CN101036932A - Original gravel additive for preventing castings stria defect - Google Patents
Original gravel additive for preventing castings stria defect Download PDFInfo
- Publication number
- CN101036932A CN101036932A CN 200710021287 CN200710021287A CN101036932A CN 101036932 A CN101036932 A CN 101036932A CN 200710021287 CN200710021287 CN 200710021287 CN 200710021287 A CN200710021287 A CN 200710021287A CN 101036932 A CN101036932 A CN 101036932A
- Authority
- CN
- China
- Prior art keywords
- defect
- additive
- vein
- sand
- stria
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a raw sand additive for preventing casting rattail defect, including following weight compositions: transparent quartz 8%, calcite 1%, sepiolite 1%, kaolinite 70%, pyrophyllite 10%, magnetite 10%; without affecting functional performance of mixture and sand mould, and mainly preventing casting rattail defect, while with assistant curative effect for the casting air-hole and the burnt-on sand (sintering) and so on defects.
Description
Technical field
The present invention relates to a kind of former sand additive that prevents foundry goods vein defective.
Background technology
Vein is particularly a kind of common casting flaw in the resin sand casting technique of sand casting, promptly at angle, cast(ing) surface garden, plane and high temperature thermal center place occur be shaped as irregular metal bump thing.The vein especially vein of engine, valve type intricate casting inner chamber not only is difficult to cleaning, and can influence the flow of foundry goods cleannes and cooling fluid, and then reduces product performance index.
The generation that solves and prevent vein is the important topic of casting industry research always.Before the sixties in last century, founder author adopts the special sand of adding the low thermal expansion of 30-50% in roughing sand mostly, for example zircon sand, chromite sand etc. solve the vein problem, but the flowability of this method affect compound, the big quickening core box wearing and tearing of unit weight, unit cost is very high, and anti-vein effect is general.Used wood chip, starch based organic composite material afterwards again, but this organic composite material burning decrement is up to 40-50%, and seriously reduce the up time and the sand core strength of compound, and the core qualification rate declines to a great extent, and bleb, scab defective significantly rise again.
Summary of the invention
The present invention seeks to: a kind of former sand additive that prevents foundry goods vein defective is provided, neither influence compound, core (type) and often show serviceability, can to bleb, scab defectives such as (sintering) auxiliary curative effect be arranged simultaneously to prevent foundry goods vein defective again.
Technical scheme of the present invention is: a kind of former sand additive that prevents foundry goods vein defective comprises following formulation by weight: suprasil 8%, calcite 1%, sepiolite 1%, kaolinite 70%, pyrophyllite 10%, magnetite 10%.
Advantage of the present invention is:
1. under normal temperature condition, it does not influence conventional serviceabilities such as resin sand up time, flowability, curing rate, room temperature strength, coated coating, storage.
2. under hot conditions, its energy and silica generation solid phase reaction generates a kind of low bulk crystal.Not only the coefficient of expansion is low for this solid solution attitude crystal, and each is less to the difference of thermal expansion, relax various intercrystalline boundary stresses, form low-melting multicomponent glass attitude material, increase the calorific intensity and the thermoplasticity of core, absorb the volumetric expansion of quartz sand when undergoing phase transition, reduce the trend of core (type) heat cracking, the shutoff crackle, increase the molten metal osmotic resistance, prevent that core gas from spreading in foundry goods, can effectively prevent foundry goods vein generation of defects, reduce the probability of bleb, the generation of permeability scab defective.
Below in conjunction with embodiment the present invention is further described:
The specific embodiment
Embodiment: a kind of former sand additive that prevents foundry goods vein defective comprises following formulation by weight: suprasil 8%, calcite 1%, sepiolite 1%, kaolinite 70%, pyrophyllite 10%, magnetite 10%.
During preparation:
1, all raw material is sieved, make it to reach distribution of particle sizes separately.
2, the raw material after will sieving stir the system of mixing, discharging, check, packing, warehouse-in by technical recipe with special equipment.
Also can in stirring dark process, add organic solvent, to improve surface-active.
The present invention sets up the test procedure of laboratory's simulation device and the anti-vein effect of laboratory evaluation according to the mechanism that the vein defective produces.Utilize this cover test simulation device, adopt single factor experiment method to screen tens of kinds of raw-material kinds and effective addition earlier, explore the feasibility technical scheme that modification is handled according to this raw-material physicochemical characteristics again, on the basis that does not influence serviceability, continue and read to improve anti-vein effect, adopt the optimized percentage of preferred each component of orthogonal experiment at last and optimize preparing process.
The product that the present invention produced is reported as follows through the check of Jiangsu Province's product quality supervision and testing institute:
| Sequence number | Interventions Requested | Unit | Specification requirement | Assay | Individual event is estimated |
| 1 2 3 4 5 6 7 8 9 | Outward appearance loose volume weight moisture; % average fineness weld point burning decrement, % vein length vein height intensity drop-out value % | ---- g/cm3 ---- ? ℃ ---- mm mm ---- | Black 2.0～2.2≤0.3 130～140 975～1025≤1≤30≤2.5≤10 | Qualified 2.0 0.1 135 998 0.3 10 1.5 7 | Qualified qualified |
The product that the present invention produced is key through countries such as Wuxi diesel engine Foundry Inc. of the First Automobile Group, west, Tyke, East China, Shanghai diesel engine joint stock company limiteds, overseas-funded enterprise is on probation, and anti-vein effect is good.
Claims (1)
1. a former sand additive that prevents foundry goods vein defective comprises following formulation by weight: suprasil 8%, calcite 1%, sepiolite 1%, kaolinite 70%, pyrophyllite 10%, magnetite 10%.