CN101084805A - Method for manufacturing skating shoe body - Google Patents
Method for manufacturing skating shoe body Download PDFInfo
- Publication number
- CN101084805A CN101084805A CN 200610083875 CN200610083875A CN101084805A CN 101084805 A CN101084805 A CN 101084805A CN 200610083875 CN200610083875 CN 200610083875 CN 200610083875 A CN200610083875 A CN 200610083875A CN 101084805 A CN101084805 A CN 101084805A
- Authority
- CN
- China
- Prior art keywords
- substrate
- masterplate
- moulding
- epoxy resin
- groove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for producing shoe body of skating shoe comprises cutting the sheet into substrate of the shoe casing part, arranging a mould capable of covering on the substrate, arranging coating holes at on the mould at the position according to requirement, coating the surface of the substrate to form reinforce ribs on the substrate, placing the casing part in the stretch, pressurizing, and cooling. The invention has the advantages of good comfortability and compact resistance due to the reinforce ribs integrated on the surface of the casing part, and is suitable for skating shoe for rapid gliding movement.
Description
Technical field
The present invention relates to a kind of manufacture method of skating shoe body.
Background technology
The making of various types ice skates such as fancy ice skate, hockey shoe, skate propulsion mechanisms at present, all be to be appearance with leather, PVC skin, PU skin or textile cloth, add supporting material (as chemical sheet, cloth, leather board etc.) again inside,, become vamp via sewing again to increase the hardness of footwear body, through hanging group's moulding, fitting becomes the footwear body behind the big end, and, nail on skates or wheel forms, or after directly putting into footwear covers, nail on skates or wheel forms with the footwear body shell of ejection formation.
The boots with straight row of rollers of above-mentioned composition or ice skates; be to be applied to the high speed gliding motility or the purposes of competing for speed, it forms structure Design, should with in light weight, intensity and hardness is good attaches most importance to; just can help being engaged in this motion, and could form perfect movement protection for foot.Yet its supporting material is arranged at inside, can't combine with footwear body parts, and the uncomfortable impression that causes supporting material and foot to press close to easily, and it adds supporting material, often causes weight significantly to increase, and is engaged in this motion and be unfavorable for wearing.
Summary of the invention
Technical problem underlying to be solved by this invention is; overcome the above-mentioned defective that prior art exists, and a kind of manufacture method of skating shoe body is provided, it can reach effect in light weight, firm, shock-resistant; and for user foot formation good protection, and be more suitable for gliding motility rapidly.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of manufacture method of skating shoe body is characterized in that, its step comprises: first step, and sheet material cuts, and cuts for the sheet material as each parts of footwear body earlier, makes it can mold the substrate of required form; Second step is made masterplate, is provided with one and can covers the masterplate that overlays on the substrate, and have the position of hardness and intensity according to desiring to form out in each parts of footwear body, at the relative position of masterplate blacking hole is set; Third step, substrate surface privileged site coating is stacking, on substrate, be coated with one deck epoxy resin earlier, treat its dry back and masterplate contraposition, and impose at the blacking hole place of masterplate once to epoxy resin coating repeatedly, make its position that on substrate, will gain in strength, can mold reinforced ribs, and produce the case member of the footwear body that reinforced ribs combines with the substrate one with the stacking thickness of coating; The 4th step, compression molding, with the case member of the above-mentioned footwear body of making, the shoe tree mould of putting into the extrusion forming of wanting pressurizes, treat its cooling after, promptly mold the footwear body structure.
The manufacture method of aforesaid skating shoe body, the case member of the footwear body that wherein forms out can be the footwear body side component of one chip.
The manufacture method of aforesaid skating shoe body, the case member of the footwear body that wherein forms out can be the heel parts of one chip.
The manufacture method of aforesaid skating shoe body wherein can be produced a shoe sole component in the case member, and it is that a molding version is set, and the groove of a sole shape is set in the moulding masterplate, and epoxy resin can be coated in the groove and mold shoe sole component.
The manufacture method of aforesaid skating shoe body, a molding version wherein is set, the groove of one sole shape is set in the moulding masterplate, and the substrate that will cut moulding is put the groove side of moulding masterplate, and in described third step for substrate on coating one deck epoxy resin, even this layer epoxy resin is coated in the groove of moulding masterplate simultaneously, the footwear body side component that shoe sole component and substrate formed out that forms out is combined, and constitute two one patterns.
The manufacture method of aforesaid skating shoe body, a molding version wherein is set, the groove of one sole shape is set in the moulding masterplate, and the substrate that will cut moulding is put the groove side of moulding masterplate, and in described third step for substrate on coating one deck epoxy resin, even this layer epoxy resin is coated in the groove of moulding masterplate simultaneously, the heel parts that shoe sole component and substrate formed out that form out is combined, and constitute two one patterns.
