CN101088669B - Bronze coated composite iron powder and its production process - Google Patents
Bronze coated composite iron powder and its production process Download PDFInfo
- Publication number
- CN101088669B CN101088669B CN2007100924419A CN200710092441A CN101088669B CN 101088669 B CN101088669 B CN 101088669B CN 2007100924419 A CN2007100924419 A CN 2007100924419A CN 200710092441 A CN200710092441 A CN 200710092441A CN 101088669 B CN101088669 B CN 101088669B
- Authority
- CN
- China
- Prior art keywords
- powder
- bronze
- coated iron
- copper
- iron composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The braze clad iron composite powder is formed through forming cladding braze layer on Cu clad Fe composite powder, and contains Cu 5-50 wt%, Zn 0.05-10 wt% and Fe for the rest. The braze clad iron composite powder is produced through mixing Cu clad Fe composite powder and Cu-Sn alloy powder or Sn powder, reducing adhesion or reducing diffusion in a reducing furnace at temperature of 400-800 deg.c for over 30 min to form cladding Cu-Sn alloy layer on Cu clad Fe composite powder, crushing, sieving, mixing and other steps. The present invention has the advantages of low cost, simple technological process, no environmental pollution, high antioxidant performance, etc.
Description
(1), technical field
The present invention relates to a kind of metal dust and manufacture method thereof, particularly a kind of composite metal powder and manufacture method thereof.
(2), background technology
At present, what be used for that the metal dust of aspects such as oiliness bearing, diamond segment, friction material mainly adopts is copper powder, bronze powder or iron powder, two kinds or the mixed metal powder that all mixes in also useful first three powder, these metal dusts exist following deficiency:
1, copper powder, iron powder are the elemental metals powder, and be in use, as easy as rolling off a log oxidized.
2, the mixed metal powder apparent density that is made of copper powder, bronze powder and iron powder is different, is prone to segregation during mixing, and the result of segregation will have a strong impact on the quality of product.
3, the cost of raw material of copper powder, bronze powder is very high, and its price is general per ton about 80,000 yuans.
Since above-mentioned, cause the product price of producing with these metal dusts very high, and also very easy oxidized, the product quality after the oxidation is very poor, and is fragile, and service life is short.
In order to address the above problem, relevant technologies personnel have developed copper-coated iron composite powder, this composite powder has the low advantage of cost, but exist powder self antioxygenic property poor, though the technical staff has carried out anti-oxidation processing to it, but in the process of producing product, its antioxygenic property is destroyed again, makes product still oxidized easily with this powder.
Therefore, produce a kind of with low cost, good metal dust of self antioxygenic property and have vast market prospect.Copper alloy has the good advantage of self antioxygenic property, relevant technologies personnel attempt directly to be coated on the surface of ferrous powder granules with copper alloy, as: the patent of invention that a kind of name is called " composite metal powder for powder metallurgy " is disclosed in CN1180904C, it is to form the copper of 5 weight %-75 weight % or the composite metal powder for powder metallurgy of copper alloy clad on iron powder, the calcium content that is contained in the iron powder as raw meal≤0.06 weight % wherein, the calcium content in this composite metal powder≤0.02 weight %.This patent disclosure one Albatra metal-iron clad composite powder, in fact because iron and copper or copper alloy do not dissolve each other each other, can not spread each other between iron and copper or the copper alloy, therefore, with the mode of physics, it is impracticable at all directly copper alloy being coated on the ferrous powder granules.
(3), summary of the invention
First purpose of the present invention just provides a kind of bronze-coated iron composite powder, and it is not only with low cost, and has very strong self antioxygenic property, belongs to non-harmful product.
Of the present invention second and third, four purposes just provide a kind of manufacture method of bronze-coated iron composite powder of production above-mentioned purpose, this method production technology is simple, production cost is low, the waste discharge of nonpollution environment belongs to non-harmful production method.
First purpose of the present invention is to realize by such technical scheme, it is the composite metal powder that forms the signal bronze clad on copper-coated iron composite powder, wherein, copper accounts for the 5%-50% of described composite metal powder gross weight, tin accounts for the 0.05%-10% of described composite metal powder gross weight, and surplus is an iron.
