CN101146968A - Shrapnel and projectile containment systems and equipment and methods for producing same - Google Patents

Shrapnel and projectile containment systems and equipment and methods for producing same Download PDF

Info

Publication number
CN101146968A
CN101146968A CNA2005800473004A CN200580047300A CN101146968A CN 101146968 A CN101146968 A CN 101146968A CN A2005800473004 A CNA2005800473004 A CN A2005800473004A CN 200580047300 A CN200580047300 A CN 200580047300A CN 101146968 A CN101146968 A CN 101146968A
Authority
CN
China
Prior art keywords
plate
layer
wall
fabric
concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2005800473004A
Other languages
Chinese (zh)
Inventor
布鲁斯·霍尔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIFE SHIELD ENGINEERED SYSTEMS
Original Assignee
LIFE SHIELD ENGINEERED SYSTEMS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIFE SHIELD ENGINEERED SYSTEMS filed Critical LIFE SHIELD ENGINEERED SYSTEMS
Publication of CN101146968A publication Critical patent/CN101146968A/en
Pending legal-status Critical Current

Abstract

A blast-resistant panel may include a layer of a pre-cured elastomeric material having a predetermined thickness, a body portion, and a plurality of flanges, each of the plurality of flanges having a substantially equal width and depending away from a same side and at approximately equivalent right angles to the body portion. The blast-resistant panel may also include a plurality of fastener elements for securing the cured elastomeric material layer to a surface of a structure through the plurality of flanges of cured elastomeric material.

Description

Fragment and projectile containment system and the apparatus and method that are used to prepare this system
The cross reference of related application
According to 35 U.S.C. § 119 (e), the present invention requires the U.S. Provisional Patent Application No.60/623 that is entitled as " Shrapnel and Projectile Containment Systems and Methods for ProducingSame " in submission on December 1st, 2004,074 and the U.S. Provisional Patent Application No.60/642 that is entitled as " Shrapnel and Projectile Containment Systems and Methods for ProducingSame " that submits on January 12nd, 2005,991 priority, these two applications are combined in this with their full content by reference; And the present invention relates to the U.S. Patent application No.10/510 that is entitled as " Shrapnel Containment System and Method for Producing Same " in submission on October 8th, 2004,691, described application No.10/510, the 691st, the American National phase application of international application No.PCT/US2004/010488, and described international application No.PCT/US2004/010488 on April 6th, 2004 submit to and be entitled as " Shrapnel Containment System andMethod for Producing Same; " and requirement is in the U.S. Provisional Patent Application No.60/460 that is entitled as " Blast-Resistant Panel and Method for Producing Same " of submission on April 7th, 2003,422 priority.
Invention field
The apparatus and method that the present invention relates generally to a kind of system and prepares this system, wherein said system is installed in or is adjacent to side, bottom or the top of wall, floor or ceiling or the vehicle of structure, to admit from the fragment of blast and/or the projectile of being launched by projectile launcher.
The accompanying drawing summary
The explanation that provides below reading in conjunction with the drawings will be understood the present invention best, and in the accompanying drawings, similar elements represents with same reference numerals, and wherein:
The schematically illustrated plate preparation facilities of Fig. 1 according to one embodiment of the invention.
Fig. 2 is the structure that is installed in building according to the shrapnel containment plate of one embodiment of the invention
The main schematic diagram of portion within the walls.
Fig. 3 illustrates the shrapnel containment plate according to one embodiment of the invention.
Fig. 4 is fastened with the cross-sectional view of the plate of pocket member according to one embodiment of the invention at its periphery.
Fig. 5 is the cross-sectional view according to two adjacent plates of one embodiment of the invention, and these two adjacent plates pass through the combination of plate tightening member at its edge.
Fig. 6 is the roughly schematic plan that designs according to the test that research of the present invention is carried out.
Fig. 7 is the side perspective view according to the plate with flange of one embodiment of the invention, described flanged ring winding board periphery and be basically perpendicular to described plate.
Fig. 8 is the cross-sectional view according to the plate 8-8 along the line of Fig. 7 of one embodiment of the invention.
Fig. 9 is the part top view according to the continuous restraint zone of one embodiment of the invention, and described continuous restraint zone has a part and the fixing securing member of concrete surface of the flange that makes plate.
Figure 10 is the part top view according to the discontinuous restraint zone of one embodiment of the invention, and described discontinuous restraint zone has a part and the fixing securing member of concrete surface of the flange that makes plate.
Figure 11 makes the part of the flange of plate be fixed to the part top view of several fastening systems of concrete surface according to one embodiment of the invention.
Figure 12 is that described wall system has the stiffener that is fastened to the available frame element with securing member according to the cross-sectional, top view of the wall system of one embodiment of the invention manufacturing.
Figure 13 is that wherein said wall system has the stiffener that is secured to the available frame element according to the part cross-sectional, top view of another wall system of one embodiment of the invention manufacturing.
Figure 14 is in the part cross-sectional, top view according to the slotted section of the framework in the wall system with stiffener of one embodiment of the invention manufacturing, and described slotted section can be used to make described plate and available frame element fastening.
Figure 15 is that described concrete floor portion within it has stiffener according to the part cross-sectional side view of the concrete floor of one embodiment of the invention manufacturing.
Figure 16 is that described concrete wall portion within it have reinforcing bar and stiffener according to the part cross-sectional, top view of the concrete wall of one embodiment of the invention structure.
Figure 17 is that described concrete wall have reinforcing bar and the stiffener on the concrete face of wall according to the part cross-sectional, top view of the concrete wall of one embodiment of the invention structure.
Figure 18 is the cross-sectional, top view of plate system that is used to protect a monoblock (one-piece) of concrete column according to one embodiment of the invention.
Figure 19 is the cross-sectional, top view according to the L shaped carriage of one embodiment of the invention, and described L shaped carriage is used to make the plate system of a monoblock or polylith to be fastened on around the concrete column.
Figure 20 is the cross-sectional, top view according to the L shaped slot type carriage of one embodiment of the invention, and described L shaped slot type carriage is used to make the plate system of a monoblock or polylith to be fastened on around the concrete column.
Figure 21 is the part cross-sectional, top view according to the L shaped carriage of Figure 18 of one embodiment of the invention, and described L shaped carriage makes the turning of the protection plate system that uses of concrete column and concrete column fastening.
Figure 22 is the cross-sectional, top view that is used to protect two formula plate systems of concrete column according to one embodiment of the invention.
Figure 23 is the part cross-sectional side view that is used to protect the plate system of concrete column according to one embodiment of the invention, and it has shown the enhancement Layer that diamond shaped is arranged.
Figure 24 is the part cross-sectional, top view according to the hollow core flush door of one embodiment of the invention, and this hollow core flush door has anti-crushing and the plate of projectile that is arranged in the door.
Figure 25 is the part cross sectional front elevation according to the two-tube channel system of one embodiment of the invention, and this two-tube channel system has anti-crushing and the plate of projectile of the outside of the interior pipe that is arranged on described two pipes.
Figure 26 is that this door-plate is set on the inner surface of door according to the lateral view of the door-plate of dismountable anti-crushing of one embodiment of the invention and projectile.
Figure 27 is anti-crushing and multiple-plate lateral view of projectile according to one embodiment of the invention.
Figure 28 is anti-crushing and multiple-plate lateral view of projectile according to another embodiment of the invention.
Figure 29 is the lateral view according to the plate of anti-crushing of one embodiment of the invention and projectile, and the plate of described anti-crushing and projectile directly is used on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.
Figure 30 is the lateral view according to the plate of anti-crushing of another embodiment of the invention and projectile, and the plate of described anti-crushing and projectile directly directly is applied on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.
Figure 31 is the lateral view that has the plate of anti-crushing of the fabric/fiber enhancement Layer and projectile according to another embodiment of the invention between two layers of elastomer, and described plate directly is applied on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.
Figure 32 is the lateral view that has the plate of anti-crushing of the fabric/fiber enhancement Layer and projectile according to another embodiment of the invention between two layers of elastomer, and described plate directly is applied on the lip-deep release agent of structure and makes a plurality of surfaces of itself and structure fastening with machanical fastener.
Figure 33 is the lateral view according to the Automatic Production System of the plate of anti-crushing of one embodiment of the invention and projectile.
Figure 34 is the Automatic Production System according to the plate of anti-crushing of another embodiment of the invention and projectile.
Figure 35 is the top view according to the Automatic Production System of the plate of in Figure 34 anti-crushing of one embodiment of the invention and projectile.
Figure 36 is the cross-sectional view according to the Automatic Production System 36-36 along the line of the plate of in Figure 35 anti-crushing of another embodiment of the invention and projectile.
Figure 37 is the top view in cross section of vehicle that has the anchor post of pre-determined bit according to one embodiment of the invention, and the anchor post of described pre-determined bit is used for plate and the vehicle grappling with anti-crushing and projectile.
Figure 38 is the lateral view according to the cross section of the vehicle chassis in Figure 37, wall, door and/or the ceiling of one embodiment of the invention.
Figure 39 is the open type lateral view according to the prefabricated wall system of one embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.
Figure 40 is the partial cross sectional view according to the prefabricated wall system 40--40 along the line in Figure 40 of one embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.
Figure 41 is the lateral view according to the prefabricated wall system in Figure 40 of another embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.
Figure 42 is the close-up side view according to the top of the prefabricated wall system of Figure 41 of one embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.
Figure 43 is the view of the shock wave/shrapnel containment plate according to another embodiment of the invention.
Figure 44 is the lateral view of shock wave/shrapnel containment plate of Figure 43.
Figure 45 is the view of the shock wave/shrapnel containment plate according to Figure 43 of the present invention.
Figure 46 is the lateral view of shock wave/shrapnel containment plate of Figure 45.
Figure 47 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 48 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 49 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 50 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 51 is the lateral view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 52 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 53 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 54 is the view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 55 is the environmental view (environmental view) of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 56 is the environmental view of the shock wave/shrapnel containment plate system according to another embodiment of the invention.
Figure 57 shows the exemplary mounting method that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 58 shows the exemplary mounting method that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 59 shows the exemplary mounting method that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 60 shows the exemplary mounting method that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 61 shows the exemplary mounting method that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 62 shows the illustrative methods that is used to make shock wave/shrapnel containment plate system shaping according to one embodiment of the invention.
Figure 63 shows the illustrative methods that is used to make shock wave/shrapnel containment plate system shaping according to one embodiment of the invention.
Figure 64 shows the illustrative methods that is used to make shock wave/shrapnel containment plate system shaping according to one embodiment of the invention.
Figure 65 shows the exemplary forming tool that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 66 shows the exemplary forming tool that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 67 shows the exemplary forming tool that is used for shock wave/shrapnel containment plate system according to one embodiment of the invention.
Figure 68 is the view of the shock wave/shrapnel containment plate plate according to another embodiment of the invention.
Figure 69 is the lateral view of exemplary shock wave/shrapnel containment plate of Figure 68.
Figure 70 is the lateral view of alternate exemplary shock wave/shrapnel containment plate of Figure 68.
Figure 71 is the lateral view of alternate exemplary shock wave/shrapnel containment plate of Figure 68.
Figure 72 is the lateral view of alternate exemplary shock wave/shrapnel containment plate of Figure 68.
Figure 73 is the environmental side elevation view of shock wave/shrapnel containment plate of Figure 68, the figure illustrates the distortion due to the power B.
Figure 74 illustrates the shock wave/fragment/projectile containment plate according to another embodiment of the invention.
Figure 75 illustrates in greater detail shock wave/fragment/projectile containment plate of Figure 74.
Figure 76 illustrates in greater detail shock wave/fragment/projectile containment plate of Figure 75.
Figure 77 illustrates in greater detail shock wave/fragment/projectile containment plate of Figure 76.
Figure 78 illustrates in greater detail shock wave/fragment/projectile containment plate of Figure 77.
Figure 79 illustrates in greater detail shock wave/fragment/projectile containment plate of Figure 78.
Figure 80 shows the lateral view of exemplary shock wave/fragment/projectile containment plate.
Figure 81 shows the lateral view of exemplary shock wave/fragment/projectile containment plate.
Figure 82 shows the lateral view of exemplary shock wave/fragment/projectile containment plate.
DESCRIPTION OF THE PREFERRED
The present invention relates to prepare preformed board, this preformed board can form with different shape, is cut to appropriate size as required, and is installed on the surface of the wall of building and/or door, or surperficial adjacent with the wall of building and/or door.Usually, in order to improve the effectiveness of protection provided by the invention, described wall can be a structural wall.When preparation elongation and the improved material of tensile strength properties,, can prepare ejecting plate by spraying polyureas or other elastomeric material of selecting especially with the performance that helps production technology and production board.By with polyurea materials or other elastomeric material brushing, roller coat and/or trowelling to forming the required thickness of production board, also can prepare ejecting plate.Alternatively, can and be directly bonded on the inner surface of structural wall or building polyurea materials or other elastomeric material coating (that is spraying,, brushing, roller coat and/or trowelling).In another kind of alternative, polyurea materials or other elastomeric material can be applied (promptly, spraying, brushing, roller coat and/or trowelling) to the release agent of the inner surface that is coated on structural wall or building in advance (for example, polytetrafluoroethylene (PTFE), silicon, wax and/or any other release agent) on, machanical fastener can be inserted elastomeric material and release agent then, enter and be anchored to inner surface.Can apply and the inner surface of fastening elastomeric material can comprise wall, ceiling, floor, post, door, window etc.
At the construction plate or when being directly bonded to one or more material layers on the wall, elastic body can be as the alternative of polyureas such as polysiloxanes, polyurethane and polyurea/polyurethane mixture (hybrids).
The present invention can also relate to the method for preparation shock resistance ripple, anti-vibration and the anti-plate that launches, this method comprises dimeric (two-part) of two-layer or multilayer but the polyurea elastomer material of high solids is coated on the release liners, to form required thickness.Can apply described two-layer or more multi-layered elastomeric material being provided with between the two-layer or more multi-layered elastomeric material or not being provided with under the situation of one or more fibers or fabric enhancement Layer, make material cured, but and shift out the plate of curing from release liners.Plate can be transplanted on the building site again away from the preparation of place, building site, or prepares in the building site.Plate can be installed on structural wall (wall), door and the other parts of building, structure or vehicle, to provide fragment and the protection of launching.In addition, plate can be installed in the inside of elevator shaft and/or stair tower, so that extra structural integrity to be provided, and be installed in dwelling house wall inside under the situation of seismic activity, to gain in strength and wind resistance.Similarly, plate can be used to cover window and door and be fastened on the appropriate location, avoid for example influence of cyclone and hurricane of high wind and harsh climate to protect them.
According to another embodiment of the invention, elastomeric material can be carried out injection moulding, forming the sealed tube can be used on the hull outside, avoid injury from other ship, harbour etc. with the protection hull.
In Fig. 1, plate substrate 10 can serve as model surface, polyurea elastomer material coating for example can be sprayed, brushing, roller coat and/or trowelling to this model surface, with produce according to the shock resistance ripple of the preferred embodiments of the invention and/or projectile or fragment stop plate 100.Although the plate substrate 10 that shows is smooth two-dimensional surface, but can consider in other embodiments, plate substrate 10 can have with its on can use the particular door, wall etc. of plate 100 consistent recessed and/or protruding profile and/or the side of structure, the structure that certain wall, door of plate 100 etc. can be used in these profiles and/or side conforms to.When needing, substrate 10 can be handled with release agent/compound, so that remove the plate of curing from substrate.
Utilize known standard spraying and applying equipment, dimeric high solids elastic composition is sprayed on the substrate 10 with liquid (uncured) form.The spraying equipment that is used for illustration purpose can comprise nozzle 20, and described nozzle is connected to coating pump 24 via flexible pipe 22.Container or storage tank 26 can be used for supplying with the component that constitutes elastic composition by feeding pipe 28,30, and wherein at described feeding pipe 28,30, component is mixed at valve 32 places.Nozzle 20 can hand control, in producing plate polyurea materials is coated on the entire substrate.Alternatively, nozzle (can use the nozzle more than) can be installed on the support (not shown) with known configuration, described support has the drive unit that is used for horizontal or level and vertical moving nozzle 20, is coated on the entire substrate with uniform thickness to guarantee composition.It also is feasible that other spraying and applying is arranged, the just example shown in Fig. 1.
