CN101070684A - Method for making paper-pulp by cold immersion for paper-making - Google Patents
Method for making paper-pulp by cold immersion for paper-making Download PDFInfo
- Publication number
- CN101070684A CN101070684A CN 200710117658 CN200710117658A CN101070684A CN 101070684 A CN101070684 A CN 101070684A CN 200710117658 CN200710117658 CN 200710117658 CN 200710117658 A CN200710117658 A CN 200710117658A CN 101070684 A CN101070684 A CN 101070684A
- Authority
- CN
- China
- Prior art keywords
- pulp
- soaks
- paper
- making
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention involves a cold dip making pulp method papermaking. First rubs the papermaking raw material into the fiber; prepare active ingredient separately to soaks the main fluid and soaks the auxiliary fluid, puts the active ingredient in the mixed fluid to soaks the main fluid and soaks the auxiliary fluid, then obtains the steep fluid. Put the fiber into the steep in the normal temperature for 36-72 hours; Carries on the attrition and beating on paper pulp, the beating to the pulp hard degree is 12-18. This method's pulping process does not use the alkali, does not need the massive laundering, avoid the sewage emissions, save water. Its thick liquid rate compares with the strong alkali method, may enhance 20%. Using this invention, its raw material origin is widespread, the water and coal used are few, the papermaking cost is low, the preparation paper pulp may make the box paperboard and the excel in corrugated paper.
Description
Technical field
The present invention relates to a kind of method that is used for the cold soaking infusion papermaking slurry of papermaking, belong to pulp technology for making paper.
Background technology
Traditional paper technology all is that its principle is a peeling reaction with the impurity such as lignin in the highly basic extracting string, and promptly highly basic extracts the impurity such as lignin in the string, makes fiber saponification pulping, reaches the requirement of the paper product of manufacturing paper with pulp.But the highly basic that uses in the traditional handicraft has destroyed staple fibre, has therefore reduced the slurry yield of paper pulp, causes the severe contamination of environment again.This makes paper-making industry have serious problems, in the big ground of China in addition to anhydrously do not pollute, the non-staining stage in no river, directly injured existent environment of people.For this reason, country has closed ten hundreds of middle small paper mills, causes large quantities of workmans to be laid off, and livelihood is unassured.Enterprises in pulp and paper industry is in order to maintain existence, and the needization huge fund is carried out alkali and reclaimed, but costly, and paper cost is increased greatly.
Summary of the invention
The objective of the invention is to propose a kind of method that is used for the cold soaking infusion papermaking slurry of papermaking, situation at present paper industry existence to severe environmental pollution, be used for the paper pulp papermaking process of papermaking, replace highly basic with the organic active agent, make harmless, the alkali-free of paper-making process, pollution-free, and reduce the papermaking cost.
The method of the cold soaking infusion papermaking slurry that is used for papermaking that the present invention proposes may further comprise the steps:
(1) the paper grade (stock) raw material is twisted into filament, making the length of silk is 1～5 centimetre, and the diameter of silk is 0.1～0.2 centimetre;
(2) prepare the auxilliary liquid of activating agent, the main liquid of immersion and immersion respectively:
Wherein the preparation method of activating agent is:
The percentage by weight of each component is:
Secondary octanol polyoxyethylene ether 6～12%
Oxidic polyethylene emulsion 6～12%
Ethanol 1～5%
Neopelex 1～5%
SODIUM PERCARBONATE 2～6%
Alkali protease 1～3%
Surplus is talcum powder
Preparation process is: above-mentioned raw materials is mixed in proportion, grind, making granularity is 100～200 orders;
The preparation method who wherein soaks main liquid is:
The weight ratio of each component is:
1000 parts in water
8～12 parts in calcium hydroxide
0.1～1 part of anthraquinone
0.1～1 part of SODIUM PERCARBONATE
0.5～2 part of neopelex
0.5～2 part of anhydrous sodium sulfite
According to the above ratio each component is mixed, reacted 1.5～3 hours, standby;
The preparation method who wherein soaks auxilliary liquid is:
The weight ratio of each component is:
1000 parts in water
1～4 part of alkali protease
1～3 part of SODIUM PERCARBONATE
According to the above ratio each component is mixed, reacted 1.5～3 hours, standby;
Above-mentioned activating agent is put into the main liquid of above-mentioned immersion and soaked the mixed liquor of assisting liquid, obtain soak, additional proportion is: it is 1～1.5% that activating agent accounts for filametntary percentage by weight, soaking main liquid, to account for filametntary percentage by weight be 180～220%, soaks that to account for filametntary percentage by weight be 90～115%;
(3) filament with step (1) adds in the soak, soak at room temperature, and additional proportion is: filament: soak=1: 2.8～3.1, soak time are 36～72 hours;
(4) paper pulp after the above-mentioned immersion is ground, the hardness that makes paper pulp is 15～20;
(5) to above-mentioned pulp beating, making pulp hardness is 12～18.
