CN101113082A - Aluminous cement containing nano calcium carbonate and preparation method thereof - Google Patents
Aluminous cement containing nano calcium carbonate and preparation method thereof Download PDFInfo
- Publication number
- CN101113082A CN101113082A CNA200710054709XA CN200710054709A CN101113082A CN 101113082 A CN101113082 A CN 101113082A CN A200710054709X A CNA200710054709X A CN A200710054709XA CN 200710054709 A CN200710054709 A CN 200710054709A CN 101113082 A CN101113082 A CN 101113082A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- aluminous cement
- nano
- calcium
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to calcium aluminate cement containing nanometer-sized calcium carbonate and a preparation method thereof. The preparation method of the calcium aluminate cement containing nanometer-sized calcium carbonate is based on calcium aluminate used in prior refractory material by adding nano calcium carbonate powder and alumina micropowder. The invention solves the shortcoming of low mid-temperature strength in prior calcium aluminate, and particularly greatly improves the strength around 800 DEG C. The monolithic refractory containing the combined nanometer-sized calcium carbonate has a small change in cold strength under 800 DEG C and 1600 DEG C burning, and the strength of the cold state and the hot state is greatly increased compared with that of prior ordinary monolithic refractory containing the same quantity of CaO made by combining calcium aluminate cement. The invented nanometer-sized calcium aluminate cement containing calcium carbonate can be broadly used in producing refractory material such as refractory casting material, spray material, etc., and can greatly improve mid-temperature strength of material.
Description
Technical field
The invention belongs to technical field of inorganic nonmetallic materials.It specifically is a kind of aluminous cement that contains nano-calcium carbonate and preparation method thereof.
Background technology
Aluminous cement is a kind of inorganic nonmetal gelled materials, be that the raw material that contains calcium oxide with salic raw material such as bauxitic clay, red bauxite or commercial alumina and Wingdale etc. is a main raw material, through oversintering or fusion, make through breaking pulverizing and fine grinding, its essential mineral is a calcium aluminate (CA) and/or two calcium aluminate (CA mutually again
2).Aluminous cement is mostly with sintering process production, and small amounts aluminium content is higher than 70% high purity aluminic acid calcium cement and produces with the electric smelting method.Aluminous cement is generally classified by alumina content, and China is divided into common aluminous cement (Al with it
2O
353%～72%, CaO 21%～35%, is luminite cement again) and pure calcium aluminate cement (Al
2O
372%～82%, CaO 19%～23%) two big classes, they are collectively referred to as refractory cements again.
Aluminous cement has higher refractoriness (generally be higher than 1380 ℃, some even reach 1770 ℃), does not contain SiO substantially
2So high temperature can not form the Calucium Silicate powder salt after burning, and can not occur because of C
2The S crystal formation transforms and causes serious volume change.Therefore aluminous cement is widely used as wedding agent at refractories industry, is used to prepare clay matter, high alumina matter, mullite, corundum matter, contains chrome corundum and spinel refractory castable, jetting material and mending material.
Aluminous cement in use produces bonding strength owing to aquation and sclerosis.Its aquation and sclerosis mainly are CA and CA
2The crystalline growth process of aquation and hydrate thereof, hydrated product change to some extent with the difference of curing condition, and normal temperature generates CaOAl down
2O
310H
2O, 2CaOAl
2O
38H
2O and Al (OH)
3CaOAl in hygrothermal environment
2O
310H
2O and 2CaOAl
2O
38H
2O is converted into 3CaOAl quickly
2O
36H
2O; 3CaOAl
2O
36H
2O is an equiaxed crystal, CaOAl
2O
310H
2O and 2CaOAl
2O
38H
2O is a hexagonal system, and crystal in the form of sheets or needle-like.Sheet, the needle crystal that generates during hydrated cementitious is interlaced, overlapping, seek connections with, and forms strong aggregate, Al (OH)
3Colloid is filled in the space between crystal, forms fine and close structure, thereby makes cement obtain very high physical strength.Therefore the mould material, jetting material etc. of making wedding agent with aluminous cement have good normal temperature performance.But because the calcium aluminate hydrate is destroyed the hydration key in dehydration and decomposition course, sheet originally, needle-shaped crystal structure will not exist; Simultaneously be converted into highdensity hydrate or anhydrous mineral by low-density hydrate, molecular volume reduces, the space increases, and does not produce as yet in middle thermophase (800 ℃～1100 ℃) nodulizing, therefore can cause aluminous cement obviously to descend in the intensity of this temperature under the stage in conjunction with mould material.When treatment temp was higher, material is sintering and produce ceramic combination progressively, and intensity improves again.When the preparation mould material, add the appropriate amount of alumina micro mist itself and cement are reacted, generate CA and CA
2, can overcome the wherein problem of warm strength degradation to a certain extent.But cement bonded mould material is burnt back intensity with its normal temperature strength and high temperature and is compared, and medium temperature intensity is still lower, and then in use produces problem such as peel off.Thereby, be necessary further to improve aluminous cement, improving wherein warm nature energy, and then improve its result of use and life-span.