Can imagine, for large-scale production, computer control and robotic component are used to control spraying equipment, spraying coating process can be substantially all automations, wherein said spraying coating process comprises the processing of transporting of moving of sprayer and material to be sprayed and plate.Yet it is identical that identical basic technology almost keeps, and Figure 33-36 provides the figure of two embodiments of the possible automatic system that the large-scale production production board uses.For example, automatic system can be prepared at least one production board at least every 5 minutes.
In an exemplary especially embodiment, described plate can be further enhanced by comprising enhancement Layer 102, and described enhancement Layer can be arranged on the external surface or the inner surface place of plate 100, maybe can be arranged on described intralamellar part.The method of producing this plate (having the enhancement Layer that is positioned at intralamellar part) can preferably include against substrate 10 and place reinforcement fabric materials and spray polyurea or other elastic body that can spray to fabric, forms half thickness of the thickness that is about production board.Then, will have fabric 102 rotation or the upset of the polyureas in the spraying, and make the polyureas faces substrate, and fabric 102 is in the face of spraying equipment.Then polyureas is applied for the second time or is ejected on the opposition side of fabric 102, have the desirable final thickness or the plate of finished product thickness with generation.
Can make amendment to this selection process order.Wanting when the external surface of plate 100 has enhancement Layer, described enhancement Layer can be placed as with substrate 10 and closely contact, and elastic body can sprayed on the described layer, up to obtaining desirable plate thickness.In plate 100 inside with placed layer 102 local time, utilize by described layer and spray to seal the polyureas of described layer 102, described layer can separate with substrate 10.Alternatively, the part of described plate can be sprayed on the described substrate, then import described layer 102, follow the residual thickness of spray coating plate, to finish described plate.
In case spraying coating process is finished, and polyurea materials partially or completely solidifies, and then described layer can separate with substrate 10, thus formation plate 100.
Therefore, can economic mode make described plate 100 basically on a large scale.If since a certain former thereby find it is less expensive or desirable, then at this moment can in the real environment of plant, realize, or in the portable or interim production equipment that build the building site, realize.Then plate 100 is transported to the building that is about to assemble these bursting diaphragms.
Will or in the initial construction process, let alone to expose with the internal construction wall 104 of the fastening building of described plate, and perhaps in the building renovation, remove and decorate internal face, with the inner surface of exposed structure wall.As required plate 100 is cut into appropriate size, and preferably use any suitable adhesive or be fixed to the inner surface of wall 104 by mechanical connection.Because structural wall 104 made by piece material or poured concrete usually, so suitable mechanical connection form can comprise screw thread concrete joist anchor or screw and anchoring piece or with the concrete cement nail stickfast of suitable infiltration.
Fig. 2 is according to the shrapnel containment plate of one embodiment of the invention main schematic diagram in the installation of the structural wall inside of building.
Fig. 3 shows a preferred embodiment of the plate 100 that is ready for installation.In this embodiment, the periphery of plate 100 is by pocket member 120 restriction, and described pocket member 120 is held in place the edge of plate 100 between two cross bars (rail) 122,124 of the opposition side (for example, front side and rear side) of plate (referring to Fig. 4).Preferably the pocket member of being made by stainless steel helps the structurally edge of stiffener, increases its hardness.In addition, plate is being fixed in the process of building wall, is using groove to improve the reliability of machanical fastener 121 at the panel edges place, described machanical fastener 121 is such as but not limited to concrete joist anchor, screw, nail etc.
Fig. 5 illustrates another plate clamp structure 126, described plate clamp structure be suitable for two harden close with cross than the width of single plate wideer apart from the time use.Use the machanical fastener 131 that is fit to the neighboring edge of two plates to be fixed to two cross bars 128,130 of this plate clamp structure.Cross bar 128,130 is by junction plate (web) 132 skews, makes clamp structure keep this two plates with the relation of edges abut substantially.Except or replace pocket member 120, can use securing member 126 in the edge that will carry out combination.Clamp structure also can such as but not limited to concrete joist anchor etc., be fixed on the building wall by suitable mechanical fasteners member.
The explosion wave of building outside or the impact force of other type can make structural wall rupture, and produce the wall fragment of all size, and these wall fragments are also referred to as fragment usually.Plate 100 with the elongation of improvement and tensile strength characteristics will be in order to absorb the major part of the kinetic energy that imposes on fragment effectively.This kinetic energy absorbs will prevent that fragment from flying over interior of building.Under explosion wave also makes the situation of plate 100 fracture, absorb or the kinetic energy that consumes will significantly reduce the amount and/or the speed of the fragment that may enter interior of building by plate.Therefore, protect the interior people of building to avoid the injury that causes owing to attack better to building.
Believe that also described plate helps the structural integrity of wall self, when particularly being fastened to wall by machanical fastener at the plate periphery.
May be in order effectively to absorb or to consume from the potential high-energy kinetic energy of blast or other shock event, preferably, plate thickness arrives in the scope of about 250 mils about 100.Even more preferably, plate thickness will be about 180 mils.Yet, also can use the plate thicker than 250 mils, be desirably in cost/performance analysis, the shrapnel containment that is provided by thicker plate or the possible increment increase of shock-resistant ripple may surpass the increase of cost (material cost).
The elastomeric material that uses in the shrapnel containment plate preferably has the special combination of physics or other material behavior under its solid state.Particularly importantly elongation at break and hot strength.Elastic body will preferably have the elongation at break of scope at about 100-800%, more preferably have the higher-end place of this scope, for example at the elongation at break of 400-800%.The preferred minimum of elastomeric hot strength is 2000psi.
In addition, no matter plate is to form in independent formation or the appropriate location on the wall of wanting protected building or other structure, thinks that all elastomeric adhesiveness is important.Preferably, elastic body present minimum (or when concrete lost efficacy) for 300psi to concrete adhesion, and minimum is the adhesion to steel of 1200psi.
As previously mentioned, polyureas, polysiloxanes, polyurethane and polyurea/polyurethane mixture can produce desirable physics and material property.At present, in one embodiment, what elastic body used is a kind of aromatic polyurea material of spraying of 100% solid content, and this material can dimeric (the accurate polymer of isocyanates; Amine blends with pigment) but blasting materials obtain, but described blasting materials is designed primarily to flexible shock-resistant waterproof coating and wadding system.
Described wadding system tests in the prepared plate with fabric enhancement Layer.The fabric enhancement Layer provides framework, and wherein in forming the plate shape, uncured elastic body will adhere to described framework.Fabric strengthens also preferably having the structural integrity when helping plate at shock-resistant ripple with at the admittance fragment, especially helps the restriction elongation that elastic body experienced when absorbing the energy of shock wave or other impact.
So far, the fabric that uses in plate in production test is made by aromatic polyamides or polyester yarn or fiber, the size of its middle open type grid (open grid) (opening between warpage and the filling yarn) is about 0.25 inch * 0.25 inch or 0.5 inch * 0.25 inch, yet less or bigger grill openings size is all thought to be suitable for using.Be about 1200psi * 1200psi in the hot strength of testing with the employed fabric of plate at present.It is believed that by Technora﹠amp; The aramid yarn of Twaron brand or be particularly suitable in this uses, using by the fabric that the fiber that Teijin Fibers produces is made.
Shrapnel containment system of the present invention and method also can be the form of layer of elastomer material, and described layer of elastomer material applies and directly adheres on the wall or other structure that will be reinforced.In this case, preferably remove the discrete material and the impurity of described wall, simultaneously to be similar in the mode that described plate is sprayed on the plate substrate, by the spray coating elastic body.As mentioned above, preferably elastic body is selected, with have minimum be 300psi to concrete bond strength or adhesion, and concrete will have the fully many little surface irregularities of quantity usually, thus the zone that elastic body will find mechanical connection to increase adherence.
When described system will have fabric or fiber reinforcing element, also preferred part coating elastomer was located reinforcing element then, then sprays the remainder of elastomer layer.Alternatively, reinforcing element can at first be placed against wall, and then the whole thickness with elastomer layer is coated on it.
Carried out test to shock-resistant ripple according to the present invention/shrapnel containment plate.Shown in the schematic plan of Fig. 6 be a physical testing layout (not being that chi is drawn in proportion).In Fig. 6, blast charging 200 is positioned at the central authorities of the concrete block masonry target wall 202 of four (4) individual same configuration, these target walls be distributed in from the explosive radius be 30 ' circumference on.Masonry target wall 202 has two and strengthens leg 204, strengthens leg with square matrix-shaped " U " shape of target wall shape for these two, makes that the structure that has is to a certain degree strengthened in the face of the target wall 202 of blast charging is the same in building usually with it.
Plate A, B and C (thickness is not drawn in proportion with respect to the wall thickness degree) are installed in the inside of three walls, and the 4th wall do not have installing plate or wadding.Described plate comprises the stainless steel tank 120 around its periphery, and uses the concrete anchor securing member to be fixed to the inside of wall 202.
This three of plate A, B and C is according to the preparation of 180 mil nominal thicknesses of polyurea materials, is provided with the fabric enhancement Layer in the wherein said polyurea materials.More CONSTRUCTED SPECIFICATIONs of described plate are as follows:
Table I
Plate Elastic body Fabric is strengthened
A AR425,180 mils Technora T200 fabric, 0.5 * 0.25 " grill openings
B AR425,180 mils Technora T200 fabric, 0.5 * 0.25 " grill openings
C AR425,180 mils Twaron T1000 fabric, 0.25 * 0.25 " grill openings
Blast charging 200 comprises 42 (52.5 Ibs.) C-4 explosives, and this explosive is set to produce blast overvoltage uniformly on the face of each target wall 202.The TNT that the amount of this C-4 explosive equals 67.2 pounds.Promote charging and make it be above the ground level four feet, so that it aims at (wall 202 is high 8 feet) with the central point of each wall.The blast charging is ignited by static, produces the instantaneous overvoltage of peak value of 17.67psi and the reflected pressure of 51.22psi.
Observation after the initial blast shows that not protected wall (not being fixed to inner plate) has been subjected to catastrophic structural failure, and in fact the concrete of target wall 202 or reinforcement leg 204 is not stayed the position of wall base top all.Find because the part of the wall that shock wave causes or fragment arrive 54 feet places, wall back (that is, arriving portion within the walls) farthest.
In contrast, three target walls with the plate that is installed in the inner surface place are still upright, and concrete block is subjected to damage in various degree.Because the stress that shock wave causes at the tie point place of target wall 202 and reinforcement leg 204, these join domains seem to stand maximum the damage.The target wall self comprises breaking and rupturing in various degree.
Inspection to plate shows that possibility is owing to the concrete fragment of the opposite side of crash panel between explosion period, the cracked or abate of the signal paint coating of the small size on the inner surface of plate.Observe plate and seldom be with or without plastic strain, and do not have cracked or perforation.(to inner) do not find the concrete fragment in the plate back.
After removing described plate, find the fragment of target wall in each breadboard back.Table 2-5 listed that the test back finds with wall fragment (fragment) relevant data.It should be noted that for there being plate to be fastened to wall on it, do not provide the data that relate to " from the distance of wall ", because there is not fragment to pass described plate.
Table 1: the fragment of finding later at baseline target wall
The fragment numbering Quality (ounce) Distance (foot) from wall
1 1.0 49
2 .4 45.2
3 .3 54
4 .1 41.5
5 .3 41
6 1.7 33
7 13.0 30
8 1.5 24.4
9 1.1 19
10 3.4 19
11 .5 18.5
12 6.7 19
13 .1 19
Table 2: the fragment that breadboard T1402 is comprised
The fragment numbering Quality (ounce)
1 .9
2 1.1
3 1.1
4 .2
5 .1
Table 3: the fragment that breadboard T1403 is comprised
The fragment numbering Quality (ounce)
1 .5
2 .2
3 1.2
4 .3
5 .1
6 .1
7 2.1
8 .6
Table 4: breadboard T1404 admits the fragment that comprises
The fragment numbering Quality (ounce)
1 .8
2 1.3
3 5.2
Fig. 7 is the side perspective view according to the plate with flange of one embodiment of the invention, and described flange is at the plate periphery and be basically perpendicular to described plate.In Fig. 7, plate 700 can be made into any size that needs, can comprise main part 710 with inner surface 711 and external surface 712, main part 710 can be for such as but not limited to 2 ' * 2 ', 2 ' * 3 ', 2 ' * 4 ', 4 ' * 8 ' and bigger and/or littler size, to cover wall or its part.Plate 700 can also comprise 2,3 or 4 flanges, for example top flange 713, base flange 714, left side flange 715 and right side flange 716, wherein each flange all dangles on the single side of main part 710 from main part 710 usually, for example has on the side of inner surface 711.Yet, can consider in some embodiments, for example top flange 713 and base flange 714 can be dangled at the opposite side of main part 710, for example, top flange 713 can be dangled in the side with external surface 712 of main part 710, and base flange 714 can be dangled in the side with inner surface 711 of main part 710.
Usually, the flange 713,714,715,716 in Fig. 7 dangles on main part 710 to become 90 ° angle basically, but other angle, promptly greater than with also all under consideration less than 90 °.In the embodiment that only has 2 flanges, these flanges are usually located on the opposite edges of plate 700, for example top and bottom or the left side and the right.As shown in Figure 7, under the situation of 4 flanges, plate 700 is similar to the opening box or the container that have by the shorter side of flange 713,714,715,716 expressions.Each flange can stretch out 1 inch or more from main part 710, and the length of that side of plate 700 that usually can the stretch flange formability place.
Can adopt the whole bag of tricks, the plate 700 of Fig. 7 and flange 713,714,715,716 are formed have the single-piece of homogeneous thickness (single piece) basically.For example, according to one embodiment of the invention, in one approach, by elastomeric material being ejected in the mould (not shown) of shape that its shape is substantially similar to plate 700, described elastomeric material being solidified, and plate 700 is shifted out from mould, can form plate 700 and flange 713,714,715,716.Make in this way, can prepare plate with 2,3 and 4 flanges.Can because they can be mounted at any time, may exist some to relate to the transportation of the plate of structure by this way and the logistical problems of storage to help quickening installation process although prepare the plate of shape shown in Figure 7.Particularly, more be difficult to a plurality of such plates 700 are piled up and/or make up transporting when plate 700 being prepared into when having flange 713,714,715,716, may becoming, so it is more expensive than flat plate.
In Fig. 7, plate 700 can be placed against the wall of structure, and normally top flange 713 and base flange 714 can be fastened to respectively near on the ceiling and floor of structure wall.If plate 700 comprises one or more side flanges 714,715, and one or more walls of these side flanges abutment structure bodies and/or one or more post part, then side flanges also can be secured to one or more walls and/or one or more post part.For example, can adopt machanical fastener, plate 700 is fastened on the described structure such as concrete anchor, screw and/or nail.In one embodiment of the invention, securing member can be a concrete fastener, such as but not limited to Hilti USA make 1/4 " diameter * 13/4 " the Kwik-Con II+ securing member of length, can be furnished with packing ring and also can be unworthy of packing ring, and separate about 12 at the center " along the length of fastened flange.Alternatively, if 700 of plates have 2 or 3 flanges, then can use the Z-shaped slot type clamp structure described in Fig. 3,4 and 5, and the wall frame that will be described below by use, for example wooden and/or metab (that is bottom) and lid (that is top) plate and/or along the pillar of side flanges, non-lipped edge is tightened together, and these edges are by adjacent non-lipped plate and have the edges abut of similar structures.
Fig. 8 is the cross-sectional view according to the plate 8-8 along the line of Fig. 7 of one embodiment of the invention.In Fig. 8, the basic uniform thickness of plate 700 can be so that look like consistent between main part 710 and top flange 713 and base flange 714.Although can being shown as, plate 700 has more sharp-pointed outward flange, in this outer edge, top flange 713 and base flange 714 are dangled from main part 710, but also can have mould round and/or curved edge by use, provide circle slightly and/or curved edge.
Fig. 9 is the part top view according to the continuous restraint zone of one embodiment of the invention, and described continuous restraint zone has a part and the fixing securing member of concrete surface of the flange that makes plate.In Fig. 9, flange 910 can have continuous restraint zone 920 disposed thereon, and a plurality of securing members 930 can pass continuous restraint zone 920 and flange 910 enters in the concrete 940, and concrete 940 can be floor, ceiling, wall and/or the post of for example structure.Restraint zone 920 can be by metal (for example continuously, thickness is 1/8 ", 1/4 " etc. and width be 1 ", 2 ", 3 " etc. cold-rolled steel and/or steel plate), timber (for example, as the plate of building wall and/or pillar 2 " * 4 ", 2 " * 6 " etc. plank) and/or any other have the intensity that is similar to metal and/or timber and the material preparation of durability.Securing member 930 can be for example Kwik-Con+II screw, concrete nail, bolt and/or other concrete fastening system of screw.Securing member 930 can be used in combination with epoxy resin and/or other adhesive or fixative, to help securing member 930 is fixed in the concrete 940.