The manufacture method of the paper pulp that is used for papermaking that the present invention proposes has the following advantages:
1, in the pulping process of the present invention, do not use alkali, need not massive laundering, avoided sewage emissions, thereby saved water greatly.
2, use the organic active agent to replace highly basic in traditional pulping and papermaking processes in the inventive method, this makes the present invention different with traditional handicraft on the mechanism that paper pulp is made.Protease in the activating agent that the present invention uses; it is alkaline compound; can make the straw molten wax degreasing in surface; secondary octanol polyoxyethylene ether wherein is a kind of nonionic penetrant, and it can make other active ingredient rapid permeability in the activating agent in the plant chain; moment is opened the connection between the string; make stripping fast such as lignin in the string, starch, tannin, sugar, ash content, pectin, and do not destroy fiber, general protection fiber and half fiber.Therefore utilize the inventive method to make paper pulp, its slurry yield is compared with strong alkali method, can improve 20%.
3, utilize the inventive method to make paper pulp, its raw material sources are extensive, can use straw, wheat, Chinese alpine rush of draft etc., the cornstalk of standing grain basis, bamboo, reed, cotton stalk, bagasse etc., and woody brush wood, leaf wood and needlebush etc., as long as have all available the inventive method slurrying of cellulosic straw.
4, the industrial chemicals consumption that uses in the inventive method is less than traditional paper technology greatly, and paper pulp is easily bleached, and water consumption is few, and contained pollutant is few, and middle section water is easily administered.
5, pulp making process of the present invention need not heating, and paper per ton can be saved about 1 ton coal-fired, and cold soak can use after filtering repeatedly, has therefore saved the water coal greatly, has reduced the papermaking cost.
6, the paper pulp that utilizes the inventive method to make, can manufacture paper with pulp boxboard and high-strength corrugated paper.
The specific embodiment
The various industrial chemicals that use in the embodiment of the invention, its source is as follows:
Secondary octanol polyoxyethylene ether is produced by Shangyu, the Zhejiang city second chemical reagent factory.Oxidic polyethylene emulsion is by Nanjing, Jiangsu Province second Organic Chemical Plant.Neopelex is produced by Red Star chemical plant, Zibo, Shandong Province.SODIUM PERCARBONATE is produced by Red Star chemical plant, Tianjin.Alkali protease is produced by Red Star chemical plant, Tianjin.
Embodiment 1
(1) with 4 tons of paper grade (stock) raw material wheat straws, be twisted into silk, making the length of silk is 1～5 centimetre, and the diameter of silk is 0.1～0.2 centimetre.
(2) prepare 40 kilograms of activating agents respectively: wherein: 2.4 kilograms of secondary octanol polyoxyethylene ether, oxidic polyethylene emulsion: 2.4 kilograms, ethanol: 0.4 kilogram, neopelex: 0.4 kilogram, SODIUM PERCARBONATE: 0.8 kilogram, alkali protease: 0.4 kilogram, talcum powder: 33.2 kilograms, above-mentioned raw materials is mixed, grind, making granularity is 200 orders;
8073.6 kilograms of main liquid are soaked in preparation: wherein, water: 8000 kilograms, calcium hydroxide: 64 kilograms, anthraquinone: 0.8 kilogram, SODIUM PERCARBONATE: 0.8 kilogram, neopelex: 4 kilograms, anhydrous sodium sulfite: 4 kilograms, above-mentioned raw materials is mixed, reacted 2 hours, standby;
4008 kilograms of auxilliary liquid are soaked in preparation, wherein, water: 4000 kilograms, alkali protease: 4 kilograms, SODIUM PERCARBONATE: 4 kilograms, above-mentioned raw materials is mixed, reacted 2 hours, standby;
At last above-mentioned activating agent is put into the mixed liquor that soaks main liquid and soak auxilliary liquid, obtained soak.
Soak soak at room temperature 36 hours in (3) 4 tons of filaments adding soaks.
(4) paper pulp after the above-mentioned immersion is ground, the hardness that makes paper pulp is 18;
(5) to above-mentioned pulp beating, making pulp hardness is 13.
Embodiment 2
(1) with 4 tons in paper grade (stock) raw material reed, be twisted into silk, making the length of silk is 1～5 centimetre, and the diameter of silk is 0.1～0.2 centimetre.
