CN101148725A - High specific gravity tungsten alloy material and preparation method for nano crystal block thereof - Google Patents
High specific gravity tungsten alloy material and preparation method for nano crystal block thereof Download PDFInfo
- Publication number
- CN101148725A CN101148725A CNA2007100311674A CN200710031167A CN101148725A CN 101148725 A CN101148725 A CN 101148725A CN A2007100311674 A CNA2007100311674 A CN A2007100311674A CN 200710031167 A CN200710031167 A CN 200710031167A CN 101148725 A CN101148725 A CN 101148725A
- Authority
- CN
- China
- Prior art keywords
- sintering
- powder
- specific gravity
- tungsten alloy
- current
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to high tungsten alloy material and the preparation process of its nanometer crystal lump. The materials including W 93.0 wt%, Ni 3.5-4.5 %, Fe 1.5-2.0 %, Co 1.0-1.5 % and small amount of inevitably impurity are mixed, high energy ball milled until the W phase crystal grains are refined to nanometer level, and DC pulse-constant current sintered quickly at the pressure of 40-50 MPa for 3-8 min to obtain the high tungsten alloy material with nanometer crystal lumps. The high tungsten alloy material has high mechanical performance.
Description
Technical field
The present invention relates to plastic forming technology and powder metallurgy technology, specifically be meant a kind of high specific gravity tungsten alloy material and preparation method for nano crystal block thereof thereof.
Background technology
Tungsten-bast alloy has a wide range of applications in national defense industry and civilian industry because of having higher density, the mechanical property of excellence and good corrosion resistance.Existing tungsten base high-specific-gravity alloy, mainly by matrix tungsten and bonding mutually nickel, cobalt, iron etc. form, and mainly adopt hot isostatic pressing, methods such as radiation heating sintering and induction sintering are prepared.Wherein, hot isostatic pressing and radiation heating sintering method are because sintering time is long and sintering temperature is higher, organizing of the agglomerated material that obtains is thicker, be unfavorable for improving the performance of agglomerated material, though induction sintering can shorten sintering time, but because of sintering pressure is not provided, there is the low and difficult fully fine and close problem of agglomerated material dimensional precision in the sintering process.
At present, investigation of materials person generally believe that the nanocrystalline microtexture of acquisition will help improving the over-all properties of block tungstenalloy both at home and abroad.In recent years rise the discharge plasma sintering method of coming, its essence is exactly pulse electric current sintering, because of the activation of strong pulse electric current to powder helps reducing sintering temperature and shortens sintering time, be considered to prepare a kind of effective way of bulk nanometer material, and, also can effectively control the dimensional precision of agglomerated material because this sintering method is applied with certain external force in sintering process.Paper " the SPS sintering behavior of W-Ni-Fe high-density alloy " (Mei Xuezhen, go into business into factory, Yin Fazhang, Chen Liliang, University of Science ﹠ Technology, Beijing's journal, 2007,29 (5), 475~478) adopt discharge plasma sintering method to prepare the 93W-5.6Ni-1.4Fe high-density alloy, confirm that discharge plasma sintering can suppress tungsten grain and grow up, and obtain grain-size microtexture comparatively uniformly.But, do not obtain bulk nanometer material owing to reasons such as tungstenalloy composition prescription and sintering process selections.In addition because discharge plasma sintering method mainly adopts single pulsed current that powder is carried out sintering, for the peak strength that has realized abundant sintering of body of powder and fine and close paired pulses electric current has proposed higher requirement, what bring immediately is the requirement more harsh to agglomerating plant, directly increase facility investment, so that increased production cost.
Summary of the invention
The objective of the invention is at prior art for preparing high-specific gravity tungsten alloy weak point, a kind of high specific gravity tungsten alloy material is provided and can effectively controls the preparation method of agglomerated material dimensional precision, realize the preparation of microtexture uniform crystal particles, nearly full densification and high performance bulk nano-crystalline high-specific gravity tungsten alloy.
