CN101158079B - Antistatic braided fabric, preparation method and antistatic flexible plastic intertexture packaging bag - Google Patents
Antistatic braided fabric, preparation method and antistatic flexible plastic intertexture packaging bag Download PDFInfo
- Publication number
- CN101158079B CN101158079B CN2007101578184A CN200710157818A CN101158079B CN 101158079 B CN101158079 B CN 101158079B CN 2007101578184 A CN2007101578184 A CN 2007101578184A CN 200710157818 A CN200710157818 A CN 200710157818A CN 101158079 B CN101158079 B CN 101158079B
- Authority
- CN
- China
- Prior art keywords
- antistatic
- braided fabric
- polyethylene
- basketwork
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to basketwork. The antistatic basketwork is formed by knitting polypropylene or polyethylene monofilament that contains calcium carbonate with conductive fiber and coating with the conductive fiber. The anti-static basketwork has reasonable raw material selection and compatibility. A plurality of conductive fibers (a product of stainless steel powder and the polyethylene) are together knitted into a piece of basic cloth during a weaving process and the polyethylene monofilament that contains CPT is used for coating the conductive fibers, thereby, the invention has relatively stronger anti-wearing and good water proof performance without any pollution and harm to human body. The basketwork products have extremely strong tensile strength and can avoid damage to goods (electronic devices, electronic equipment, chemicals, inflammable goods, etc.) and harm to human body.
Description
Technical field:
The present invention relates to braided fabric, particularly antistatic braided fabric also relates to its method for making, goods in addition.
Background technology:
Static has in various degree injury to the person and environment, particularly in the transportation of some goods, electronic device, electronic equipment, chemical substance, combustible and explosive articles and other items friction easily produces static, also there is not the direct antistatic of braided fabric at present, and be mostly by on the goods container bag, adding the antistatic silk, the antistatic silk contacts with electrostatic prevention film, and electrostatic prevention film is made at seam crossing.Utilize the electric conductivity of antistatic silk, the electric charge that produces is derived, reach the purpose that prevents static.But this based article number of plies is many, and the antistatic silk is fragile and influence anti-static effect, and makes the goods complex process.
Summary of the invention:
The objective of the invention is to overcome above-mentioned not enough problem, a kind of antistatic braided fabric is provided, anti-static effect is good, and is wear-resisting, and its method for making also is provided in addition, and technology is simple, and is easy to operate, and product properties is good, is widely used.
The technical scheme that the present invention is adopted for achieving the above object is: antistatic braided fabric by polypropylene calciferous or polyethylene monofilament and conducting fiber braiding and coated with conductive filament, forms antistatic braided fabric.
Described filament is that radial parallel distributes.
Described filametntary spacing is 10-30mm, and optimal spacing is 17mm.
The method for making of antistatic braided fabric of the present invention:
(1) get the raw materials ready: prepare raw material: PP (polypropylene) by weight: 100 parts, PE (polyethylene): 5 parts, M/B (Masterbatch): 0.4 part, CPT (calcium carbonate): 4 parts, UV (age resister): 0.4 part, filament.
(2) wire drawing: raw material polypropylene, polyethylene wire drawing are handled rolling moulding to the required width.
(3) braiding: the raw material monofilament and the filament of rolling moulding are pressed the setting spacing in order
Braiding envelopes filament with polyethylene monofilament calciferous in the time of braiding,
After performance test, get antistatic braided fabric.
Described polyethylene monofilament calciferous is after polyethylene and calcium carbonate mix, wire-drawing shape.
The goods that adopt braided fabric of the present invention to make are that antistatic flexible plastic is compiled pack, packaging bag etc.
Described antistatic flexible plastic is compiled the pack bag and is provided with suspender belt (lifting rope), and a kind of have braided button for the bag top is provided with charging aperture on the charging aperture, and the bag profile is a circle or square etc.
Described bag bottom is provided with discharge gate, and braided button is housed on the discharge gate.
Antistatic braided fabric of the present invention, material choice, compatibility are reasonable, in the braiding process, the some filaments that can conduct electricity (stainless steel powder and poly product) are together woven and advance base cloth, and it is encased with the polyethylene monofilament of a kind of CPT of containing, have stronger anti-wear performance, favorable waterproof property, to the air human body without any pollute, infringement.Can the damaged fiber silk in making, transportation and use, thus reach better anti-static effect.
