CN101045183A - Gold club head with modified surface and its making method - Google Patents
Gold club head with modified surface and its making method Download PDFInfo
- Publication number
- CN101045183A CN101045183A CNA2006100584906A CN200610058490A CN101045183A CN 101045183 A CN101045183 A CN 101045183A CN A2006100584906 A CNA2006100584906 A CN A2006100584906A CN 200610058490 A CN200610058490 A CN 200610058490A CN 101045183 A CN101045183 A CN 101045183A
- Authority
- CN
- China
- Prior art keywords
- surfaction
- golf club
- bulb
- ion
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A golf club head with modified surface is made up through manufacturing golf club head, and modifying surface. Said surface modifying procedure includes such steps as putting it in a vacuum environment, generating high-temp ions by ion generator, and bombarding on part of its surface to soften the surface structure for releasing the adsorbed gas and impurities while compacting.
Description
Technical field
The present invention relates to a kind of golf club and manufacture method thereof, particularly relate to a kind of golf club and manufacture method thereof with surfaction.
Background technology
Generally speaking, the material of Chang Zuowei golf club has titanium alloy, reaches materials such as stainless steel, but because the demand of function can improve its case hardness and intensity to add the mode of lining usually.For example: electroplate (Electroplate), long-pending (the Physical VaporDeposition in physical vapor Shen, PVD), long-pending (the Chemical Vapor Deposition in chemical evapn Shen, CVD), thermal response diffusion lining (Thermal Reactive Diffusion, TRD).Yet, in the above-mentioned mode that adds the lining plated film, using a period of time, the part of the strength that particularly need withstand shocks, the material that is covered have peels off the doubt that comes off, so that the outward appearance ugliness.
In addition, also utilize heat treated mode, improve the hardness of golf head surface.This mode is that golf club is placed under the high temperature, and the hardness of whole bulb is promoted simultaneously and has identical hardness.Unfortunately, for the striker, golf club must have the softer material of part to increase the sensation and the function that shock-absorbing is provided of batting.Therefore, the golf club made from heat treatment mode is to reach the effect that points hardness strengthens.
In recent years, someone utilizes hardness height and particle little (40～200 microns, μ m) small steel ball, with the high speed of 100m/s the local surfaces of golf club is carried out pearl and hit, cause Facing material closely knit, improve hardness and intensity, yet, this processing needs the little steel ball of high-power air compressor machine, high rigidity, and equipment and the technology such as surface temperature that need accurate control hit by pearl, and case hardness is difficult for evenly.
Summary of the invention
The objective of the invention is for a kind of golf club with surfaction is provided, can be effectively and improve the hardness and the intensity of golf club partly, produce and do not have the problem of peeling off.
Another object of the present invention is to provide a kind of manufacture method, in order to make the golf club that this has surfaction with golf club of surfaction.
For achieving the above object, the present invention has the golf club of surfaction, comprises a bulb, and this bulb has a surfaction portion that is positioned at outer surface, and this surfaction portion utilizes the ion bombardment and makes organizing of top layer more fine and close.
The present invention has the manufacture method of the golf club of surfaction, comprises a step for preparing that prepares a bulb, and a surfaction step.This surfaction step is under vacuum environment, utilizes an ion generator to produce ion, to bombard the surface of this bulb, makes the tissue on its top layer become fine and close more.
Effect of the present invention is to utilize ion to bombard the textura epidermoidea of this bulb, makes Facing material temperature rise and softening, and because of the effect of bombardment, gas and impurity that the surface is adsorbed hit, and make textura epidermoidea more fine and close, to improve its hardness and intensity simultaneously.Owing to there is no the material that adds, therefore do not have the problem that comes off of peeling off.
Description of drawings
Fig. 1 is a partial cutaway schematic, illustrates that the present invention has the preferred embodiment of the golf club of surfaction.
Fig. 2 is a flow chart, illustrates that the present invention has the preferred embodiment of manufacture method of the golf club of surfaction.
Fig. 3 is a manufacturing schematic diagram, and explanation is in a vacuum drying oven, utilizes an ion generator to produce ion, to bombard a bulb surface.
Fig. 4 is a surface electronic micrograph, illustrates that this bulb does not carry out the surface appearance of high temperature ion bombardment.
Fig. 5 is a surface electronic micrograph, illustrates that this bulb has carried out the surface appearance of high temperature ion bombardment.
The specific embodiment
Below by preferred embodiment and accompanying drawing golf club and the manufacture method thereof that the present invention has surfaction is elaborated.
As shown in Figure 1, the present invention has the preferred embodiment of the golf club of surfaction, comprises a bulb 1, and this bulb 1 has a surfaction portion 11 that is positioned at outer surface, and this surfaction portion 11 utilizes the ion bombardment and makes organizing of top layer more fine and close.In this preferred embodiment, this bulb 1 is that stainless steel is made, but also can be materials such as titanium alloy or carbon steel.
In this preferred embodiment, this surfaction portion 11 is the front end faces that are positioned at this bulb 1, or claims the scope of attack, is the part of directly clashing into golf, improves the hardness and the intensity of the scope of attack whereby.In fact, this surfaction portion 11 also is positioned at rear end face, the end face of this bulb 1, or on the bottom surface, should not limit to claim scope of the present invention with this.
As shown in Figure 2, the present invention has the preferred embodiment of manufacture method of the golf club of surfaction, and comprise one and prepare step 2, a pre-treatment step 3, and a surfaction step 4.
Cooperate Fig. 1 and Fig. 3 simultaneously, this prepares step 2 is to prepare to mold a bulb 1.This bulb 1 is that stainless steel is made, but also can be titanium alloy, or carbon steel.Generally speaking, be based on metal material.