A kind of high specific gravity tungsten alloy material, it contains tungsten, nickel and iron powder, it is characterized in that: it also contains cobalt, concrete prescription component and content thereof by mass percentage is: tungsten W93.0%, nickel 3.5~4.5%, iron Fe1.5~2.0%, cobalt Co1.0~1.5%, all the other are inevitable trace impurity.
The preparation method of above-mentioned this bulk nanometer high specific gravity tungsten alloy material is characterized in that: this method comprises the steps:
Step 1: the prescription of high-specific gravity tungsten alloy
Tungsten, nickel, cobalt and iron powder are carried out proportioning by following mass percent consumption: tungsten W93.0%, nickel 3.5~4.5%, iron Fe1.5~2.0%, cobalt Co1.0~1.5%, all the other are inevitable trace impurity;
Step 2: mix powder
Be no less than 24 hours by above-mentioned powder stock mass percent consumption dried mixing in mixed powder machine;
Step 3: high-energy ball milling
The powder of doing after mixing is carried out high-energy ball milling, and the grain refining of tungsten phase is to nano level in ball-milled powder;
Step 4: electric current sintering ball-milled powder
Adopt pack into ball-milled powder in the electric current sintering mould of square wave direct current pulse-continuous current Fast Sintering, electric current Fast Sintering processing condition are as follows:
The sintering current type: square-wave pulse galvanic current and continuous current combine
Sintering pressure: 40MPa~50MPa
Sintering time: 3~8 minutes
Promptly obtain the bulk nanometer high specific gravity tungsten alloy material through sintering.
Described square wave direct current pulse-continuous current Fast Sintering, its selection process is: adopted square-wave pulse galvanic current sintered powder earlier 1~3 minute, adopted the continuous current sintered powder again 1~5 minute.
The peak value of described square-wave pulse galvanic current, base value, frequency and dutycycle are respectively 3150~3600A, 120~350A, 60~100Hz and 55~80%, and the continuous current preferred value is 1575A~1650A.
The present invention compared with prior art has the following advantages:
1, high-specific gravity tungsten alloy prescription of the present invention is reasonable, can help to obtain nanocrystalline sintered state material, and can improve the sintered state comprehensive mechanical performance.
2, but the electric current sintering technology of the present invention's employing is the Fast Sintering of square wave direct current pulse-continuous current sintering technology realization within a short period of time to the high-specific gravity tungsten alloy powder body.Compare with technologies such as hot isostatic pressings with traditional radiation heating sintering, adopt square wave direct current pulse-continuous current sintering method not only the thermo-efficiency height, sintering temperature is low, sintering time is short, sintered state organizes more tiny all even porosity low, and the shape and size precision of sintered compact is easy to control, powder forming and sintering integratedization have been realized, do not need preliminary shaping, the material preparation process route is simplified, and can reduce the preparation cost of high-specific gravity tungsten alloy block materials.In addition, carry out the agglomerating discharge plasma sintering process with the single pulsed current of employing and compare, the pulse current peak intensity in the time of can lowering sintering, thus reduction is to the requirement of agglomerating plant.
3, the high-specific gravity tungsten alloy block materials of the present invention's preparation has nanocrystalline microtexture, and is near complete fine and close, the cross-breaking strength that the hardness that has is higher and good.
4, preparation method of the present invention obviously reduces the requirement of equipment, and is simple to operate, and the cycle is short, has improved efficient, has reduced cost; Be particularly conducive to the production domesticization that the bulk nano-crystalline high specific gravity tungsten alloy material is produced.
Embodiment
The invention will be further described by following embodiment, but embodiments of the present invention are not limited only to this.
