CN101200787A - Method for preparing Mo-Si-Al-K cold-rolling thin molybdenum plate band - Google Patents
Method for preparing Mo-Si-Al-K cold-rolling thin molybdenum plate band Download PDFInfo
- Publication number
- CN101200787A CN101200787A CNA2007101796649A CN200710179664A CN101200787A CN 101200787 A CN101200787 A CN 101200787A CN A2007101796649 A CNA2007101796649 A CN A2007101796649A CN 200710179664 A CN200710179664 A CN 200710179664A CN 101200787 A CN101200787 A CN 101200787A
- Authority
- CN
- China
- Prior art keywords
- molybdenum
- rolling
- high temperature
- cold
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a Mo-Si-Al-K cold rolling thin molybdenum strip and a preparation method thereof. The invention is characterized in that the preparation process is: sintering the Mo-Si-Al-K into high temperature molybdenum billet; pre-annealing before the rolling at the temperature of 1300-1400 DEG C; implementing the hot rolling cogging processing on the high temperature molybdenum billet with the first pass deformation of 20 to 30 percent; implementing the intermediate annealing, the alkali washing and the warm rolling at the temperature of 900-1100 DEG C when the rolling deformation reaches to 70 to 75 percent to obtain a middle thick molybdenum strip; cold cooling the middle thick molybdenum strip into the specification of a finally finished product; implementing the vacuum stress relief annealing on the finished product at the temperature of 800-850 DEG C. And then the high temperature cold rolling thin molybdenum strip required by the invention is obtained. The product obtained through the invention is provided with strong high temperature strength and high recrystallization temperature. The cold rolling thin molybdenum strip product has the good properties of surface quality, high size precision, strong high temperature strength, good plasticity, long service life, etc. and can be widely used to produce molybdenum crucibles, boats, anodes of transmitting tubes with large power (U type), gate molybdenum tubes, heating unit, heat shields and other structural parts.
Description
Technical field
The present invention relates to a kind of Mo-Si-Al-K cold-rolling thin molybdenum plate band and preparation method thereof.
Background technology
Because refractory metal molybdenum has higher high temperature strength, favorable conductive thermal conductivity, the lower coefficient of expansion and workability, thereby in special bulb such as automobile halogen tungsten lamp, high-pressure mercury lamp, tubular halogen tungsten lamp and electric lighting device, be extensive use of the molybdenum filament material make their required bulbs hook, around filament with component such as heart yearn, guide rod, outlet line and plasticity supports, in the metal processing industry, be widely used as line cutting molybdenum filament, be used as the hydrogen furnace heating unit in the kiln industry.
Cold-rolling thin molybdenum plate, band, be mainly used in electrovacuum, the electric light source industry, through secondary forming process such as deep-draw, drawing, spinning, be processed into the goods of different shape, specification by thin molybdenum plate, band, as molybdenum crucible, burning boat, high-power transmitting tube anode (U type), gate molybdenum tube etc.If in above-mentioned industry, use, all require thin molybdenum plate, band to have good low-temperature plasticity and good high-temperature use properties, the recrystallization temperature of pure molybdenum plate has only 1000~1200 ℃, thereby fragility and fracture often appear, its hot strength is also low and yielding, can not satisfy the service requirements of these industries far away.And the recrystallization temperature of the thin molybdenum plate of ASK high temperature, band is more than 1650 ℃, this be because this moment its recrystal grain grow up and behind recrystallize, form due to the crystalline-granular texture of overlap joint mutually and interlocking, and because microstructure still keeps tangible directivity after perfect recrystallization, so the high temperature molybdenum plate of recrystallize still can keep good plasticity.
Summary of the invention
The object of the present invention is to provide a kind of good processability, surface quality is good, dimensional precision is high, hot strength is high, recrystallization temperature is high, technology simply, the Mo-Si-Al-K cold-rolling thin molybdenum plate band of not flexible brittle failure, yield rate height, material high conformity, long service life and preparation method thereof.
The objective of the invention is to be achieved through the following technical solutions.
