CN101118026A - FTPV flexible fluorine material low pervasion fuel oil pipe - Google Patents
FTPV flexible fluorine material low pervasion fuel oil pipe Download PDFInfo
- Publication number
- CN101118026A CN101118026A CNA2007101470273A CN200710147027A CN101118026A CN 101118026 A CN101118026 A CN 101118026A CN A2007101470273 A CNA2007101470273 A CN A2007101470273A CN 200710147027 A CN200710147027 A CN 200710147027A CN 101118026 A CN101118026 A CN 101118026A
- Authority
- CN
- China
- Prior art keywords
- rubber
- layer
- ftpv
- flexible
- fluorine material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a fuel pipe, in particular to an FTPV flexible fluoride material low-penetration fuel pipe for a vehicle, and comprises a modified nitrile-butadiene rubber layer. The present invention is characterized in that the composite structure has at least one FTPV flexible fluoride material structure layer. The outer and the inner FTPV flexible fluoride material structure layers are compounded with an ECO epichlorohydrin rubber /NBR nitrile-butadiene rubber +PVC polyvinyl chloride/CSM chlorosulfonated polyethylene/CM chlorinated polyethylene rubber layer. The FTPV flexible fluoride material low-penetration fuel pipe has three layer structures of an FKM fluorine containing rubber/NBR nitrile-butadiene rubber layer, an FTPV flexible fluoride material, and an ECO epichlorohydrin rubber/NBR nitrile-butadiene rubber+PVC polyvinyl chloride/CSM chlorosulfonated polyethylene/CM chlorinated polyethylene rubber layer; four layer structures of an FTPV flexible fluoride material structure layer, a NBR nitrile-butadiene rubber/ ECO epichlorohydrin rubber/AEM elayl-methacrylate rubber layer, an AR aramid fiber/PES polyestr fiber reinforced layer, and an ECO epichlorohydrin rubber/AEM elayl-methacrylate rubber/CSM chlorosulfonated polyethylene/CM chlorinated polyethylene rubber layer; five layer structures of an FTPV flexible fluoride material layer, an FKM fluorine containing rubber/ NBR nitrile-butadiene rubber layer, a NBR nitrile-butadiene rubber layer/ ECO epichlorohydrin rubber/ AEM elayl-methacrylate rubber layer, an AR aramid fiber/ PES polyestr fiber reinforced layer, and an ECO epichlorohydrin rubber/ AEM elayl-methacrylate rubber/CSM chlorosulfonated polyethylene/ CM chlorinated polyethylene rubber layer.
Description
Technical field
The present invention relates to a kind of fuel pipe, particularly a kind of FTPV flexible fluorine material low-penetration fuel pipe that is used for automobile.
Background technique
Though at present the NBR rubber that uses of vehicle fuel system both nitrile rubber have many advantages such as oil resistant, ageing-resistant, and wear-resisting, low ventilative and coagulate performance such as power height but ozone resistance is poor.
Although the fuel hose that the present high fluoroelastomer that uses is made the liner separation layer has plurality of advantages, but exist osmotic-pressure-tolerant, anti-variable chemical corrosivity, subduing property of high-low temperature resistant and propagation tear are poor, body is too hard, rigidity is too strong, and in use the fluorine material layer is easily peeled off technological deficiency such as come off.
Summary of the invention
Purpose of the present invention is exactly in order to overcome above technical deficiency, provide a kind of weatherability stronger, elasticity and ductility are better, in use composite bed be difficult for peeling off come off, subduing property of high-low temperature resistant and the stronger FTPV flexible fluorine material low-penetration fuel pipe of propagation tear.
The object of the present invention is achieved like this:
A kind of FTPV flexible fluorine material of the present invention low-penetration fuel pipe comprises one deck modified butadiene acrylonitrile rubber layer, it is characterized in that having at least in the composite structure one deck FTPV flexible fluorine material construction layer.
Purpose of the present invention can be achieved like this equally:
Inside and outside FTPV flexible fluorine material construction layer, be compounded with ECO chlorohydrin rubber/NBR nitrile butadiene rubber+PVC PVC/CSM chlorosulfonated polyethylene/CM haloflex glue-line.
Purpose of the present invention equally also can be achieved like this:
FTPV flexible fluorine material low-penetration fuel pipe has FKM fluorine rubber/NBR nitrile butadiene rubber layer, FTPV flexible fluorine material construction layer, ECO chlorohydrin rubber/NBR nitrile butadiene rubber+PVC PVC/CSM chlorosulfonated polyethylene/CM haloflex glue-line three-decker.
Purpose of the present invention also can be achieved like this:
FTPV flexible fluorine material low-penetration fuel pipe has FTPV flexible fluorine material construction layer, NBR nitrile butadiene rubber/ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber glue-line, AR aramid fibre/PES polyester fiber enhancement layer, ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber/CSM chlorosulfonated polyethylene/CM haloflex glue-line.
Purpose of the present invention also can also realize like this:
FTPV flexible fluorine material low-penetration fuel pipe has FTPV flexible fluorine material construction layer, FKM fluorine rubber/NBR nitrile butadiene rubber layer, NBR nitrile butadiene rubber/ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber layer, AR aramid fibre/PES polyester fiber enhancement layer, ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber/CSM chlorosulfonated polyethylene/CM haloflex glue-line.