Bronze is exactly a signal bronze.Bronze-coated iron composite powder of the present invention is to be that core, intermediate layer are that copper, skin are the composite metal powder of the three-decker of signal bronze with iron.According to existing technology, it is impracticable directly signal bronze being coated on the ferrous powder granules, its reason is: copper, tin, signal bronze are all and immiscible between the iron, copper, tin, signal bronze both be difficult to stick on the ferrous powder granules with physics mode, also be difficult to and iron powder between diffusion each other, form iron-copper, ferro-tin alloy or iron signal bronze.Allow iron powder be coated on technical barrier in the signal bronze in order to solve, can only on the iron powder surface, coat one deck copper film with chemical mode, form copper-coated iron composite powder, the production method of copper-coated iron composite powder belongs to existing mature technology, because copper and tin, dissolve each other each other between the signal bronze, therefore, just can adopt physics mode that the signal bronze powder is adhered on the copper-coated iron composite powder surface, also tin can be spread in the copper film of copper-coated iron composite powder from outside to inside, make the outer signal bronze that forms of copper film, internal layer remains the copper layer, thereby obtains bronze-coated iron composite powder.
Because signal bronze self has stronger antioxygenic property, therefore, resulting bronze-coated iron composite powder does not need to carry out anti-oxidant treatment again, just has good antioxygenic property, and with the product that it is produced, antioxygenic property also is significantly improved.Compare with bronze powder,, not only can keep the physical property of bronze powder, also have the performance of the intensity of iron, and significantly reduced manufacturing cost owing to be primary raw material with iron mainly in the bronze-coated iron composite powder.
Second purpose of the present invention is to realize by following step:
(1), the signal bronze powder that in copper-coated iron composite powder, adds described ratio, abundant mixing, send into then and reduce adhesion in the reduction furnace of band reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time that reduction adheres to is no less than 30 minutes, the signal bronze powder is adhered on the surface of copper-coated iron composite powder, form the signal bronze clad, that is: bronze-coated iron composite powder; Stanniferous is lower than the fusing point of 20% signal bronze in 900 ℃ of-1083 ℃ of scopes, therefore, in 400 ℃ of-800 ℃ of scopes, signal bronze in the reduction furnace still is in solid-state, the contact-making surface of the copper on signal bronze and copper-coated iron composite powder surface spreads each other, and signal bronze is sticked on the surface of copper-coated iron composite powder.Because metal dust is in production or transportation, all can there be oxidation in various degree on the surface, generates oxide, and the metal that has oxide is difficult to adhere to each other each other, has only pure metal surface could adhere to each other well under high temperature action.Therefore, the purpose that copper-coated iron composite powder, signal bronze powder are sent in the reduction furnace after mixing together is exactly the oxide generation chemical reaction that makes the metal surface, seize the oxygen in the oxide, the surface that makes metal dust is pure, under corresponding high temperature action, the signal bronze powder is sticked on the surface of copper-coated iron composite powder securely.
(2), the bronze-coated iron composite powder that reduction adhesion back is generated carries out fragmentation, screening;
(3), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
The 3rd purpose of the present invention is to realize by following step:
(1), the glass putty that in copper-coated iron composite powder, adds described ratio, abundant mixing, send into then and reduce diffusion in the reduction furnace of band reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time of reduction diffusion was at 30 minutes-120 minutes, glass putty is diffused in the copper layer of copper-coated iron composite powder, and making the copper layer form the outside is that signal bronze, inboard are the composite bed of copper, that is: bronze-coated iron composite powder; Because the fusing point of tin is 232 ℃, therefore, under 400 ℃ of-800 ℃ of temperature actions, tin in the reduction furnace is in liquid state, liquid tin spreads from the copper film surface ecto-entad of copper-coated iron composite powder, in 30 minutes-120 minutes time, makes the outer signal bronze that forms of copper film, internal layer remains copper, thereby obtains bronze-coated iron composite powder.Another effect that copper-coated iron composite powder, Sillim's powder are sent in the reduction furnace after mixing together is exactly the oxide generation chemical reaction that makes the metal surface, seize the oxygen in the oxide, the surface that makes metal dust is pure, under corresponding high temperature action, glass putty is diffused in the copper film of copper-coated iron composite powder better.