Embodiment 1
Step 1: the prescription of high-specific gravity tungsten alloy
Component by mass percentage and content thereof are: tungsten W:93.0%, and nickel: 4.5%, iron Fe:1.5%, cobalt Co:1.0% contains inevitable trace impurity;
Tungsten, nickel, iron and cobalt all add with simple substance form, wherein, and about 2.3~2.7 μ m of tungsten powder flat diameter particle diameter, purity 〉=99.0%; About 1~3 μ m of nickel powder flat diameter particle diameter, purity 〉=99.8%; About 1~3 μ m of iron powder flat diameter particle diameter, purity 〉=99.5%; About 1~3 μ m of cobalt powder flat diameter particle diameter, purity 〉=99.0%;
Step 2: mix powder
Mix dried mixing 24 hours in the powder machine by above-mentioned powder stock mass percent consumption in the V-0.002 type;
Step 3: high-energy ball milling
Mechanical milling process is finished in QM-2SP20 type planetary ball mill, abrading-ball and ball grinding cylinder inwall material all adopt the YG8 Wimet, and ball material mass ratio is 10: 1, and drum's speed of rotation is 266r/min, and adopt high-purity Ar gas as protective atmosphere, the ball milling time is 15 hours;
Step 4: electric current sintering ball-milled powder
With the 20g ball-milled powder diameter of packing into is in the ceramic post sintering mould of Ф 20mm, by applying 1 minute square-wave pulse galvanic current earlier, and then applies 5 minutes continuous currents again powder is carried out Fast Sintering.Wherein, the peak value of pulsed current, base value, frequency and dutycycle are respectively 3600A, 120A, 100Hz and 55%, and continuous current is 1575A.In the whole process of energising sintering, by positive and negative electrode body of powder is applied the 40MPa sintering pressure, through the bulk nanometer high specific gravity tungsten alloy material of sintering acquisition in 6 minutes.The density of this material is 17.39g/cm
3, the about 200nm of tungsten phase grain-size, normal temperature hardness and bending strength are respectively 84HRA and 1384MPa.
Embodiment 2
Step 1: the prescription of high-specific gravity tungsten alloy
Component by mass percentage and content thereof are: W:93.0%, and Ni:3.5%, Fe:2.0%, Co:1.5% contains inevitable trace impurity.
Tungsten, nickel, iron and cobalt all add with simple substance form, wherein, and about 2.3~2.7 μ m of tungsten powder flat diameter particle diameter, purity 〉=99.0%; About 1~3 μ m of nickel powder flat diameter particle diameter, purity 〉=99.8%; About 1~3 μ m of iron powder flat diameter particle diameter, purity 〉=99.5%; About 1~3 μ m of Co powder flat diameter particle diameter, purity 〉=99.0%;
Step 2: mix powder
Mix dried mixing 24 hours in the powder machine by above-mentioned powder stock mass percent consumption in the V-0.002 type;
Step 3: high-energy ball milling
Mechanical milling process is finished in QM-2SP20 type planetary ball mill, abrading-ball and ball grinding cylinder inwall material all adopt the YG8 Wimet, and ball material mass ratio is 10: 1, and drum's speed of rotation is 266r/min, and adopt high-purity Ar gas as protective atmosphere, the ball milling time is 15 hours;
Step 4: electric current sintering ball-milled powder
With the 20g ball-milled powder diameter of packing into is in the ceramic post sintering mould of Ф 20mm, by applying 3 minutes square-wave pulse galvanic current earlier, and then applies 5 minutes continuous currents again powder is carried out Fast Sintering.Wherein, the peak value of pulsed current, base value, frequency and dutycycle are respectively 3150A, 350A, 80Hz and 80%, and continuous current is 1575A.In the whole process of energising sintering, by positive and negative electrode body of powder is applied the 40MPa sintering pressure, through the bulk nanometer high specific gravity tungsten alloy material of sintering acquisition in 8 minutes.The density of this material is 17.55g/cm
3, the about 250nm of tungsten phase grain-size, normal temperature hardness and bending strength are respectively 83HRA and 1496MPa.
Embodiment 3
Step 1: the prescription of high-specific gravity tungsten alloy
Component by mass percentage and content thereof are: W:93.0%, and Ni:4.0%, Fe:1.8%, Co:1.2% contains inevitable trace impurity.
