CN101007355A - Preparation method of nano-powder aluminum alloy brazing flux - Google Patents

Preparation method of nano-powder aluminum alloy brazing flux Download PDF

Info

Publication number
CN101007355A
CN101007355A CN 200710026305 CN200710026305A CN101007355A CN 101007355 A CN101007355 A CN 101007355A CN 200710026305 CN200710026305 CN 200710026305 CN 200710026305 A CN200710026305 A CN 200710026305A CN 101007355 A CN101007355 A CN 101007355A
Authority
CN
China
Prior art keywords
brazing flux
preparation
potassium fluoride
aluminium chloride
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200710026305
Other languages
Chinese (zh)
Other versions
CN100469496C (en
Inventor
揭晓华
梁兴华
卢国辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong University of Technology
Original Assignee
Guangdong University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong University of Technology filed Critical Guangdong University of Technology
Priority to CNB200710026305XA priority Critical patent/CN100469496C/en
Publication of CN101007355A publication Critical patent/CN101007355A/en
Application granted granted Critical
Publication of CN100469496C publication Critical patent/CN100469496C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a preparation method of nanometer powder aluminum alloy brazing flux method, the brazing flux is made by the chemical reaction of aluminium chloride (AlCl3) and potassium fluoride (KF), the main phase of product is K2ALF5 .H2O; the brazing flux is added poly-hexandiol (PEG4000) as disperser and fluohydric acid (HF)to adjusting the product pH to 4. In preparation process, the resultant is filtered, washed and vacuum dried, then the brazing flux powder is prepared by sintering the dried resultant. The invention prepares the nanometer aluminum brazing flux powder through the chemical precipitation elementary, the grain size of the brazing flux powder, the component is uniform and accurate, melting point low brazability is good.