Figure 10 is the part top view according to the discontinuous restraint zone of one embodiment of the invention, and described discontinuous restraint zone has a part and the fixing securing member of concrete surface of the flange that makes plate.In Figure 10, flange 1010 can have at least one discontinuous restraint zone/part 1020 disposed thereon, and a plurality of securing members 1030 can pass each discontinuous restraint zone/part 1020 and flange 1010 enters in the concrete 1040, and concrete 1040 can be floor, ceiling, wall and/or the post of structure.Discontinuous restraint zone 1020 can be by metal (for example, thickness is 1/8 ", 1/4 " and width be 1 ", 2 ", 3 " etc. cold-rolled steel and/or steel plate), timber (for example, as the plate of building wall and/or pillar 2 " * 4 ", 2 " * 6 " etc. plank) and/or any other have the intensity that is similar to metal and/or timber and the material preparation of durability.Securing member 1030 can be used in combination with epoxy resin and/or other adhesive or fixative, to help securing member 1030 is fixed in the concrete 1040.
Figure 11 makes the part of the flange of plate be fixed on the part top view of the several independent fastening system on the concrete surface according to one embodiment of the invention.In Figure 11, each in a plurality of securing members 1130 all passes packing ring 1135 and flange 1110 enters in the concrete 1140, floor, ceiling, wall and/or post that described concrete 1140 can be a structure.Packing ring 1135 can have the intensity that is similar to metal and the material of durability is made by metal (for example, steel, zinc etc.) and/or other.Securing member 1130 can be used in combination with epoxy resin and/or other adhesive or fixative, to help securing member 1130 is fixed in the concrete 1140.
Figure 12 is the cross-sectional, top view of the wall system made according to one embodiment of the invention, and described wall system has with securing member and is fastened to stiffener on the available frame element.In Figure 12, a side of wall system part 1200, for example in a side of the wall system part 1200 of metal building thing and/or vehicle, be shown as with the exterior lateral sides 1202 of interior wall 1203 and link to each other, and the opposite sides of wall system 1200 links to each other with the inner side 1204 of exterior panel 1205.Wall system part 1200 can comprise a pair of reverse U-lag assembly, the i.e. first U-lag assembly 1210 and the second U-lag assembly 1215, the described first U-lag assembly 1210 and the second U-lag assembly 1215 can extend along the whole vertical length of the opposite side of wall system part 1200 separately.Each reverse U-lag formula assembly can comprise a pair of left flange and right flange 1211,1212 and 1216,1217 respectively, wherein each flange all dangles from main part 1213 and 1218 with 90 ° angle, and extend the vertical height of wall system part 1200 usually usually.
Although not shown, can be along the top of wall system part 1200 and the extention of bottom margin layout U-lag, to form framework.Can reequip these extentions of U-lag, make its just in time with the first and second U-lag formula assemblies, 1210,1215 fits.Between U-lag formula assembly 1210,1215, one or more stiffener 1220,1225 parts can be set, can be along fastening these stiffeners of the vertical height of right flange 1212.Usually, each stiffener 1220,1225 can be made various sizes,, and can have scope at about 100 mil to 250 mils or bigger thickness such as but not limited to 2 ' * 2 ', 2 ' * 3 ', 4 ' * 8 ' etc.In case of necessity, wall system part 1200 can also comprise and one or morely is set between the first U-lag formula assembly 1210 and the second U-lag formula assembly 1215 and the I shape slot type assembly 1230 substantially parallel with them.Each I shape slot type assembly 1230 similar I shape crossbeam, and can have two pairs of counter flanges, promptly first flange 1231 and second flange 1232 are paired, and the 3rd flange 1233 and the 4th flange 1234 are paired, and these flanges all vertically dangle from the main part 1235 of I shape slot type assembly 1230 usually.
In Figure 12, adopt for example a plurality of nuts 1240 and bolt 1242, can stiffener 1220 is fastening along the length of the right flange 1212 of first U-lag 1210, and fastening along the length of the 3rd flange 1233 of I shape slot type assembly 1230.Alternatively, adopt a plurality of rivets 1244 and packing ring 1245, can finish described fastening.Wall system part 1200 can also comprise one or more foam segments 1250,1255 between stiffener and flange 1211,1231,1232,1216.
Usually, the U-lag of Figure 12 and I shape slot type assembly 12110,1215 and 1230 respectively can be by for example preparations such as metal, composite material of the material with sufficient intensity and rigidity, with knee wall wall system part 1200, and give structural strength with support and connection inner wall section and exterior panel thereon and wall and the ground plate portion that is placed on wall system part 1200 tops.
Figure 13 is the part cross-sectional, top view according to another wall system of one embodiment of the invention, and wherein said wall system has the stiffener that is fastened on the available frame element.In Figure 13, shown the wall system part 1300 of the wall system part 1200 that is similar to Figure 12, wherein do not use machanical fastener that stiffener 1220 is connected in first U-lag 1210 and the I shape groove 1230 any.What replace is that stiffener 1220 can be connected to the flange on first U-lag 1210 and the I shape groove 1230 gluingly.Alternatively, the flange on U-lag 1210 and I shape groove 1230 can be arranged to have a slotted section, the vertical edge of stiffener 1220 can insert this slotted section.Show with reference to Figure 14 and describe this design at this.Slotted section can be positioned at or the next door of all flanges on each U-lag 1210 and the I shape groove 1230.
Figure 14 is in the part cross-sectional, top view according to the slotted section of the framework in the wall system with stiffener of one embodiment of the invention manufacturing, and described slotted section can be used for making plate and available frame element fastening.The right side that in Figure 14, has shown U-lag formula assembly 1410 with slotted section 1411, described slotted section 1411 is limited by first flange 1412 and first flange lips 1413, wherein, first flange 1412 substantially perpendicularly dangles from the main part 1415 of U-lag formula assembly 1410, and first flange lips 1413 is dangled with vertical substantially angle from the lower end of flange 1412 and be substantially parallel with main part 1415.Similarly, shown second flange 1414 originally vertically dangles from the main part 1415 of U-lag formula assembly 1410 side group identical with first flange 1412.Second flange 1414 can also have second flange lips 1414, and described second flange lips 1414 is dangled from the lower end of flange 1412 with the angle of perpendicular and be substantially parallel with main part 1415.Usually, first flange lips 1413 and second flange lips 1416 be coplane and have a basic equal lengths.
In Figure 14, can find out, stiffener 1420 can comprise along the wedge-like portion 1430 of its edge mate in slotted section 1411, and wedge-like portion 1430 can be located along the edge of stiffener 1420 indefinitely, make the external surface 1421 of stiffener 1420 align with the outward flange of first flange 1412, perhaps external surface 1422 aligns with the inward flange of first flange 1412.By for example wedge-like portion 1430 being slipped into slotted section 1411 or, wedge-like portion 1430 can being installed in the slotted section 1411 by wedge-like portion 1430 is suppressed (snap) in slotted section 1411.In the expection embodiment of wall system part 1200, can use or not use one or more fabric/fiber enhancement Layers to prepare stiffener, described fabric/fiber enhancement Layer is used to make wall system part 1200 in stiffener 1220.
Figure 15 is that described concrete floor portion within it has stiffener according to the part cross-sectional side view of the concrete floor of one embodiment of the invention manufacturing.In Figure 15, concrete slab 1500 can comprise top concrete part 1510 and bottom concrete part 1520, and can accompany stiffener 1530 between them.Stiffener 1530 can comprise a plurality of plates, and these plates have one or more elastomer layers, all has in these elastomer layers or all neither one or a plurality of fabric/fiber enhancement Layer.In one embodiment of the invention, concrete slab 1500 can prepare by the following method: concrete perfusion is to form bottom concrete part 1520, before concrete curing and/or afterwards, with one or more stiffeners 1530 be placed on bottom concrete part 1520 above, and with concrete spouting to the stiffener 1530 to form top concrete part 1510.Usually, described one or more stiffeners 1530 are previously prepared cured plate, and such as described here, have and do not have one or more fabric/fiber layers.Yet, no matter be to have one or more fabric/fiber layers and/or do not have one or more fabric/fiber layers, stiffener 1530 can be sprayed on the bottom concrete part 1520, then, top concrete part 1510 can be poured on the stiffener 1530.
In Figure 15, although not shown, concrete slab 1500 can also comprise I ellbeam, reinforcing bar, steel wire and/or other reinforcement and/or structural support elements.For example, one or two in top concrete part 1510 and the bottom concrete part 1520 can comprise steel mesh reinforcement and/or the reinforcing cage that has tied together, to improve the intensity and the rigidity of concrete slab 1500.The example of the Figure 16 and the 17 pairs of possible reinforcements and/or structural support elements is described.
Figure 16 is that described concrete wall have reinforcing bar and stiffener in inside according to the part cross-sectional, top view of the concrete wall of one embodiment of the invention structure.In Figure 16, concrete wall 1600 can comprise first concrete side 1610, second concrete side 1620 and be clipped in reinforcement flaggy 1630 between described first concrete side 1610 and second concrete side 1620.Enhancement Layer 1630 can comprise a plurality of plates, and these plates have one or more elastomer layers, all has in these elastomer layers or all neither one or a plurality of fabric/fiber enhancement Layer.Although concrete wall 1600 are similar to the concrete slab 1500 among Figure 15 in appearance, construction process can be different.For example, be generally 4 inches to thick more than 12 inches (height) and different with concrete wherein along the concrete slab of horizontal plane orientation, in concrete wall, concrete is generally 4 inches to thick more than 12 inches (wide) and along the vertical plane orientation, and this vertical plane is four feet tall to extending more than 10 feet and along the whole side/part of structure.As a result, concrete wall must be poured into usually by in the high and big die plate (form) that strengthens that metal is made and combine with part reinforcing bar and/or other metal reinforcing element.Usually, the concrete wall in dwelling house and/or the building can be about 4 feet high to 12 feet.Certainly, according to the needs that special building is used, these walls can be shorter and/or higher.Concrete in addition, reinforcing bar and/or gauze wire cloth and/or cage can also be placed within described these templates, so that can wrap up reinforcing bar and/or steel wire in it is perfused in template the time.
For example, according to one embodiment of the invention, the construction method of concrete wall 1600 can comprise assembling one or more reinforcing bars and/or steel screen layer and described one or more reinforcing bars and/or steel screen layer are put into template.One or more stiffeners 1630 approximately can be placed on the centre of described template and be placed between one or more reinforcing bars 1640 and/or the steel screen layer.In at least one embodiment, can use Z-shaped groove and/or I shape groove connector 1650 and securing member, bolt, screw, U sprig, band etc., connect one or more at least stiffeners 1630.In addition, can be passed in hole on one or more stiffeners 1630, one or more reinforcing bars and/or steel screen layer are tied together by making reinforcing bar and/or steel wire.In the method, concrete poured into described template and be poured in plate and reinforcing bar and/or gauze wire cloth around, and make its curing.In case concrete curing can be removed template, to manifest the concrete wall 1600 that are embedded with enhancement Layer 1630.
Figure 17 is that described concrete wall have reinforcing bar and the stiffener on the concrete face of wall according to the part cross-sectional, top view of the concrete wall of one embodiment of the invention structure.In Figure 17, concrete wall 1700 can comprise concrete part 1710 and at least one the stiffener part on the one or both sides of concrete wall 1700.By one or more stiffeners 1720 being placed against the one or both sides of template and reinforcing bar and/or gauze wire cloth and/or cage being placed on the centre of described template basically, can make up concrete wall 1700.Concrete can be poured in the template, and its is in case solidify, and just template can be removed, so that the concrete wall 1700 that have a stiffener 1720 in a side appear.As among Figure 16, the adjacent stiffener that is used for the concrete wall 1700 of Figure 17 can be as above-mentioned secured together describing for Figure 16.
Figure 18 is the cross-sectional, top view of plate system that is used to protect a monoblock of concrete column according to one embodiment of the invention.In Figure 18, post plate cover 1800 can be formed and be essentially for example square of rectangle, or other profile (for example, ellipse, annular etc.) is complementary with the external dimensions with post arbitrarily.The shape of tubing string is not how, and post plate cover 1800 can match with the shape with post around suitable shape mould preformed.As shown in figure 18, this can be such square shape basically: the outward flange 1802,1804 of post plate cover 1800 does not connect, so that the opening 1810 that extends along the length of outward flange 1802,1804 to be provided.
In Figure 18, opening 1810 can make edge 1802,1804 spread aparts, and post plate cover 1800 can be around the post placed around.Alternatively, can afterwards with its outer bend, form post plate cover 1800 by the stiffener of heated flat around post.Usually, when post plate cover 1800 is settled around post, outward flange 1802,1804 will be closer to each other as far as possible, so that opening 1810 is closed fully or make it as far as possible little.Alternatively, outward flange 1802,1804 in fact can be overlapping.Whether tube edges 1802,1804 is not overlapping, using or do not using under the situation of epoxy resin, can use as machanical fastener described herein, make post plate cover 1800 along the edge 1802,1804 formed seams, the turning around post is fastened on the post at least.In case of necessity, then can also post plate cover 1800 is fastening around each edge of post, and be fastened on each face/surface of post.Adhesive can also be used with machanical fastener, so that post plate cover 1800 is attached on the post.
In another embodiment of the invention, the post plate cover 1800 of Figure 18 can comprise two or more separating plates, and these plates can be manufactured and/or cutting, matches with each side with post, make separating plate on each turning of post in abutting connection with and/or overlapping.For example, post plate cover 1800 can comprise two L shaped bulk-breakings (half) such as grade; Cover the U-shaped spare of three sides and the planar member of the 4th side of covering; And/or the planar member of four separation of each side of covering post.
Figure 19 is the cross-sectional, top view according to the L shaped carriage of one embodiment of the invention, and described L shaped carriage is used to make the plate system of a monoblock or polylith to be fastened on around the concrete column.In Figure 19, L shaped carriage 1900, for example width range can use with machanical fastener, so that post plate cover 1800 is fastened on around the turning of post at 1/2 inch to 2 inches more than 4 inches, 3 inches, 4 inches etc. L shaped carriage.Usually, a plurality of L shaped carriage 1900 that each L shaped carriage all can be had two or more securing members, and anchors in the post to the top along opening 1810 and be spaced equably on edge 1802,1804 from the bottom of post plate cover 1800.In alternative embodiment, L shaped carriage 1900 can be a single-piece, and the width that described single-piece has can be substantially equal to the height of post plate cover 1800, thereby covers opening 1810 and/or each outward flange of post plate cover 1800 effectively fully.
Figure 20 is the cross-sectional, top view according to the L shaped slot type carriage of one embodiment of the invention, and described L shaped slot type carriage is used to make the plate system of a monoblock or polylith to be fastened on around the concrete column.In Figure 20, similar with L shaped carriage 1900, can be with L shaped slot type carriage 2000, for example width range is 1/2 inch to 2 inches more than 4 inches, 3 inches, 4 inches etc. a L shaped slot type carriage, use with machanical fastener, so that post plate cover 1800 is fastened on the post.Usually, from the bottom of post plate cover 1800 to the top, the a plurality of L shaped slot type carriage 2000 that each L shaped slot type carriage all can be had two or more securing members is spaced equably along opening 1810, and edge 1802,1804 can be inserted in the groove 2005,2010 of L shaped slot type carriage, and around the turning of post and in the post, described securing member can pass L shaped slot type carriage 2000 and post plate cover 1800 with the securing member anchor.Usually, to the top, a plurality of L shaped slot type carriage 2000 that each L shaped slot type carriage all can be had two or more securing members is spaced equably along opening 1810 and on edge 1802,1804, and anchors in the post from the bottom of post plate cover 1800.In alternative embodiment, L shaped slot type carriage 2000 can be a single-piece, and the width that described single-piece has can be substantially equal to the height of post plate cover 1800, thereby covers opening 1810 and/or each outward flange of post plate cover 1800 effectively fully.
Figure 21 is the part cross-sectional, top view according to the L shaped carriage of Figure 18 of one embodiment of the invention, and described L shaped carriage makes the turning of the protection plate system that uses of concrete column and concrete column fastening.In Figure 21, use L shaped carriage 1900 and two to pass L shaped carriage 1900, post plate cover 1800 and enter securing member 2110 in the concrete column 2000, post plate cover 1800 intactly is installed in around the concrete column 2000.Although not shown, also can use epoxy resin to adhere to post plate cover 1800 on the concrete column 2000 and with securing member 2110 attached in the concrete column 2000.
