CN101195864A - Nickel cobalt waste material recycling and processing method - Google Patents
Nickel cobalt waste material recycling and processing method Download PDFInfo
- Publication number
- CN101195864A CN101195864A CNA2007103036221A CN200710303622A CN101195864A CN 101195864 A CN101195864 A CN 101195864A CN A2007103036221 A CNA2007103036221 A CN A2007103036221A CN 200710303622 A CN200710303622 A CN 200710303622A CN 101195864 A CN101195864 A CN 101195864A
- Authority
- CN
- China
- Prior art keywords
- nickel cobalt
- nickel
- waste material
- cobalt waste
- recovery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a recycling and treating method of nickel cobalt waste alloy material, which relates to a nickel cobalt waste alloy material treating process during the nickel cobalt recycling process of the nickel cobalt waste alloy material. The invention is characterized in that high grade nickel matte is generated by the air refining of the nickel cobalt waste alloy material, and then the nickel cobalt is recycled in the nickel cobalt production process. In the method of the invention, air refining high grade nickel matte is added in the nickel cobalt waste alloy in the later stage of air refining in a nickel tilting converter, and then the nickel cobalt recycling is performed. The recycling and treating method of the nickel cobalt waste alloy material has the advantages that the metal recovery ratio is high, the process is simple, and the cost is low.
Description
Technical field
A kind of recovery and treatment method of nickel cobalt waste material relates to the treating processes that a kind of nickel cobalt waste material reclaims the nickel cobalt waste material in the nickel cobalt process.
Background technology
Contain valuable metals such as metallic nickel, cobalt and tungsten in the nickel cobalt waste material.At present, the recovery and treatment method of nickel cobalt waste material has and uses earlier the thermal process concentration and separation, and then carries out method recovery nickel, cobalt and the tungsten of the step of acid dissolving leaching with the wet processing process.Its technical process is long, the processing cost height, and operational condition is poor.
Summary of the invention
Purpose of the present invention is exactly the deficiency of depositing at above-mentioned prior art, and the recovery and treatment method of a kind of nickel cobalt metal recovery rate height, technology is simple, cost is low nickel cobalt waste material is provided.
The objective of the invention is to be achieved through the following technical solutions.
A kind of recovery and treatment method of nickel cobalt waste material is characterized in that its recycling process is that nickel cobalt waste material blowing is generated high ice nickel, enters and reclaims the nickel cobalt in the nickel cobalt production process.
The recovery and treatment method of a kind of nickel cobalt waste material of the present invention is characterized in that nickel cobalt waste material blowing generates high ice nickel process and nickel cobalt waste material is added in the nickel converter blows.
The recovery and treatment method of a kind of nickel cobalt waste material of the present invention is characterized in that described nickel cobalt waste material bessemerizes the later stage at nickel and add, and the blowing temperature is 1200-1350 ℃, and duration of blast is 0.8~1.5 hour.
The recovery and treatment method of a kind of nickel cobalt waste material of the present invention is characterized in that described nickel cobalt waste material adds the 2%-5% of the weight blowing melt weight of nickel converter.
The recovery and treatment method of a kind of nickel cobalt waste material of the present invention, nickel cobalt waste material comprise useless nickel cobalt superalloy, useless magnet steel and magnet steel crumb, nickel cobalt expansion alloy, hard alloy scraps and spent catalyst etc.Because each element is Cu<Ni<Co<Fe<W<Cr<Mo<V<Mn<Ta<Nb<Al to the size order of the avidity of oxygen in the alloy, in the alloy with the avidity of the oxygen Elements C o bigger, Fe, W, Cr, Mo, V, Mn, Ta, Nb, Al than nickel all with preferential oxidation.According to the avidity size, the order of element oxidation is undertaken by Al, Nb, Ta, Mn, V, Mo, Cr, W, Fe, Co, Ni, Cu in the converting process, before nickel is near complete oxidation, element al, Nb, Ta, Mn, V, Mo, Cr, W, Fe, Co etc. can both be by complete oxidations, and generate corresponding stable state oxide compound and quartzite slag making.
Method of the present invention, waste alloy of nickel cobalt is bessemerized the high ice of later stage adding blowing nickel at nickel, carries out the nickel cobalt again and reclaims.The recovery and treatment method of nickel cobalt metal recovery rate height, technology is simple, cost is low nickel cobalt waste material.
Embodiment
A kind of recovery and treatment method of nickel cobalt waste material, its recycling process be that nickel cobalt waste material blowing is generated high ice nickel, reclaims the nickel cobalt again in nickel cobalt technological process; The blowing of its nickel cobalt waste material generates high ice nickel process and nickel cobalt waste material is added in the nickel converter blows; Described nickel cobalt waste material is bessemerized the later stage adding at nickel, and the blowing temperature is 1200-1350 ℃, and duration of blast is 0.8~1.5 hour; Described nickel cobalt waste material adds the 2%-5% of the weight blowing melt weight of nickel converter; After described blowing reaction is finished, will bessemerize slag and pour cinder ladle into and forward the ore-smelting furnace dilution to.
Embodiment 1
Nickel cobalt waste material is useless high temperature (heat-resisting) alloy, and its moiety (wt%) is Ni+Co:50~70, and all the other are Cr, iron and a spot of Mo, W, Nb, Ti, Al;
2 tons of nickel cobalt waste materials are joined in the nickel converter in the later stage of blowing, use converting with air 1.2 hours under 1200-1350 ℃ temperature, the height ice nickel with blowing generates enters and reclaims the nickel cobalt in the existing nickel cobalt production process.The direct yield 91.16% of nickel in the nickel cobalt waste material, the direct yield 54.8% of cobalt.
Embodiment 2
Nickel cobalt waste material for or give up magnet steel and magnet steel crumb, its moiety is (wt%): Co14~34, Ni14~24, Al8, Cu3, all the other are iron;
2 tons of nickel cobalt waste materials are joined unclassified stores blowing in the converter in later stage, under 1200 ~ 1350 ℃ temperature, put high ice nickel in 0.8 hour, enter again and reclaim the nickel cobalt in the existing nickel cobalt production process with converting with air.The direct yield 91.34% of nickel in the nickel cobalt waste material, the direct yield 54.75% of cobalt.
Embodiment 3
Nickel cobalt waste material is or nickel cobalt expansion alloy, and its moiety is (wt%): Ni28.5~29.5, Co16.8~17.8, and all the other are the mixing nickel cobalt waste material of iron;
5 tons of nickel cobalt waste materials are joined unclassified stores blowing in the converter in later stage, under 1200-1350 ℃ temperature, put high ice nickel in 1 hour, enter again and reclaim the nickel cobalt in the existing nickel cobalt production process with converting with air.
Claims (4)
1. the recovery and treatment method of a nickel cobalt waste material is characterized in that its recycling process is that the nickel cobalt waste material blowing is generated high ice nickel, enters and reclaims the nickel cobalt in the nickel cobalt production process.
2. the recovery and treatment method of a kind of nickel cobalt waste material according to claim 1 is characterized in that the nickel cobalt waste material blowing generates high ice nickel process and nickel cobalt waste material is added in the nickel converter blows.
3. the recovery and treatment method of a kind of nickel cobalt waste material according to claim 1 is characterized in that described nickel cobalt waste material bessemerizes the later stage at nickel and add, and the blowing temperature is 1200-1350 ℃, and duration of blast is 0.8~1.5 hour.
4. the recovery and treatment method of a kind of nickel cobalt waste material according to claim 1 is characterized in that described nickel cobalt waste material adds the 2%-5% of the weight blowing melt weight of nickel converter.