Beneficial effect of the present invention:
The FTPV flexible fluorine material that the present invention selects for use is a kind of thermoplastic elastic material between fluororesin and fluorine rubber performance, thereby it is stronger to have weatherability, and elasticity and ductility are better, and in use composite bed is difficult for peeling off and comes off.
After the present invention used the fluorine material of partially crystallizable to replace fluorine rubber, the tear-proof of fuel hose, anti-variable chemical corrosion, high-low temperature resistant was subdued and performance such as anti-fuel oil infiltration is significantly increased.Realize ultra-low penetration, satisfy new automobile low emission regulation (ULEV II) requirement of European environment protection emission IV, V standard and California, USA, and the needs of novel fuel media such as the unleaded gas of satisfied fully interpolation alcohols and biodiesel.
Advantage of the present invention also has: multi-layer structure, the sebific duct internal layer is a FKM/NBR material structure layer, the FTPV flexible fluorine material is a screen layer, fiber-reinforced layer is selected according to product work pressure-bearing situation, the middle level according to product heat-resisting requirement determine the NBR/ECO/AEM material, skin is selected heat-resisting radiation for use, the CSM/CM/ECO/AEM material of anti-ozone aging.
Description of drawings
Fig. 1 is an embodiment of the invention two-layer structure schematic representation;
Fig. 2 is an embodiment of the invention three-decker schematic representation;
Fig. 3 strengthens structure four-layer structure schematic representation for the embodiment of the invention;
Fig. 4 strengthens structure five-layer structure schematic representation for the embodiment of the invention.
Embodiment
As shown in Figure 1, be FTPV flexible fluorine material low-penetration fuel pipe two-layer structure, be followed successively by from inside to outside: FTPV flexible fluorine material screen layer (1), ECO chlorohydrin rubber/NBR nitrile butadiene rubber+PVC PVC/CSM chlorosulfonated polyethylene/CM haloflex glue-line (2).
As shown in Figure 2, be FTPV flexible fluorine material low-penetration fuel pipe three-decker, be followed successively by from inside to outside: FKM fluorine rubber/NBR nitrile butadiene rubber layer (3), FTPV flexible fluorine material screen layer (1), ECO chlorohydrin rubber/NBR nitrile butadiene rubber+PVC PVC/CSM chlorosulfonated polyethylene/CM haloflex glue-line (2).
As shown in Figure 3, be FTPV flexible fluorine material low-penetration fuel pipe four-layer structure, be followed successively by from inside to outside: FTPV flexible fluorine material screen layer (1), NBR nitrile butadiene rubber/ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber layer (4), AR aramid fibre/PES polyester fiber enhancement layer (5), ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber/CSM chlorosulfonated polyethylene/CM haloflex glue-line (6).
Embodiment 4
As shown in Figure 4, be FTPV flexible fluorine material low-penetration fuel pipe five-layer structure, be followed successively by from inside to outside: FTPV flexible fluorine material screen layer (1), FKM fluorine rubber/NBR nitrile butadiene rubber layer (3), NBR nitrile butadiene rubber/ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber layer (4), AR aramid fibre/PES polyester fiber enhancement layer (5), ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber/CSM chlorosulfonated polyethylene/CM haloflex glue-line (6).
Claims (5)
1. a FTPV flexible fluorine material low-penetration fuel pipe comprises one deck modified butadiene acrylonitrile rubber layer, it is characterized in that having at least in the composite structure one deck FTPV flexible fluorine material construction layer (1).
2. the described a kind of FTPV flexible fluorine material low-penetration fuel pipe of root a tree name claim 1 is characterized in that being compounded with ECO chlorohydrin rubber/NBR nitrile butadiene rubber+PVC PVC/CSM chlorosulfonated polyethylene/CM haloflex glue-line (2) inside and outside the FTPV flexible fluorine material construction layer (1).
3. the described a kind of FTPV flexible fluorine material low-penetration fuel pipe of root a tree name claim 1 is characterized in that having FKM fluorine rubber/NBR nitrile butadiene rubber layer (3), FTPV flexible fluorine material construction layer (1), ECO chlorohydrin rubber/NBR nitrile butadiene rubber+PVC PVC/CSM chlorosulfonated polyethylene/CM haloflex glue-line (2) three-decker.
4. the described a kind of FTPV flexible fluorine material low-penetration fuel pipe of root a tree name claim 1 is characterized in that having FTPV flexible fluorine material construction layer (1), NBR nitrile butadiene rubber/ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber layer (4), AR aramid fibre/PES polyester fiber enhancement layer (5), ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber/CSM chlorosulfonated polyethylene/CM haloflex glue-line (6) four-layer structure.
5. the described a kind of FTPV flexible fluorine material low-penetration fuel pipe of a tree name claim 1 is characterized in that having FTPV flexible fluorine material layer (1), FKM fluorine rubber/NBR nitrile butadiene rubber layer (3), NBR nitrile butadiene rubber/ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber glue-line (4), AR aramid fibre/PES polyester fiber enhancement layer (5), ECO chlorohydrin rubber/AEM ethylene acrylic fat rubber/CSM chlorosulfonated polyethylene/CM haloflex glue-line (6) five-layer structure.