The manufacture method of aforesaid skating shoe body, a molding version wherein is set, the groove of one sole shape is set in the moulding masterplate, and two plate bases that will cut moulding are put groove two sides of moulding masterplate, and in described third step for substrate on coating one deck epoxy resin, even this layer epoxy resin is coated in the groove of moulding masterplate simultaneously, the footwear body side component that shoe sole component and substrate formed out that forms out is combined, and constitute three one patterns.
The manufacture method of aforesaid skating shoe body wherein imposes once to epoxy resin coating repeatedly for substrate in described third step, can add fabric in the coating layer of epoxy resin.
The made footwear body structure of method whereby, can make reinforced ribs one-body molded in the case member of footwear body, make the dress of foot can be more comfortable, and the reinforced ribs of its institute's moulding on demand be positioned at privileged site on the substrate, make the setting of supporting material, meet the requirement of expection, gain in strength and the hardness effect and reach, and, have the firm and impulse-durability effect of light weight, the ice skate that are more suitable for gliding motility are rapidly adopted.
The invention has the beneficial effects as follows that it can reach effect in light weight, firm, shock-resistant, and form good protection, and be more suitable for gliding motility rapidly for user foot.
Description of drawings
The present invention is further described below in conjunction with drawings and Examples.
Fig. 1 is the making flow chart of the inventive method.
Fig. 2 A is that the present invention makes template and at the one chip schematic diagram of substrate surface particular portion with the stacking formation reinforced ribs of coating.
Fig. 2 B is that the present invention makes template and has the in addition one chip schematic diagram of the reinforced ribs of style moulding in the substrate surface particular portion with the stacking formation of coating.
Fig. 3 is the present invention molds reinforced ribs at substrate surface a cutaway view.
Fig. 4 is the present invention molds another content pattern reinforced ribs at substrate surface a cutaway view.
Fig. 5 is that to mold each parts of footwear body be the perspective exploded view of monolithic pattern to the inventive method.
Fig. 6 be the inventive method to mold each parts of footwear body be that shoe sole component and footwear body side component form two one patterns, and with the perspective exploded view of a slice footwear body side component, a slice heel parts.
Fig. 7 be the inventive method to mold each parts of footwear body be that shoe sole component and heel parts form two one patterns, and with two single footwear body side components, and the perspective exploded view of a shoe sole component.
Fig. 8 be the inventive method to mold each parts of footwear body be that shoe sole component and footwear body side component form two one patterns, and with the perspective exploded view of a slice footwear body side component, a slice heel parts.
The number in the figure explanation:
1 footwear body side component 1A heel parts
10 substrates, 11 footwear body parts
20 reinforced ribs, 21 epoxy resin
22 fabrics, 30 shoe sole shells
40 masterplates, 41 blacking holes
A first step B second step
C third step D the 4th step
The specific embodiment
As shown in Figure 1, be the flow chart of the present invention's " manufacture method of skating shoe body ", cooperate and consult Fig. 2 A, shown in Figure 3, wherein, and the present invention's " manufacture method of skating shoe body ", its step comprises:
First step (A), sheet material cuts, and cuts for the sheet material as each parts of footwear body earlier, makes its substrate that can mold required form 10;
Second step (B) is made masterplate 40, is provided with one and can covers the masterplate 40 that overlays on the substrate 10, and have the position of hardness and intensity according to desired forming out in each parts of footwear body, at the relative position of masterplate blacking hole 41 is set;
Third step (C), substrate 10 surperficial privileged site coating are stacking, on substrate 10, be coated with one deck epoxy resin 21 earlier, treat its dry back and masterplate 40 contrapositions, and impose at blacking hole 41 places of masterplate 40 once to epoxy resin 21 coatings repeatedly, make its position that on substrate 10, will gain in strength, can mold reinforced ribs 20, and produce the case member of the footwear body that reinforced ribs 20 combines with substrate 10 one with the stacking thickness of coating.
The case member of the footwear body that it formed out can be one chip or multiple-piece, its one chip is the side component of footwear body shown in Fig. 2 A 1, or the footwear body parts 11 shown in Fig. 2 B, its multiple-piece footwear body side component 1 and heel parts 1A as shown in Figure 5, all can be by above-mentioned steps moulding in addition, and 30 of shoe sole components can be one-body molded by epoxy resin.
The 4th step (D), compression molding, with the case member of the above-mentioned footwear body of making, after the combination of monolithic or multiple-piece sewing, the shoe tree mould of putting into the extrusion forming of wanting pressurizes, treat that it cools off after, promptly mold the footwear body structure.
In the above-mentioned first step (A), substrate 10 materials can be the preimpregnation cloth that PU skin or fabric comprise carbon fiber and various fabrics.
On the footwear body parts 11 shown in above-mentioned Fig. 2 B air-vent 12 can be set, the dress after making footwear body formed has air permeable effect.
In the above-mentioned third step (C), can add fabric 22 or supporting material in the coating layer of epoxy resin 21, for example parts of ejection formation or metal reinforcement sheet as shown in Figure 4, and can form the reinforced ribs 20 of another content pattern.