(2), the bronze-coated iron composite powder that reduction diffusion back is generated carries out fragmentation, screening;
(3), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
The 4th purpose of the present invention is to realize by following step:
(1) transfers to 0.1~5 with copper sulphate and stannous sulfate dissolving, and with the copper sulphate of dissolving and the pH value of stannous sulfate solution;
(2) under stirring, add reduced iron powder rapidly, continue to stir 1~10 minute, the copper that chemical replacement reflects is coated on the surface of ferrous powder granules fully, promptly form copper-coated iron composite powder, tin and copper-coated iron composite powder that displacement reaction goes out mix, and form metal powder mixture;
(3) allow metal powder mixture separate, wash metal powder mixture with clear water with reaction liquid, make it no acidic till;
(4) metal powder mixture after washing is delivered to centrifuge and is dewatered, send into then and dry, reduce diffusion in the reduction furnace of being with reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time of reduction diffusion was at 30 minutes-120 minutes, glass putty is diffused in the copper layer of copper-coated iron composite powder, making and forming the outside in the copper layer is that signal bronze clad and inboard are the composite bed of copper layer, that is: bronze-coated iron composite powder;
(5), the bronze-coated iron composite powder that reduction diffusion back is generated carries out fragmentation, screening;
(6), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
What the present invention mainly adopted is the chemical replacement method, according to electrochemical principle, reduced iron powder is mixed mutually with, copper sulphate and stannous sulfate solution, and following chemical reaction can take place, and its reaction equation is as follows:
Fe+CuSO
4=======Cu+FeSO
4
Fe+SnSO
4=======Sn+FeSO
4
In the method:
1, the pH value of adjusting copper sulphate and stannous sulfate solution is 0.1-5, make it to be acid solution, its effect is: in copper sulphate and stannous sulfate solution and process that iron powder mixes mutually, because the effect of acid solution, the lip-deep oxide of iron powder is corroded, make the iron powder surface purer, the copper that cements out can be coated on the surface of iron powder rapidly, evenly, securely.
2, the copper that comes out of displacement reaction evenly, closely is coated on the surface of iron powder, forms copper-coated iron composite powder; The tin that displacement reaction is come out can not stick on the iron powder surface, exists in solution with the form of tin atom, and mixes with the copper-coated iron composite powder that generates, and constitutes metal powder mixture.
3, the effect of the mixture of tin and copper-coated iron composite powder being delivered to reduction furnace has following three:
(1), under high temperature action, tin and copper-coated iron composite powder are dried.
(2), in the step in front, because tin, copper-coated iron composite powder all will contact with water, air, there is oxidation in various degree on its surface and the oxide that generates, in reduction furnace, make the oxide generation chemical reaction of metal surface, seize the oxygen in the oxide, make the surface of metal dust purer.
(3), because 232 ℃ of the fusing points of tin, therefore, under 400 ℃ of-800 ℃ of temperature actions, tin in the reduction furnace is in liquid state, liquid tin spreads from the copper film surface ecto-entad of copper-coated iron composite powder, in 30 minutes-120 minutes time, makes the outer signal bronze that forms of copper film, internal layer remains copper, thereby obtains bronze-coated iron composite powder.Because tin is cemented out by chemical reaction, therefore, the granularity of tin is minimum, makes diffusion effect more remarkable.
Since adopted technique scheme, bronze-coated iron composite powder of the present invention to have with low cost and very strong self antioxygenic property, the genus non-harmful product, production cost per ton is at 2.5 ten thousand yuans, and cost of material is 1/3rd of a bronze powder.The method that the present invention produces bronze-coated iron composite powder has that technology is simple, production cost is low, and the waste discharge of nonpollution environment belongs to non-harmful production method.
(4), the specific embodiment
The invention will be further described below in conjunction with embodiment:
The present invention is the composite metal powder that forms the signal bronze clad on copper-coated iron composite powder, and wherein, copper accounts for the 5%-50% of described composite metal powder gross weight, and tin accounts for the 0.05%-10% of described composite metal powder gross weight, and surplus is an iron.
