CN101116645A - Resin-imitated cinerary casket and manufacturing method thereof - Google Patents
Resin-imitated cinerary casket and manufacturing method thereof Download PDFInfo
- Publication number
- CN101116645A CN101116645A CNA2006100409042A CN200610040904A CN101116645A CN 101116645 A CN101116645 A CN 101116645A CN A2006100409042 A CNA2006100409042 A CN A2006100409042A CN 200610040904 A CN200610040904 A CN 200610040904A CN 101116645 A CN101116645 A CN 101116645A
- Authority
- CN
- China
- Prior art keywords
- cinerary casket
- resin
- casting material
- formwork
- rubber soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a resin-imitated cinerary casket and a manufacturing method thereof, which takes magnesium chloride, magnesium oxide, ferric oxide (iron red), ferroferric oxide (iron black), urea-formaldehyde resin, silica sol and wood dust as raw materials and is formed by pouring a rubber soft mould, a hard mould shell, a mould core and a movable mould plate. Because magnesium chloride and magnesium oxide are used as main raw materials, the product has excellent fireproof performance and can effectively prevent fire; the purpose of adding iron oxide red and iron oxide black is to change the color of the product; the urea-formaldehyde resin and the silica sol are added, so that the water absorption rate of the product can be reduced, and the compactness of the product can be greatly improved; the wood chips in the invention not only play a role of fibers, enhance the strength and impact resistance of the product, have the performance equivalent to that of the resin cinerary casket, but also reduce the weight of the product. Through measurement and calculation, the synthetic cost of the resin-imitated cinerary casket manufactured by the method is only 10.2 yuan/urn, and the yield is high.
Description
Technical field:
The present invention relates to a kind of cinerary casket, relate in particular to a kind of cinerary casket and preparation method thereof with excellent flame retardancy energy.
Background technology:
Existing cinerary casket product category is various, and high-grade crystal cinerary casket, Achates cinerary casket are arranged; Middle-grade redwood cinerary casket; Low and middle-grade resin cinerary caskets.General public is generally all selected the resin cinerary casket, because it is cheap relatively that the resin cinerary casket has price, and be convenient to make fine pattern in its appearance, presentation quality is better, thereby the consumption maximum of resin cinerary casket, this class cinerary casket is a product the most salable at present, yet the resin cinerary casket is produced by very easily incendiary resin and other auxiliary chemicals, in its production, very easily produce fire in the storage process, safety is lower, and production cost is higher, the production cost of general every resin cinerary casket is about 30 yuan, adopt cement in order to address this problem the someone with the right performance of resistance, Gypsum Fibrosum carries out the die casting cinerary casket, though do not have disaster hidden-trouble, and cost is not high yet, its intensity, weight indicator can not satisfy the requirement of cinerary casket, the surface smoothness of cinerary casket also is difficult to reach requirement simultaneously, thereby fails to be applied.
Summary of the invention:
The purpose of this invention is to provide a kind of is resin imitated cinerary casket of making of raw material and preparation method thereof with magnesium chloride, magnesium oxide, iron sesquioxide (iron oxide red), ferroso-ferric oxide (iron oxide black), Lauxite, Ludox, wood flour.
Resin imitated cinerary casket of the present invention is formed by die casting by the casting material of following component and weight proportion:
1. concentration is the magnesium chloride brine 25～42 of 20～30 degree (measuring with gravimeter);
2. magnesium oxide 35～65; 3. iron sesquioxide (iron oxide red) 0～2.5; 4. ferroso-ferric oxide (iron oxide black) 0～2.5;
5. Lauxite 0～8; 6. Ludox 0～8; 7. wood flour 0～5;
As to optimization of the present invention, the weight proportion of described casting material component is:
1. concentration is the magnesium chloride brine 30～35 of 22～26 degree (measuring with gravimeter);
2. magnesium oxide 40～50; 3. iron sesquioxide (iron oxide red) 1～1.5; 4. ferroso-ferric oxide (iron oxide black) 1～1.5;
5. Lauxite 1～5; 6. Ludox 1～5; 7. wood flour 2～3;
The manufacture method of described resin imitated cinerary casket is as follows:
(1) preparation of casting material:
1. choose the each component material by above-mentioned weight ratio;
2. add Lauxite, Ludox in the magnesium chloride brine and stir;
3. powder magnesium oxide, iron oxide red, iron oxide black and wood flour are mixed and stir;
4. the solution that 2. step is obtained is poured in the mixture that 3. step obtain, and fully stirs, material to be cast;
(2) pouring procedure:
Make the rubber soft mode by predetermined moulding, inside and outside the rubber soft mode, make hard core rod, formwork and collapsible form again; Casting material is poured in the rubber soft mode, under hard formwork and core rod qualification, move down collapsible form, unnecessary casting material overflows from collapsible form and hard formwork junction, and is manual with unnecessary casting material removal, and make collapsible form and hard formwork be maintained fixed state, after making casting material in die cavity, solidify 0.5～5 hour, remove collapsible form, hard formwork and core rod, peel off the rubber soft mode, it is carried out the deburring polishing, at last its outer surface is decorated processing.
Owing to adopt magnesium chloride and magnesium oxide as main material, thereby this product has good fire protecting performance, and it can prevent effectively that fire from taking place; The purpose of adding iron oxide red, iron oxide black is the color that changes product; Increase Lauxite and Ludox, can not only reduce the water absorption rate of product, and can increase substantially the degree of compaction of product; Wood flour had both played fibration in the present invention, had strengthened the intensity and the resistance to impact of product, and its performance is suitable with the resin cinerary casket, can also alleviate product weight.Through measuring and calculating, adopt the integrated cost of the made resin imitated cinerary casket of this method to have only 10.2 yuan/, and yield rate is very high.
