CN101117481A - Water-dispersing cold curing rubber waterproofing paint - Google Patents
Water-dispersing cold curing rubber waterproofing paint Download PDFInfo
- Publication number
- CN101117481A CN101117481A CNA200610015144XA CN200610015144A CN101117481A CN 101117481 A CN101117481 A CN 101117481A CN A200610015144X A CNA200610015144X A CN A200610015144XA CN 200610015144 A CN200610015144 A CN 200610015144A CN 101117481 A CN101117481 A CN 101117481A
- Authority
- CN
- China
- Prior art keywords
- percent
- mixed
- minutes
- water
- stirred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a rubber waterproof coating which is dispersed in water and cured in room temperature. 45 percent of silicone is added into 1 percent of glyoxal and crosslinked for 60 minutes in room temperature. After modification, 10 percent of styrene-acrylic emulsion and 4 percent of benzyl alcohol are added, mixed uniformly and stirred for 10-20 minutes. Then 20 percent 107 adhesive, 5 percent of asbestos powder, 4 percent of talcum powder and 15 percent of pearl powder are mixed, and 1 percent of light calcium carbonate, 5 percent of sodium fluosilicate, 1 percent of gypsum powder and 10 percent of white cement are mixed and compounded to prepare an additive, and then stirred for 40 minutes and filtered. The invention has the following advantages of simple process, low cost, convenient operation, no crack in low temperature, no flow in high temperature, anti-aging, long service life, strong waterproofness and weatherability and high compressive strength.
Description
Technical field
The present invention relates to a kind of water-dispersion, the rubber waterproofing paint of self-vulcanizing.
Background technology
At present, the plastic ointment that the impervious waterproof of building trade is used, anti-aging poor, cold(ing)crack, high temperature trickling; Liquid water-proofing seepage agent bonding force is poor, easily be full of cracks, and the asphalt felt that the water leakage agent is used is often because of vibrations, high temperature seepage.
Summary of the invention
The objective of the invention is to overcome above-mentioned defective, a kind of water-dispersion is provided, the rubber waterproofing paint of self-vulcanizing.
Technical scheme of the present invention is: a kind of water-dispersion, and the rubber waterproofing paint of self-vulcanizing is characterized in that: it is composed as follows: silicone binder 45%, oxalic dialdehyde 1%, benzene-acrylic emulsion 10%, phenylcarbinol 4%, building glue 20%, asbestos powder 5%, talcum powder 4%, perlite powder 15%, polyacrylamide 0.1%, light calcium carbonate 1%, Sodium Silicofluoride 5%, terra alba 1%, white cement 10%, organosilicon is added oxalic dialdehyde, crosslinking time is 60 minutes under the normal temperature, after modification finishes, adds benzene-acrylic emulsion and phenylcarbinol, mix and stirred 10-20 minute, add 107 glue then, asbestos powder, talcum powder, precious different rock dust is mixed, by light calcium carbonate, Sodium Silicofluoride, terra alba, white cement is mixed and makes additive, stirred 40 minutes, and filtered.
The present invention has the following advantages: technology is simple, and cost is low, and is easy to operate, and low temperature does not chap, and high temperature does not trickle, anti-aging, and the life-span is long, and water-repellancy and weather resisteant are strong, the ultimate compression strength height.
Embodiment
Embodiment: a kind of water-dispersion, the rubber waterproofing paint of self-vulcanizing adds 1% oxalic dialdehyde with 45% organosilicon, and crosslinking time is 60 minutes under the normal temperature, after modification finishes, add 10% benzene-acrylic emulsion and 4% phenylcarbinol, mix and stirred 10-20 minute, add 20%107 glue then, 5% asbestos powder, 4% talcum powder, 15% precious different rock dust are mixed, be mixed by 1% light calcium carbonate, 5% Sodium Silicofluoride, 1% terra alba, 10% white cement and make additive, stirred 40 minutes, filter.
Claims (1)
1. water-dispersion, the rubber waterproofing paint of self-vulcanizing is characterized in that: 45% organosilicon is added 1% oxalic dialdehyde, and crosslinking time is 60 minutes under the normal temperature, after modification finishes, add 10% benzene-acrylic emulsion and 4% phenylcarbinol, mix and stirred 10-20 minute, add 20%107 glue then, 5% asbestos powder, 4% talcum powder, 15% precious different rock dust are mixed, be mixed by 1% light calcium carbonate, 5% Sodium Silicofluoride, 1% terra alba, 10% white cement and make additive, stirred 40 minutes, filter.