Bronze is exactly a signal bronze.Bronze-coated iron composite powder of the present invention is to be that core, intermediate layer are that copper, skin are the composite metal powder of the three-decker of signal bronze with iron.According to existing technology, it is impracticable directly signal bronze being coated on the ferrous powder granules, its reason is: copper, tin, signal bronze are all and immiscible between the iron, copper, tin, signal bronze both be difficult to stick on the ferrous powder granules with physics mode, also be difficult to and iron powder between diffusion each other, form iron-copper, ferro-tin alloy or iron signal bronze.Allow iron powder be coated on technical barrier in the signal bronze in order to solve, can only on the iron powder surface, coat one deck copper film with chemical mode, form copper-coated iron composite powder, the production method of copper-coated iron composite powder belongs to existing mature technology, because copper and tin, dissolve each other each other between the signal bronze, therefore, just can adopt physics mode that the signal bronze powder is adhered on the copper-coated iron composite powder surface, also tin can be spread in the copper film of copper-coated iron composite powder from outside to inside, make the outer signal bronze that forms of copper film, internal layer remains the copper layer, thereby obtains bronze-coated iron composite powder.
Because signal bronze self has stronger antioxygenic property, therefore, resulting bronze-coated iron composite powder does not need to carry out anti-oxidant treatment again, just has good antioxygenic property, and with the product that it is produced, antioxygenic property also is significantly improved.Compare with bronze powder,, not only can keep the physical property of bronze powder, also have the performance of the intensity of iron, and significantly reduced manufacturing cost owing to be primary raw material with iron mainly in the bronze-coated iron composite powder.
Bronze-coated iron composite powder of the present invention is to be that core, intermediate layer are that copper, skin are the composite metal powder of the three-decker of signal bronze with iron.The ratio of copper and tin can be allocated according to the needs in market:
In the described composite metal powder, copper accounts for 5% of gross weight, and tin accounts for the 0.05%-0.5% of gross weight, and wherein, tin can account for 0.05% of composite metal powder gross weight, also can account for 0.5% of composite metal powder gross weight.
In the described composite metal powder, copper accounts for 18% of gross weight, and tin accounts for the 0.18%-1.8% of gross weight, and wherein, tin can account for 0.18% of composite metal powder gross weight, also can account for 1.8% of composite metal powder gross weight.Copper accounts for the 18%-22% of gross weight, the 1.8%-2.2% that tin accounts for gross weight, the combination that surplus is iron is a preferred version, and preferred plan is: copper account for gross weight 18%, tin account for gross weight 2%, surplus is iron.
In the described composite metal powder, copper accounts for 50% of gross weight, and tin accounts for the 0.5%-5% of gross weight, and wherein, tin can account for 0.5% of composite metal powder gross weight, also can account for 5% of composite metal powder gross weight.
First kind of manufacture method of bronze-coated iron composite powder of the present invention carried out as follows:
(1), the signal bronze powder that in copper-coated iron composite powder, adds described ratio, abundant mixing, send into then and reduce adhesion in the reduction furnace of band reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time that reduction adheres to is no less than 30 minutes, the signal bronze powder is adhered on the surface of copper-coated iron composite powder, form the signal bronze clad, that is: bronze-coated iron composite powder; Stanniferous is lower than the fusing point of 20% signal bronze in 900 ℃ of-1083 ℃ of scopes, therefore, in 400 ℃ of-800 ℃ of scopes, signal bronze in the reduction furnace still is in solid-state, the contact-making surface of the copper on signal bronze and copper-coated iron composite powder surface spreads each other, and signal bronze is sticked on the surface of copper-coated iron composite powder.Because metal dust is in production or transportation, all can there be oxidation in various degree on the surface, generates oxide, and the metal that has oxide is difficult to adhere to each other each other, has only pure metal surface could adhere to each other well under high temperature action.Therefore, the purpose that copper-coated iron composite powder, signal bronze powder are sent in the reduction furnace after mixing together is exactly the oxide generation chemical reaction that makes the metal surface, seize the oxygen in the oxide, the surface that makes metal dust is pure, under corresponding high temperature action, the signal bronze powder is sticked on the surface of copper-coated iron composite powder securely.
(2), the bronze-coated iron composite powder that reduction adhesion back is generated carries out fragmentation, screening;
(3), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
In the said method, in order to improve the effect of producing product, the signal bronze powder is coated on the copper-coated iron composite powder better, the granularity of signal bronze powder is laminated with the granularity of powder less than copper-clad iron, makes copper tin close powder at least and can be coated on the surface of copper-coated iron composite powder.The granularity of copper-coated iron composite powder can be below 80 orders, little 100 orders of the granularity of the fineness ratio copper-coated iron composite powder of signal bronze powder.The granularity of copper-coated iron composite powder is preferably less than 100 orders, and the granularity of signal bronze powder is preferably less than 300 orders.