Figure 22 is the cross-sectional, top view that is used to protect two formula plate systems of concrete column according to one embodiment of the invention.Two formula post plate covers 2200 that show in Figure 22 comprise first half block 2210 and second half block 2220.Adopt above-mentioned similar method and the fastener material that is used for post plate cover 1800, two formula post plate covers 2200 are installed, to cover two openings that two formula post plate covers 2200 exist.
Figure 23 is used to protect the part of the plate system of concrete column to launch lateral view according to one embodiment of the invention, and this plate system has shown the enhancement Layer that similar rhombus is arranged.As seen, post plate cover 2300 comprises the fabric/fiber layer of settling with similar argyle design 2310 in Figure 23.Alternatively, fabric/fiber layer 2310 can also be arranged as pattern intersection and/or overlapping.
Figure 24 is the part cross-sectional, top view according to the hollow core flush door of one embodiment of the invention, and this hollow core flush door has anti-crushing and the plate of projectile that is placed in the door.In Figure 24, hollow core flush door/wall part 2400 can comprise first side 2410, second side surface opposite 2420, first end 2430 and the second relative end 2440.The structure stand 2450 of one monoblock or polylith can extend to the top from the bottom of hollow core flush door/wall part 2400 basically along the inner surface of first end 2430 and the inner surface of second end 2440.For example, structure stand 2450 can be by timber, metal, Masonite and/or composite material manufacturing.Although not shown, one or more similar structure stands can stride across the top and the bottom of hollow core flush door/wall part 2400 and extend, thereby complete structural inner frame is provided.As shown in figure 24, according to one or more embodiments described herein, stiffener 2460 can be arranged between the inside and structure stand 2450 of hollow core flush door/wall part 2400.Usually, stiffener 2460 can extend the whole width and the height of hollow core flush door/wall part 2400 basically, and uses in the multiple fastening method described herein any fastening.Any interval 2470,2475 between stiffener 2460 and first side 2410 and second side 2420 can be empty, and/or can be filled with foam, isolator and/or other material so that sound insulation/heat insulation, density and/or reinforcement to be provided in addition.Stiffener 2460 can also extend, to comprise one or more sides or the terminal flange that extends to door.For example, flange can extend to the hinge side part of door 2400, and will allow stiffener 2460 further to be fixed to the hinge (not shown) of door 2400.
The material that employing is applicable to aircraft construction is aluminium, carbon fibre composite etc. for example, the basic structure of the hollow core flush door among Figure 24/wall part 2400 can be used to make spacecraft and sit hatch door and bulkhead.Stiffener can also comprise one or more fabric/fiber layers and have different thickness.Following Figure 27 and 28 has described the example of the possible alternative embodiment of stiffener.
Adopt the Modular building material, the sheet material of for example two inches * four inches (2 * 4) or bigger (2 * 6,2 * 8 etc.) can also manufacture prefabricated wall part 2400 with hollow core flush door/wall part 2400 of Figure 24.In this embodiment of the present invention, wall part 2400, first terminal 2430 and second end 2440 can be for example 2 * 4 plate, and the width of stiffener 2460 can be just enough wide being engaged between first edge 2430 and second edge 2440, and paired structure stand 2450 can be attached to other edge of an edge, second edge 2440 and the stiffener 2460 of first edge 2430, stiffener 2460.Prefabricated wall part 2400 can also have one or more intermediate supports 2480, and these supports 2480 are placed with almost equal distance between first edge 2430 and second edge 2440.For example, in wall 2400, be that each intermediate support 2480 can be 2 * 2,2 * 3 and/or 2 * 4 plate under 2 * 4 the situation at first and second ends 2430,2440.Be under 2 * 4 the situation at intermediate support 2480, intermediate support 2480 can have a slit, cutting downwards of this slit and the middle part by 4-inch side basically, and, make stiffener 2460 can pass this slit basically along 2 * 4 whole length.If adopt a pair of 2 * 2,2 * 3 and/or 2 * 4 sheet material, then stiffener 2460 can be sandwiched in this between the sheet material and be attached to this to sheet material.In the present embodiment, first side 2410 and second side 2420 can be any Modular building materials, include but not limited to, for example dry wall, veneer, shaving board, foamed core material insulation materials etc.
Figure 25 is the part cross sectional front elevation according to the two-tube channel system of one embodiment of the invention, and this two-tube channel system has anti-crushing and the plate of projectile of the outside of the interior pipe that is arranged on described two pipes.In Figure 25, two-tube channel system 2500 can comprise the outer tunnel 2510 with inner surface 2512 and external surface 2514, and described inner surface 2512 limits outer tunnel open space 2520; And less internal channel 2530 with inner surface 2532 and external surface 2534, described inner surface 2532 limits internal channel open space 2536, described external surface 2534 is set within the open space 2520, so that internal channel 2530 not exclusively is full of open space 2520.For example, as the embodiment finding at Figure 25, internal channel 2530 and outer tunnel 2510 can have flat basically and coplanar bottom and conglobate basically wall separately, and the part of open space 2520 is not still filled by internal channel 2530.Other embodiment has considered that passage can have different shape, and these shapes include but not limited to, for example has the better rectangular shape, triangular shaped etc. on vertical side wall and arch roof.In addition, in other other embodiment, the inner surface 2512 of outer tunnel 2510 can have the embodiment of settling plate on it.
In Figure 25, can adopt any design disclosed herein to use the prefabricated multiple protective plate 2540 of elastic body, these multiple protective plates have one or more fabric/fiber layers or do not have the fabric/fiber layer.Each guard shield 2540 can be prefabricated into the profile with shape approximately identical with the external surface 2534 of internal channel 2530; and can adopt machanical fastener and/or epoxy resin that it is attached to the external surface 2534 of passage 2530, with the external surface 2534 that seals described passage 2530.Alternatively, elastic body and/or fibre/fibre layer can be applied directly on the external surface 2534 of internal channel 2530.Yet usually, for directly coating can be successful, the external surface 2534 of internal channel 2530 should clean and be dry.
Figure 26 is the lateral view according to the door-plate of dismountable anti-crushing of one embodiment of the invention and projectile, and this door-plate is positioned on the inner surface of door of vehicle.The door-plate 2600 of show in Figure 26 anti-crushing and projectile is located on 2610 the slot type fixed cell 2614 in, and slot type fixed cell 2614 is on the inner surface 2616 of door 2610.In embodiment shown in Figure 26, anti-crushing door-plate 2600 with projectile is dismountable, yet consideration can forever be fastened to anti-crushing door-plate 2600 with projectile the inner surface 2616 of door 2610 in some embodiments, and the inner surface that spreads all over vehicle.
Usually, slot type fixed cell 2614 can comprise the upright groove 2621 in a left side, right upright groove 2622 and kerve 2623, described kerve 2623 connects upright groove 2621 in a left side and right upright groove 2622 bottom separately, and these three kinds of grooves can for good and all be fastened to the inner surface 2616 of door 2610.Slot type fixed cell 2614 can also comprise top slot 2624, and described top slot 2624 can be at arbitrary terminal upright groove 2621 in a left side and right upright groove 2622 top separately of connecting.Usually, the preceding thus described for example Fig. 4 of slot type fixed cell 2614,13 and 14 described U-lag shape material preparations.Alternatively, top slot 2624 can for good and all be attached to the door-plate 2600 of anti-crushing and projectile, and in it can be configured to removably connect upright groove 2621 in a left side and the right upright groove 2622 each.For example, top slot 2623, the upright groove 2621 in a left side and right upright groove 2622 can have the latch and/or the locking mechanism of common running, to allow the detachable installation of door-plate 2600 in slot type fixed cell 2614 of anti-crushing and projectile.In addition, can for good and all be fixed to and pass each groove 2621,2622,2623,2624, and the door-plate 2600 that passes anti-crushing and projectile is to engage with door 2610 and to fix with manually tightening securing member.
In Figure 26,, left vertical channel 2621 and right vertical channel 2622 can be arranged to be similar to the described slot driller of above-mentioned Figure 14 according to alternative embodiment of the present invention.Therefore, with described such, anti-crushing left hand edge and right hand edge with the door-plate 2600 of projectile also can be wedge shape, in the slot driller that is engaged in left vertical channel 2621 and right vertical channel 2622 as shown in figure 14.Because the embodiment of the door-plate 2600 of anti-crushing and projectile comprises demountable plate, therefore the door-plate 2600 of anti-crushing and projectile can take out from vehicle, and it is installed on the interior wall of the building that the people with this vehicle journeys may pass through similarly.
In addition, according to another embodiment of the invention, anti-crushing door-plate 2600 with projectile can be arranged to floor panel, the common most probable of described floor panel for good and all is installed on the floor of vehicle.For example, floor panel can have the profile that cooperates the floor shape, and punches in advance, to admit from the floor upwardly extending bolt, packing ring and nut can be fixed on the described floor, so that floor panel is attached on the floor of vehicle.By in mould, making floor panel or will flat substantially plate heating and process, floor panel can be made shape of floor so that it is consistent with shape of floor with vehicle floor shape.Usually, floor panel can have scope at about 1/4 inch to 3/4 inch or bigger thickness.
Figure 27 is anti-crushing and multiple-plate lateral view of projectile according to one embodiment of the invention.In Figure 27, the stiffener 2700 that is embedded with two-layer fabrics/fiber comprises elastomeric top layer 2710, wherein said elastomeric top layer 2710 is on fabric/fiber top layer 2720, and fabric/fiber top layer 2720 is on elastic body intermediate layer 2730, described elastic body intermediate layer 2730 is on fabric/fiber bottom 2740, and fabric/fiber bottom 2740 is on elastic body bottom 2750.
Usually, the fabric/fiber layer of Figure 28 can comprise the perforate braid, such as previously described by Technora﹠amp; Twaron brand aramid yarn or the fabric of making from the fiber of Teijin.In addition, these layers can be setovered and/or be placed with alternant, so that in the minimized in size of any perforate of the perforate fabric of each fabric/fiber layer.The embodiment of stiffener 2700 can provide the withstand force to ballistic projectile.
Figure 28 is anti-crushing and multiple-plate lateral view of projectile according to another embodiment of the invention.In Figure 28, the stiffener 2800 that is embedded with treble cloths/fiber comprises first floor elastic body 2810, wherein said first floor elastic body 2810 is on first floor tapping machine woven fabric/fiber 2820, described first floor tapping machine woven fabric/fiber 2820 is on second layer elastic body 2830, second layer elastic body 2830 is on the tight woven fabric/fiber 2840 of the second layer, and the tight woven fabric/fiber 2840 of the second layer is on the 3rd layer of elastic body 2850, described the 3rd layer of elastic body 2850 is on the 3rd layer of tapping machine woven fabric/fiber 2860, and described the 3rd layer of tapping machine woven fabric/fiber 2860 is on the 4th layer of elastic body 2870.Shown in the embodiment of Figure 28, although closely woven fabric/fiber 2840 is between two-layer tapping machine woven fabric/fiber 2820,2860, but can consider in other embodiment that the order of fabric/fiber layer is opposite with Figure 28, and any other various possible combinations.Although 2800 of the stiffeners of Figure 28 have treble cloths/fiber, can consider in other embodiments to use more multi-layered fabric/fiber, and the fabric/fiber direction in each layer can be offset with other tissue layer.For example, by with the orientation of the fabric/fiber of each layer subsequently around circumference rotation such as but not limited to the fixing number of degrees, spend etc. such as 1,2,3, can realize this skew.In addition, can consider in some embodiments the fabric/fiber layer to coat elastic body then going up stratification and together each other with epoxy resin bonding.
Usually, the fabric/fiber layer comprises fabric, and is for example, previously described by Technora﹠amp; The aramid yarn of Twaron brand or the fabric of making from the fiber of Teijin.In addition, these layers can be setovered and/or be placed with alternant, so that the minimized in size of any opening between the perforate fabric of each layer fabric/fiber.The embodiment of stiffener 2800 can provide the withstand force to ballistic projectile.
Figure 29 is the cross-sectional side view according to the plate of anti-crushing of one embodiment of the invention and projectile, and the plate of described anti-crushing and projectile directly is applied on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.In Figure 29, according to an embodiment of the invention, device 2900 can comprise the structural wall 2902 of building and/or structure, scribbles release agent 2910 on the surface 2903 of structural wall 2902.Release agent 2910 can be coated on the surface 2903 by spraying, brushing, roller coat, trowelling etc., and release agent 2910 can comprise, such as but not limited to, polytetrafluoroethylene (PTFE), oil, wax, silicon and other release agent.Structural wall 2902 can also be floor and/or ceiling.Be similar to release agent 2910, elastomer layer 2920 can be applied directly on the surface 2903 and be higher than release agent 2910, and adopt mechanical fastening system 2930 to make it be fastened to structural wall 2902.Mechanical fastening system 2930 can comprise continuous metal restraint zone/flange 2932, a plurality of metal fastening elements 2934 and anchor mechanism 2936 (for example, epoxy resin, concrete anchor etc.), to help the metal fastening elements of protecting in the structural wall 2,902 2934.Other embodiment of mechanical fastening system 2930 can be included in arbitrary fastening system of describing among above-mentioned Fig. 9,10 and/or 11.
Figure 30 is the cross-sectional side view according to the plate of anti-crushing of another embodiment of the invention and projectile, and the plate of described anti-crushing and projectile directly is applied on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.In Figure 30, according to an embodiment of the invention, device 3000 can comprise structural wall 3002, and described structural wall 3002 connects the structure roof 3004 of building and/or structure on the top, connects the structure base plate 3006 of described building and/or structure in the bottom; On the surface 3007 of the surface 3005 of the surface 3003 of structural wall 3002, top board 3004 and base plate 3006, scribble release agent 3010.Described release agent 3010 can be coated on the surface 3003,3005,3007 by spraying, brushing, roller coat, trowelling etc., and release agent 3010 can comprise, such as but not limited to, polytetrafluoroethylene (PTFE), oil, wax, silicon and other release agent.
Can similarly elastomer layer 3020 be applied directly on the release agent 3010 of surface on 3003,3005,3007 and be higher than release agent 3010, and adopt mechanical fastening system 3030 that it is fastened to structure roof 3004 and structure base plate 3006.Use mechanical fastening system 3030, elastic body 3020 can also be fastened to structural wall shown in Figure 29 3002.Mechanical fastening system 3030 can comprise continuous metal restraint zone/flange 3032, metal fastening elements 3034 and anchor mechanism 3036 (for example, epoxy resin, concrete anchor etc.), to help the metal fastenings 3034 of protection in structural wall 3002.Other embodiment of mechanical fastening system 3030 can be included in arbitrary fastening system of describing among above-mentioned Fig. 9,10 and/or 11.
Figure 31 is the cross-sectional side view that has the plate of anti-crushing of the fabric/fiber enhancement Layer and projectile according to another embodiment of the invention between two layers of elastomer, and this plate directly is applied on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.In Figure 31, according to one embodiment of the invention, device 3100 can comprise the structural wall 3102 of building and/or structure, scribbles release agent 3110 on the surface 3103 of structural wall 3102.Release agent 3102 can be coated on the surface 3103 by spraying, brushing, roller coat, trowelling etc.Structural wall 3102 can also be floor and/or ceiling.Be similar to release agent 3110, first floor elastic body 3120 can be applied directly on the surface 3103 and be higher than release agent 3110.
Fabric/fiber layer 3130 can be adhered to first floor elastic body 3120, and a kind of in the use said method is coated in second layer elastic body 3140 on the fabric/fiber layer 3130, and all layers can use mechanical fastening system 3150 to be fastened to structural wall 3102.Mechanical fastening system 3150 can comprise continuous metal restraint zone/flange 3152, metal fastening elements 3154 and anchor mechanism 3156 (for example, epoxy resin, concrete anchor etc.), to help the metal fastenings 3154 of protection in structural wall 3102.Other embodiment of mechanical fastening system 3150 can be included in arbitrary fastening system of describing among above-mentioned Fig. 9,10 and/or 11.
