CN101081945A - Composite zinc phosphate rust-preventive pigment - Google Patents
Composite zinc phosphate rust-preventive pigment Download PDFInfo
- Publication number
- CN101081945A CN101081945A CN 200710035278 CN200710035278A CN101081945A CN 101081945 A CN101081945 A CN 101081945A CN 200710035278 CN200710035278 CN 200710035278 CN 200710035278 A CN200710035278 A CN 200710035278A CN 101081945 A CN101081945 A CN 101081945A
- Authority
- CN
- China
- Prior art keywords
- zinc phosphate
- rust
- phosphate
- preventive pigment
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses one kind of composite antirust zinc phosphate pigment. The composite antirust zinc phosphate pigment consists of zinc phosphate 10-30 wt%, ferric phosphate 30-70 wt% and wollastonite 10-30 wt%. The present invention has ferric phosphate to replace partial zinc phosphate, and this can lower the consumption of zinc phosphate, reduce production cost and decrease environment pollution while maintaining the antirust effect of the antirust paint.
Description
Technical field
The present invention relates to a kind of rust-stabilising pigment.
Background technology
Zinc phosphate is as a kind of rust-stabilising pigment, use commonplace in the rust proof paint field, but because metallic zinc is a kind of noble metal, the zinc phosphate price that with the metallic zinc is main material production is higher, causing with the zinc phosphate is the rust proof paint price residence height of main material production, and also there is environmental pollution in production process.
Summary of the invention
The purpose of this invention is to provide a kind of a kind of composite zinc phosphate rust proof paint that reduces zinc phosphate content.
The objective of the invention is to realize in the following way: a kind of composite zinc phosphate rust-preventive pigment, this rust-stabilising pigment contain following weight percent component:
Zinc phosphate 10-30%
Tertiary iron phosphate 30-70%
Wollastonite 10-30%.
A kind of composite zinc phosphate rust-preventive pigment, rust-stabilising pigment contain following weight percent component:
Zinc phosphate 10-20%
Tertiary iron phosphate 30-50%
Wollastonite 10-15%
Stopping composition 10-30%.
Described stopping composition is calcium hydroxide or yellow soda ash.
The present invention has following beneficial effect, do not reduce with the zinc phosphate be the rust-proof effect of rust proof paint of main material production in, with the low tertiary iron phosphate instead of part zinc phosphate of price, reduce the consumption of zinc phosphate, greatly reduce production cost, also alleviated pollution environment.
Embodiment
The present invention will be further described below in conjunction with embodiment:
Embodiment 1
A kind of composite zinc phosphate rust-preventive pigment is got the zinc phosphate of 25Kg, the tertiary iron phosphate of 40Kg%, the wollastonite of 12Kg, the calcium hydroxide of 23Kg.Said components thing powder mix is broken to 325 screen residues≤1%, dries, the weighing packing to moisture≤1%.
Embodiment 2
A kind of composite zinc phosphate rust-preventive pigment contains the zinc phosphate of 28Kg, the tertiary iron phosphate of 45Kg%, the wollastonite of 13Kg, the yellow soda ash of 14Kg.Said components thing powder mix is broken to 325 screen residues≤1%, dries, the weighing packing to moisture≤1%.
Embodiment 3
A kind of composite zinc phosphate rust-preventive pigment is got the zinc phosphate of 20Kg, the tertiary iron phosphate of 50Kg%, the wollastonite of 18Kg, the calcium hydroxide of 12Kg.Said components thing powder mix is broken to 325 screen residues≤1%, dries, the weighing packing to moisture≤1%.
Claims (3)
1, a kind of composite zinc phosphate rust-preventive pigment is characterized in that this rust-stabilising pigment contains following weight percent component:
Zinc phosphate 10-30%
Tertiary iron phosphate 30-70%
Silicon ash 10-30%.
2, a kind of composite zinc phosphate rust-preventive pigment according to claim 1 is characterized in that this rust-stabilising pigment contains following weight percent component:
Zinc phosphate 10-20%
Tertiary iron phosphate 30-50%
Wollastonite 10-15%
Stopping composition 10-30%.
3, a kind of composite zinc phosphate rust-preventive pigment according to claim 2 is characterized in that described stopping composition is calcium hydroxide or yellow soda ash.