Summary of the invention
The object of the invention is just at existing problem in the above-mentioned prior art and a kind of aluminous cement that contains nano-calcium carbonate of special development and preparation method thereof.
Characteristics of the present invention are to utilize the nano-calcium carbonate powder granularity tiny, its degradation production calcium oxide is active high, generating calcium aluminate with the aluminum oxide reaction in is advantages such as high-melting-point mineral, improve the low shortcoming of aluminous cement medium temperature intensity, prepare a kind of novel aluminous cement that contains nano-calcium carbonate.
The objective of the invention is to be achieved through the following technical solutions: the aluminous cement that contains nano-calcium carbonate of the present invention is characterized in that: be added with nano-calcium carbonate calcium powder and active oxidation aluminium powder in aluminous cement.
In the present invention, the quality proportioning between aluminous cement, nano-calcium carbonate calcium powder and the active oxidation aluminium powder three is: aluminous cement: the nano-calcium carbonate calcium powder: active oxidation aluminium powder=1: 0.1～0.7: 0.1～1.
Nano-calcium carbonate of the present invention is a hydrophilic lime carbonate, its granularity＜100nm, CaCO
3Quality percentage composition＞95.0%; The chemical ingredients of used active oxidation aluminium powder requires Al
2O
3〉=98.5%, mean particle size requires less than 5 μ m; Used aluminous cement is the used aluminous cement of present field of inorganic materials, Al
2O
3Content is 53%～82%.
Used nano-calcium carbonate is the commercial goods, increases the cost of ortho-aluminic acid calcium cement after the adding hardly.
The preparation method who contains the aluminous cement of nano-calcium carbonate of the present invention is: make it even nano-calcium carbonate calcium powder, active oxidation aluminium powder and aluminous cement thorough mixing according to described ratio, get final product.Can mix by 1～8 hour ball milling.Also can directly add the common ball milling of nano-calcium carbonate and activated alumina in proportion to requiring granularity, mixing and get final product in the levigate stage in the later stage of aluminous cement production.
Activated alumina micro mist add-on is adjusted according to the variation of nano-calcium carbonate powder add-on, so that aluminous cement finally meets the requirements of CaO content and appropriate C aO and Al
2O
3Ratio.
The present invention has the following advantages:
1, the nano-calcium carbonate granularity is little, and (about 690 ℃) begin to decompose under lower temperature, decompose fully basically in the time of 800 ℃.Decomposing the calcium oxide granularity that produces is nano level, has very high specific surface area and reactive behavior, the aluminum oxide reaction during heating and in the aluminous cement, and progressively generating calcium aluminate under differing temps is mineral CA, CA
2And CA
6, produce the reaction in combination.This reaction process is attended by volumetric expansion, thereby compensated the contraction that produces because of hydrated product dehydration, make aluminous cement under 800 ℃, have very high intensity (comprising cold strength and hot strength), until 1400 ℃, its intensity remains unchanged substantially in whole temperature-rise period.Compare with the aluminous cement that does not contain nano-calcium carbonate, the intensity between its 800 ℃～1400 ℃ is greatly improved, and increases with the increase increase rate of nano-calcium carbonate add-on.
When 2, being used to prepare refractory castable, the aluminous cement that contains nano-calcium carbonate with have identical mineral facies after present aluminous cement high temperature burns.But because nano-calcium carbonate generates the calcium oxide that granularity is tiny, be more evenly distributed, it generates equally distributed new ore deposit mutually with reaction such as aluminum oxide, make material structure more even, thereby its intensity is also far above the aluminous cement bonded refractory materials of identical calcium oxide content.
