CN101074169A - Slabstone dyed by liquid medicine and its manufacture - Google Patents
Slabstone dyed by liquid medicine and its manufacture Download PDFInfo
- Publication number
- CN101074169A CN101074169A CN 200610050891 CN200610050891A CN101074169A CN 101074169 A CN101074169 A CN 101074169A CN 200610050891 CN200610050891 CN 200610050891 CN 200610050891 A CN200610050891 A CN 200610050891A CN 101074169 A CN101074169 A CN 101074169A
- Authority
- CN
- China
- Prior art keywords
- slabstone
- grouan
- look liquid
- time
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A dyed stone plate and its production are disclosed. The process is carried out by cutting natural granite, sanding to make stone plate, putting it into baker, drying, putting color-liquid into color liquid pool, soaking in color-liquid pool, taking soaked granite out, naturally drying, putting it into baker, baking, cooling, taking it out, grinding and polishing. It has various colors, better appearance and multiple usages.
Description
Technical field
The present invention relates to a kind of working method that lithotome can be made into paring stone sheet material after liquid medicine soaks with different colours.
Background technology
Along with improving constantly of people's economy, the level of cultural life, requirement to household, Working environment is also more and more higher, therefore the construction and decoration industry is also more and more higher to the requirement of building materials, for example wish to have the stone material of various different colours, yet the color of general domestic natural granite building material all is white and lead, the quantity of import is few, price is very expensive again, and the color of generally crossing stone slab through artificial also has only redness and yellow, color is more dull than imitating, and can not satisfy the growing demand of human consumer.
Summary of the invention
In order to overcome the deficiency of existing processing stone slab color dullness, it is a kind of with natural stone sheet material medication water logging bubble and be made into the peculiar method with versicolor paring stone sheet material that present method invention provides, can remedy the color that lithotome itself is lacked, the stone material that can produce more kinds of different colours dyes plate, such as: coffee color, light coffee color, dark coffee-like, brown, light brown, burgundy, brown, light brown, dun, grey, light grey, lead, dark brown, reddish brown, dark red, light red, light black, pitch black, garnet, orange or the like, and present method can make the slabstone that dyed forever colour-fast, from then on can satisfy human consumer's different needs for a long time.Present method invention is the result who draws after practical experience is year in year out debugged repeatedly, thereby makes paring stone sheet material increase multicolour, and more create an aesthetic feeling is the senior finishing stone slab of a kind of ideal.
In order to achieve the above object, the present invention adopts following technical scheme:
1, natural granite stone is cut, polishes, be made into the slabstone of certain specification.
2, grouan slabstone that roughing is good is put into roaster and is dried processing.The purpose of oven dry is to allow the moisture in the grouan slabstone fully evaporate, and can absorb look liquid fully thereby be convenient to this grouan slabstone, and the time of grouan slabstone oven dry is long more, and the color relation that then follow-up immersion toasts out is dark more.The time of oven dry was controlled at 1 to 4 hour, and the temperature of oven dry is controlled at 145 degree between 205 degree.After the oven dry, wait for that grouan slabstone cooling back taking-up is standby.
3, in the look liquid pool, put into look liquid, the main component of look liquid is iron nitrate, manganous nitrate and water, they can determine grouan slabstone to dye next color in different ratio preparations, iron nitrate shared weight percent in look liquid is 26.8～32%, manganous nitrate shared weight percent in look liquid is 8～13.2%, and water shared weight percent in look liquid is 60%.
4, the grouan slabstone after will drying is put into the look liquid pool and is soaked, and look liquid will flood grouan slabstone fully, and the time of immersion is controlled at: 1 to 4 hours.
5, the grouan slabstone after will soaking takes out nature and dries.
6, the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is controlled at 145 degree between 205 degree, and the time of baking was controlled at 1 to 4 hours.
7, the cooling of the grouan slabstone after will toasting is taken out again.
8, decide according to the depth of required color and repeat the number of times that soaks and toast.
9, will soak as required, baked grouan slabstone polishes, polishes.
