CN101173080A - Fire resistant anti-deforming material for air-conditioning fan and production method thereof - Google Patents
Fire resistant anti-deforming material for air-conditioning fan and production method thereof Download PDFInfo
- Publication number
- CN101173080A CN101173080A CNA200710113888XA CN200710113888A CN101173080A CN 101173080 A CN101173080 A CN 101173080A CN A200710113888X A CNA200710113888X A CN A200710113888XA CN 200710113888 A CN200710113888 A CN 200710113888A CN 101173080 A CN101173080 A CN 101173080A
- Authority
- CN
- China
- Prior art keywords
- air
- percent
- fire resistant
- resistant anti
- conditioning fan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a heat resisting and distortion preventing material used for an air conditioning fan and a manufacturing method thereof. The invention aims at solving the problems existing in the prior art that the fan has poor running stability and increased noise after the long-term use. In order to reach the aim of solving the technical problems, the invention has the technical proposal that the weight percentage and the ingredient proportion are as follows: the plastic backing material is 50 to 70 percent, the glass fiber is 10 to 30 percent, the mica is 3 to 5 percent, the wood flour is 1 to 2 percent, the solubilizer is 1 to 5 percent, the dispersant agent is 1 to 4 percent, and the antioxidant is 1 to 4 percent. The mica, the wood flour and the plastic backing material form a copolymer with a continuous structure and even distribution under the mixing action of the solubilizer and the dispersant agent. The invention adopts a blending modification method, thereby improving the rigidity of new blend obviously and greatly increasing the ability for preventing distortion.
Description
Technical field
The present invention relates to a kind of manufacture method of fire resistant anti-deforming material for air-conditioning fan.
Background technology
Along with growth in the living standard, people more and more pay attention to the requirement of living environment, and as the conditioner that uses under indoor closed environment, its influence to fan noise also receives publicity day by day.The air conditioner room unit fan is the air-supply key part of conditioner, thereby the size of indoor fan noise is played material impact.
Existing air conditioner room unit axial-flow fan adopts common glass to strengthen materials such as AS, ABS or PP mostly and makes, because rigidity of itself and resistance to elevated temperatures exist not enough, deform easily in the transportation and behind the life-time service, can produce the problem that vibratory noise strengthens in the use.
Because the air conditioner room unit fan is the build-in components of air-conditioning system, therefore, how to start with from the air-conditioner fan material, strengthens the on-deformable performance of its heatproof, becomes a problem that needs to be resolved hurrily thereby address the above problem.
Summary of the invention
The invention provides a kind of fire resistant anti-deforming material for air-conditioning fan and preparation method thereof, it or poor with smoothness of operation after solving the fan life-time service that prior art exists, problems such as noise increasing.
In order to reach the purpose that solves the problems of the technologies described above, technical scheme of the present invention is, a kind of fire resistant anti-deforming material for air-conditioning fan, weight percent, its set of dispense ratio is: plastic basis material 50%-70%, glass fibre 10%-30%, mica 3%-5%, wood powder 1-2%, solubilizing agent 1%-5%, dispersion agent 1%-4%, antioxidant 1%-4%.
The present invention also has following supplementary technology scheme.
Described plastic basis material is AS, ABS or PP.
Described solubilizing agent includes but not limited at least a in benzoate, thiocyanate-and the salicylate.
Described dispersion agent includes but not limited at least a in hexenyl bis-stearamides, glyceryl monostearate, the Tristearoylglycerol.
Described antioxidant includes but not limited to phosphorous acid esters, and model is TNPP, 618,626, PL-40, PL-440.
Described glass fibre is the alkali free glass fibre T635B/T635C that Taishan Fibreglass Co., Ltd produces.
Make the method for fan material, comprise the following steps:
(1) mix: by weight percentage, its set of dispense ratio is: plastic basis material 50%-70%, and glass fibre 10%-30%, mica 3%-5%, wood powder 1-2%, solubilizing agent 1%-5%, dispersion agent 1%-4%, container is put in the preparation of antioxidant 1%-4% ratio;
(2) stir: make that starting material are full and uniform to dissolve each other;
(3) extruding pelletization: make the forming polymer after dissolving each other, use tablets press to finish.
Described tablets press is single screw pelletizer or dual-screw pelletizer.
The present invention compared with prior art has the following advantages and positively effect:
1. under the effect that solubilizing agent, dispersion agent are stirring, mica, wood powder and plastic basis material form the continuous and equally distributed multipolymer of structure; Because the present invention adopts the method for blending and modifying, causes new blend rigidity obviously to improve, and has strengthened non-deformability greatly.
2. solve problem such as indoor machine fan distortion behind the air-conditioning life-time service, improved behind the air-conditioning life-time service phenomenons such as smoothness of operation is poor, noise raising.