Figure 32 is the cross-sectional side view that has the plate of anti-crushing of the fabric/fiber enhancement Layer and projectile according to another embodiment of the invention between two layers of elastomer, and this plate directly is applied on the lip-deep release agent of structure and makes itself and structure surface fastening with machanical fastener.In Figure 32, device 3200 according to one embodiment of the invention can comprise structural wall 3202, described structural wall 3202 connects the structure roof 3204 of building and/or structure and connects the structure base plate 3206 of building and/or structure in the bottom on the top, scribble release agent 3210 on the surface 3207 of the surface 3205 of the surface 3203 of structural wall 3202, top board 3204 and base plate 3206.Release agent 3210 can be coated to it on surface 3203,3205,3207 by spraying, brushing, roller coat, trowelling etc.
Can similarly elastomer layer 3220 directly be coated on the release agent 3210 on the surface 3203,3205,3207.Fabric/fiber layer 3230 can be adhered to first floor elastic body 3220, and can use a kind of in the said method that second layer elastic body 3240 is coated on the fabric/fiber layer 3230, and all layers all use mechanical fastening system 3250 to be fastened to structure roof 3204 and structure base plate 3206.Use mechanical fastening system 3250, elastic body 3220 can also be fastened to the structural wall 3202 shown in Figure 29,30 and/or 31.Mechanical fastening system 3250 can comprise continuous metal restraint zone/flange 3252 and metal fastening elements 3254 and anchor mechanism 3256 (for example, epoxy resin, concrete anchor etc.), to help the metal fastening elements 3254 of protection in structural wall 3202.Other embodiment of mechanical fastening system 3250 can be included in arbitrary fastening system of describing among above-mentioned Fig. 9,10 and/or 11.
Figure 33 is the lateral view according to the Automatic Production System of the plate of anti-crushing of one embodiment of the invention and projectile.In Figure 33, anti-crushing Automatic Production System 3300 with the plate of projectile can comprise the first spraying portion 3310, and the described first spraying portion 3310 can comprise first pair of driven roller 3311, to help fabric/fiber layer 3302 being pulled out fabric/fiber roller system 3305 and entering the first spraying portion 3310.The first spraying portion 3310 can also comprise one or more automatic first nozzles 3312, so that elastic body (for example is ejected into induction system 3313, but be not limited to belt system) on first side of fabric/fiber layer 3302 on form intermediate laminae 3315, induction system 3313 moves through the first spraying portion 3310 with the fabric/fiber layer 3302 and the first floor elastic body 3314 of combination.The first spraying portion 3310 can further include second pair of driven roller 3316 of the output that is positioned at the first spraying portion 3310.Second pair of driven roller 3316 can be pulled out intermediate laminae 3,315 the first jet deck portion 3310, and it is supplied to turning part 3320, and described turning part 3320 can effectively connect the output of the first spraying portion 3310, to receive intermediate laminae 3315.
In Figure 33, turning part 3320 can comprise at least one big roller/cylinder 3321, or the structure of performance same function, and can comprise one or more littler cylinders 3324, around cylinder, intermediate laminae 3315 can be passed through and upset effectively, makes that the fabric/fiber layer 3302 in the intermediate laminae 3315 faces up when the 3rd driven roller 3341 is drawn in the second jet deck portion 3340 with intermediate laminae 3315.Though turning part 3320 may appear to by the U-z bend and make intermediate laminae 3315 upsets, this causes plate Automatic Production System 3300 may look like the two-stage structure, can consider other structure and upset shape.
For example, one or more rollers and jet deck portion 3310 are angled and be arranged on after the jet deck portion 3310 and on the plane that is higher than jet deck portion 330, so that intermediate laminae 3315 is overturn fully.For example, single roller is placed on the terminal of jet deck portion 3310 and becomes miter angle with the transmission route of intermediate laminae 3315, so that when middle flaggy 3315 this above roller through out-of-date, second side of tissue layer reveals, and when middle flaggy 3315 was in jet deck portion 3310, described intermediate laminae 3315 can just in time an angle of 90 degrees transmits to become basically with its transmission route.At this moment, intermediate laminae 3315 may be on a certain plane of the surface of jet deck portion 3310, thereby the second jet deck portion 3310 may need higher or intermediate laminae 3315 may need to turn back to height before its 45 degree roller.This situation can realize by for example following method: make intermediate layer 3315 be arranged on an angle of 90 degrees roller that the second jet deck portion, 3310 fronts and its highly be substantially equal to 45 degree roller height below by.
Alternatively, in another embodiment of the turning part 3320 in Figure 33, can realize three roller systems by for example identical first roller at miter angle with previous embodiments.Described three roller systems can also comprise second roller that becomes an angle of 90 degrees with the end of jet deck portion 3310 and be higher than first roller, with allow intermediate laminae 3315 second roller below by, and around the second roller wraparound, make intermediate laminae 3315 move 180 degree in the opposite direction, wherein said jet deck portion 3310 is parallel to the transmission route of intermediate laminae 3315 in jet deck portion 3310.
Described three roller systems can comprise the 3rd roller that becomes reverse miter angle with first roller at last, and the 3rd roller can be arranged on the plane that is higher than first and second rollers, and it directly can be arranged to basically directly above first roller, thereby first roller and the 3rd roller can seem to form one from above " X " shape.Intermediate laminae 3315 can transmit under the 3rd roller, and is wound on the 3rd roller, so that intermediate laminae 3315 transmits with its direction identical in jet deck portion 3310 and route once more, but on the plane that raises a little.
If desired, the additional rollers of employing after the 3rd roller, make intermediate laminae 3315 from this additional rollers below by and arrive in the second jet deck portion 3340, can make intermediate laminae 3315 turn back to its equal height in jet deck portion 3310, described additional rollers can just be positioned at before the second jet deck portion 3340, and equate basically with the height of first roller, be crossed as 90 degree with the route of intermediate laminae 3315.Certainly, in the time of suitable, use in the jet deck portion 3310 and the second jet deck portion 3340 under each the surface and/or on roller, also can realize above-mentioned alternative.
Should be understood that the above-mentioned embodiment that is used for the alternative roller of turning part 3320 is illustrative, and never to should be understood to be unique, also do not will be understood that it is the possible expection embodiment of restriction.
The second jet deck portion 3340 may further include one or more automatic second nozzles 3342, on second side that elastic body is sprayed to fabric/fiber layer 3302, and (for example comprise another induction system 3343, but be not limited to belt system, a plurality of free-moving rollers etc.), to form final flaggy 3345, and move this final flaggy 3345, make it by and leave the second jet deck portion 3340.The second jet deck portion 3340 can further include the 4th pair of driven roller 3346 of the output that is positioned at the second jet deck portion 3340.The 4th pair of driven roller 3346 can turn round, so that final flaggy 3345 is pulled out the second jet deck portion 3340, and it is supplied to finishing portion 3350, described finishing portion 3350 can effectively be connected with the output of the second spraying portion 3340, to receive the final flaggy 3315 by the 5th pair of driven roller 3351.
The 5th pair of driven roller 3351 that can turn round is to draw in final flaggy 3345 and by finishing portion 3350, to cross finishing bed 3354 and enter the 6th pair of driven roller 3356.The 6th pair of driven roller 3356 that can turn round crosses finishing bed 3354 and leaves finishing portion 3350 to spur final flaggy 3345.Can between the second spraying portion 3340 and finishing portion 3350, cutter sweep 3360 be set, and if desired, final flaggy 3345 can be cut into the plate 3355 with predetermined length.Cutter sweep 3360 can comprise big blade, anvil cutter, spray water with high pressure cutting machine and/or any other fast the final flaggy 3345 of crosscut whole width and do not hinder final flaggy 3345 to move through the cutting mechanism of the second jet deck portion 3340.Alternatively, in another embodiment, cutter sweep 3360 can be arranged on finishing portion 3350 near the output of the 6th driven roller 3356.Alternatively, cutter sweep 3360 can insert in the hole of final flaggy with any direction.
In Figure 33, plate Automatic Production System 3300 can also comprise reel system 3370, and described reel system 3370 can comprise take up roll system 3371, to receive the final flaggy 3345 that leaves finishing portion 3350 by the 6th pair of driven roller 3356.Take up roll system 3371 can comprise the roller 3372 that is driven by motor 3373, and the front end width of final flaggy 3345 can be attached to roller 3372, and around the roller 3372 final flaggy 3345 of can reeling.Roller 3372 can receive the coiling volume of empty pressboard etc.The front end of final flaggy 3345 can be rolled up attached to coiling, and can supply with thin plastic sheet 3375 (for example being similar to plastic package material) by a volume plastic sheet 3380, when final flaggy 3345 is applied to plastic sheet 3375 during rolling a side of final flaggy 3345 on roller 3372, to help preventing final flaggy 3345 self adhering to when reeling.
Figure 34 is that Figure 35 then is the top view of this Automatic Production System according to the lateral view of the Automatic Production System of the plate of anti-crushing of another embodiment of the invention and projectile.In Figure 34 and 35, anti-crushing Automatic Production System 3400 with the plate of projectile can comprise the cloth supply system 3402 that fabric is supplied to plate production system 3404.
Cloth supply system 3402 can comprise fabric supply subsystem 3410, and (operative) supplied with fabric feeder/cutting machines 3420 with fabric 3411 from rolling up 3412 when described fabric was supplied with subsystem 3410 runnings.Fabric feeder/cutting machine 3420 can comprise jockey pulley 3421 and feed roller/driving 3423, the fabric 3411 that described jockey pulley 3421 receives from volume 3412, and described feed roller/driving 3423 can spur the cloth table portion 3430 that fabric 3411 strides across jockey pulley 3421 and fabric 3411 supplied with plate production systems 3404 when operation.Feed roller/driving 3423 can comprise electric drive unit and cutter sweep, described electric drive unit drives one or more rollers so that fabric 3411 is supplied to cloth table portion 3430, and described cutter sweep has the sheet material of producing the required length of plate so that fabric 3411 is cut into after described one or more rollers.Plate production system 3404 can also comprise jet deck portion 3460 and plate stripper portion 3480, described jet deck portion 3460 connects cloth table portion 3430 in the end opposite of fabric feeder/cutting machine 3420, and described plate stripper portion 3480 connects the end opposite of jet deck portions 3460.
Cloth table portion 3430 in Figure 34 and 35 can comprise cloth table 3431, and cloth table 3431 has table top 3432, and the height of described table top 3432 height with feed roller/when driving 3423 can be exported fabric 3411 is identical basically.Table top 3432 can be arranged to the surface of solids, across a series of rollers parallel to each other basically of the width of table top 3432, along one group of the length of table top 3432 track of equal intervals basically, etc.Cloth table portion 3430 may further include guide rail 3433, and guide rail 3433 can be fixed on the cloth table 3431 and extend (run) above cloth table 3431, so that fabric frame 3434 moves back and forth along guide rail 3433.Guide rail 3433 can extend along the whole length of plate production system 3404, and is fixed to the other parts of described plate production system 3404, comprises jet deck portion 3460 and plate stripper portion 3470.Fabric frame 3434 can comprise fabric clamping device 3435, described fabric clamping device 3435 can vertically be caught this cutting blade along the opposite side of the cutting blade of fabric 3411 in when work, it is lifted from table top 3432, and the cutting blade of fabric 3411 is strained across its width.Fabric frame 3434 can further include fabric filling mechanism 3436, and described fabric filling mechanism 3436 can connect the top of fabric frame 3434 and movably between the top and table top 3432 of fabric frame 3434.Fabric filling mechanism 3436 can have the size that almost equates with the sheet material of fabric 3411, and can comprise single part or a plurality of independently control section that can move up and down with respect to table top 3432.Usually, such material is gone up in the fabric filling mechanism 3436 material manufacturing and/or the coating that are used to make the polymer of plate by inadhesion.For example, such material can include but not limited to polytetrafluoroethylene (PTFE), oil, wax, silicon and other non-cohesive material.
Fabric frame 3434 can further include near first drive unit 3437 the front end 3450 that is positioned at fabric frame 3434, fabric frame 3434 can be moved to jet deck 3460 and removes from jet deck 3460 along guide rail 3433 during the work of first drive unit 3737, or alternatively, plate stripper assembly 3482 can be moved to jet deck 3460 and removes from jet deck 3460 along guide rail 3433 slave plate stripper portions 3480.Fabric frame 3434 can further include the ejecting gun 3440 of the front end 3450 that is fixed to fabric frame 3434.Usually, ejecting gun 3440 can be rigidly fixed on the fabric frame 3434, to guarantee and to obtain even and coherent distribution of polymer from ejecting gun 3440.
According to one embodiment of the invention, jet deck portion 3460 can comprise the jet deck 3461 with flat basically jet deck surface 3462, and described jet deck surface 3462 has and is suitable for producing multiple different board size and the normally length and the width of the board size of rectangle.For example, in one embodiment, jet deck surface 3462 can be rectangular shape, and wide at least 48 inches, is about 15 feet.Alternatively, jet deck surface 3462 can be bigger and/or littler, but usually, and jet deck surface 3462 is not designed to can be by fast and dismounting/replacing easily.For the ease of producing less plate, jet deck surface 3461 can have many less table tops attached to it, system can be subjected to programme-control fabric is cut into different sizes, elastic body (is included but not limited to specific pattern, for example less rectangle, square, avette, oval, circular, parallelogram etc.) only be injected on the less table top, the fabric of cutting is placed on the elastic body that sprays on the less table top exactly, and production board is selected and shifted out to selectivity from the less table top.Even now may to be cut to the smaller portions of standard rectangular size (for example 2 feet * 4 feet etc.) then so efficient not as making the big plate in school, but can confirm that these assemblies and this program are useful when production has the plate of special tectonic of non-rectangular shape.And jet deck surface 3462 can comprise pattern or design, makes the surface of production board have this pattern or design.For example, pattern or design can be multidimensional, and for aesthetic purpose and/or improve the multidimensional of the practicality of plate such as sound insulation/noise reduction ability.
In addition, described system can be configured to the elastic body selectivity is injected on the jet deck surface 3462, and () precast plate for example, window and door opening, described opening have preliminary dimension and be positioned at precalculated position on the plate to have opening to provide.Usually, from the not precut opening that is used for window or door of fabric 3411 sheet materials of fabric warrping 3412 cuttings, but be kept perfectly, handle and the stability of transportation to provide, and it can be appropriately cut and in installation process around twining at the structural wall element.For example, in plate with prefabricated rectangular window, fabric from fabric 3411 sheet materials can form four tablets that are essentially leg-of-mutton fabric 3411 through two diagonal cuttings, and described tablet can twine and be fastened on this framework around window frame.Similar technology can be used for difform window and door and other opening (for example, heating gravity vent and cooling vent, socket etc.).
Plate stripper portion 3480 can comprise plate stripper frame 3481, plate stripper assembly 3482, described plate stripper assembly 3482 removably engages with plate stripper frame 3481, and can move to jet deck portion and shift out, return to pick up and to carry production board from jet deck portion.Plate stripper assembly 3482 can comprise that the alternative plate that engages picks up element 3483, and described plate is picked up element 3483 and can be placed in size symmetrically with a kind of pattern form and equal on the zone on jet deck surface 3462.Plate stripper assembly 3482 can further include near second drive unit 3487 the rear end 3488 that is positioned at plate stripper assembly 3482, and fabric frame 3434 can be moved to jet deck 3460 and removes from jet deck 3460 along guide rail 3433 during the work of second drive unit 3487, or alternatively, plate stripper assembly 3482 can be moved to jet deck 3460 and removes from jet deck 3460 along guide rail 3433 slave plate stripper portions 3480.
In Figure 35, anti-crushing Automatic Production System 3400 with the plate of projectile may further include control panel 3505 and multicomponent metering machine 3510, described control panel 3505 can be individually with the Automatic Production System 3400 of the plate of anti-crushing and projectile in each element get in touch and control described each element, described multicomponent dosing machine 3510 can be communicated with ejecting gun assembly 3440 fluids.Dosing machine 3510 can comprise a pair of fluid storage case 3511,3513 that is used for separate storage polymeric matrix and isocyanates, and a pair ofly returns their storage bins separately at polymeric matrix and isocyanates and be used to cool off the polymeric matrix that returns and the heat interchanger 3512,3514 of isocyanates at 3511,3513 o'clock.Dosing machine 3510 can also comprise hydraulic pump system 3516,3518,3525, and each hydraulic pump system all only is connected to the fluid storage case to one in 3511,3513.Hydraulic pump system 3516,3518,3525 can also be communicated with ejecting gun 3440 fluids via a plurality of services, described a plurality of service can be supported by swing arm unit 3520, described swing arm unit 3520 can comprise two-part rotatable vertical component 3522, described two-part rotatable vertical component 3522 has fixing bottom and rotatable top, rotatable top can be attached to spray boom part 3524 regularly, so that rotatable top and spray boom part 3524 can as one man move with ejecting gun 3440.Dosing machine 3510 can also comprise the power supply to ejecting gun 3440 and hydraulic pump system 3516,3518,3525 power supplies, and they are all under control panel 3505 controls.