(2) prepare 40 kilograms of activating agents respectively: wherein: 3.6 kilograms of secondary octanol polyoxyethylene ether, oxidic polyethylene emulsion: 3.6 kilograms, ethanol: 1.24 kilograms, neopelex: 1.2 kilograms, SODIUM PERCARBONATE: 1.6 kilograms, alkali protease: 0.8 kilogram, talcum powder: 28 kilograms, above-mentioned raw materials is mixed, grind, making granularity is 150 orders;
8108.8 kilograms of main liquid are soaked in preparation: wherein, water: 8000 kilograms, calcium hydroxide: 80 kilograms, anthraquinone: 6.4 kilograms, SODIUM PERCARBONATE: 6.4 kilograms, neopelex: 8 kilograms, anhydrous sodium sulfite: 8 kilograms, above-mentioned raw materials is mixed, reacted 2 hours, standby;
4014 kilograms of auxilliary liquid are soaked in preparation, wherein, water: 4000 kilograms, alkali protease: 8 kilograms, SODIUM PERCARBONATE: 6 kilograms, above-mentioned raw materials is mixed, reacted 2 hours, standby;
At last activating agent is put into the mixed liquor that soaks main liquid and soak auxilliary liquid, obtained soak.
Soak soak at room temperature 50 hours in (3) 4 tons of filaments adding soaks.
(4) paper pulp after the above-mentioned immersion is ground, the hardness that makes paper pulp is 18;
(5) to above-mentioned pulp beating, making pulp hardness is 14.
Embodiment 3
(1) with 4 tons of paper grade (stock) raw material quick growth poplar woods, be twisted into silk, making the length of silk is 1～5 centimetre, and the diameter of silk is 0.1～0.2 centimetre.
(2) prepare 40 kilograms of activating agents respectively: wherein: 4.8 kilograms of secondary octanol polyoxyethylene ether, oxidic polyethylene emulsion: 4.8 kilograms, ethanol: 2 kilograms, neopelex: 2 kilograms, SODIUM PERCARBONATE: 3 kilograms, alkali protease: 1.2 kilograms, talcum powder: 18.2 kilograms, above-mentioned raw materials is mixed, grind, making granularity is 150 orders;
8144 kilograms of main liquid are soaked in preparation: wherein, water: 8000 kilograms, calcium hydroxide: 96 kilograms, anthraquinone: 8 kilograms, SODIUM PERCARBONATE: 8 kilograms, neopelex: 16 kilograms, anhydrous sodium sulfite: 16 kilograms, above-mentioned raw materials is mixed, reacted 2 hours, standby;
4028 kilograms of auxilliary liquid are soaked in preparation, wherein, water: 4000 kilograms, alkali protease: 16 kilograms, SODIUM PERCARBONATE: 12 kilograms, above-mentioned raw materials is mixed, reacted 2 hours, standby;
At last activating agent is put into the mixed liquor that soaks main liquid and soak auxilliary liquid, obtained soak.
Soak soak at room temperature 70 hours in (3) 4 tons of filaments adding soaks.
(4) paper pulp after the above-mentioned immersion is ground, the hardness that makes paper pulp is 18.
(5) to above-mentioned pulp beating, making pulp hardness is 15.
Claims (1)
1, a kind of method that is used for the cold soaking infusion papermaking slurry of papermaking is characterized in that this method may further comprise the steps:
(1) the paper grade (stock) raw material is twisted into filament, making the length of silk is 1～5 centimetre, and the diameter of silk is 0.1～0.2 centimetre;
(2) prepare the auxilliary liquid of activating agent, the main liquid of immersion and immersion respectively:
Wherein the preparation method of activating agent is:
The percentage by weight of each component is:
Secondary octanol polyoxyethylene ether 6～12%
Oxidic polyethylene emulsion 6～12%
Ethanol 1～5%
Neopelex 1～5%
SODIUM PERCARBONATE 2～6%
Alkali protease 1～3%
Surplus is talcum powder
Preparation process is: above-mentioned raw materials is mixed in proportion, grind, making granularity is 100～200 orders;
The preparation method who wherein soaks main liquid is:
The weight ratio of each component is:
1000 parts in water
8～12 parts in calcium hydroxide
0.1～1 part of anthraquinone
0.1～1 part of SODIUM PERCARBONATE
0.5～2 part of neopelex
0.5～2 part of anhydrous sodium sulfite
According to the above ratio each component is mixed, reacted 1.5～3 hours, standby;
The preparation method who wherein soaks auxilliary liquid is:
The weight ratio of each component is:
1000 parts in water
1～4 part of alkali protease
1～3 part of SODIUM PERCARBONATE
According to the above ratio each component is mixed, reacted 1.5～3 hours, standby;
Above-mentioned activating agent is put into the main liquid of above-mentioned immersion and soaked the mixed liquor of assisting liquid, obtain soak, additional proportion is: it is 1～1.5% that activating agent accounts for filametntary percentage by weight, soaking main liquid, to account for filametntary percentage by weight be 180～220%, soaks that to account for filametntary percentage by weight be 90～115%;
(3) filament with step (1) adds in the soak, soak at room temperature, and additional proportion is: filament: soak=1: 2.8～3.1, soak time are 36～72 hours;
(4) paper pulp after the above-mentioned immersion is ground, the hardness that makes paper pulp is 15～20;
(5) to above-mentioned pulp beating, making pulp hardness is 12～18.