CN101195699A - Verelite baume panel and production method thereof - Google Patents
Verelite baume panel and production method thereof Download PDFInfo
- Publication number
- CN101195699A CN101195699A CNA2006101345122A CN200610134512A CN101195699A CN 101195699 A CN101195699 A CN 101195699A CN A2006101345122 A CNA2006101345122 A CN A2006101345122A CN 200610134512 A CN200610134512 A CN 200610134512A CN 101195699 A CN101195699 A CN 101195699A
- Authority
- CN
- China
- Prior art keywords
- polystyrene
- baume
- magnesium oxide
- magnesium chloride
- panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to building material technical field, in particular to a polystyrene baume plate and a relative production method, wherein the baume plate is composed of following components of volume percentages as 80-90% polystyrene, 6-13% magnesium oxide and 4-7% magnesium chloride, while the consumptions of magnesium oxide and magnesium chloride are decided by the grain size of polystyrene. The production method comprises breaking polystyrene into 0.5-2mm, weighting polystyrene, magnesium oxide and magnesium chloride to be poured into a mixer to be mixed uniformly, arranging one layer of non-woven cloth on the bottom of a thin-plate mould, stuffing the uniform mixture into the mould, arranging one glass silk cloth, treating and obtainsing product blank, demoulding the product blank, and naturally solidifying or heating to solidify to obtain final product. The product has low weight, high strength, good thermal insulation, and flameproof and waterproof properties. The main material polystyrene can utilize waste recovered material, to reduce product cost and eliminate white pollution.
Description
Technical field
The present invention relates to building material technical field, particularly a kind of verelite baume panel and preparation method thereof.
Background technology
Along with improving constantly of people's living standard, also more and more higher to the requirement that beautifies living environment, it is also more and more to decorate materials.Baume panel as one of important decoration materials also is widely used.It is that major ingredient is made with the perlite that a kind of baume panel is arranged at present.Perlite is a kind of natural resource, can only be more with few more.On the other hand, polystyrene board is used as wrapping material in a large number, uses up the white pollution that causes after discarding environment, if can be recycled, and then helps environment protection.Simultaneously since polystyrene density low, in light weight, intensity is high, thermal and insulating performance good, fire-retardant water-fast, if can be used to make baume panel, then not only help improving its performance, and help eliminating white pollution.
Summary of the invention
The purpose of this invention is to provide a kind of reasonable recipe, manufacture craft is simple and reliable, in light weight, intensity is high, thermal and insulating performance is good, fire-retardant water-proof verelite baume panel and preparation method thereof.
The objective of the invention is to realize by following technical proposals.
According to verelite baume panel of the present invention, formed by the volume percent of following component:
Polystyrene 80-90%
Magnesium oxide 6-13%
Magnesium chloride 4-7%.
Described polystyrene is the 0.5-2mm size particles.The consumption of magnesium oxide and magnesium chloride depends on the particle diameter of polystyrene.
For the polystyrene of big particle diameter, baume panel is made up of the volume percent of following component:
Polystyrene 88-90%
Magnesium oxide 6-7%
Magnesium chloride 4-5%.
For the polystyrene of small particle size, baume panel is made up of the volume percent of following component:
Polystyrene 80-82%
Magnesium oxide 12-13%
Magnesium chloride 6-7%.
The described verelite baume panel method of a kind of making comprises the following steps:
1) polystyrene is ground into the 0.5-2mm size particles,
2) it is standby to measure described components in percentage by volume polystyrene, magnesium oxide, magnesium chloride,
3) successively polystyrene, magnesium oxide, magnesium chloride are poured in the agitator and are stirred,
4) in shop, the bottom surface of book template mould layer of non-woven fabric, inserted mould in through the compound that stirs the sixth of the twelve Earthly Branches, repave one deck glass wool cloth after filling up compound, be squeezed into goods base type again.
Spontaneous curing or be heating and curing and be finished product after the goods base type demoulding that 5) will be squeezed into.
Prescription according to verelite baume panel of the present invention has only three kinds of components: polystyrene, magnesium oxide and magnesium chloride, with the polystyrene is major ingredient, account for the 80-90% of volume total amount, with the magnesium oxide and the magnesium chloride that evenly are coated on the polystyrene surface is wedding agent and fire-resistant waterproof agent, form in light weight, intensity is high, thermal and insulating performance good, fire-retardant water-proof light-high-strength verelite baume panel, manufacture craft is simple and reliable, in pressing process, a large amount of magnesium oxide and magnesium chloride mixture are pressed onto on the surface of plate, have strengthened the fire-resistant waterproof function.The employing method of being heating and curing can significantly shorten set time, increases substantially labour productivity and plant factor.According to the present invention, used major ingredient polystyrene can adopt waste and old reclaimed materials, and this can significantly reduce the cost of product on the one hand, can eliminate the white pollution to environment on the other hand, kills two birds with one stone, and benefits the nation and the people.
Embodiment
The following describes the specific embodiment of the present invention.
According to verelite baume panel of the present invention, it is characterized in that being formed by the volume percent of following component:
Polystyrene 80-90%
Magnesium oxide 6-13%
Magnesium chloride 4-7%.
Described polystyrene is the 0.5-2mm size particles.
Embodiment 1:
For the polystyrene of big particle diameter, baume panel is made up of the volume percent of following component:
Polystyrene 88-90%
Magnesium oxide 6-7%
Magnesium chloride 4-5%.
Embodiment 2:
For the polystyrene of small particle size, baume panel is made up of the volume percent of following component:
Polystyrene 80-82%
Magnesium oxide 12-13%
Magnesium chloride 6-7%.
The described verelite baume panel method of a kind of making comprises the following steps:
1) polystyrene is ground into the 0.5-2mm size particles,
2) it is standby to measure described components in percentage by volume polystyrene, magnesium oxide, magnesium chloride,
3) successively polystyrene, magnesium oxide, magnesium chloride are poured in the agitator and are stirred,
4) in shop, the bottom surface of book template mould layer of non-woven fabric, inserted mould in through the compound that stirs the sixth of the twelve Earthly Branches, repave one deck glass wool cloth after filling up compound, be squeezed into goods base type again.
Spontaneous curing or be heating and curing and be finished product after the goods base type demoulding that 5) will be squeezed into.
Claims (5)
1. verelite baume panel is characterized in that being made up of the volume percent of following component:
Polystyrene 80-90%
Magnesium oxide 6-13%
Magnesium chloride 4-7%.
2. according to the described verelite baume panel of claim 1, it is characterized in that being formed by the volume percent of following component:
Polystyrene 88-90%
Magnesium oxide 6-7%
Magnesium chloride 4-5%.
3. verelite baume panel according to claim 1 is characterized in that being made up of the volume percent of following component:
Polystyrene 80-82%
Magnesium oxide 12-13%
Magnesium chloride 6-7%.
4. light-high-strength heat preserving and insulating material according to claim 1 is characterized in that described polystyrene is the 0.5-2mm size particles.
5. make claim 1,2 or 3 described verelite baume panel methods for one kind, it is characterized in that comprising the following steps:
1) polystyrene is ground into the 0.5-2mm size particles,
2) it is standby to measure described components in percentage by volume polystyrene, magnesium oxide, magnesium chloride,
3) successively polystyrene, magnesium oxide, magnesium chloride are poured in the agitator and are stirred,
4) in shop, the bottom surface of book template mould layer of non-woven fabric, the compound that has stirred is inserted in the mould, repaved one deck glass wool cloth after filling up compound, be squeezed into goods base type again.
Spontaneous curing or be heating and curing and be finished product after the goods base type demoulding that 5) will be squeezed into.