Embodiment
Embodiment 1
Make the method for fan material, comprise the following steps:
(1) mix, by weight percentage, its set of dispense ratio is: plastic basis material 50%, and glass fibre 30%, mica 5%, wood powder 2%, solubilizing agent 5%, dispersion agent 4%, container is put in the preparation of antioxidant 4% ratio;
(2) stir: make that starting material are full and uniform to dissolve each other;
(3) extruding pelletization: make the forming polymer after dissolving each other, use tablets press to finish.
Embodiment 2
Make the method for fan material, comprise the following steps:
(1) mix, weight percent, its set of dispense ratio is: plastic basis material 70%, glass fibre 11%, mica 5%, wood powder 1%, solubilizing agent 5%, dispersion agent 4%, antioxidant 4%;
(2) stir: make that starting material are full and uniform to dissolve each other;
(3) extruding pelletization: make the forming polymer after dissolving each other, use tablets press to finish.
Embodiment 3
Make the method for fan material, comprise the following steps:
(1) mix, weight percent, its set of dispense ratio is: plastic basis material 66%, glass fibre 26%, mica 4%, wood powder 1%, solubilizing agent 1%, dispersion agent 1%, antioxidant 1%;
(2) stir: make that starting material are full and uniform to dissolve each other;
(3) extruding pelletization: make the forming polymer after dissolving each other, use tablets press to finish.
Embodiment 4
Make the method for fan material, comprise the following steps:
(1) mix, weight percent, its set of dispense ratio is: plastic basis material 58%, glass fibre 28%, mica 5%, wood powder 1%, solubilizing agent 4%, dispersion agent 3%, antioxidant 1%;
(2) stir: make that starting material are full and uniform to dissolve each other;
(3) extruding pelletization: make the forming polymer after dissolving each other, use tablets press to finish.
In the above-described embodiments, described plastic basis material is AS, ABS or PP.
Described solubilizing agent includes but not limited at least a in benzoate, thiocyanate-and the salicylate.
Described dispersion agent includes but not limited at least a in hexenyl bis-stearamides, glyceryl monostearate, the Tristearoylglycerol.
Described antioxidant includes but not limited to phosphorous acid esters, and model is TNPP, 618,626, PL-40, PL-440.
Described glass fibre is the alkali free glass fibre T635B/T635C that Taishan Fibreglass Co., Ltd produces.
Described tablets press is single screw pelletizer or dual-screw pelletizer.
The above only is preferred embodiment of the present invention, is not to be the restriction of the present invention being made other form, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equivalent variations.But every technical solution of the present invention content that do not break away to any simple modification, equivalent variations and remodeling that above embodiment did, still belongs to the protection domain of technical solution of the present invention according to technical spirit of the present invention.
Claims (8)
1. fire resistant anti-deforming material for air-conditioning fan, weight percent, its set of dispense ratio is: plastic basis material 50%-70%, glass fibre 10%-30%, mica 3%-5%, wood powder 1-2%, solubilizing agent 1%-5%, dispersion agent 1%-4%, antioxidant 1%-4%.
2. a kind of fire resistant anti-deforming material for air-conditioning fan according to claim 1 is characterized in that described plastic basis material is AS, ABS or PP.
3. a kind of fire resistant anti-deforming material for air-conditioning fan according to claim 2 is characterized in that described solubilizing agent includes but not limited at least a in benzoate, thiocyanate-and the salicylate.
4. a kind of fire resistant anti-deforming material for air-conditioning fan according to claim 3 is characterized in that described dispersion agent includes but not limited at least a in hexenyl bis-stearamides, glyceryl monostearate, the Tristearoylglycerol.
5. a kind of fire resistant anti-deforming material for air-conditioning fan according to claim 4 is characterized in that described antioxidant includes but not limited to phosphorous acid esters, and model is TNPP, 618,626, PL-40, PL-440.
6. according to the described a kind of fire resistant anti-deforming material for air-conditioning fan of any claim in the claim 1 to 5, it is characterized in that described glass fibre is the alkali free glass fibre T635B/T635C that Taishan Fibreglass Co., Ltd produces.
7. a method of making the described air conditioner fan material of claim 1 is characterized in that comprising the following steps:
(1) mix: by weight percentage, its set of dispense ratio is: plastic basis material 50%-70%, and glass fibre 10%-30%, mica 3%-5%, wood powder 1-2%, solubilizing agent 1%-5%, dispersion agent 1%-4%, container is put in the preparation of antioxidant 1%-4% ratio;
(2) stir: make that starting material are full and uniform to dissolve each other;
(3) extruding pelletization: make the forming polymer after dissolving each other, use tablets press to finish.
8. method according to claim 7 is characterized in that described tablets press is single screw pelletizer or dual-screw pelletizer.