CN101104732A - Nylon/acrylonitrile-butadiene-styrene resin mixing material - Google Patents
Nylon/acrylonitrile-butadiene-styrene resin mixing material Download PDFInfo
- Publication number
- CN101104732A CN101104732A CNA200610028938XA CN200610028938A CN101104732A CN 101104732 A CN101104732 A CN 101104732A CN A200610028938X A CNA200610028938X A CN A200610028938XA CN 200610028938 A CN200610028938 A CN 200610028938A CN 101104732 A CN101104732 A CN 101104732A
- Authority
- CN
- China
- Prior art keywords
- nylon
- abs
- butadiene
- acrylonitrile
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Form | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Comparative example 1 |
PA6-2 | 55 | 65 | 75 | 50 | 70 |
ABS-1 | 35 | ||||
ABS-2 | 30 | 25 | 20 | 30 | |
Copolymer 1, S-MI-MAH | 15 | 10 | 5 | 2 | |
Multipolymer 2, S-MI | 13 | ||||
Oxidation inhibitor 1098 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
Performance | |||||
Tensile strength, MPa | 49.5 | 52.4 | 54.1 | 51.3 | 42.3 |
Elongation at break, % | 90 | 62 | 40 | 88 | 45 |
Flexural strength, MPa | 68.5 | 70.2 | 72.6 | 70.5 | 65.3 |
Modulus in flexure, MPa | 1900 | 2010 | 2080 | 2000 | 1740 |
The Izod notched Izod impact strength, J/m | 920 | 760 | 470 | 520 | 160 |
Vicat softening temperature, ℃ | 122 | 130 | 146 | 127 |
Form | Comparative example 2 | Embodiment 5 | Embodiment 6 | Embodiment 7 | Embodiment 8 | Embodiment 9 |
PA6-1 | 65 | 65 | ||||
PA6-2 | 65 | 65 | 80 | |||
PA6-3 | 65 | |||||
ABS-1 | 25 | |||||
ABS-2 | 25 | 25 | ||||
ABS-3 | 25 | 10 | ||||
ABS-4 | 25 | |||||
S-MI-MAH | 10 | 10 | 10 | 10 | 10 | 10 |
Oxidation inhibitor 1098 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
Performance | ||||||
Melt flow rate (MFR), g/10min | 43 | 32 | 32 | 12 | 24 | 26 |
Tensile strength, MPa | 54.4 | 54.6 | 52.6 | 52.5 | 49.1 | 58.3 |
Elongation at break, % | 32 | 48 | 50 | 60 | 40 | 90 |
Flexural strength, MPa | 73.2 | 73.5 | 71.5 | 70.5 | 71.6 | 75.3 |
Modulus in flexure, MPa | 2210 | 2100 | 2000 | 1980 | 2000 | 2240 |
The Izod notched Izod impact strength, J/m | 310 | 520 | 820 | 1040 | 980 | 500 |
Vicat softening temperature, ℃ | 136 | 130 | 126 | 128 | 116 | 137 |
Claims (4)