parts, thinner 3 weight parts, coupling agent 1.5 weight parts, SBS rubber 15 weight parts.
Production method is identical with embodiment 1.
The foregoing description only is used for that the present invention will be described, does not constitute the restriction to the claim scope, and other alternative means that it may occur to persons skilled in the art that are all in claim scope of the present invention.
Claims (4)
1. a novel modified asphalt composition is characterized in that, comprises following component, pitch 100 weight parts; Rubber 25-35 weight part, fiber 1-6 weight part, thinner 1-3 weight part, coupling agent 0.2-2 weight part.
2. novel modified asphalt composition according to claim 1 is characterized in that, described pitch is petroleum pitch.
3. novel modified asphalt composition according to claim 1 is characterized in that, described rubber is rubber for tire.
4. novel modified asphalt composition according to claim 1 is characterized in that, also includes 10-30 part SBS rubber.