A kind of preparation method of Mo-Si-Al-K cold-rolling thin molybdenum plate band, it is characterized in that its preparation process is with Mo-Si-Al-K sintering high temperature molybdenum base, be rolled heating under 1300~1500 ℃, it is the processing of 20%~30% hot rolling cogging that high temperature molybdenum base is made first pass deformation; When rolling total deformation reached 70%~75%, rolling interruption made them under 900~1100 ℃ of temperature, carries out process annealing, and annealing time is 60min; Carry out alkali cleaning after the annealing, and warm-rolling be δ=1.0mm in thick molybdenum plate; Thick molybdenum plate among the 1.0mm is carried out cold rolling, the final finished specification is δ=0.1~0.5mm; After finished product carried out the annealing of 800~850 ℃ of vacuum stress-removals, obtain high temperature cold-rolling thin molybdenum plate band required for the present invention.
A kind of Mo-Si-Al-K cold-rolling thin molybdenum plate band preparation method of the present invention, the preparation process that it is characterized in that described alloy billet are to be that raw material adds hydrogen and once reduces and obtain molybdenum dioxide with the ammonium dimolybdate; Take by weighing K according to weight percent
2SiO
3And Al (NO
3)
3Dissolve standby; With molybdenum dioxide and K
2SiO
3, Al (NO
3)
3Solution mixes, dries in pot is mixed in bipyramid vacuum-drying; Molybdenum dioxide is carried out the secondary hydrogen reducing in four pipe high temperature retort furnaces; The Mo-Si-Al-K doped molybdenum is carried out isostatic cool pressing be pressed into, obtain high temperature molybdenum base, after the compacting of isostatic cool pressing, sinter the molybdenum base into.
A kind of Mo-Si-Al-K cold-rolling thin molybdenum plate band preparation method of the present invention is characterized in that described Mo-Si-Al-K high temperature sintering becomes in the molybdenum base to contain K
2O, SiO
2And Al
2O
3The weight percent that three kinds of oxide compounds, three kinds of oxide compounds account for molybdenum is K
2O:0.01%~0.08%, SiO
2: 0.02%~0.05%, Al
2O
3: 0%~0.005%.
Method of the present invention, adopt traditional powder metallurgical production technique, difference is to carry out the liquid-solid doping of bipyramid vacuum-drying in the molybdenum dioxide stage, then carry out secondary reduction and produce the Si-Al-K doped molybdenum, it is δ 0.1~0.5mmMo-Si-Al-K cold-rolling thin molybdenum plate, band that operation such as repressed again, sintering, hot rolling, warm-rolling, cold rolling, alkali cleaning, annealing is prepared specification.Raw material cheapness of the present invention, be easy to get, prepared thin molybdenum plate, the strip surface quality is good, dimensional precision is high, hot strength is high, recrystallization temperature is high, technology simply, not flexible brittle failure, yield rate height, material high conformity, long service life, can be widely used for making the molybdenum crucible, burn boat, high-power transmitting tube anode (U type), gate molybdenum tube, heating element, thermoscreen and other structural parts.
Method of the present invention, it is cheap and easy to get to have following process characteristic (a 1) raw material: the molybdenum source is an ammonium dimolybdate; (2) employed additive K
2SiO
3, Al (NO
3)
3Cheap, to operator's not injury of health; (3) production technique is easy to control, and is easy and simple to handle, safe, reliable, need not big input and transformation on equipment, is suitable for scale operation; (4) Gu adopt liquid-solid adulterating method and solid-adulterating method to compare the alloying element that is added being evenly distributed in material, good product consistency; (5) be rolled heating under 1300~1500 ℃, it is 20~30% hot rolling cogging that the molybdenum base is made first pass deformation; (6) when rolling total deformation reaches 70~75%, rolling interruption makes it carry out process annealing between 900~1100 ℃; (7) annealing after carry out alkali cleaning, and warm-rolling be δ=1.0mm in thick molybdenum plate; (8) thick molybdenum plate among the 1.0mm is carried out cold rolling, the final finished specification is δ=0.1~0.5mm; (9) finished product is carried out 800~850 ℃ of vacuum annealings.
Method of the present invention, the Mo-Si-Al-K high temperature molybdenum alloy sheet material of preparation contains K in its alloy
2O, SiO
2And Al
2O
3The weight percent that three kinds of oxide compounds, three kinds of oxide compounds account for molybdenum is K
2O:0.01%~0.08%, SiO
2: 0.02%~0.05%, Al
2O
3: 0%~0.005%.Compare with pure molybdenum, the hot strength height of the inventive method products obtained therefrom, the recrystallization temperature height, 500~600 ℃ have been improved than pure molybdenum, the cold-rolling thin molybdenum plate of gained of the present invention, strip product have premium propertiess such as surface quality is good, dimensional precision is high, hot strength is high, plasticity is good, long service life, can be widely used for making the molybdenum crucible, burn boat, high-power transmitting tube anode (U type), gate molybdenum tube, heating element, thermoscreen and other structural parts.
