CN101117413A - Antistatic rubber cushion - Google Patents
Antistatic rubber cushion Download PDFInfo
- Publication number
- CN101117413A CN101117413A CNA2007102008879A CN200710200887A CN101117413A CN 101117413 A CN101117413 A CN 101117413A CN A2007102008879 A CNA2007102008879 A CN A2007102008879A CN 200710200887 A CN200710200887 A CN 200710200887A CN 101117413 A CN101117413 A CN 101117413A
- Authority
- CN
- China
- Prior art keywords
- parts
- shares
- rubber cushion
- antistatic rubber
- static
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a new-type static-free electricity rubber pad, belonging to the technical field of static-free electricity rubber mat. The weight part compositions of ingredients of the static-free electricity rubber mat are as follows: 28-31 shares of nitrile rubber, 1.2-1.6 shares of zinc oxide, 0.35-0.50 shares of stearic acid, 0.8-1.2 shares of engine oil, 3.0-4.0 shares of dioctyl, 0.3-0.8 shares of sulfur, 0.8-1.4 shares of accelerant, 11-15 shares of carbon black, 2.5-3.5 shares of white soot, 0.7-1.0 shares of xylene resin, 2.6-3.2 shares of light calcium and 0.5-0.85 shares of vesicant. The invention is made by common technique. The invention has good static-free electricity effects and can be applied on occasions where high requirements on static electricity are needed, so as to guard against the bad effects of static electricity and potential dangers.
Description
Technical field
The present invention relates to a kind of rubber pad, particularly relate to a kind of rubber pad of anti-electrostatic.
Background technology
In daily life and work place, if a large amount of existence of static will bring harm to live and work.Use the place of high most advanced and sophisticated precision instrument at some, static can have influence on the sensitivity of instrument, causes the mistake of test result; The electrostatic existence can make airborne grit be adsorbed onto body surface in a large number in the workshop in addition, thereby has influence on the quality of product.Generation of static electricity makes us uncomfortable electric shock greatly about 15KV when stepping out from car as a people.20 to 60KV voltage right and wrong are usually seen in plastics and processing industry.Not only bring discomfort by the electric shock that static causes, people's hiding reaction and also may cause more serious accident after getting shocked.When operation was carried out in Flammable atmosphere, the static electric charge of quick travel had and causes the enough energy of incendiary.The ground connection object can produce spark when electric field strengthens, or the electric charge on the isolator also flashover over the ground can take place when reaching place value.The fire that brings thus not only brings loss to production, also may cause the damage fully of factory.Therefore eliminating the electrostatic influence all is significant to live and work.At present, though but the rubber cushion and the floor of some anti-electrostatics are also arranged, performance is different, and difference in selling prices is also bigger, and the effect of use is also had nothing in common with each other.
Summary of the invention
The objective of the invention is to, a kind of new good rubber pad of antistatic performance is provided.It is better that the present invention has anti-static effect, the characteristics that production cost is lower.
Technical scheme of the present invention: a kind of antistatic rubber cushion, it is characterized in that: this antistatic rubber is to use following materials of weight proportions, 28～31 parts of paracrils, 1.2～1.6 parts in zinc oxide, 0.35～0.50 part of hard ester acid, 0.8～1.2 part in machine oil, 3.0～4.0 parts of dioctyl esters, 0.3～0.8 part in sulphur, 0.8～1.4 part of promotor, 11～15 parts of carbon blacks, 2.5～3.5 parts of white carbon blacks, 0.7～1.0 part of xylene resin, 2.6～3.2 parts of fine particle calcium carbonates, 0.45～0.8 part of antisatics, 0.5～0.85 part of whipping agent adopt conventional manufacture craft to make.
Above-mentioned antistatic rubber cushion is to use following materials of weight proportions, 29.5～31 parts of paracrils, 1.4～1.5 parts in zinc oxide, 0.4～0.50 part of hard ester acid, 0.9～1.1 part in machine oil, 3.3～3.9 parts of dioctyl esters, 0.5～0.7 part in sulphur, 1 part of promotor, 12～14 parts of carbon blacks, 2.5～3.5 parts of white carbon blacks, 0.8～1.0 part of xylene resin, 2.6～3.2 parts of fine particle calcium carbonates, 0.5～0.7 part of antisatics, 0.6～0.8 part of whipping agent adopt conventional manufacture craft to make.
Aforesaid antistatic rubber cushion, described paracril are N-41 paracril or SR-N240S paracril.
Aforesaid antistatic rubber cushion, described machine oil is 46
#Machine oil.
Aforesaid antistatic rubber cushion, described whipping agent is AC-3000.
Aforesaid antistatic rubber cushion, described carbon black are N330 carbon black and ethene sooty mixture, and wherein N330 carbon black and ethene sooty usage ratio are N330 carbon black 50～60%, ethene carbon black 40～50%.
Aforesaid antistatic rubber cushion, described antisatics are antisatics SN.
Aforesaid antistatic rubber cushion, described promotor are the material formations with following weight proportion, DM0.36 part, M0.21 part, TMTD0.07 part, RD0.36 part.