Its method for making is simple, realizes the filametntary coating to conduction when weaving, and by its goods packaging bag of making or container bag packing chemical substance, electronic device etc. is had good protective action.Particularly antistatic flexible plastic is compiled pack, can effectively prevent the static that goods (electronic device, electronic equipment, chemical substance, combustible and explosive articles etc.) produces in transportation.Antistatic flexible plastic is compiled pack multiple shapes such as square, circle, can fully satisfy client's packing instructions.Make and transportation in can the damaged fiber silk, thereby reach better anti-static effect.Antistatic flexible plastic all is surrounded by filament when compiling each parts of pack (main body, low, lid, throw, row mouthful, suspender belt) braiding, comprises sewing thread.Utilize circuit theory that each parts is sewed up on request, so just formed conductor, filament has the ability of powerful absorption static, exceeds up to ten thousand times in wire.Compile the pack filament from antistatic flexible plastic and distribute, filament is that radial parallel distributes, and can prevent that like this each position is at static that moment produced.Not only can antistatic and tensile strength also big especially, can also prevent damage and the safety and the personal injury of goods (electronic device, electronic equipment, chemical substance, inflammable articles etc.).
Description of drawings:
Fig. 1 is a braided fabric flow sheet of the present invention.
Fig. 2 is a container bag flow sheet of the present invention.
Fig. 3 is a container bag structural representation of the present invention,
The specific embodiment:
The present invention is described in further detail below in conjunction with specific embodiment, but be not limited to specific embodiment.
Produce antistatic braided fabric by following raw material and method:
(1) get the raw materials ready: prepare raw material: PP (polypropylene) by weight: 100 parts, PE (polyethylene): 5 parts, M/B (Masterbatch): 0.4 part, CPT (calcium carbonate): 4 parts, UV (age resister): 0.4 part, raw material together adds when mixing.
(2) wire drawing: raw material polypropylene, polyethylene wire drawing are handled rolling moulding to the required width.
(3) braiding: the raw material monofilament and the filament of rolling moulding are pressed setting spacing 17mm mixed weaving, in the time of braiding polyethylene monofilament calciferous is enveloped filament, after performance test, get antistatic braided fabric.
Container bag is 17mm with main body, the end, lid, throwing, the filametntary spacing of row's mouth braided fabric, and the filament radical of suspender belt is 5, and average mark is knitted in the suspender belt of wide 70mm into.
Adopt above-mentioned base cloth to compile pack by prepared shown in Figure 2 antistatic flexible plastic shown in Figure 3, circular bag 1 is provided with suspender belt 4, bag top 5 is provided with charging aperture 2, bottom 8 is provided with discharge gate 7, button knot 3 is arranged on charging aperture and the discharge gate, bag filament 6 distributes for radial parallel, and filametntary spacing is 17mm.
The antistatic flexible plastic that makes is compiled and is packed that the result is as follows after testing:
Tensile strength, percentage elongation testing result:
Main body | Suspender belt | Low, lid | Throw, arrange mouth | Percentage elongation % |
1800N | 20000N | 1800N | 870 | 20 |
Tensile strength, percentage elongation national standard:
Main body | The charging and discharging mouth | Suspender belt | Percentage elongation (%) | |
≤1000kg | ≥828N | ≥16000N | ≤40 | |
Endwise tensile strength N/50mm | ≥1470N | |||
Transverse tensile strength N/50mm | ≥1470N |
The antistatic standard: earth resistance is less than 110
8Ω, inner with outside puncture decomposition voltage is less than 6KV.
Antistatic measures test result:
The test position | Unit | Test value |
Inlet | Ω | ?4.9·10 3to2.4·10 5 |
Whole | Ω | ?3.8·10 3to3.8·10 5 |
Outlet | Ω | 2.2·10 3to1.0·10 5 |
Annotate: static electricity resistance testing location Japan, the testing standard of existing domestic no antistatic container bag.
Claims (2)
1. the method for making of antistatic braided fabric is characterized in that:
(1) get the raw materials ready: prepare raw material by weight: polypropylene: 100 parts, polyethylene: 5 parts, Masterbatch: 0.4 part, calcium carbonate: 4 parts, age resister: 0.4 part, filament;
(2) wire drawing: raw material polypropylene, polyethylene wire drawing are handled rolling moulding to the required width;
(3) braiding: the raw material monofilament and the filament of rolling moulding are woven in order by setting spacing, in the time of braiding polyethylene monofilament calciferous is enveloped filament, after performance test, get antistatic braided fabric.
2. the method for making of antistatic braided fabric according to claim 1, it is characterized in that: wherein conducting fiber is a net distribution, the conducting fiber spacing is 17mm.