3, manufacture craft is simple, whole technological process does not need cost and complex equipment, has kept the production technique of existing aluminous cement, just adds certain amount of nano lime carbonate and activated alumina in producing later stage or finished product, mix and get final product, be suitable for large-scale industrial production.
4, the used nano-calcium carbonate calcium source of the present invention is easy, and large-scale industrial production, and price is lower, does not increase the cost of present aluminous cement.
Embodiment
Characteristics of the present invention are especially to improve the low shortcoming of its medium temperature intensity by introducing the performance that nano-calcium carbonate improves present aluminous cement.The adding of nano-calcium carbonate does not change present calcium aluminate Cement Production technology, just at manufacture of cement later stage shredding stage or producing and add certain amount of nano lime carbonate in the good cement and mix and get final product.The present invention is actually a kind of method of improving present cement performance, a kind of aluminous cement with calcium oxide content about 30% is an example below, design of the present invention and characteristics are described, but do not think that the present invention only limits to material and the composition that relates among the following embodiment.
Raw materials used is aluminous cement (Al
2O
369.4wt%, CaO 29.8wt%), alumina powder (Al
2O
398.5wt%) and nano-calcium carbonate (CaO 54.0wt%).
Embodiment 1: aluminous cement, nano-calcium carbonate and alumina powder through 1 hour ball milling mixing of ball milling, obtain CaO 29.3wt% Al according to 1: 0.1: 0.1 quality proportioning
2O
3The aluminous cement of 66.0wt%.
Embodiment 2: aluminous cement, nano-calcium carbonate and alumina powder through 4 hours ball milling mixings of ball milling, obtain CaO 30.7wt% Al according to 1: 0.3: 0.2 quality proportioning
2O
3The aluminous cement of 59.4wt%.
Embodiment 3: aluminous cement, nano-calcium carbonate and alumina powder through 8 hours ball milling mixings of ball milling, obtain CaO 32.2wt% Al according to 1: 0.7: 0.4 quality proportioning
2O
3The aluminous cement of 51.8wt%.
Embodiment 4: aluminous cement, nano-calcium carbonate and alumina powder through 2 hours ball milling mixings of ball milling, obtain CaO 20.7wt% Al according to 1: 0.1: 0.6 quality proportioning
2O
3The aluminous cement of 75.6wt%.
Embodiment 5: aluminous cement, nano-calcium carbonate and alumina powder through 7 hours ball milling mixings of ball milling, obtain CaO 22.7wt% Al according to 1: 0.5: 0.5 quality proportioning
2O
3The aluminous cement of 67.2wt%.
Claims (7)
1. an aluminous cement that contains nano-calcium carbonate is characterized in that: be added with nano-calcium carbonate calcium powder and active oxidation aluminium powder in aluminous cement.
2. the aluminous cement that contains nano-calcium carbonate according to claim 1 is characterized in that: the quality proportioning between aluminous cement, nano-calcium carbonate calcium powder and the active oxidation aluminium powder three is: aluminous cement: the nano-calcium carbonate calcium powder: active oxidation aluminium powder=1: 0.1～0.7: 0.1～1.
3. the aluminous cement that contains nano-calcium carbonate according to claim 1 and 2 is characterized in that: nano-calcium carbonate is a hydrophilic lime carbonate, its granularity＜100nm, CaCO
3Quality percentage composition＞95.0%.
4. the aluminous cement that contains nano-calcium carbonate according to claim 1 and 2 is characterized in that: the chemical ingredients of used active oxidation aluminium powder requires Al
2O
3〉=98.5%, mean particle size requires less than 5 μ m.
5. the aluminous cement that contains nano-calcium carbonate according to claim 1 and 2 is characterized in that: used aluminous cement is the used aluminous cement of present field of inorganic materials, Al
2O
3Content is 53%～82%.
6. one kind according to claim 1 or the 2 described preparation methods that contain the aluminous cement of nano-calcium carbonate, it is characterized in that: make it even nano-calcium carbonate calcium powder, active oxidation aluminium powder and aluminous cement thorough mixing according to described ratio, be product of the present invention.
7. one kind according to claim 1 or the 2 described preparation methods that contain the aluminous cement of nano-calcium carbonate, it is characterized in that: directly add nano-calcium carbonate and activated alumina and thorough mixing in proportion in the levigate stage in the later stage of aluminous cement production and make it even, promptly make product of the present invention.