CN101204768A - Repair process of centrifugal compressor runner blade - Google Patents
Repair process of centrifugal compressor runner blade Download PDFInfo
- Publication number
- CN101204768A CN101204768A CN 200610134960 CN200610134960A CN101204768A CN 101204768 A CN101204768 A CN 101204768A CN 200610134960 CN200610134960 CN 200610134960 CN 200610134960 A CN200610134960 A CN 200610134960A CN 101204768 A CN101204768 A CN 101204768A
- Authority
- CN
- China
- Prior art keywords
- rotor
- blade
- cladding
- centrifugal compressor
- impeller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a technique for repairing a passage blade of a centrifugal compressor which is integrally carried out by an impeller 1 arranged on a rotor shaft 2 and comprises the following working procedures: 1 detecting the rotor: carrying out a jump detection and a dimension detection on the rotor on a lathe; 2 manufacturing a repair frock 7 of the blade including a front plywood 71, a back plywood 72, a binding bolt 73 and a supporting bolt 74; 3 laser cladding repairing on the hurt part and the parameters s are: a laser power of 1200 to 2000W, a facula diameter of 2 to 6mm and a facula moving speed of 2 to 20mm/s; carrying out facula scanning radiation along the hurt area of the passage with a cladding layer thickness of 1 to 3mm; 4 the shape resuming of the passage blade 13 of the compressor and adopting a straight mill to repair the cladding part of the blade 13; 5 dynamic balance checking on the rotor: carrying out the dynamic balance check on the rotor after repaired on a dynamic balancer. The technique has the advantages of being able to not disassembling the impeller, not having a restoration heat treatment, simple operation, fast repair speed, high suitability and can realize automation.
Description
Technical field
The present invention relates to the maintenance technique of centrifugal compressor runner blade, a kind of renovation technique that utilizes laser melting and coating technique to repair centrifugal compressor runner blade is provided especially.
Background technology
The centrifugal compressor rotor is its accuracy class height of key equipment in the shop equipment, complex manufacturing technology, and the production cost height, the cycle is long, and in case its influence that goes wrong of being in operation is huge, its quality requirement is all than higher.Because the operating temperature of rotor, rotating speed is all very high, so require material that higher creep limit, good creep rupture strength and thermal fatigue resistance and fracture property are preferably arranged.The unit that capacity is big more, the requirement of these technical indicators is just strong more.Such rotor is because of its rotating speed height, and the industrial and mineral inclement condition because of the factor blades such as impurity in the gas very easily wear and tear, causes rotor power to descend in running, and balance is destroyed, influences the normal operation of equipment.
For the manufacture process of rotor from smelting, forging, the machine of material add, operation such as heat treatment, dynamic balancing all has clear and definite, strict quality requirement.So the manufacturing cost of rotor is very high, the manufacturing cycle is also very long.Therefore, be in operation, in a single day rotor goes wrong, and its consequence formula is very serious.If make again, all be that the user is unaffordable from the duration to the cost.Therefore, must take certain mode to keep in repair.But no matter be various thermal processing methods such as electric welding, argon arc welding, vibration weldering, the capital inevitably produces injurious effects such as distortion, crackle, heat affected area tissue inter-variable, residual stress, and causing using on equipment part important, that precision is high has great limitation.
The way reparation of electric welding or thermal spraying is generally adopted in the damage of compressor runner blade in the past.These two kinds of methods all have bigger defective.
Compressor runner blade is repaired in electric welding, and its heat affected area is big, very easily produces distortion, and the weld zone organizes crystal grain thick, and there is very big internal stress in intensity difference.
Hot-spraying technique is repaired compressor runner blade, and anchoring strength of coating is low, very easily comes off, and can't repair damaging big compressor runner blade.
Summary of the invention
The object of the present invention is to provide a kind of renovation technique that utilizes laser melting and coating technique to repair centrifugal compressor runner blade 13 abrading sections.