Figure 36 is according to the Automatic Production System of the plate of anti-crushing of one embodiment of the invention and the projectile cross-sectional view along the line 36-36 among Figure 34.In Figure 36, the leg-of-mutton spray pattern that is essentially that shows from the injector head 3441 of ejecting gun 3440 shows ejecting gun 3440 just at work.
Figure 37 is the top view in cross section that has the vehicle of pre-aligned anchor post according to one embodiment of the invention, and described pre-aligned anchor post is used for the plate of anti-crushing and projectile is anchored on vehicle.In Figure 37, the part of surface of vehicle 3700 can comprise, such as but not limited to, have the chassis (floor pan) 3710 of a plurality of pre-aligned posts 3720 that evenly separate basically.Alternatively, the part of surface of vehicle 3700 can also comprise wall, door and/or ceiling (roof pan).Can consider in other embodiments: pre-aligned post 3720 can evenly not separate, but separate around chassis 3710, to meet the shape on chassis 3710, make that the loose and/or relatively poor part that cooperates between the plate of anti-crushing of installing on it on chassis 3710 and projectile minimizes.Pre-aligned post can be solid, level and smooth and/or threaded, and the part hollow with inside and/or external screw-thread.
Alternatively, the surface of vehicle 3700 among Figure 37 in fact can be in vehicle, but can be for having the independent mold with the similar character of other mold described herein.Therefore, surface of vehicle 3700 can be designed to and can be recycled and reused for and make new preformed anti-crushing and the plate of projectile, this plate can be installed in the vehicle with like configurations.Usually, if surface of vehicle 3700 is molds, then pre-aligned post 3720 will be solid and not have screw thread, thereby can easily shift out molded plate.
Figure 38 is the lateral view according to the cross section of the vehicle chassis in Figure 37, wall, door and/or the ceiling of one embodiment of the invention.In Figure 38, releasing agent layer 3810 can be applied directly on chassis 3710 and a plurality of pre-aligned post 3720 that evenly separates basically, and elastomer layer 3820 can be applied directly on releasing agent layer 3810 and a plurality of pre-aligned post 3720 that evenly separates basically.The two can apply releasing agent layer 3810 and elastomer layer 3820 by spraying, roller coat, brushing, trowelling, cast etc., and can use sharp-pointed cutting tool, for example multi-function pocket knife, circular cutter etc., the arbitrary releasing agent layer 3810 and the elastomer layer 3820 that may cover a plurality of pre-aligned posts 3720 that evenly separate are basically removed, so that each in a plurality of pre-aligned post 3720 that evenly separates basically all exposes.Can form packing ring and/or other retention mechanism 3830, such as but not limited to, those retention mechanisms of describing in above-mentioned Fig. 9,10,11 and 12 at least are to meet the shape on chassis 3710 basically.Can be with locking mechanism 3840, such as but not limited to nut, locking nut etc., be fixed on each in a plurality of pre-aligned posts 3720 that evenly separate basically, and each locking mechanism all can be tightened to downwards on the retention mechanism 3830 separately, so that elastomer layer 3820 is firmly remained on the chassis 3710.
In other embodiment of the present invention, elastomer layer 3820 at Figure 38 can also comprise one or more tissue layer that are embedded in the elastomer layer 3820, and has elastomer layer 3820 tissue layer and that do not have tissue layer and can be applied directly on the chassis plate 3710.
Figure 39 is the open type lateral view according to the prefabricated wall system of one embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.In Figure 39, prefabricated wall system 3900 can be made various height (such as but not limited to, 6 ', 8 ', 9 ' etc.), width (such as but not limited to, 18 ", 2 ', 4 ', 6 ', 8 ' etc.) and thickness (such as but not limited to; 4 ", 6 ", 8 " etc.), and described prefabricated wall system 3900 can comprise two external vertical supporting members 3910 of the end opposite of the end opposite that is attached to top board 3920 and base plate.Although Figure 39 only shows single top board and base plate and solid wall, but in alternative embodiment, can consider to use two or more top boards and/or base plate, and can be configured to the opening of window and door, these openings can comprise outside and/or the internal vertical supporting member and the header support (header support) of a plurality of adjacency.Prefabricated wall system 3900 can also comprise a plurality of internal vertical supporting members 3940, usually, described a plurality of internal vertical supporting member 3940 is basically equally spaced between external vertical support member 3910, and the opposite end of each internal vertical support member 3940 all is attached to top board 3920 and base plate 3930.
In Figure 39, prefabricated wall system 3900 can also comprise bursting diaphragm 3950, and bursting diaphragm 3950 can be attached to front side, rear side and/or the centre of prefabricated wall system 3900.Prefabricated wall system 3900 can also comprise a plurality of vertical frame members 3960, and described a plurality of vertical frame members 3960 can be attached to each the inboard 3911 in a plurality of vertical frame members 3960.Prefabricated wall system 3900 can also comprise the under(-)chassis member 3970 of a plurality of levels, the under(-)chassis member 3970 of described a plurality of levels can be attached to the externally inboard 3911 of the base plate 3930 between the vertical support 3910 and a plurality of internal vertical supporting member 3940, and can comprise that the top frame member 3980 of a plurality of levels, the top frame member 3980 of described a plurality of levels can be attached to the inboard 3921 of the top board 3920 between each the end opposite of externally vertical support 3910 and a plurality of internal vertical supporting members 3940.Bursting diaphragm 3950 can be attached to each vertical support 3910,3940 and each horizontal vertical member 3970,3980, and can further be attached on each independent framing component 3960,3970,3980.
Figure 40 is the partial cross sectional view according to the prefabricated wall system 40--40 along the line in Figure 40 of one embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.In Figure 40, prefabricated wall system 3900 can comprise vertical fastener 4010, described vertical fastener 4010 is vertical to be inserted in each of a plurality of horizontal top framing components 3980 and enters in the top board 3920, thereby makes a plurality of horizontal top framing component 3980 attached to it.Similarly, horizontal fastener 4020 can level be inserted in each in a plurality of horizontal top framing components 3980 on the side of prefabricated wall system 3900, and pass the plate 3950 of anti-crushing and projectile, enter in another a plurality of horizontal top framing components 3980 on the opposite side of the plate 3950 of anti-crushing and projectile.Horizontal fastener 4020 can be inserted in a plurality of horizontal top framing components 3980 from the both sides of prefabricated wall system 3900.Similarly, vertical fastener 4010 can also be passed horizontal frame member 3980 and insert in the top boards 3920, or pass top board 3920 and be inserted in the horizontal frame member 3980.Two fasteners 4010,4020 can include but not limited to screw, nail, lag screw, nut/bolt/washer etc., can also be with using at the adhesive between framework and the plate/vertical support and/or using under the situation that does not have adhesive between framework and the plate/vertical support.Although do not illustrate for ease of explanation, can usage level and vertical fastener 4020,4010 at base plate 3930 places.
As shown in figure 40, usually, explosion-proof and plate 3950 projectile can be arranged on the center of prefabricated wall system 3900.Therefore, a plurality of internal vertical supporting members 3940 vertically can be divided into two basic bulk-breakings such as grade that equate, between can sandwich explosion-proof and plate 3950 projectile.Although it is not shown, but in some embodiments, can be with or without under the situation of adhesive between the plate 3950 of explosion-proof and projectile and horizontal fastener 3950, usage level fastener 4020 waits bulk-breakings and explosion-proof and plate 3950 projectile to tighten together with two.
Figure 41 is the lateral view according to the prefabricated wall system in Figure 40 of another embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.In Figure 41, explosion-proof and plate 3950 projectile is shown as and inserts in the opening, and this opening passes one the longitudinal axis in a plurality of internal vertical supporting members 3940 and extends along this longitudinal axis.Explosion-proof and plate 3950 projectile can be clamp-oned wherein around its periphery, and be adopted fastening and bonder described herein attached on the framework 3960,3970,3980.
Figure 42 is the close-up side view according to the top of the prefabricated wall system among Figure 41 of one embodiment of the invention, embeds the plate that anti-crushing and projectile are arranged in described wall system.In Figure 42, in the internal vertical supporting member 3940 has groove/opening 4210 along its longitudinal axis as can be seen, places the plate 3950 of explosion-proof and projectile by described groove/opening 4210.Explosion-proof and plate 3950 projectile can be that single-piece is to extend the length of prefabricated wall system 3900, and slot within a predetermined distance at its top and bottom, so that it can be passed in the groove/opening 4210 in each internal vertical supporting member 3940 of prefabricated wall system 3900.The fastener 4020 of level can insert in the horizontal frame 3980 in a side of prefabricated wall system 3900, passes the plate 3950 of explosion-proof and projectile and is inserted in the horizontal frame 3980 on the opposite side of plate 3950 of explosion-proof and projectile.
Although it is not shown, but horizontal fastener 4020 also can be vertical and insert on the side of each internal vertical supporting member 3940 of groove/opening 4210 and pass described each internal vertical supporting member 3940, passes the plate 3950 of explosion-proof and projectile and enter the opposite side of internal vertical supporting member 3940.Can also use adhesive between the plate 3950 of framework and explosion-proof and projectile and in groove/opening 4210, described groove/opening 4210 is between the plate 3950 of internal vertical supporting member 3904 and insertion explosion-proof and projectile wherein.
In Figure 42, explosion-proof and plate 3950 projectile can also provide as a plurality of separated portions, and is fastened on together such as but not limited in groove/opening 4210.This can realize by the following method: with the imbricate of the adjacent part of the plate 3950 of the explosion-proof and projectile of adjacent sheet, and with a plurality of horizontal fasteners 4020 internally a side of vertical support 3940 insert, be passed in the plate 3950 of the explosion-proof and projectile in groove/opening 4210 and enter in the opposite side of internal vertical supporting member 3940.This can use or not use adhesive in groove/opening 4210.
Therefore can see, the invention provides a kind of device of economy, can greatly improve building or the workman of other structure inside and/or the safety of equipment or other object of the large impact that stands blasting impact ripple or other form, otherwise the large impact of these blasting impact ripples or other form will make the wall fragment pass described structure inside.System of the present invention can be easy to pack in existing building and the structure, when particularly using the form of pilot injection plate, maybe can be contained in any new building of building or structure.The interior wall of finishing can have the outward appearance identical substantially with the interior wall that system of the present invention is not housed, thereby does not influence the aesthetic property of workplace.
Barrier shield is inner has done disclosure by the fragment that wall produces down with admittance shock wave or other impact although system and method for the present invention is mainly to be used for, but can think, system and method of the present invention, the system that particularly is the plate form provides high-caliber penetration-resistant under the impact condition of more concentrated or localization.Like this, expect that described plate or system are suitable for requiring energy absorption and to for example being had in the application of penetration-resistant by the common less projectile of rifle and other firearms and rifle emission, as armoring " plate ", comprise being used in and defeat or resist that to be designed to be the projectile of " piercing through plate armour " in essence.This specific character described herein can use term " explosion-proof " to summarize, and as employed term here, this specific character is used for " shrapnel containment ".
Figure 43 is the elevation of the shock wave/shrapnel containment plate according to an exemplary of the present invention.In Figure 43, plate 4300 shows and shows that plate is bent to form the top dash line 4310 and the bottom dash line 4320 of the apparent position of top flap and bottom flap.Plate can be prepared into any size, for example, 4 ' x 8 ', 4.5 ' x 10 ' etc.Usually, top and bottom dash line 4310,4320 can be positioned at from about 3 to 4 inches of the top of plate 4300 and bottom margin.Bending can be by carrying out like this: plate 4300 basically along top and 4310,4320 heating of bottom dash line, is become flexible up to plate 4300 in heat affected zone, then each end on the plate 4300 is folded to form described flap.For example, the end of plate 4300 can be folded on the crust, to help to form described flap.Described processing can be carried out in the step of for example using standard heating gun heating panel.In addition, can use the bar type heater to heat described plate, described bar type heater can be the same with the width of described plate long, shorter or longer.Plate 4300 can also have the flap that is formed on one or more sides.Shown in dash line 4320, described flap can also be cut or have perforation.For example, these perforation can be installed in around the object of structure plate.The part of plate 4300 can also be heated and be placed to enter in the mould or around mould and place, and forms the shape of plate thus.Yet described mould needs not to be traditional mould, but can also comprise any object that plate is placed, heated and be out of shape thereon or in it.For example, can be with suitable heater with the architectural feature bending of plate around the building at scene.
Figure 44 is the lateral view of the shock wave/shrapnel containment plate according to Figure 43 of an exemplary of the present invention.
Figure 45 is the front perspective view of shock wave/shrapnel containment plate of Figure 43 according to an embodiment of the invention, is created in the flap 4330,4340 on top and the bottom after wherein display board is bent.Have almost perpendicular to the flap of described plate although plate 4300 shows, be to be understood that described flap can be bent to any angle and with the different directions bending.And such as mentioned above, flap can be cut, and makes the independent flap can be in the different directions bending thus.Use has and does not have the machanical fastener of protected apron (fender) and/or packing ring, plate can be installed in ceiling and the floor by these flaps.In addition, identical or different securing member can be used with groove, protected apron and/or packing ring, so that plate is fastened to the wall surface.Normally, install securing member relate to optional preboring pass plate and enter wall/ceiling/base plate the hole, optional with epoxy resin be coated with described securing member and will have and/or not have protected apron/packing ring/etc. securing member tighten and pass described plate and enter in the described hole, expand or the inwall of holes for clamping up to this securing member.For example, the securing member that is used for metope can comprise Tap-con_, and this is that a kind of screw that makes anchors into the interior concrete screw designs of concrete, brick and stone.Tapcon_ concrete screw is screwed in (tapthread) prebored hole in concrete, brick or stone.
Figure 46 is the lateral view of shock wave/shrapnel containment plate of Figure 45 according to an embodiment of the invention, and it shows top and bottom flap 4330,4340.Total method of plate can comprise shown in preparation Figure 43 to 46: plate is precut to cooperate described wall, heating and to go out flaps near 90 degree to cooperate the bottom of wall/floor joint in the bottom bend of plate; The top of heating panel; Plate is placed against wall and ceiling, and bottom flap and floor is fastening; Top along the profile twisted plate of ceiling; And it is top flap and ceiling is fastening.
Figure 47 is the front perspective view of the shock wave/shrapnel containment plate according to two of one embodiment of the invention overlapping Figure 43.In Figure 47, generally speaking, can be with 2 or more a plurality of plate 4700 and 4710 overlapping near 4 to 8 inches 4720 places, and can adopt machanical fastener, have groove, adhesive, band and/or these any combination of machanical fastener, by lap it is fastened to wall, or it is not fastened to wall.
Figure 48 is the front perspective view according to the shock wave of Figure 43 of two adjacency of another embodiment of the invention/shrapnel containment plate, the figure illustrates the installation constitution of plate.In Figure 48, plate 4800 and 4810 is being engaged side, 4820 place to the side adjacency, and can use machanical fastener, groove, adhesive and/or these any combination with machanical fastener be fastened to wall with it, or it be not fastened to wall.
Figure 49 is two the overlapping shock wave/shrapnel containment plates 4900 that are similar to Figure 47 according to one embodiment of the invention, 4910 front perspective view, it has is with 4930 such as the elastic type band, and this element covers the whole overlapping sutures on the side of the plate with flap basically.In Figure 49, band can be applied in overlapping suture above, normally on a side of the inside of structure, use along the whole length of seam basically, the whole length of described seam can comprise or not comprise flap.Band can also be applied on the opposite side in the seam both sides.For example, described band can be the Best Roofing Systems in Oklahoma city, Oklahoma, Metal-Gard " E " the band system that Inc. produces.
Figure 50 is that two according to the Figure 47 with elastic webbing 5020 elements/48 of one embodiment of the invention are overlapping or in abutting connection with the front perspective view of shock wave/shrapnel containment plate, and described elastic webbing 5020 elements cover the whole overlapping sutures on plate one side that plate has flap basically fully.Described band can also be placed in any direction, such as placing like that, and can as being with 5040, be placed along flap by tape 5030.
Figure 51 is the part cross-sectional side view according to the outside concrete wall part of the building with shock wave/shrapnel containment plate 5140 of one embodiment of the invention, wherein said outside concrete wall partly have ceiling 5110 and floor 5120 slabs, and described shock wave/shrapnel containment plate 5140 is next to concrete wall 5130 and places.Go out as shown, flap 5150 and 5160 respectively with slab 5110 and 5120 adjacency.