This pre-treatment step 3 is that this bulb 1 is ground, polishes, cleans, and reaches oven dry and waits processing.Certainly, the surface appearance after also visual this bulb 1 moulding increases and decreases above-mentioned processing, should not limit to claim scope of the present invention with this.
This surfaction step 4 is that this bulb 1 is placed a vacuum drying oven 5, then, utilize an ion generator 6 that is arranged in this vacuum drying oven 5, mode with the discharge of high temperature electricity slurry, make the inert gas of feeding, producing the ion of high temperature as argon gas ionization, can certainly be to feed gases such as nitrogen or helium.Wherein, the parameter of being controlled has current strength, voltage, time, and temperature.And employed electric current, voltage and time, then looking the metal material that clashed into and the gaseous species of feeding can determine.
The high temperature ion that utilizes this ion generator 6 to be produced bombards the surface of this bulb 1, gas adsorbed on the surface and impurity can be bombarded out, and simultaneously, the ion of high temperature also can make this bulb 1 surface soften because of temperature rise.Utilize the effect of bombardment, the tissue on top layer can be compacted equably and become more fine and close, form a hardness, the higher surfaction portion 11 of intensity, improve the hardness on this bulb 1 surface whereby.In this preferred embodiment, the surface of being bombarded, the degree of depth of its influence can reach in 30 microns (μ m).
As shown in Figure 4, be one not carry out the surface electronic micrograph of high temperature ion bombardment, be at the SUS474 stainless steel, and take, the straight vestige of processing when demonstrating its surface appearance and only existing previous moulding with 500 times multiplying power.
As shown in Figure 5, be one to have carried out the surface electronic micrograph of high temperature ion bombardment, be similarly the SUS474 stainless steel, and take with 500 times multiplying power, demonstrate its surface after carrying out the ion bombardment, the straight vestige of processing when not seeing moulding has become many small and fine and close small shrinkage pools.
Get back to Fig. 1, what deserves to be mentioned is, in the process that ion bombards at a high speed, this bulb 1 lip-deep atom also might be clashed into out, and form the effect that part ion is implanted, simultaneously, also because be to utilize the high temperature ion, can make the material on top layer reach the effect that the heat treatment lattice changes, more than all can reach the effect that improves case hardness and intensity.In addition, owing to be not the extra high material of plating hardness again, therefore,, do not have material yet and produce the problem generation of peeling off even under the bump of batting.
With manufacture method of the present invention hardness is promoted more than 20%, for example, 17-4 stainless steel (17Cr-4Ni Stainless Steel) be carried out the bombardment of high temperature ion, its case hardness can be brought up to 500Hv by 300Hv, and the amplitude of increase is 66%.For the SUS304 stainless steel, its case hardness can be increased to 350Hv by 180Hv, and the amplitude of increase is 94%.For the SUS450 stainless steel, its case hardness can be increased to 600Hv by 390Hv, and the amplitude of increase is 54%.
It should be noted, because the part of bombarding with ion makes the hardness of the part below the 30 μ m of top layer improve only, other inner materials still can be kept original hardness, form outer hard interior soft aspect, so that shock-absorbing effect to be provided, increase the feel of the ball of striker's batting by the softer part of material.
Conclude above-mentioned, the present invention has the golf club and the manufacture method thereof of surfaction, is to utilize the high temperature ion to bombard the surface of this bulb 1, makes the tissue on top layer be subjected to thermal softening, and can be by compacting equably and become more fine and close hard, improve the hardness of this bulb 1.Simultaneously, compare down the softer part of material, shock-absorbing effect can be provided and increase the batting sensation because of this bulb 1 also has.The more important thing is, owing to be that originally material bombardment is made it consolidation, rather than extra plating material again, do not have and peel off the problem that comes off and take place, so can reach purpose of the present invention really.
Claims (9)
1. manufacture method with golf club of surfaction comprises a step for preparing that prepares a bulb, and a surfaction step, it is characterized in that:
This surfaction step is under vacuum environment, utilizes an ion generator to produce ion, to bombard the surface of this bulb, organizes more fine and close surfaction portion to form one.
2. have the manufacture method of the golf club of surfaction according to claim 1, it is characterized in that:
In this surfaction step, be that this bulb is placed a vacuum drying oven, and this bulb is heated.
3. as having the manufacture method of the golf club of surfaction as described in the claim 2, it is characterized in that:
In this surfaction step, this ion generator is with high temperature electricity slurry discharge mode, makes inert gas ionization and produces the ion of bombardment usefulness.
4. as having the manufacture method of the golf club of surfaction as described in claim 1 or 3, it is characterized in that:
Also comprise one and prepare pre-treatment step between step and the surfaction step between this, this pre-treatment step is that this bulb is ground, polishes, cleans, and oven dry is handled.
5. have the manufacture method of the golf club of surfaction according to claim 1, it is characterized in that:
In this surfaction step, by the surfaction portion that ion bombards, it influences the degree of depth is within 30 microns.
6. have the manufacture method of the golf club of surfaction according to claim 1, it is characterized in that:
This bulb be selected from following metal material one of them: titanium alloy, stainless steel, and carbon steel.
7. golf club with surfaction is characterized in that:
This golf club has a surfaction portion that is positioned at extexine, and this surfaction portion utilizes the ion bombardment and makes organizing of top layer more fine and close.
8. as having the golf club of surfaction as described in the claim 7, it is characterized in that:
By the surfaction portion that ion bombards, it influences the degree of depth is within 30 microns.
9. as having the golf club of surfaction as described in the claim 7, it is characterized in that:
This golf club be selected from following metal material one of them: titanium alloy, stainless steel, and carbon steel.