Description

A kind of preparation method of nano-powder aluminum alloy brazing flux
Technical field
The invention belongs to a kind of welding material, be specifically related to a kind of preparation method of nano-powder aluminum alloy brazing flux.
Background technology
Aluminium alloy has that density is little, intensity is high and advantage such as corrosion-resistant, thereby is widely used in automobile, high-speed railway vehicle, Aero-Space and war industry.Because its distinctive physics, chemical property can run into a series of difficulties in its welding process, as oxidation, weld seam fire check and pore etc.For the welding of aluminium alloy, traditional method is mainly based on molten solder, the equipment complexity, and also relatively stricter to welder's specification requirement.Aluminium soldering has little, the dimensional accuracy advantages of higher of brazing member distortion as the important method that aluminium alloy connects, and is widely used in China in recent years.In soldering, the solder brazing brazing flux tradition of aluminium and alloy thereof is all occupied an leading position with villaumite base brazing flux.But such brazing flux exists the strong electrochemical corrosion of halogen ion pair mother metals such as chlorine, and hygroscopicity is very strong.At brazing area, meeting heavy corrosion brazing member after the postwelding residue moisture absorption, and, cause the brazing flux performance depreciation in the easy hydrolysis of heating process, even lost efficacy.In addition, postwelding is higher to the cleaning requirement of residue, and the residue of failing thoroughly to clean is the serious hidden danger of workpiece weld zone corrosion.The later stage seventies, a kind of insoluble brazing flux that develops rapidly, this brazing flux is by KF-AlF 3The potassium fluoroaluminate mixed salt that system constitutes.This brazing flux is two intermediate compound KAlF 4-K 3AlF 6Between the salt formed of eutectic point.As KF and AlF 3When forming eutectic point, eutectic temperature is 560 ℃, and brazing flux is just got the composition of this eutectic point.The performance of this brazing flux possesses unquestionable advantage than chloride brazing flux, and it is non-hygroscopic, does not corrode, and is called as " not having corrosion " brazing flux or Nocolok brazing flux, thereby is subjected to paying attention to widely.Prepare the four kinds of more common methods that mainly contain of NOCOLOK brazing flux at present, promptly smelting process, mechanical milling method, sintering process and water are transferred method (or water-boiling method).Adopt the NOCOLOK brazing flux of these four kinds of method preparations to contain free fluoride, these free fluorides are soluble in water, and welding work pieces is had corrosion.And smelting process power consumption is high, the wayward one-tenth shortcoming of grading.In recent years, there is report to adopt the synthetic NOCOLOK brazing flux of wet method (or chemical combination method).
The synthetic method of Nocolok brazing flux and prescription, total following eight kinds of comprehensive relevant reported in literature:
A. add water mill with quantitative AlF3 and KF and become to stick with paste, be lower than 200 ℃ of oven dry 1 hour then.
B. use quantitative AlF3 and KF heating and melting it, it is levigate to (150~200) sieve mesh to cool off thing.
C. synthesize K3AlF6 and KAlF4 respectively, then they are blended together in proportion the composition of minimum fusing point in the phasor.
D. with anhydrous AlF3 and KF dry powder mixing porphyrize in proportion, 300 ℃ of following roastings 1 hour.
E. quantitative Al (OH) 3 is dissolved in HF, uses quantitative KOH solution-treated then.Temperature keeps 30 ℃~100 ℃, acidity pH<4.
F. (or KOH is in mixed liquor K2CO3) to use unbodied Al (OH) 3 to join HF and KF; Or with (KOH K2CO3) joins in the mixed liquor of HF and amorphous Al (OH) 3.50 ℃~60 ℃ of temperature, pH=5~10.Can obtain fine size, suspension brazing flux that specific surface is big thus.
G. quantitative Al (OH) 3 or metallic aluminium bits are dissolved in the quantitative KOH solution, generate the mixed liquor of NaAlO2 and KOH, be converted into potassium aluminum fluoride flux with excessive HF again.
H. adopt wet method synthetic step by step, promptly use quantitative Al (OH) 3 to be dissolved in the HF of certainty ratio amount, then K2CO3 solution is slowly added, fully stir, regulate different pH values, change different evaporate to dryness temperature.Under suitable preparation condition (pH value approximate 4 or be slightly less than 4, about 100 ℃ of evaporate to dryness temperature), can make epigranular, tiny, specific area is big, and composition is potassium aluminum fluoride flux very accurately.
Summary of the invention
The preparation method who the purpose of this invention is to provide a kind of nano-powder aluminum alloy brazing flux.
Technical scheme of the present invention is that this brazing flux is by aluminium chloride (AlCl 3) and potassium fluoride (KF) generate by chemical reaction, the principal phase of product is K 2ALF 5H 2O has wherein added poly-hexylene glycol (PEG4000) as dispersant, adds the pH value to 4 that hydrofluoric acid (HF) is regulated product, in the preparation process with product after filtration, cleaning, vacuum drying treatment, dried reactant sintering obtains the brazing flux powder.
In the above-mentioned preparation process, the preferred mass percentage of aluminium chloride and potassium fluoride is: 9.16: 17.24.
Above-mentioned aluminium chloride (AlCl 3) adopt to analyze the aluminium chloride (AlCl of pure A.R 3), potassium fluoride (KF) adopts the potassium fluoride (KF) of chemical pure CP, and poly-hexylene glycol (PEG4000) adopts the poly-hexylene glycol (PEG4000) of chemical pure CP.
Above-mentioned dispersant addition is 8~13% of a solution concentration, and wherein preferred addition is 10%, 12%.
The reaction temperature of above-mentioned preparation process is 65~75 ℃, aluminium chloride (AlCl 3), the concentration of potassium fluoride (KF) solution is 1mol/L.
Used magnetic stirrer constant temperature to stir supersonic oscillations 20 minutes 1 hour in the above-mentioned preparation process.With dried reactant in 250 ℃ of sintering 2h.