Figure 52 is the part cross-sectional side view according to the outside concrete wall part with ceiling 5110 and floor 5120 slabs of Figure 51 of one embodiment of the invention, this figure shows and added wall framework 5150 and interior wall surface 5160, and shock wave/shrapnel containment plate 5140 and then concrete wall 5130 place.
Figure 53 is the part cross-sectional side view according to the outside concrete wall part with ceiling 5110 and floor 5120 slabs of Figure 52 of one embodiment of the invention, and this figure shows wall framework 5150 and interior wall surface 5160 be fastened to enter by shock wave/shrapnel containment plate and is next in the top portion base plate slab that concrete wall 5130 place.In Figure 53, securing member 5170 can be the Hilti_HSLB M 16/50 that diameter is about 16mm, described Hilti_HSLB M 16/50 is by Hilti Inc.of Tulsa, and Oklahoma produces and in the 155th page of 2005 Hilti_Product Technical Guide description arranged.Usually, the mounting method of these securing members can comprise: pass the prebored hole of flap 5150,5160, and this securing member is passed flap enter in the slab under the situation of epobond epoxyn having or do not have on the screw thread of securing member.In addition, by securing member, can be with about 1/4 " to 1/2 " the slab (not shown) is fastened on the top of flap.Alternatively, can be with 1/4 " to 1/2 " the threaded bar part is with bolt and sheet (plate)/packing ring/wait and use as securing member.In this case, described rod will be with epoxy resin (epoxied) to enter in the hole, and epoxy resin can solidify (up to 24 hours), plate and sheet/packing ring/wait to be mounted, and with the bared end of nut tightening in threaded bar.The kind of the size of securing member, sheet and epoxy resin can change according to threat level.
Figure 54 is the cross-sectional side view of the shock wave/shrapnel containment plate 5400 according to one embodiment of the invention, and described shock wave/shrapnel containment plate 5400 is to use the alternating layer of polymer 5410 and alumina particle 5420 to prepare.In Figure 54, alumina particle 5420 can be changed to bulky grain from granule dimensionally.The thickness of each polymeric layer can be about 5 to 10 mils, and the gross thickness of production board can be about 1 ".If suitable, the kind/size of other plate thickness and particle also is fine, and wherein has alternating layer more or less.Usually, polymeric layer can replace with the material of any other kind, to produce shock wave/shrapnel containment plate.Particle can also mix with one or more polymeric layers.Be about 7 day in room temperature hardening time, and be about 24 hours at about 140 degree.
Figure 55 is the elevation of the wall of the building that is equipped with a plurality of shock waves/shrapnel containment plate 5510,5520,5530,5540,5550 and 5560 according to an embodiment of the invention.Usually, can with plate cutting be engaged in window, door and other element in the wall around, and can use caulking joint and/or fastening system on every side at one or more windows and one or more s' edge.Plate can in abutting connection with against the framework of door and window, be placed on door and window framework down and/or secure it to the framework of door and window.Door 5570 shock wave that the becomes one/shrapnel containment plates that can also comprise as described in Figure 24.By for example using band, shock wave/shrapnel containment plate can be fixed together, if thereby when blasting, a plurality of plates play single element.
Figure 56 is the part elevation according to the wall with window in building of one embodiment of the invention, wherein said wall is equipped with a plurality of shock waves/shrapnel containment plate 5610 and polymer glass coating 5620, described polymer glass coating 5620 covers window 5630 and the framework 5840 that links to each other, and extends on the wall.In Figure 56, can spray transparent polyureas (aliphatic) layer 5620 (for example, from VisuronTechnologies, Inc.of Bay City, Polypro 6062 clearcoat of Michigan) to cover window (for example, glass, framework and wall surface on every side).This spraying can be accomplished like this: adopt the airless spray unit unit to operate minimum thickness with about 30 mils that produce two coatings at about 5000psi and 120 degree Fahrenheit temperature.Allow each coating drying, apply next coating afterwards.Thickness depends on the protection needs of threat level.Before using, for example use denatured alcohol with cleaning surfaces and dry.Plate can be installed on the coating around the window, and can use securing member to pass described plate and the clear glass coating enters within the walls.Can be with the one or both sides of transparent glass applications to window, and normally, if only handle a side, then the inboard is processed side.
Figure 57-the 59th, according to the part cross-sectional side view of the outside concrete wall part 1502 with ceiling and floor slab of one embodiment of the invention, this figure shows the method that adopts adjustable jack machinism 5750 that shock wave/shrapnel containment plates are installed.
In Figure 57, precut shock wave/shrapnel containment plate 5710 usefulness are passed flap 5720 fixing securing members 5730 be fixed to the floor slab.Then, in Figure 58, flap 5740 is placed in abutting connection with the ceiling slab with adjustable jack machinism 5750.Then, shown in Figure 59, flap 5740 is fixed to the ceiling slab with securing member 5760.
Figure 60 is the part cross-sectional side view according to the outside concrete wall part 6010 with ceiling 6020 and floor 6030 slabs of one embodiment of the invention, this figure show with shock wave/shrapnel containment plate 6040 be installed in framework 6060 and interior wall 6050 above, and use securing member 6070 to be fastened to described ceiling 6020 and floor 6030 slabs.Plate 6040 can be coated with lacquer, stick wallpaper etc., and can skim coat (skim-coated) before japanning etc. so that more level and smooth finishing to be provided.In exemplary embodiment, in installation process, floor covering 6080 is folded back, so that the passage of slab to be provided.
Figure 61 is the part cross-sectional side view with outside concrete wall part 6010 of ceiling 6020 and floor 6030 slabs, this figure show with shock wave/shrapnel containment plate 6040 be installed in interior wall 6050 above, and use securing member 6070 to be fastened to described ceiling 6020 and floor 6030 slabs.In the present embodiment, shown the floor covering 6080 that is in final position, wherein plate 6040 extends to furred ceiling 6170 tops.
Figure 62 is the lateral view of the hinged forming jig (hingedforming jig) according to an exemplary of the present invention, and described hinged forming jig is used for forming flap or profile on shock wave/shrapnel containment plate.On initial position, plate 6210 is placed between the top board 6220 and base plate 6230 of hinged forming jig 6200.
Figure 63 is that wherein plate 6210 mediates according to the lateral view of the hinged forming jig 6200 of one embodiment of the invention.More specifically, on the zone of the plate 6210 of the hinge area between top board 6220 and the base plate 6230, apply heat.When plate 6210 alternating temperatures heat and when becoming flexible, with base plate 6230 around hinge 6240 with direction A rotation, make that plate 6210 beginnings are crooked.
Figure 64 is that wherein plate 6210 is in exemplary final position according to the lateral view of the hinged forming jig 6200 of one embodiment of the invention.In this exemplary, the plate 6,210 90 ° of bendings that have been done, wherein top board 6220 is perpendicular to base plate 6230.Keep this position with forming hinged forming jig 6200, cooled off and solidify up to plate 6210.Although not shown, hinged forming jig can also comprise template (form), plate this above template bending so that the sweep of plate has the shape such as specific radius, fold etc.
Figure 65 is the lateral view according to the hinged forming jig 6500 of another embodiment of the invention, and described hinged forming jig 6500 is used for forming flap on the shock wave/shrapnel containment plate 6210 of the heating element 6510 of the plate 6210 formation one that have and be in initial position.Heating element can comprise open/close switch 6520, and can insert power supply to plug.Heating element can also comprise regulates the temperature and the thermostat of the flexible of adjustable plate 6210 thus.Figure 66 is that wherein exemplary panels 6210 is in exemplary final position according to the lateral view of the hinged forming jig of one embodiment of the invention.
Figure 67 is the elevation according to the hinged forming jig of one embodiment of the invention, and described hinged forming jig is used for forming flap being on the shock wave of initial position/shrapnel containment plate 6210.Described forming jig can also comprise manually operated leverage and/or mechanical actuation device, to help that plate 6210 is bent to required structure.
The polymer that can be used to prepare described plate can comprise from the Envirolastic425 of Sherwin Williams with from the Versaflex 45DC of Dow Chemical Company, and they can mix with isocyanates before the spray coating plate being about to.For example, isocyanates can comprise the TONE polycaprolactone from Dow.
Shock wave/shrapnel containment plate can partly be united use with the prefabricated wall that is used to build prefabricated building.Shock wave/shrapnel containment plate is embedded in the described wall part.Described wall partly comprises external aluminium wall surface, and externally injection moulding has fluid insulation between the aluminium wall surface, and described plate is embedded in the described cellular insulation.Around the edge of each wall part can be sealing mat, to form the sealing with bonding part when they are assembled.Usually, plate can be placed near the inside on one or another aluminium surface.
Figure 68-73 shows another exemplary of shock wave/shrapnel containment plate.With a side of plate or many side engagement be enhancement Layer, such as the fabric of describing herein, described enhancement Layer produces a certain amount of slack such as bag, to help the elastic expansion of plate.Plate can have or not have to embed wherein polyureas or another one or a plurality of enhancement Layer or the fabric of other elastomeric material.
Figure 68 is depicted as plate 6800.Plate 6800 comprises polyureas or other elastomeric material part 6810 and enhancement Layer 6820.Enhancement Layer 6820 can be fixed to the plate 6810 on one or more in top, bottom or a plurality of side, and adopt any adhering mode, comprise the part of enhancement Layer 6820 is gluing, fastening or embed medium one or more of polyureas or other elastomeric material part 6810.Discuss as following Figure 73, can also enhancement Layer 6820 be engaged with plate 6810 by using securing member, adhesive, groove etc.
Figure 69-72 shows the alternative cross-sectional view of the plate 6800 of Figure 68 along the A-A intercepting.In Figure 69, polyureas or other elastomeric material part 6810 have embedding enhancement Layer 6820 wherein.Enhancement Layer 6820 also comprises the dilation 6910 that allows polyureas or 6810 elongations of other elastomeric material part.
Figure 70 shows another configuration that enhancement Layer 6820 combines with polyureas or other elastomeric material part 6810.One or more ends of enhancement Layer 6820 are embedded within described polyureas or other elastomeric material part 6810 in the mode that increases the confining force between enhancement Layer 6820 and polyureas or other elastomeric material part 6810.
Figure 71 shows the enhancement Layer 6820 around the part of polyureas or other elastomeric material part 6810.Except that reeling, can also use adhesive, one or more machanical fasteners etc. that enhancement Layer 6820 is fixed to polyureas or other elastomeric material part 6810.
In Figure 72,, enhancement Layer 6820 and polyureas or other elastomeric material part 6810 are bonded together by using carriage 7210.Carriage 7210 is support reinforcing layer 6820 securely, and can be bonded together with polyureas or other elastomeric material part 6810 by using securing member, adhesive etc.
Figure 73 shows the lateral view of the mounted shock wave/shrapnel containment plate with enhancement Layer 6820 and polyureas or other elastomeric material part 6810, and described shock wave/shrapnel containment plate is installed on the concrete wall 7300 with ceiling 7310 and floor 7320 slabs.According to one embodiment of the invention, securing member 7330 passes shock wave/shrapnel containment plate 6810 and enhancement Layer 6820 is fastened in the top board and base plate that is next to concrete wall 7300 placements.Securing member 7330 can be the Hilti_HSLB M 16/50 that diameter is about 16 mm, described Hilti_HSLB M 16/50 is by Hilti Inc.of Tulsa, and Oklahoma produces and in the 155th page of 2005 Hilti_Product Technical Guide description arranged.Usually, the mounting method of these securing members can comprise: preboring passes the hole of flap 7340 and enhancement Layer 6820 parts that are adjacent, and have or do not having on the screw thread of securing member under the situation of epobond epoxyn, this securing member is being passed flap insert in the slab.In addition, by securing member, can be with about 1/4 " to 1/2 " the slab (not shown) is fastened on the top of flap and adjacent enhancement Layer 6820.Before fastening, enhancement Layer 6820 can also be being twined above-mentioned plate and twine.Can also be with 1/4 " to 1/2 " the threaded bar part is with bolt and sheet/packing ring/wait and use as securing member.In this case, described rod will enter in the hole that gets out in slab with epoxy resin (epoxied), and epoxy resin can solidify (up to 24 hours), plate and sheet/packing ring/wait to be mounted, and with the bared end of nut tightening in threaded bar.The kind of the size of securing member, sheet and epoxy resin can change according to threat level.
Although too simplify for ease of explanation, in blast process, active force B is applied on the concrete wall 7300.Concrete wall 7300 are towards shock wave/shrapnel containment plate bending.When concrete wall are crooked, polyureas or other elastomeric material part 6810 are out of shape at direction B, and filled the space between polyureas or other elastomeric material part 6810 and enhancement Layer 6820, strained slack thus and power is passed to enhancement Layer 6820.
Make the length of dilation and enhancement Layer thus be in the structure that allows polyureas or other elastomeric material elongation scheduled volume.For example, the 400-800% of polyureas or other elastomeric material elongation if desired then can be determined the length of polyureas or other elastomeric material part with this elongation rate, and enhancement Layer is installed so that enhancement Layer is substantially equal to the length of this elongation.Thereby when polyureas or other elastomeric material reached the length of described elongation, enhancement Layer can provide extra support.
Plate 6800, especially plate have a side of reinforcement fabric, can also be coated with the skim coat of material, to allow that the finish product is applied to described plate such as paint.
Another exemplary of the present invention relate to be installed on the structure or the system adjacent with structure to admit from blast and/or by the projectile of projectile generator emission, and the method that is used to prepare these systems, wherein said structure is included in this structure interior window, floor or ceiling or side, bottom or the top of vehicle.
Described system comprises the generation preformed board, described preformed board can be formed different shape, cut into size in case of necessity, and is installed to or adjacent to the surface at side, bottom or the top of wall, floor, ceiling and/or the door or the vehicle of structure.By spray polyurea or other elastomeric material, can partly prepare plate, described polyureas or other elastomeric material are selected especially with when preparing the improved material of character of elongation and hot strength, help the performance of production technology and production board.Can also prepare plate by the following method: with polyurea materials or other elastomeric material brushing, roller coat and/or trowelling to desired thickness to form production board.Alternatively, polyurea materials or other elastomeric material directly can be applied (that is spraying,, brushing, roller coat and/or trowelling) and be engaged to the inner surface of structural wall or building.In addition, one or more fabric enhancement Layers can be attached to each other and/or adhere to, and it is adhered to and/or adhere to the first floor elastomeric material, these layers can be covered by second layer elastomeric material.In another embodiment, can also be applied in the field of individual body armor as the plate with multiply cloth described herein.
Building plate or when one or more layers material is directly engaged with wall, can adopt such as the elastic body of polysiloxanes, polyurethane and polyurea/polyurethane mixture and so on sub as polyureas.
Figure 74 is the graphic top view of a part of technology that is used to prepare shock wave/fragment/projectile containment plate according to one embodiment of the invention.In Figure 74, as can be seen first tissue layer (layer 1) have at above-below direction stroke (run) and at the weavy grain of left-to-right direction, vertical with first floor basically placement of second tissue layer (layer 2) make that the stroke of the second layer is the direction in left-to-right, and weavy grain is upper and lower.Although the stroke of layer and the over-over mode of weavy grain just are described to be perpendicular to one another herein, but can also be used singly or in combination alternate manner, for example, in the mode of diagonal way, the diagonal biasing of any increment between 0 to 180 degree, move the mode of but upper and lower biasing and/or left-to-right biasing identical etc. with weaving direction.Usually, described layer can be positioned to and have any direction between them.
In an exemplary, first floor can be applied to for example top of epoxy resin layer of a side, then with the bottom of the second layer to place with the direction of first floor biasing, then, place against epoxy resin layer, to form the multiply cloth element, this can be counted as a layer 1﹠amp in Figure 75; 2.Alternatively, epoxy resin can be applied to the second layer below, then can be by locating the second layer as mentioned above like that and placing against first floor.Also alternative is, with layer 1﹠amp; 2 placed against each other before, they are all carried out preliminary treatment by spraying, roller coat, brushing, dip-coating etc. with epoxy resin.