Second kind of manufacture method of bronze-coated iron composite powder of the present invention carried out as follows:
(1), the glass putty that in copper-coated iron composite powder, adds described ratio, abundant mixing, send into then and reduce diffusion in the reduction furnace of band reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time of reduction diffusion was at 30 minutes-120 minutes, glass putty is diffused in the copper layer of copper-coated iron composite powder, and making the copper layer form the outside is that signal bronze, inboard are the composite bed of copper, that is: bronze-coated iron composite powder; Because the fusing point of tin is 232 ℃, therefore, under 400 ℃ of-800 ℃ of temperature actions, tin in the reduction furnace is in liquid state, liquid tin spreads from the copper film surface ecto-entad of copper-coated iron composite powder, in 30 minutes-120 minutes time, makes the outer signal bronze that forms of copper film, internal layer remains copper, thereby obtains bronze-coated iron composite powder.Another effect that copper-coated iron composite powder, Sillim's powder are sent in the reduction furnace after mixing together is exactly the oxide generation chemical reaction that makes the metal surface, seize the oxygen in the oxide, the surface that makes metal dust is pure, under corresponding high temperature action, glass putty is diffused in the copper film of copper-coated iron composite powder better.
(2), the bronze-coated iron composite powder that reduction diffusion back is generated carries out fragmentation, screening;
(3), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
The third manufacture method of bronze-coated iron composite powder of the present invention is carried out as follows:
(1) transfers to 0.1~5 with copper sulphate and stannous sulfate dissolving, and with the copper sulphate of dissolving and the pH value of stannous sulfate solution;
(2) under stirring, add reduced iron powder rapidly, continue to stir 1~10 minute, the copper that chemical replacement reflects is coated on the surface of ferrous powder granules fully, promptly form copper-coated iron composite powder, tin and copper-coated iron composite powder that displacement reaction goes out mix, and form metal powder mixture;
(3) allow metal powder mixture separate, wash metal powder mixture with clear water with reaction liquid, make it no acidic till;
(4) metal powder mixture after washing is delivered to centrifuge and is dewatered, send into then and dry, reduce diffusion in the reduction furnace of being with reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time of reduction diffusion was at 30 minutes-120 minutes, glass putty is diffused in the copper layer of copper-coated iron composite powder, making and forming the outside in the copper layer is that signal bronze clad and inboard are the composite bed of copper layer, that is: bronze-coated iron composite powder;
(5), the bronze-coated iron composite powder that reduction diffusion back is generated carries out fragmentation, screening;
(6), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
What the present invention mainly adopted is the chemical replacement method, according to electrochemical principle, reduced iron powder is mixed mutually with, copper sulphate and stannous sulfate solution, and following chemical reaction can take place, and its reaction equation is as follows:
Fe+CuSO
4=======Cu+FeSO
4
Fe+SnSO
4=======Sn+FeSO
4
In the method:
1, the pH value of adjusting copper sulphate and stannous sulfate solution is 0.1-5, make it to be acid solution, its effect is: in copper sulphate and stannous sulfate solution and process that iron powder mixes mutually, because the effect of acid solution, the lip-deep oxide of iron powder is corroded, make the iron powder surface purer, the copper that cements out can be coated on the surface of iron powder rapidly, evenly, securely.
2, the copper that comes out of displacement reaction evenly, closely is coated on the surface of iron powder, forms copper-coated iron composite powder; The tin that displacement reaction is come out can not stick on the iron powder surface, exists in solution with the form of tin atom, and mixes with the copper-coated iron composite powder that generates, and constitutes metal powder mixture.
3, the effect of the mixture of tin and copper-coated iron composite powder being delivered to reduction furnace has following three:
(1), under high temperature action, tin and copper-coated iron composite powder are dried.
(2), in the step in front, because tin, copper-coated iron composite powder all will contact with water, air, there is oxidation in various degree on its surface and the oxide that generates, in reduction furnace, make the oxide generation chemical reaction of metal surface, seize the oxygen in the oxide, make the surface of metal dust purer.