The above-mentioned footwear body structure that forms out can with resilient protective material such as sponge, PU foaming material fit form inside sewing after; remove to engage toe-cap; and heat, put into shoe tree again, hang group or straight forming, at the bottom of the subsides after, then plasticly go out skating shoe footwear body structure.
Again, footwear body of the present invention is made, and the shoe sole component 30 that made comes out in its case member is that a molding version is set, and the groove of a sole shape is set in the moulding masterplate, molds shoe sole component 30 in the groove and epoxy resin can be coated.
Described shoe sole component 30 can be one-body molded with footwear body side component 1, cooperation is consulted shown in Figure 6, and constitute two one patterns, wherein, the substrate 10 that cuts moulding can be put the groove side of moulding masterplate, and in third step (C) for substrate 10 on during coating one deck epoxy resin 21, even this layer epoxy resin 21 is coated in the groove of moulding masterplate simultaneously, the shoe sole component 30 that forms out can be combined with footwear body side component 1, and when carrying out the 4th step (D), equally can be with each housing department of the footwear body that forms out, comprise that the shoe tree mould that the footwear body side component 1 of a heel parts 1A and another one chip is put into the extrusion forming of wanting pressurizes, after treating its cooling, and mold the footwear body structure.
Cooperate and consult Fig. 7 and shown in Figure 8, it equally can be by said method, heel parts 1A and shoe sole component 30 is one-body molded, and constitute two one patterns, or with two one chip footwear body side components 1 in third step (C) for substrate 10 on during coating one deck epoxy resin 21, two plate bases 10 are placed on the groove both sides of the moulding masterplate of sole, and make the coating of epoxy resin 21, can be coated on simultaneously in the groove of moulding masterplate of sole, two footwear body side components 1 can be combined with shoe sole component 30, and constitute three one patterns, the shoe tree mould of putting into the extrusion forming of wanting with the heel parts 1A of one chip pressurizes again, after treating its cooling, promptly mold the footwear body structure.
Claims (8)
1. the manufacture method of a skating shoe body is characterized in that, its step comprises:
First step, sheet material cuts, and cuts for the sheet material as each parts of footwear body earlier, makes it can mold the substrate of required form;
Second step is made masterplate, is provided with one and can covers the masterplate that overlays on the substrate, and have the position of hardness and intensity according to desiring to form out in each parts of footwear body, at the relative position of masterplate blacking hole is set;
Third step, substrate surface privileged site coating is stacking, on substrate, be coated with one deck epoxy resin earlier, treat its dry back and masterplate contraposition, and impose at the blacking hole place of masterplate once to epoxy resin coating repeatedly, make its position that on substrate, will gain in strength, can mold reinforced ribs, and produce the case member of the footwear body that reinforced ribs combines with the substrate one with the stacking thickness of coating;
The 4th step, compression molding, with the case member of the above-mentioned footwear body of making, the shoe tree mould of putting into the extrusion forming of wanting pressurizes, treat its cooling after, promptly mold the footwear body structure.
2. the manufacture method of skating shoe body according to claim 1 is characterized in that the case member of the described footwear body that forms out, and can be the footwear body side component of one chip.
3. the manufacture method of skating shoe body according to claim 1 is characterized in that the case member of the described footwear body that forms out, and can be the heel parts of one chip.
4. the manufacture method of skating shoe body according to claim 1, it is characterized in that to produce a shoe sole component in the described case member, it is that a molding version is set, and the groove of a sole shape is set in the moulding masterplate, and epoxy resin can be coated in the groove and mold shoe sole component.
5. the manufacture method of skating shoe body according to claim 1, it is characterized in that being provided with a molding version, the groove of one sole shape is set in the moulding masterplate, and the substrate that will cut moulding is put the groove side of moulding masterplate, and in described third step for substrate on coating one deck epoxy resin, even this layer epoxy resin is coated in the groove of moulding masterplate simultaneously, the footwear body side component that shoe sole component and substrate formed out that forms out is combined, and constitute two one patterns.
6. the manufacture method of skating shoe body according to claim 1, it is characterized in that being provided with a molding version, the groove of one sole shape is set in the moulding masterplate, and the substrate that will cut moulding is put the groove side of moulding masterplate, and in described third step for substrate on coating one deck epoxy resin, even this layer epoxy resin is coated in the groove of moulding masterplate simultaneously, the heel parts that shoe sole component and substrate formed out that form out are combined, and constitute two one patterns.
7. the manufacture method of skating shoe body according to claim 1, it is characterized in that being provided with a molding version, the groove of one sole shape is set in the moulding masterplate, and two plate bases that will cut moulding are put groove two sides of moulding masterplate, and in described third step for substrate on coating one deck epoxy resin, even this layer epoxy resin is coated in the groove of moulding masterplate simultaneously, the footwear body side component that shoe sole component and substrate formed out that forms out is combined, and constitute three one patterns.
8. according to the manufacture method of each described skating shoe body in the claim 1 to 7, it is characterized in that in described third step imposing once to epoxy resin coating repeatedly for substrate, can in the coating layer of epoxy resin, add fabric.