In Figure 74, can apply and/or not exert pressure, be attached to and combine and reduce and/or remove bubble between the tissue layer to help layer 1 and layer 2 with epoxy resin.For example, can the working pressure machine, one or more roller and/or other device of exerting pressure exert pressure.Ideally, pressure can be applied on the whole surface of the plate that is forming equably, and any air that allows to be trapped between the tissue layer is overflowed.Each tissue layer of Tian Jiaing can adopt identical pressure to apply subsequently, and can apply final pressure and/or unique pressure to the integral body of fabric and epoxy resin layer.Can with epoxy resin spraying and roller coat, brush and/or be poured into first floor and subsequently each the layer on.Described epoxy resin can be any suitable air with good wettability and/or heat-curable epoxy resin material, for example, but be not restricted to the General Polymers 3504 High Solids Primer/Sealer epoxy resin products of producing by Sherwin-Williams Company.
In order to be easy to illustrate technology, the layer 1 and 2 among Figure 74 is shown as piece single, that size equates basically, for example, 1 ' x 1 '.Bigger plate with various sizes and structure is also interim in advance.For example, described plate can be the sheet material (for example, 2 ' x 2 ', 4 x 8 ', 2 ' x 4 ', 3.5 ' diameter etc.) and the difform conformal pattern of square, circle, ellipse, ovoid, rectangle and/or any other shape.Yet the automatic device of the plate help producing in batches disclosed herein and a plurality of embodiments of describing is adopted in expection, can realize this technology.Device described herein can be improved to and comprise as using the alternated travels/weave pattern layer of the fabric that has epoxy resin therebetween as described in herein.For example, according to embodiment of the present invention, fabric warrping (roll), fabric sheet and/or other unit that can proper orientation before handling or in the processing procedure, and by spraying, roller coat etc. epoxy resin automatically is applied between these layers.In addition, can comprise alternative materials in the plate, for example, other fabric, material and/or Web materials are such as wire lath, silk screen, composite material or these any combination.Textile-like, alternative materials also can be by volume, sheet material and/or other unit of described material with suitable direction feedwaies.
In Figure 74 and other figure relevant with the present embodiment, described fabric can comprise by aromatic polyamides and/or polyester yarn or fiber production and have the open type grid (warpage and fill opening between the yarn) of about 0.25 inch * 0.25 inch or 0.5 inch * 0.25 inch.Yet, it is believed that littler or bigger grill openings size also is suitable for using.The hot strength that is used for the fabric of plate can be at about 1200psi * 1200psi.It is believed that by Technora﹠amp; The aramid yarn of Twaron brand or be particularly useful for use in this applications by the fabric that the fiber that Teijin Fibers produces is made, for example but be not restricted to, have 0.5 " x 0.25 " grill openings Technora T200 fabric and/or have 0.25 " x 0.25 " the Twaron T1000 fabric of grill openings.
In Figure 75, shown in above-mentioned Figure 74 and the result of the technology of describing by layer 1﹠amp; 2 show, another epoxy resin layer can be coated in the top of layer 2, or as described in above-mentioned Figure 74, can suitably be orientated and be placed on the top of the second layer with seeming the 3rd layer (layer 3) with up and down stroke and left-to-right weavy grain, thereby form the pattern of the layer 1-3 shown in Figure 76.The alternating pattern of tissue layer and orientation will be implemented in the production board that does not pass the direct access of original grill openings in the tissue layer basically.In other words, plate has biasing and the vertical orientated solid basically core of tissue layer.
In Figure 76, result in the method for also describing shown in above-mentioned Figure 74 and 75 is shown by layer 1-3, another epoxy resin layer can be applied to the top of layer 3, or as described in above-mentioned Figure 74 and 75, can have the left-to-right stroke with seeming and the 4th layer of weavy grain up and down (layer 4) suitably is orientated and is placed on the 3rd layer top, thereby form the pattern of the layer 1-4 shown in Figure 77.
Figure 77-79 continues the technology of description in Figure 74-76, obtains having the more and more littler a plurality of tissue layer of opening.Describedly be appreciated that technology of the present invention can continue by top, up to the plate of the solid basically core of realizing having biasing and vertical orientated tissue layer.
In order to finish the technology of the described plate of preparation, can coated polymeric each surface of part plate recited above (for example, top, bottom and side) on, to prepare production board.Can with polymer top and lower surface be applied to scope be about 10 mils (1 mil=mil) to 100 mils or bigger thickness, and be applied to the thickness of scope in the side in about 5 mil to 30 mils.Can use conventional method that plate is repaired, to realize more homogeneous thickness and exquisite outward appearance.Can on each side, all can have in the mould of the available predetermined thickness of polymer and finish described plate.Usually, the thickness range that plate is designed to comprise the layer of fabric and polymer is about 0.50 inch to about 2.00 inches.In addition, the weight range that plate is designed to have arrives less than 10 pounds per square foots about 1 pounds per square foot, have based on following zones of different density: the particular type of threat level, for example but be not restricted to type i, II-A, II, III-A, III, IV, and at National Institute of Justice (NIJ) Standard 0101.04, Revision A, June calendar year 2001, the specific type of stipulating among the Ballistic Resistance of PersonalBody Armor.
Fabric layers in the plate is determined by required protection class; for certain embodiments of the present invention; can with; such as but not limited to; the NIJ Standard 0101.04 in June calendar year 2001; Revision A is limited, described NIJ Standard 0101.04, and the performance that Revision A device for limiting should satisfy and other require to satisfy the needs of criminal justice agency for high-quality service.
Can use adhesive, lamination, machanical fastener and/or its any combination, all using and do not using under the situation of lateral groove/protected apron and/or packing ring, realization (implementation) and location according to plate are installed to plate in door, wall, surface, ceiling and/or the floor.In addition, can be for example with similar or different securing members, nuts and bolt, rivet etc. uses with groove, protected apron and/or packing ring, so that plate is fastened to the surface.Normally, in being applied to the building situation of concrete or similar material, install securing member can comprise preboring pass plate and enter the hole on wall/ceiling/floor, randomly with epoxy resin coating securing member and will have and/or not have the securing member of protected apron/packing ring etc. to pass plate and be screwed in the described hole, expanded or clamped the inwall in described hole up to securing member.For example, the securing member that is used for the surface of concrete wall can comprise Tap-con_, and this is a kind of concrete screw of holes for clamping inwall.
Alternatively, plate can also be prepared on a side, opposite side and/or all sides of similar above-mentioned plate and have the flap that stretches out.Usually, flap can not have the main body of plate so thick, and can have a certain quantity extend into and pass the tissue layer of at least a portion of each flap from main body.The quantity and the ductility of the layer in flap can change according to the requirement of various application.For example, for the low requirement that threatens, can only need few to one deck, two-layer and/or three layers fabric, and high/extremely threaten requirement can need in the flap tissue layer with in the main body of plate as many.Therefore, can use multiple preparation method, for example comprise that preparation has the plate of the flap of single two dimensional sheets form, on the installation site of installing plate, flap bent to required structure then, or be three dimensional panel by the sheet metal forming that will have flap on the bent position at them.
Another kind of alternative fastening method can comprise the fastener of pre-determined bit, and for example, groove, anchor point, joint, post etc. are during they can insert, face, following etc. onboard, so that plate is fastened on desired location.In addition, other alternative can comprise directly plate is formed on on the protected surface, the surface in and/or the surface around etc.In this alternative, by at first the polymeric layer of outside directly being applied (adopting one or more methods described herein) to the surface and enclose first tissue layer immediately, plate can be attached to the surface, wherein use or do not use epoxy resin to depend on the hardening time of polymer and when first tissue layer is applied to described polymeric layer.
Top from layer, alternative plate according to one embodiment of the invention is such: a plurality of tissue layer of first group, be the wire mesh cloth of individual layer afterwards, a plurality of tissue layer of second group, the wire mesh cloth of the second layer, a plurality of tissue layer of the 3rd group, a plurality of tissue layer of the 3rd layer wire mesh cloth and the 4th group.As described in Figure 74-79, fabric and oven wire mesh blanket replace with the biasing pattern form, and stick together with epoxy resin, thereby produce as described in above-mentioned Figure 74-79 and as shown in plate.Oven wire mesh blanket can be located and align toward each other, therefore stroke in oven wire mesh blanket and weavy grain form all be similar to tissue layer be like that biasing and alternately.Usually, wire mesh cloth can have closely/little weavy grain, and can all have elasticity on both direction, for example, but is not restricted to the Cambridge from GKD-USA of, the wire mesh cloth 452KP of Maryland.
The alternative embodiment of plate can comprise tissue layer, metal forming and the wire mesh cloth of various quantity and layout.For example, in these embodiments some can include but not limited to: seven plywoods, described seven plywoods have two outer stack and three inner stacks that are made of single-layer metal with five layers of fabric, these three inner stacks are by two other folded separating of inner textile layer that are made of five layers of fabric, and all stackedly all combine with epoxy resin and cover polymer; With identical plate is just described, difference is that described two inner stacks can comprise the fabric greater or less than 5 layers; 11 plywoods, it has outer stack and five inner stacks that are made of single-layer metal of two band quadruple cloths, described five inner stacks are by other four stacked separating of interior fabric that are made of quadruple cloth, and all stackedly all are bonded together with epoxy resin and cover polymer; Deng.The quantity of the tissue layer of using on outer stack and inner stacks can change as required, but usually, overall pattern should be along the plane centreline symmetry, and described plane centreline symmetry is parallel with the front and rear surfaces of plate and between front and rear surfaces.As described in above-mentioned Figure 74-79, in the various embodiments of the plate of containing metal screen fabric, can realize alternately and the various structures of biasing weave pattern.
The embodiment of illustrative (all embodiments all comprise outside polymer coating) can include but not limited to: the plate of 26-layer fabric and epoxy resin; The plate of 40-layer fabric and epoxy resin; The plate of 100-layer fabric and epoxy resin; And the 23-laminate, it has 5 layers of fabric, 1 layer of oven wire mesh blanket afterwards, 5 layers of fabric afterwards, 1 layer of oven wire mesh blanket afterwards, 5 layers of fabric afterwards, 1 layer of oven wire mesh blanket afterwards and 5 layers of fabric afterwards; And the 30-laminate, it has 5 layers of fabric, 1 layer of oven wire mesh blanket afterwards, 5 layers of fabric afterwards, 1 layer of oven wire mesh blanket afterwards, 5 layers of fabric afterwards, 1 layer of oven wire mesh blanket afterwards, 5 layers of fabric afterwards; 1 layer of oven wire mesh blanket afterwards, 5 layers of fabric afterwards, 1 layer of oven wire mesh blanket afterwards and 5 layers of fabric afterwards.
In the application of two or more plate covering surfaces of needs, can with they overlapping about 4 to 8 inches, and can be connected to each other/adhere to, perhaps be not connected to each other/adhere to, and/or use securing member, have the groove, adhesive etc. of machanical fastener and/or these any combination, these plates are fastened to wall by lap.Alternatively, can be with two or more plate sides to the side adjacency, and can use machanical fastener, have the groove, adhesive etc. of machanical fastener and/or these any combination is fastened to wall with it, perhaps it is not fastened to wall.Usually for the protection of necessary grade is provided; can adopt aforesaid any fastening method and device herein and/or cover all overlappingly and/or in abutting connection with the elastic webbing element of seam basically, the length that will have the panel material that is equivalent to the protection intensity that is mounted plate is fastening at their front side or the adjoiner on the rear side along two boards.If use band, then it can be basically along the whole length of seam be applied in overlapping suture above, usually in that side of the inside of structure.For example, described band can include but not limited to Best Roofing Systems, Inc.of OklahomaCity, Metal-Gard " E " the band system that Oklahoma produces.
Figure 80-82 is depicted as exemplary shock wave/fragment/projectile containment plate.Comprise a plurality of composite board 8000 that shown in Figure 74-79, on a side or many sides, are coated with polyureas or other elastomeric material like that at the plate among Figure 80-82.Figure 80 is depicted as the plate 8000 that has polyureas or other elastomeric material 8010 on first side.Figure 81 is depicted as the plate 8000 that has polyureas or other elastomeric material 8010 around plate 8000.Figure 82 is depicted as the plate 8000 that has polyureas or other elastomeric material 8010 on opposite side.Usually, polyureas or other elastomeric material can be applied on any or a plurality of surface of plate 8000, and can be sandwiched between a plurality of plates 8000.
The illustrative methods of the anti-projectile plate of preparation comprises to be supplied with first tissue layer, supplies with second tissue layer, supply with the adhesive that first tissue layer and second tissue layer is fixing and at least the elastomeric material coating of one deck cover at least a portion of plate.
The description of front provides for illustration purpose.After those skilled in the art read the present invention, the changes and improvements that will make embodiment described herein came into plain view, condition be these changes and improvements without departing from the spirit and scope of the present invention.Can use with any other embodiment described herein about the illustrated one or more special characteristics of specific embodiments herein.

Claims (30)

1. bursting diaphragm system comprises:
The pre-cure elastomer material layer, it has predetermined thickness, main part and a plurality of flange, and each in described a plurality of flanges is all dangled from same side, and
A plurality of tightening members are used to pass the surface that described a plurality of flange is fixed to the pre-cure elastomer material layer structure.
2. the described system of claim 1, wherein said elastomeric material is selected from polyureas, polysiloxanes, polyurethane and polyurea/polyurethane mixture.
3. the described system of claim 2, wherein said elastomeric material is a polyurea materials.
4. the described system of claim 2, wherein said elastomeric material has the elongation at break in about 100-800% scope, and has the hot strength greater than about 2000psi.
5. the described system of claim 1, the pre-hardening thickness of the predetermined thickness of wherein said elastomeric material is to spray to predetermined thickness by the uncured layer with elastomeric material to form.
6. the described system of claim 1, the pre-hardening thickness of the predetermined thickness of wherein said elastomeric material comprises at least two relative flanges.
7. the described system of claim 1, it further comprises the fabric enhancement Layer that combines with elastomeric material, described elastomeric material comprises the main part flange relative with at least two.
8. the described system of claim 1, wherein said a plurality of tightening members comprise the discontinuous restraint zone of the continuous restraint zone of the Z-shaped groove of the U-lag of multiple length, multiple length, multiple length, multiple length and at least one in a plurality of packing ring.
9. the described system of claim 8, wherein said a plurality of tightening members further comprise at least one in a plurality of nails, a plurality of screw, a plurality of concrete nail and a plurality of concrete screw.
10. the described system of claim 8, wherein said a plurality of tightening members further comprise bonding adhesive or epoxy resin.
11. the described system of claim 1, wherein said plate comprises one or more perforation that help described flanges flex.
12. the described system of claim 1, wherein said flange adopts thermal source to carry out bending.
13. the described system of claim 1 is wherein placed adjacent one another with at least two plates, makes the part of overlapping second plate of first plate portion.
14. the described system of claim 1 is wherein placed adjacent one another with at least two plates, makes the marginal portion adjacency of first plate and second plate.
15. the described system of claim 1, wherein adjacent plate is fixing with band.
16. the described system of claim 1 wherein is fixed on framework and precision-machined plate on the described plate.
17. the described system of claim 1, it further comprises and the door that is combined with bursting diaphragm.
18. the described system of claim 1, it further comprises the transparent polyurea layer that covers one or more windows and be combined as a whole with one or more bursting diaphragms.
19. the described system of claim 1 is wherein with anchor clamps and the collaborative use of thermal source, so that described a plurality of flanges flex.
20. a bursting diaphragm comprises:
Pre-cure elastomer material layer with predetermined thickness; And
At least one deck tissue layer, described tissue layer is fixed to the pre-cure elastomer material layer, and described tissue layer is configured to allow distortion of pre-cure elastomer material layer and elongation.
21. the described plate of claim 20, the length of the wherein said tissue layer of one deck at least equals the length at the pre-cure elastomer material at elongation rate place.
22. the described plate of claim 20, it further comprises a plurality of tightening members, with will be at least one deck tissue layer be fixed to the surface of structure.
23. an anti-projectile plate comprises:
First tissue layer;
Second tissue layer;
Adhesive is fixed to second tissue layer with first tissue layer; And
Layer of elastomer material, it covers at least a portion of described plate.
24. the described plate of claim 23, it further comprises one or more additional tissue layer, and each in described one or more extra plays is all used adhesive.
25. the described plate of claim 23, wherein said adhesive are epoxy resin.
26. the described plate of claim 23, wherein said plate have the solid basically core of biasing and vertical orientated tissue layer.
27. the described plate of claim 23, wherein said plate is fixed to the surface.
28. be used for preparing the method for front each described plate of claim.
29. be used for installing the method for each described plate of claim 1-27.
30. basically as shown with described invention.
CNA2005800473004A 2004-12-01 2005-11-30 Shrapnel and projectile containment systems and equipment and methods for producing same Pending CN101146968A (en)