(3), because the fusing point of tin is 232 ℃, therefore, under 400 ℃ of-800 ℃ of temperature actions, tin in the reduction furnace is in liquid state, liquid tin spreads from the copper film surface ecto-entad of copper-coated iron composite powder, in 30 minutes-120 minutes time, makes the outer signal bronze that forms of copper film, internal layer remains copper, thereby obtains bronze-coated iron composite powder.Because tin is cemented out by chemical reaction, therefore, the granularity of tin is minimum, makes diffusion effect more remarkable.
In order to alleviate the oxidized corrosion in the displacement reaction process of iron, copper, tin, in above-mentioned the third step of manufacturing (2), in copper sulphate and stannous sulfate solution, add corrosion inhibiter earlier, and then operate (2) set by step.After adding corrosion inhibiter, can form an adsorption layer in the metal surface, very thin, theoretically, be no more than the thickness of a molecular layer, but can stop the dissolving of metal, slow down and prevent corrosion of metal.The corrosion inhibiter that is added can be the 2-mercapto benzothiazole, also can be sulphur urine, all right copper tin-91, copper tin-the 91st, a kind of brightener.Certainly, corrosion inhibiter of the present invention can also be other any corrosion inhibiter that plays same function.
In order to prolong the storage period of bronze-coated iron composite powder, further strengthen its antioxygenic property, can carry out anti-oxidation processing to the bronze-coated iron composite powder of producing.The method of anti-oxidation processing is: add a spot of corrosion inhibiter in bronze-coated iron composite powder.Corrosion inhibiter can be a benzotriazole, also can zinc stearate, and can also be other any corrosion inhibiter that plays same function.
In the third manufacture method of the present invention, (1), (2) step can adopt the following step that is equal to finish:
(1), with copper sulphate dissolving, and the pH value of the copper-bath of dissolving transferred to 0.1~5, under stirring, add reduced iron powder rapidly, continue to stir 1~10 minute, the copper that chemical replacement reflects is coated on the surface of ferrous powder granules fully, promptly forms copper-coated iron composite powder;
(2), with stannous sulfate dissolving, and the pH value of the stannous sulfate solution of dissolving transferred to 0.1~5, under stirring, add reduced iron powder rapidly, and allow iron powder generation complete reaction, the chemical replacement reaction obtains tin;
(3), the tin that obtains in the copper-coated iron composite powder that obtains in the step (1) and the step (2) is evenly mixed, to obtain metal powder mixture.
The third step of manufacturing of above-mentioned method and the present invention (1), (2) are compared, though change at production order, but essence all is chemical reactions generates copper-coated iron composite powder and tin, the metal powder mixture that is mixed each other, therefore belong to the technological means that is equal to, within the scope of the present invention.
Claims (20)
1. bronze-coated iron composite powder, it is characterized in that: it is the composite metal powder that forms the signal bronze clad on copper-coated iron composite powder, and wherein, copper accounts for the 5%-50% of described composite metal powder gross weight, tin accounts for the 0.05%-10% of described composite metal powder gross weight, and surplus is an iron.
2. bronze-coated iron composite powder as claimed in claim 1 is characterized in that: in the described composite metal powder, copper accounts for 5% of gross weight, and tin accounts for the 0.05%-0.5% of gross weight.
3. bronze-coated iron composite powder as claimed in claim 2 is characterized in that: in the described composite metal powder, tin accounts for 0.05% of composite metal powder gross weight.
4. bronze-coated iron composite powder as claimed in claim 2 is characterized in that: in the described composite metal powder, tin accounts for 0.5% of composite metal powder gross weight.
5. bronze-coated iron composite powder as claimed in claim 1 is characterized in that: in the described composite metal powder, copper accounts for 18% of gross weight, and tin accounts for the 0.18%-1.8% of gross weight.
6. bronze-coated iron composite powder as claimed in claim 5 is characterized in that: in the described composite metal powder, tin accounts for 0.18% of composite metal powder gross weight.
7. bronze-coated iron composite powder as claimed in claim 5 is characterized in that: in the described composite metal powder, tin accounts for 1.8% of composite metal powder gross weight.
8. bronze-coated iron composite powder as claimed in claim 1 is characterized in that: in the described composite metal powder, copper accounts for 50% of gross weight, and tin accounts for the 0.5%-5% of gross weight.
9. bronze-coated iron composite powder as claimed in claim 8 is characterized in that: in the described composite metal powder, tin accounts for 0.5% of composite metal powder gross weight.