Compared with prior art, the present invention has obtained following effect:
1. be main component with the paracril, and adopt proper raw material proportioning, make the rubber pad made from the present invention (as sole, work top etc.) have good antistatic effect, made people's work and part safety and the guarantee of how having lived.
2. make sole with the present invention, have good elasticity, the shoes of making are put on afterwards comfortable and are difficult for injured; Make work top, car mat etc. with the present invention, damage in the time of can preventing the human body collision.
The present invention has good anti-static effect and elastic while, has also guaranteed its intensity, other performances such as anti-skidding.Therefore, antistatic rubber cushion of the present invention can be widely used in the workplace that static is had relatively high expectations, thereby avoids eliminating accident potential because there is the detrimentally affect that brings in static.And production cost is lower, helps applying.
Embodiment
Embodiments of the invention 1: adopt conventional manufacture craft to make antistatic rubber cushion with following materials of weight proportions, in grinding tool, be hot pressed into sole.0.45 part, 46 of paracril 30 parts of (N-41 paracril or SR-N24OS paracril), 1.5 parts in zinc oxide, hard ester acid
#0.7 part in 1 part in machine oil, 3.6 parts of dioctyl esters, 0.6 part in sulphur, promotor 1 part of (DM0.36 part, M0.21 part, TMTD0.07 part, RD0.36 part), carbon black 13.5 parts of (7.5 parts of N330 carbon blacks, 6 parts of ethene carbon blacks), 3 parts of white carbon blacks, 0.9 part of xylene resin, 3 parts of fine particle calcium carbonates, antisatics SN0.6 part, AC-3000 whipping agent.This sole has the good anti-static effect, and the workman puts on the shoes that used this sole, causes the out of true of meter reading in the time of can preventing to enter the workshop owing to generation static, even initiation fire.
Embodiments of the invention 2: adopt conventional manufacture craft to make antistatic rubber cushion with following materials of weight proportions, according to service requirements cutting press forming.0.35 part, 46 of paracril 28 parts of (N-41 paracril or SR-N240S paracril), 1.3 parts in zinc oxide, hard ester acid
#0.55 part in 1.2 parts in machine oil, 3.2 parts of dioctyl esters, 0.4 part in sulphur, promotor 1.25 parts of (DM0.4 part, M0.25 part, TMTD0.1 part, RD0.5 part), carbon black 15 parts of (8 parts of N330 carbon blacks, 7 parts of ethene carbon blacks), 2.5 parts of white carbon blacks, 0.7 part of xylene resin, 2.7 parts of fine particle calcium carbonates, antisatics SN0.8 part, AC-3000 whipping agent.Be used for working space that static is had relatively high expectations, good anti-static effect is arranged, can effectively prevent the harm that static brings.
Claims (8)
1. antistatic rubber cushion, it is characterized in that: this antistatic rubber is to use following materials of weight proportions, 28～31 parts of paracrils, 1.2～1.6 parts in zinc oxide, 0.35～0.50 part of hard ester acid, 0.8～1.2 part in machine oil, 3.0～4.0 parts of dioctyl esters, 0.3～0.8 part in sulphur, 0.8～1.4 part of promotor, 11～15 parts of carbon blacks, 2.5～3.5 parts of white carbon blacks, 0.7～1.0 part of xylene resin, 2.6～3.2 parts of fine particle calcium carbonates, 0.45～0.8 part of antisatics, 0.5～0.85 part of whipping agent adopt conventional manufacture craft to make.
2. antistatic rubber cushion according to claim 1, it is characterized in that: this antistatic rubber is to use following materials of weight proportions, 29.5～31 parts of paracrils, 1.4～1.5 parts in zinc oxide, 0.4～0.50 part of hard ester acid, 0.9～1.1 part in machine oil, 3.3～3.9 parts of dioctyl esters, 0.5～0.7 part in sulphur, 1 part of promotor, 12～14 parts of carbon blacks, 2.5～3.5 parts of white carbon blacks, 0.8～1.0 part of xylene resin, 2.6～3.2 parts of fine particle calcium carbonates, 0.5～0.7 part of antisatics, 0.6～0.8 part of whipping agent adopt conventional manufacture craft to make.
3. antistatic rubber cushion according to claim 1 and 2 is characterized in that: described paracril is N-41 paracril or SR-N240S paracril.
4. antistatic rubber cushion according to claim 1 and 2 is characterized in that: described machine oil is 46# machine oil.
5. antistatic rubber cushion according to claim 1 and 2 is characterized in that: described whipping agent is the AC-3000 whipping agent.
6. antistatic rubber cushion according to claim 1 and 2 is characterized in that: described carbon black is N330 carbon black and ethene sooty mixture, and wherein N330 carbon black and ethene sooty usage ratio are N330 carbon black 50～60%, ethene carbon black 40～50%.
7. antistatic rubber cushion according to claim 1 and 2 is characterized in that: described antisatics is antisatics SN.
8. antistatic rubber cushion according to claim 2 is characterized in that: described promotor is the material formation with following weight proportion, DM0.36 part, M0.21 part, TMTD0.07 part, RD0.36 part.