The invention has the beneficial effects as follows, can remedy the color that lithotome itself is lacked, the stone material that can produce more kinds of different colours dyes plate, and the stone material after the present invention processes dyeing some still can keep original crystalline structure of stone material and decorative pattern, present different gradation sense, make more create an aesthetic feeling of stone slab, purposes is more extensive.
Further specify the present invention below in conjunction with drawings and Examples.
Description of drawings
Fig. 1 is with natural stone sheet material medication water logging bubble and is made into the process flow sheet with versicolor paring stone sheet material.
Embodiment
Enforcement is steeped natural stone sheet material medication water logging and be made into the equipment that relates generally in the process with versicolor paring stone sheet material and comprises:
1, cutting machine can be selected general stone material cutting specific equipment for use, and its effect is to come cutting stone material by required specification.
2, sander can be selected general stone material polishing specific equipment for use, is to be used for the surface rubbing of the slabstone that will cut down, and the effect that polishes is in order to allow grouan slabstone absorb look liquid equably, thereby the color that guarantees the finished product that processes reaches the ideal effect.
3, roaster, roaster can be homemade roasters, also can be the roasters of being produced by special roaster manufacturer.Roaster generally is made up of mechanical, electrical source temperature controlling box of diesel combustion and baking burner hearth.It is fixed that the big I of baking burner hearth is come according to stone material length, width, thickness and the quantity of the maximum specification of production to be processed.
4, look liquid pool, the look liquid pool can be welded with steel plate or stainless steel, also can form with cement-bonded, and its dimensions can be decided according to largest stones specification to be processed and quantity.
Embodiment one
1, natural granite stone is cut, polishes with sander with cutting machine, be made into the slabstone of certain specification.
2, grouan slabstone that roughing is good is put into roaster and is dried processing, and the time value of oven dry is 1.5 hours, and the temperature of oven dry is 160 degree.Oven dry back naturally cooling also takes out.
3, immersion roasting procedure in first road is:
1) put into look liquid in the look liquid pool made from stainless steel plate, iron nitrate shared weight percent in look liquid is 32%, and manganous nitrate shared weight percent in look liquid is 8%, and water shared weight percent in look liquid is 60%.
2) the grouan slabstone after will drying is put into the look liquid pool and is soaked, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
3) the grouan slabstone after will soaking takes out nature and dries.
4) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 180 degree, and the time of baking is 2 hours.
5) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was light coffee color.
4, immersion roasting procedure in second road is:
1) the grouan slabstone after will drying is put into weight percent once more and is soaked the identical look liquid pool of roasting procedure with first road and soak, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
2) the grouan slabstone after will soaking takes out nature and dries.
3) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 180 degree, and the time of baking is 2 hours.
4) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was coffee-like.
5, immersion roasting procedure in the 3rd road is:
1) the grouan slabstone after will drying is put into weight percent for the third time and is soaked the identical look liquid pool of roasting procedure with first road and soak, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
2) the grouan slabstone after will soaking takes out nature and dries.
3) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 180 degree, and the time of baking is 2 hours.
4) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was brown.
6, carry out last polishing, polishing process together as required again.
Embodiment two
1, natural granite stone is cut, polishes with sander with cutting machine, be made into the slabstone of certain specification.
2, grouan slabstone that roughing is good is put into roaster and is dried processing, and the time value of oven dry is 1.5 hours, and the temperature of oven dry is 175 degree.Oven dry back naturally cooling also takes out.
3, immersion roasting procedure in first road is:
1) put into look liquid in the look liquid pool made from stainless steel plate, iron nitrate shared weight percent in look liquid is 29%, and manganous nitrate shared weight percent in look liquid is 11%, and water shared weight percent in look liquid is 60%.
2) the grouan slabstone after will drying is put into the look liquid pool and is soaked, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
3) the grouan slabstone after will soaking takes out nature and dries.
4) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 190 degree, and the time of baking is 2 hours.
5) the grouan slabstone naturally cooling after will toasting and taking out, this moment grouan slabstone color to be coffee color shallow slightly.