10. bronze-coated iron composite powder as claimed in claim 8 is characterized in that: in the described composite metal powder, tin accounts for 5% of composite metal powder gross weight.
11. the manufacture method as claim 1,2,3,4,5,6,7,8,9 or 10 described bronze-coated iron composite powders, its step is as follows:
(1), the signal bronze powder that in copper-coated iron composite powder, adds described ratio, abundant mixing, send into then and reduce adhesion in the reduction furnace of band reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time that reduction adheres to is no less than 30 minutes, the signal bronze powder is adhered on the surface of copper-coated iron composite powder, form the signal bronze clad, that is: bronze-coated iron composite powder;
(2), the bronze-coated iron composite powder that reduction adhesion back is generated carries out fragmentation, screening;
(3), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
12. the manufacture method of bronze-coated iron composite powder as claimed in claim 11 is characterized in that: the granularity of signal bronze powder makes the signal bronze powder can be coated on the surface of copper-coated iron composite powder less than the granularity of copper-coated iron composite powder at least.
13. the manufacture method of bronze-coated iron composite powder as claimed in claim 12 is characterized in that: the granularity of copper-coated iron composite powder below 80 orders, little 100 orders of the granularity of the fineness ratio copper-coated iron composite powder of signal bronze powder.
14. the manufacture method of bronze-coated iron composite powder as claimed in claim 12 is characterized in that: the granularity of copper-coated iron composite powder is less than 100 orders, and the granularity of signal bronze powder is less than 300 orders.
15. the manufacture method as claim 1,2,3,4,5,6,7,8,9 or 10 described bronze-coated iron composite powders, its step is as follows:
(1), the glass putty that in copper-coated iron composite powder, adds described ratio, abundant mixing, send into then and reduce diffusion in the reduction furnace of band reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time of reduction diffusion was at 30 minutes-120 minutes, glass putty is diffused in the copper layer of copper-coated iron composite powder, and making the copper layer form the outside is that signal bronze, inboard are the composite bed of copper, that is: bronze-coated iron composite powder;
(2), the bronze-coated iron composite powder that reduction diffusion back is generated carries out fragmentation, screening;
(3), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
16. the manufacture method as claim 1,2,3,4,5,6,7,8,9 or 10 described bronze-coated iron composite powders, its step is as follows:
(1) transfers to 0.1~5 with copper sulphate and stannous sulfate dissolving, and with the copper sulphate of dissolving and the pH value of stannous sulfate solution;
(2) under stirring, add reduced iron powder rapidly, continue to stir 1~10 minute, the copper that chemical replacement reflects is coated on the surface of ferrous powder granules fully, promptly form copper-coated iron composite powder, tin and copper-coated iron composite powder that displacement reaction goes out mix, and form metal powder mixture;
(3) allow metal powder mixture separate, wash metal powder mixture with clear water with reaction liquid, make it no acidic till;
(4) metal powder mixture after washing is delivered to centrifuge and is dewatered, send into then and dry, reduce diffusion in the reduction furnace of being with reduction, protective atmosphere, temperature is controlled in 400 ℃ of-800 ℃ of scopes in the stove of reduction furnace, the time of reduction diffusion was at 30 minutes-120 minutes, glass putty is diffused in the copper layer of copper-coated iron composite powder, making and forming the outside in the copper layer is that signal bronze clad and inboard are the composite bed of copper layer, that is: bronze-coated iron composite powder;
(5), the bronze-coated iron composite powder that reduction diffusion back is generated carries out fragmentation, screening;
(6), the bronze-coated iron composite powder after the screening is mixed powder, check, metering, packing warehouse-in.
17. the manufacture method of bronze-coated iron composite powder as claimed in claim 16 is characterized in that in the described step (2), add corrosion inhibiter earlier in copper sulphate and stannous sulfate solution, and then operates (2) set by step.
18. the manufacture method of bronze-coated iron composite powder as claimed in claim 17 is characterized in that described corrosion inhibiter is the 2-mercapto benzothiazole.
19. the manufacture method of bronze-coated iron composite powder as claimed in claim 17 is characterized in that described corrosion inhibiter is a sulphur urine.
20. the manufacture method of bronze-coated iron composite powder as claimed in claim 17 is characterized in that described corrosion inhibiter is a copper tin-91.