Description of drawings:
Fig. 1 is a pouring technology sketch map of the present invention; 1-hard formwork; 2-rubber soft mode; The 3-core rod; The 4-collapsible form;
The specific embodiment:
Below in conjunction with the full and accurate embodiments of the present invention of introducing of description of drawings:
(1) choosing of material: choose material by following weight proportion
1. magnesium chloride brine 25kg, its concentration is 22 degree, measures with gravimeter;
2. magnesium oxide 35kg; 3. iron oxide red 0.5kg; 4. iron black 0.5kg; 5. Lauxite 0.1kg;
6. Ludox 0.1kg; 7. wood flour 1kg;
(2) preparation of casting material:
1. Lauxite, Ludox are added in the magnesium chloride brine and stir;
2. with powder magnesium oxide, iron oxide red, iron oxide black, wood flour mix homogeneously;
3. the solution that 1. step is obtained is poured in the powder that 2. step obtain, and fully stirs, casting material;
(3) pouring procedure:
1. the making of mould: make the rubber soft mode 2 of predetermined moulding, make hard core rod 3, formwork 1 and collapsible form 4 according to rubber soft mode 2 usefulness epoxy resin again;
2. mould is installed, and formwork 1, core rod 3 are accurately located, and rubber soft mode 2 is placed between formwork 1 and the core rod 3;
3. the cast: with casting material from injection rubber soft mode 2 suitable for reading, this moment, rubber soft mode 2 was limited by hard formwork 1 and core rod 3, casting material enters between rubber soft mode 2 and the core rod 3, cover collapsible form 4, unnecessary casting material then overflows from collapsible form 4 and hard formwork 1 junction, manual with unnecessary casting material removal, and make collapsible form 4 and hard formwork 1 be maintained fixed state, make casting material at picture glue soft mode 2, solidify after 0.5～5 hour in the die cavity that core rod 3 and collapsible form 4 are formed, remove collapsible form 4, hard formwork 1 and core rod 3, peel off rubber soft mode 2, get the resin imitated cinerary casket blank;
4. the deburring polishing is decorated: the resin imitated cinerary casket blank is carried out the deburring polishing, at last its outer surface is decorated processing.
In this example, the height of magnesium chloride brine concentration influences the intensity of hardening time and plastid; The height of iron oxide red, iron black content influences the depth of product colour; The water absorption rate that how much directly has influence on product of Lauxite addition; The closely knit number of degrees that how much directly have influence on product of Ludox content; Wood flour plays fibration, also can alleviate product weight simultaneously.
Embodiment of the present invention are a lot, can't be exhaustive, as long as each component thing content within the listed scope of the present invention, all belongs to protection scope of the present invention.
Claims (3)
1. resin imitated cinerary casket, it is formed by rubber soft mode, hard formwork, core rod and collapsible form cast by casting material, and it is characterized in that: the component of described casting material and weight proportion are:
1. concentration is the magnesium chloride brine 25～42 of 20～30 degree (measuring with gravimeter);
2. magnesium oxide 35～65; 3. iron sesquioxide (iron oxide red) 0～2.5; 4. ferroso-ferric oxide (iron oxide black) 0～2.5;
5. Lauxite 0～8; 6. Ludox 0～8; 7. wood flour 0～5.
2. according to the described resin imitated cinerary casket of claim 1, it is characterized in that: the component of described casting material and weight proportion are:
1. concentration is the magnesium chloride brine 30～35 of 22～26 degree (measuring with gravimeter);
2. magnesium oxide 40～50; 3. iron sesquioxide (iron oxide red) 1～1.5; 4. ferroso-ferric oxide (iron oxide black) 1～1.5;
5. Lauxite 1～5; 6. Ludox 1～5; 7. wood flour 2～3.
3. the manufacture method of described resin imitated cinerary casket is as follows:
(1) preparation of casting material:
1. choose the each component material by above-mentioned weight ratio;
2. add Lauxite, Ludox in the magnesium chloride brine and stir;
3. powder magnesium oxide, iron oxide red, iron oxide black and wood flour are mixed and stir;
4. the solution that 2. step is obtained is poured in the mixture that 3. step obtain, and fully stirs, material to be cast;
(2) pouring procedure:
1. the making of mould: make the rubber soft mode (2) of predetermined moulding, make hard core rod (3), formwork (1) and collapsible form (4) according to rubber soft mode (2) again;
2. mould is installed, and formwork (1), core rod (3) are accurately located, and rubber soft mode (2) is placed between formwork (1) and the core rod (3);
3. the cast: with casting material from injection rubber soft mode suitable for reading (2), rubber soft mode this moment (2) is limited by hard formwork (1) and core rod (3), casting material enters between rubber soft mode (2) and the core rod (3), cover collapsible form (4), unnecessary casting material then overflows from collapsible form (4) and hard formwork (1) junction, manual with unnecessary casting material removal, and make collapsible form (4) and hard formwork (1) be maintained fixed state, after making casting material in die cavity, solidify 0.5～5 hour, remove collapsible form (4), hard formwork (1) and core rod (3), peel off rubber soft mode (2), get the resin imitated cinerary casket blank;
4. the deburring polishing is decorated: the resin imitated cinerary casket blank is carried out the deburring polishing, at last its outer surface is decorated processing.