4, immersion roasting procedure in second road is:
1) the grouan slabstone after will drying is put into weight percent once more and is soaked the identical look liquid pool of roasting procedure with first road and soak, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
2) the grouan slabstone after will soaking takes out nature and dries.
3) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 190 degree, and the time of baking is 2 hours.
4) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was brown.
5, immersion roasting procedure in the 3rd road is:
1) the grouan slabstone after will drying is put into weight percent for the third time and is soaked the identical look liquid pool of roasting procedure with first road and soak, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
2) the grouan slabstone after will soaking takes out nature and dries.
3) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 190 degree, and the time of baking is 2 hours.
4) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was dark-brown.
6, carry out last polishing, polishing process together as required again.
Embodiment three
1, natural granite stone is cut, polishes with sander with cutting machine, be made into the slabstone of certain specification.
2, grouan slabstone that roughing is good is put into roaster and is dried processing, and the time value of oven dry is 1.5 hours, and the temperature of oven dry is 180 degree.Oven dry back naturally cooling also takes out.
3, immersion roasting procedure in first road is:
1) put into look liquid in the look liquid pool made from stainless steel plate, iron nitrate shared weight percent in look liquid is 26.8%, and manganous nitrate shared weight percent in look liquid is 13.2%, and water shared weight percent in look liquid is 60%.
2) the grouan slabstone after will drying is put into the look liquid pool and is soaked, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
3) the grouan slabstone after will soaking takes out nature and dries.
4) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 200 degree, and the time of baking is 2 hours.
5) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was the coffee color depth.
4, immersion roasting procedure in second road is:
1) the grouan slabstone after will drying is put into weight percent once more and is soaked the identical look liquid pool of roasting procedure with first road and soak, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
2) the grouan slabstone after will soaking takes out nature and dries.
3) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 200 degree, and the time of baking is 2 hours.
4) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was dark-brown.
5, immersion roasting procedure in the 3rd road is:
1) the grouan slabstone after will drying is put into weight percent for the third time and is soaked the identical look liquid pool of roasting procedure with first road and soak, and look liquid will flood grouan slabstone fully, and the time of immersion is 1.5 hours.
2) the grouan slabstone after will soaking takes out nature and dries;
3) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is 200 degree, and the time of baking is 2 hours.
4) the grouan slabstone naturally cooling after will toasting and taking out, this moment, the color of grouan slabstone was burgundy.
6, carry out last polishing, polishing process together as required again.
Claims (1)
1, a kind of through painted stone slab of liquid medicine and processing and fabricating method thereof, it is characterized in that: the inventive method comprises the selection preparation of look liquid and comprises the painted processing and making process of natural stone sheet material medication water.
(1) selection of look liquid preparation: its main component is: iron nitrate, manganous nitrate and water, and the shared weight percent of each main component is:
Iron nitrate: 26.8～32%
Manganous nitrate: 8～13.2%
Water: 60%
(2) the painted processing and making process of natural stone sheet material medication water is specially: 1. natural granite stone is cut, polishes, be made into the slabstone of certain specification; 2. roughing is good grouan slabstone is put into roaster dries processing, and the time of oven dry was controlled at 1 to 4 hour, and the temperature value of oven dry is controlled at 145 degree between 205 degree.After the oven dry, wait for grouan slabstone cooling taking-up again; 3. in the look liquid pool, put into the look liquid that iron nitrate and manganous nitrate are prepared by a certain percentage; 4. soak for the first time roasting procedure: the grouan slabstone after a) will drying is put into the look liquid pool and is soaked, and look liquid will flood grouan slabstone fully, and the time of immersion was controlled at 1 to 4 hour; B) the grouan slabstone after will soaking takes out nature and dries; C) the grouan slabstone after will drying is put into the roaster baking, and the temperature of baking is: 145 degree are between 205 degree, and the time of baking is: 1 to 4 hour; D) cooling of the stone slab after will toasting is taken out again; 5. the needs according to concrete color determine whether entering for the second time, soak for the third time even more frequently roasting procedure; 6. grouan slabstone polished, polish and get product.