The invention provides a kind of renovation technique of centrifugal compressor runner blade, it is characterized in that: be that rotor (being contained in the impeller 1 on the armature spindle 2) integrally carries out, form by following operation:
1. the detection of rotor detects rotor and size detection at the enterprising line bounce of lathe, and Fig. 1 is seen at glitch detection position 5 and size detection position 6;
2. blade is repaired the making of frock 7, comprises front plate 71, rear plate 72, fastening bolt 73 and carrying bolt 74; Front plate 71, rear plate 72 and fastening bolt 73 combine and ensure that front shroud of impeller 11 and back shroud of impeller 12 can not expand outwardly distortion, carrying bolt 74 ensures that (see figure 2) can not take place inwardly to shrink for front shroud of impeller 11 and back shroud of impeller 12, to guarantee the cladding quality.
3. the laser melting coating of damage location, technological parameter is:
Laser power 1200~2000W,
Hot spot translational speed 2~20mm/s,
Along the runner damage field, carry out the hot spot scanning and irradiation, cladding bed thickness 1~3mm;
4. compressor runner blade 13 complex adopt straight grinder with blade 13 cladding position corrections of the flank shape, recover the life size form;
5. the dynamic balance check of rotor at the enterprising action balance check of dynamic balancing machine, makes its amount of unbalance reach designing requirement the rotor after repairing.
The renovation technique of centrifugal compressor runner blade provided by the invention, the laser melting coating of its damage location adopts the mode that presets cladding material.
The renovation technique of centrifugal compressor runner blade provided by the invention, the cladding layer of the laser melting coating of its damage location is made of nickel-base alloy bottom and/or cobalt-base alloys surface layer.
The renovation technique of centrifugal compressor runner blade provided by the invention, its advantage is: can not dismantle impeller 1, not do reparation heat treatment, easy and simple to handle, reparation speed is fast, and adaptability is strong, can realize automation; Compressor runner blade thermal deformation after the reparation is little, weld structure is even, and residual stress is little, and performance is better than other method, and rotor matrix does not have distortion, defectives such as flawless, slag inclusion, and the security and the serviceability of rotor increase substantially, and economic effect is obvious.
Description of drawings
Fig. 1 detects for rotor;
Fig. 2 is for repairing the frock schematic diagram.
The specific embodiment
The reparation of embodiment 1D1400-33 centrifugal compressor blade
About 3.5 tons of rotor weight, length is 4m, maximum rotating diameter (exhaust stage blade) 1.4m, 5600 rev/mins of rotor speeds, blade 13 material 2Cr13, rotor blade 13 sheet erosion attenuates, maximum lesion depths is that the above also many places of 1mm exist crackle.
1. the detection of rotor detects the chuck 3 and the top 4 enterprising line bounces of rotor at lathe and size detection, and Fig. 1 is seen at glitch detection position 5 and size detection position 6;
2. blade 13 is repaired the making of frock, comprises front plate 71, rear plate 72, fastening bolt 73 and carrying bolt 74; Front plate 71, rear plate 72 and fastening bolt 73 combine and ensure that front shroud of impeller 11 and back shroud of impeller 12 can not expand outwardly distortion, carrying bolt 74 is a stud, directly withstand on the front and rear cover plate inwall, ensure that inside contraction (seeing accompanying drawing 2) can not take place for front shroud of impeller 11 and back shroud of impeller 12, to guarantee the cladding quality.
3. the laser melting coating of damage location, technological parameter is:
Laser power 2000W,
Spot diameter 5mm,
Hot spot translational speed 20mm/s,
The mode of cladding material Co-based alloy powder is preset in employing, and the composition of nickel-base alloy is, percentage by weight, and Cr15~30, Mo2~6, W2~10, surplus are Ni.