Embodiment
Be that raw material adds hydrogen and once reduces and obtain molybdenum dioxide with the ammonium dimolybdate; Take by weighing K according to weight percent
2SiO
3And Al (NO
3)
3Dissolve standby; With molybdenum dioxide and K
2SiO
3, Al (NO
3)
3Solution mixes in pot is mixed in bipyramid vacuum-drying, and wherein the pressure of air compressor pump is 0.2MPa, and the bake out temperature of the pot that mixes is 70 ℃, and the inner vacuum tightness of pot of mixing need be controlled at more than the 0.06MPa; Molybdenum dioxide is carried out the secondary hydrogen reducing in four pipe high temperature retort furnaces, hydrogen flowing quantity is 5.0M
3/ H, boat charge is the 1.0kg/ boat, pushing away boat speed is 4 boats/60min; The Mo-Si-Al-K doped molybdenum is carried out isostatic cool pressing be pressed into, obtain substance 9.0kgMo-Si-Al-K high temperature molybdenum base, the pressing pressure of isostatic cool pressing is 175MPa, and the dwell time is 10min, and a release time is 45s, and the secondary release time is 5s; And carry out 1250 ℃ of retort furnace presintering and 1900 ℃ of intermediate frequency high temperature sinterings obtain substance 9.0kg thickness 24~30mmMo-Si-Al-K sintering high temperature molybdenum base; Mo-Si-Al-K sintering high temperature molybdenum base is rolled preceding heating under 1300~1500 ℃, it is the processing of 20~30% hot rolling cogging that high temperature molybdenum base is made first pass deformation; When rolling total deformation reached 70~75%, rolling interruption made it carry out process annealing between 900~1100 ℃, and annealing time is 60min; Carry out alkali cleaning after the annealing, and warm-rolling be δ=1.0mm in thick molybdenum plate; Thick molybdenum plate among the 1.0mm is carried out cold rolling, the final finished specification is δ=0.1~0.5mm; Finished product is carried out obtaining high temperature cold-rolling thin molybdenum plate, band required for the present invention after 800~850 ℃ of vacuum stress-removal annealing.
Embodiment 1
Be that raw material adds hydrogen and once reduces and obtain molybdenum dioxide with the ammonium dimolybdate, it is standby to get molybdenum dioxide 30kg; According to weight percent is 0.2%K
2O, 0.13%SiO
2, Al
2O
30.001% takes by weighing 100gK
2SiO
3, 6.5g Al (NO
3)
39H
2O dissolves standby; With molybdenum dioxide and K
2SiO
3, Al (NO
3)
3Solution mixes in pot is mixed in bipyramid vacuum-drying, and wherein the pressure of air compressor pump is 0.2MPa, and the bake out temperature of the pot that mixes is 70 ℃, and the inner vacuum tightness of pot of mixing need be controlled at more than the 0.06MPa, obtains molybdenum dioxide 29.0kg after the doping; Molybdenum dioxide is carried out the secondary hydrogen reducing in four pipe high temperature retort furnaces, hydrogen flowing quantity is 5.0M
3/ H, boat charge is the 1.0kg/ boat, pushing away boat speed is 4 boats/60min, obtains Mo-Si-Al-K doped molybdenum 21.0kg; The Mo-Si-Al-K doped molybdenum is carried out isostatic cool pressing be pressed into, obtain substance 9.0kg Mo-Si-Al-K high temperature molybdenum base, the pressing pressure of isostatic cool pressing is 175MPa, and the dwell time is 10min, and a release time is 45s, and the secondary release time is 5s; And carry out 1250 ℃ of retort furnace presintering and 1900 ℃ of intermediate frequency high temperature sinterings obtain substance 9.0kg thickness 24~30mmMo-Si-Al-K sintering high temperature molybdenum base; Mo-Si-Al-K sintering high temperature molybdenum base is rolled preceding heating under 1450 ℃, soaking time is 60min; It is the processing of 20~30% hot rolling cogging that high temperature molybdenum base is made first pass deformation; When rolling total deformation reached 70~75%, rolling interruption made it carry out process annealing at 1000 ℃, and annealing time is 60min; Carry out alkali cleaning after the annealing, and warm-rolling is the middle thickness molybdenum plate of δ=1.0mm; Thick molybdenum plate among the 1.0mm is carried out cold rolling, the final finished specification is δ=0.3,0.4mm; Finished product is carried out obtaining high temperature cold-rolling thin molybdenum plate, band required for the present invention after 820 ℃ of vacuum stress-removal annealing.Shown in detection data in the process see the following form.