Tungsten, nickel, iron and cobalt all add with simple substance form, wherein, and about 2.3~2.7 μ m of tungsten powder flat diameter particle diameter, purity 〉=99.0%; About 1~3 μ m of nickel powder flat diameter particle diameter, purity 〉=99.8%; About 1~3 μ m of Co powder flat diameter particle diameter, purity 〉=99.0%; About 1~3 μ m of iron powder flat diameter particle diameter, purity 〉=99.5%;
Step 2: mix powder
Mix dried mixing 24 hours in the powder machine by above-mentioned powder stock mass percent consumption in the V-0.002 type;
Step 3: high-energy ball milling
Mechanical milling process is finished in QM-2SP20 type planetary ball mill, abrading-ball and ball grinding cylinder inwall material all adopt the YG8 Wimet, and ball material mass ratio is 10: 1, and drum's speed of rotation is 266r/min, and adopt high-purity Ar gas as protective atmosphere, the ball milling time is 15 hours;
Step 4: electric current sintering ball-milled powder
With the 20g ball-milled powder diameter of packing into is in the ceramic post sintering mould of Ф 20mm, by applying 2 minutes square-wave pulse galvanic current earlier, and then applies 1 minute continuous current again powder is carried out Fast Sintering.Wherein, the peak value of pulsed current, base value, frequency and dutycycle are respectively 3500A, 180A, 60Hz and 65%, and continuous current is 1650A.In the whole process of energising sintering, by positive and negative electrode body of powder is applied the 50MPa sintering pressure, through the bulk nanometer high specific gravity tungsten alloy material of sintering acquisition in 3 minutes, the density of this material is 17.46g/cm
3, the about 180nm of tungsten phase grain-size, normal temperature hardness and bending strength are respectively 84HRA and 1480MPa.
Claims (4)
1. high specific gravity tungsten alloy material, it contains tungsten, nickel and iron powder, it is characterized in that: it also contains cobalt, concrete prescription component and content thereof by mass percentage is: tungsten W93.0%, nickel 3.5~4.5%, iron Fe1.5~2.0%, cobalt Co1.0~1.5%, all the other are inevitable trace impurity.
2. the preparation method of a bulk nanometer high specific gravity tungsten alloy material, it is characterized in that: this method comprises the steps:
Step 1: the prescription of high-specific gravity tungsten alloy
Tungsten, nickel, iron and cobalt dust are carried out proportioning: W93.0% by following mass percent consumption, Ni3.5~4.5%, Fe1.5~2.0%, Co1.0~1.5%, all the other are inevitable trace impurity;
Step 2: mix powder
Be no less than 24 hours by above-mentioned powder stock mass percent consumption dried mixing in mixed powder machine;
Step 3: high-energy ball milling
The powder of doing after mixing is carried out high-energy ball milling, and the grain refining of tungsten phase is to nano level in ball-milled powder;
Step 4: electric current sintering ball-milled powder
Adopt pack into ball-milled powder in the electric current sintering mould of square wave direct current pulse-continuous current Fast Sintering, electric current Fast Sintering processing condition are as follows:
The sintering current type: square-wave pulse galvanic current and continuous current combine
Sintering pressure: 40MPa~50MPa
Sintering time: 3~8 minutes
Promptly obtain the bulk nanometer high specific gravity tungsten alloy material through sintering.
3. the preparation method of a kind of bulk nanometer high specific gravity tungsten alloy material according to claim 2, it is characterized in that: described square wave direct current pulse-continuous current Fast Sintering, its technology is: adopted square-wave pulse galvanic current sintered powder earlier 1~3 minute, adopted the continuous current sintered powder again 1~5 minute.
4. according to the preparation method of claim 2 or 3 described a kind of bulk nanometer high specific gravity tungsten alloy materials, it is characterized in that: the peak value of described square-wave pulse galvanic current, base value, frequency and dutycycle are respectively 3150~3600A, 120~350A, 60~100Hz and 55~80%, and the Constant Electric Current flow valuve is 1575A~1650A.