Along the runner damage field, carry out the hot spot scanning and irradiation, cladding bed thickness 3mm;
4. compressor runner blade 13 complex adopt straight grinder with blade 13 cladding position corrections of the flank shape, recover the life size form;
5. the dynamic balance check of rotor at the enterprising action balance check of dynamic balancing machine, makes its amount of unbalance reach designing requirement the rotor after repairing.
Through various tests, its hardness number reaches HB250~280 that former blade 13 hardness require, and nondestructive inspection detects does not have defectives such as hole, slag inclusion, crackle.The Metallographic Analysis result, cladding layer is organized as fine and close austenite structure.Running through the time more than 1 year does not come off, bad phenomenon such as peeling produces, and works well.
The reparation of embodiment 2D900 centrifugal compressor blade
About 1.8 tons of rotor weight, length is 3m, 8200 rev/mins of rotor speeds, blade 13 material 1Cr17Ni4Cu4Nb, its damage width 80mm, maximum lesion depths is more than the 1mm.
1. the detection of rotor detects the chuck 3 and the top 4 enterprising line bounces of rotor at lathe and size detection, and Fig. 1 is seen at glitch detection position 5 and size detection position 6;
2. blade 13 is repaired the making of frock, comprises front plate 71, rear plate 72, fastening bolt 73 and carrying bolt 74; Front plate 71, rear plate 72 and fastening bolt 73 combine and ensure that front shroud of impeller 11 and back shroud of impeller 12 can not expand outwardly distortion, carrying bolt 74 is a stud, directly withstand on the front and rear cover plate inwall, ensure that inside contraction (seeing accompanying drawing 2) can not take place for front shroud of impeller 11 and back shroud of impeller 12, to guarantee the cladding quality.
3. the laser melting coating of damage location, technological parameter is:
Laser power 1800W,
Spot diameter 3mm,
Hot spot translational speed 10mm/s,
The mode of cladding material cobalt-base alloys is preset in employing.
Along the runner damage field, carry out the hot spot scanning and irradiation, cladding bed thickness 2mm;
4. compressor runner blade 13 complex adopt straight grinder with blade 13 cladding position corrections of the flank shape, recover the life size form;
5. the dynamic balance check of rotor at the enterprising action balance check of dynamic balancing machine, makes its amount of unbalance reach designing requirement the rotor after repairing.
Qualified by inspection.Through various tests, its hardness number reaches HB360~380 that former blade 13 hardness require, and nondestructive inspection detects does not have defectives such as hole, slag inclusion, crackle.The Metallographic Analysis result, cladding layer is organized as fine and close austenite structure.Running through the time more than 1 year does not come off, bad phenomenon such as peeling produces, and works well.
Claims (3)
1. the renovation technique of a centrifugal compressor runner blade is characterized in that: be that the impeller (1) that is contained on the armature spindle (2) integrally carries out, be made up of following operation:
1. the detection of rotor detects rotor and size detection at the enterprising line bounce of lathe;
2. blade is repaired the making of frock (7), comprises front plate (71), rear plate (72), fastening bolt (73) and carrying bolt (74);
3. the laser melting coating of damage location, technological parameter is:
Laser power 1200~2000W,
Spot diameter 2~6mm,
Hot spot translational speed 2~20mm/s,
Along the runner damage field, carry out the hot spot scanning and irradiation, cladding bed thickness 1~3mm;
4. compressor runner blade (13) complex adopts straight grinder with blade (13) cladding position correction of the flank shape, recovers the life size form;
5. the dynamic balance check of rotor, with the rotor after repairing at the enterprising action balance check of dynamic balancing machine.
2. according to the renovation technique of the described centrifugal compressor runner blade of claim 1, it is characterized in that: the laser melting coating of described damage location adopts the mode that presets cladding material.
3. according to the renovation technique of the described centrifugal compressor runner blade of claim 1, it is characterized in that: the cladding layer of the laser melting coating of described damage location is made of nickel-base alloy bottom and/or cobalt-base alloys surface layer.