CN101100358A - Process for preparing toughened interlayer glass - Google Patents
Process for preparing toughened interlayer glass Download PDFInfo
- Publication number
- CN101100358A CN101100358A CNA2006100285340A CN200610028534A CN101100358A CN 101100358 A CN101100358 A CN 101100358A CN A2006100285340 A CNA2006100285340 A CN A2006100285340A CN 200610028534 A CN200610028534 A CN 200610028534A CN 101100358 A CN101100358 A CN 101100358A
- Authority
- CN
- China
- Prior art keywords
- glass
- high pressure
- sheet
- tempering
- toughened
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention relates to an armoured glass sheet with intermediate film between two glass sheets. The production procedures are: first, plate-glass is placed in tempering furnace for preheating, then high temperature formations and tempering treatment, cooling, washing, combining two plate-glass together; after that proceeding vacuum pre-pressing, high pressure pressing to obtain final products. Compared with prior art produced glass, this inventive armoured glass has advantages of: when the glass is broken into pieces, due to collision, all of the pieces are adhered onto the intermediate film, no flying-off of broken glass pieces occurs, so the automobile can be driven continuously with safety.
Description
Technical field
The present invention relates to the manufacture method of glasswork, relate in particular to a kind of manufacture method of automotive glass plate.
Background technology
Vehicle glass is the important component part of automobile, and vehicle glass comprises windshield glass, crosswind retaining glass, rear windshield glass etc. according to the position difference of automobile of living in; These windshields have different functions, and in order to satisfy these different functional requirements, they adopt laminated glass, toughened glass, double glazing, bound edge glass, sound-insulating and heat-insulating glass and heating glass etc. respectively; These vehicle glasses all are to come machine-shaping by sheet glass according to the shape requirement of automobile, and the glass that uses on the automobile all is shatter proof glass at present, and shatter proof glass has toughened glass and laminated glass two big classes.And automobile side window glass mainly is a toughened glass, and under can being scattered from vehicle window after fragmentation, under mal-conditions such as sleet, strong wind, automobile is inconvenient to travel.
Summary of the invention
Purpose of the present invention is exactly to provide a kind of fragment can not spill for the defective that overcomes above-mentioned prior art existence, the manufacture method of the toughened interlayer glass that security improves greatly.
Purpose of the present invention can be achieved through the following technical solutions: a kind of manufacture method of toughened interlayer glass, it is characterized in that, this method comprises following processing step: at first sheet glass is placed on preheating in the annealing furnace, carry out the high-temperature molding tempering then and handle, cool off, wash, close sheet, get product through after vacuumizing first pressing, high pressure again.
Described method specifically comprises following processing step: (1) raw glass last slice, (2) come out of the stove behind stove internal heating to 600～750 ℃, (3) edge forming limit tempering, by air grid blow out high pressure fast freezing air glass is quenched rapidly, the surface forms stress, the inner tension stress that produces, 5～30 seconds tempering time, below the glass cools to 35 after (4) tempering moulding ℃, (5) are sheet down, (6) flowing into washing machine cleans up, (7) and various needed PVB close sheet, (8) lasso vacuumizes first pressing, (9) enter the autoclave high pressure, two sheet glass and PVB are bonded together fully, (10) toughened interlayer glass finished product.
Described finished product is between two blocks of toughened glass intermediate coat to be set, and by first high pressure integrator.
Compared with prior art, the present invention is owing to be folded with intermediate coat between two toughened glass, after its fragmentation, fragment can be adsorbed on the intermediate coat securely, still is bonded on the vehicle window by intermediate coat, and fragment can not spill, automobile can continue to run at high speed, and security improves greatly.
Embodiment
A kind of manufacture method of toughened interlayer glass, this method comprises following processing step: at first prepare two blocks of simple glasses, place it in preheating in the annealing furnace, carry out the high-temperature molding tempering then and handle, cool off, wash, close sheet, get product through after vacuumizing first pressing, high pressure again.The present invention clips together two toughened glass by intermediate coat, after its fragmentation, fragment can be adsorbed on the intermediate coat securely, still is bonded on the vehicle window by intermediate coat, and security improves greatly, and fragment can not spill, and automobile can continue to run at high speed.
Embodiment 1
A kind of manufacture method of toughened interlayer glass, this method comprises following processing step: (1) raw glass last slice, (2) come out of the stove behind stove internal heating to 600～750 ℃, (3) edge forming limit tempering (by air grid blow out high pressure fast freezing air glass is quenched rapidly, the surface forms stress, the inner tension stress that produces, 5～30 seconds tempering time), (4) below the glass cools to 35 after the tempering moulding ℃, (5) are sheet down, and (6) flow into washing machine and clean up, (7) and various needed PVB close sheet, (8) lasso vacuumizes first pressing, and (9) enter autoclave high pressure (two sheet glass and PVB are bonded together fully), (10) toughened interlayer glass finished product.
Claims (3)
1. the manufacture method of a toughened interlayer glass, it is characterized in that, this method comprises following processing step: at first sheet glass is placed on preheating in the annealing furnace, carries out the high-temperature molding tempering then and handle, cool off, wash, close sheet, get product through after vacuumizing first pressing, high pressure.
2. the manufacture method of a kind of toughened interlayer glass according to claim 1, it is characterized in that, described method specifically comprises following processing step: (1) raw glass last slice, (2) come out of the stove behind stove internal heating to 600～750 ℃, (3) edge forming limit tempering, by air grid blow out high pressure fast freezing air glass is quenched rapidly, the surface forms stress, the inner tension stress that produces, 5～30 seconds tempering time, below the glass cools to 35 after (4) tempering moulding ℃, (5) are sheet down, (6) flowing into washing machine cleans up, (7) and various needed PVB close sheet, (8) lasso vacuumizes first pressing, (9) enter the autoclave high pressure, two sheet glass and PVB are bonded together fully, (10) toughened interlayer glass finished product.
3. the manufacture method of a kind of toughened interlayer glass according to claim 1 and 2 is characterized in that, described finished product is between two blocks of toughened glass intermediate coat to be set, and by first high pressure integrator.