Table 1 Mo-Si-Al-K doped molybdenum physical and chemical index
Lot number | Fisher particle size (μ m) | Loose density (g/cm 3 ) | Constituent content (ppm) | ||||||||
Si | Al | K | Ca | Mg | C | O | Fe | Ni | |||
MASK-2# | 3.50 | 1.13 | 46 0 | 50 | 64 2 | 6 | 1 | 20 | 1300 | 18 | 7 |
The physicochemical property of table 2 Mo-Si-Al-K high temperature molybdenum base
Lot number | Hardness (HRA) | Density (g/cm 3 ) | Constituent content (ppm) | ||||||||
Si | Al | K | Ca | Mg | C | O | Fe | Ni | |||
MASK-2# | 44.2, 44.5 | 9.48 | 36 0 | 20 | 30 6 | 14 | 1 | 20 | 34 0 | 54 | 6 |
Mechanical property after table 3 δ=0.3,820 ℃ of vacuum annealings of 0.4mmMo-Si-Al-K cold-rolling thin molybdenum plate
Lot number | Tensile strength (MPa) | Unit elongation (%) | Specification (m) |
MASK-2# | 825 | 11.5 | δ=0.3 |
780 | 11.0 | ||
795 | 11.0 | ||
1230 | 5.0 | δ=0.4 | |
1240 | 5.0 | ||
1240 | 5.0 |
Cupping performance after table 4 δ=0.3,820 ℃ of vacuum annealings of 0.4mmMo-Si-Al-K cold-rolling thin molybdenum plate
Lot number | Punch diameter (mm) | Deep-draw value (mm) | Specification (mm) |
MASK-2# | 20 | 5.7 | δ=0.3 |
20 | 5.5 | ||
20 | 5.6 | ||
20 | 5.4 | δ=0.4 | |
20 | 5.7 | ||
20 | 5.6 |
Claims (3)
1. the preparation method of a Mo-Si-Al-K cold-rolling thin molybdenum plate band, it is characterized in that its preparation process is with Mo-Si-Al-K sintering high temperature molybdenum base, be rolled preceding preannealing under 1300~1400 ℃, it is the processing of 20%~30% hot rolling cogging that high temperature molybdenum base is made first pass deformation; When rolling total deformation reached 70%~75%, rolling interruption made them under 900~1100 ℃ of temperature, carries out process annealing, and annealing time is 60min; Carry out alkali cleaning after the annealing, and warm-rolling be δ=1.0mm in thick molybdenum plate; Thick molybdenum plate among the 1.0mm is carried out cold rolling, the final finished specification is δ=0.2~0.5mm; After finished product carried out the annealing of 800~850 ℃ of vacuum stress-removals, obtain high temperature cold-rolling thin molybdenum plate band required for the present invention.
2. a kind of Mo-Si-Al-K cold-rolling thin molybdenum plate band preparation method according to claim 1, the preparation process that it is characterized in that described alloy billet are to be that raw material adds hydrogen and once reduces and obtain molybdenum dioxide with the ammonium dimolybdate; Take by weighing K according to weight percent
2SiO
3And Al (NO
3)
3Dissolve standby; With molybdenum dioxide and K
2SiO
3, Al (NO
3)
3Solution mixes, dries in pot is mixed in bipyramid vacuum-drying; Molybdenum dioxide is carried out the secondary hydrogen reducing in four pipe high temperature retort furnaces; The Mo-Si-Al-K doped molybdenum is carried out isostatic cool pressing be pressed into, obtain high temperature molybdenum base, after the compacting of isostatic cool pressing, sinter the molybdenum base into.
3. a kind of Mo-Si-Al-K cold-rolling thin molybdenum plate band preparation method according to claim 1 is characterized in that described Mo-Si-Al-K high temperature sintering becomes in the molybdenum base to contain K
2O, SiO
2And Al
2O
3The weight percent that three kinds of oxide compounds, three kinds of oxide compounds account for molybdenum is K
2O:0.01%~0.08%, SiO
2: 0.02%~0.05%, Al
2O
3: 0%~0.005%.