The present invention adopts the chemical precipitation method principle to prepare nano level aluminum brazing flux powder.This brazing flux diameter of particle is minimum, composition is evenly accurate, the low brazing property of fusing point is good.
The invention has the beneficial effects as follows:
1) this brazing flux is a nano-powder, its fusing point lower (551 ℃), sprawl and gap filling performance better.
2) to have adopted aluminium chloride, potassium fluoride and hydrogen fluoride be primary raw material to this brazing flux prescription, and this NOCOLOK brazing flux prescription with relevant report at present is different, and especially aluminium chloride and hydrogen fluoride are that the prescription of major ingredient yet there are no report.
3) this brazing flux utilizes the chemical precipitation method principle, and the preparation method has innovation, controls reaction speed by control reaction temperature (as constant temperature) and solution concentration, and being determined by experiment reaction temperature is 70 ℃, AlCl 3Solution concentration is 1mol/L.
4) added poly-hexylene glycol PEG4000 (chemical pure CP) in the preparation process as dispersant, this dispersant has the long-chain macromolecule structure, forms the space network structure in solution, has hindered the reunion of product, is the key of this nanometer brazing flux dry powder of preparation.The dispersant addition is the 10~13% comparatively suitable of solution concentration.In addition, used supersonic oscillations in the preparation process,
The specific embodiment
Following embodiment does further concrete description to the present invention, but embodiments of the present invention are not limited thereto.
Embodiment 1
By the AlCl that to certainty ratio is 9.16: 17.24 3With the KF batching, the addition that dispersant gathers hexylene glycol (PEG4000) is 10% of a solution concentration, adds excessive HF, 70 ℃ of control reaction temperatures, regulate pH value, use the electromagnetic agitation instrument to stir 1h, supersonic oscillations 20min, reaction generates precipitation, it is filtered, cleans, vacuum drying.In 250 ℃ of sintering 2h, finally obtaining average-size is the aluminum brazing flux powder of 35 nanometers with dried sample.
Prepared brazing flux sprawl and gap filling performance sees the following form 1.As seen it is sprawled and gap filling performance is better than the prepared similar brazing flux of other method.
The spreading area of the different preparation method's brazing fluxes of table 1 and the contrast of joint filling length
Figure A20071002630500061
Adopt above-mentioned nanometer brazing flux and AL-Si solder to cooperate soldering LF21 aluminium alloy, and sample has been carried out tensile strength, and adopt SEM to observe the soldered fitting fracture apperance.The result shows that soldered fitting intensity reaches 146.2MPa near mother metal.
Embodiment 2
Repeat the step of example 1, difference is that the addition that dispersant gathers hexylene glycol PEG4000 (chemical pure CP) is 8% of a solution concentration.The average-size of gained powder is 45nm.
Embodiment 3
Repeat the step of example 1, difference is that the addition that dispersant gathers hexylene glycol PEG4000 (chemical pure CP) is 9% of a solution concentration.The gained powder is of a size of 38nm.
Embodiment 4
Repeat the step of example 1, difference is that the addition that dispersant gathers hexylene glycol PEG4000 (chemical pure CP) is 12% of a solution concentration.The gained powder is of a size of 48nm.
The present invention tests and raw materials usedly is: hydrofluoric acid (content 〉=40% is analyzed pure A.R); Potassium fluoride (analyzing pure A.R); Aluminium chloride (analyzing pure A.R); PEG4000 (chemical pure CP).The proportioning of chemical precipitation method adopts the mass percent KF of preparation gained brazing flux composition: AlF 3=45.8: 54.2, the mass percent of each raw material of the participation of seizing back confiscated property out reaction, this ratio is: KF: AlCl 3=9.16: 17.24.The specimen preparation step is as follows:
1. by AlCl to certainty ratio 3With the KF batching, this ratio is: KF: AlCl 3=9.16: 17.24.
2. KF and AlCl 3Be mixed with the solution of 1mol/L concentration, and be heated to 70 ℃.
3. at AlCl 3After adding dispersant PEG4000 in the solution, mix two kinds of solution.Add excessive HF in the course of reaction, regulate pH value.
4. use 90-2 type magnetic stirrer constant temperature to stir 1 hour, supersonic oscillations 20 minutes, reaction generates precipitation.
5. product is filtered, cleaned, vacuum drying.Dried sample in 250 ℃ of sintering 2h, is finally obtained nano level aluminum brazing flux powder.
It is eutectic point composition, i.e. AlF that proportioning adopts KF-AlF3 3With the molar percentage of KF be 45mol%: 55mol%, the percentage of each raw material of the participation of seizing back confiscated property out reaction, wherein HF is excessive.By AlCl to certainty ratio 3With the KF batching, add certain amount of dispersant and excessive HF, control reaction speed and temperature are regulated pH value, use the electromagnetic agitation instrument to stir 1h, supersonic oscillations 20min, reaction generates precipitation, it is filtered, cleans, vacuum drying.Dried sample in 250 ℃ of sintering 2h, is finally obtained nano level aluminum brazing flux powder.

Claims (7)

1. the preparation method of a nano-powder aluminum alloy brazing flux, it is characterized in that: this brazing flux is by aluminium chloride (AlCl 3) and potassium fluoride (KF) generate by chemical reaction, the principal phase of product is K 2ALF 5H 2O has wherein added poly-hexylene glycol (PEG4000) as dispersant, adds the pH value to 4 that hydrofluoric acid (HF) is regulated product, in the preparation process with product after filtration, cleaning, vacuum drying treatment, dried reactant sintering obtains the brazing flux powder.
2. preparation method according to claim 1 is characterized in that: in the above-mentioned preparation process, the preferred mass percentage of aluminium chloride and potassium fluoride is: 9.16: 17.24.
3. preparation method according to claim 1 and 2 is characterized in that: above-mentioned aluminium chloride (AlCl 3) adopt to analyze the aluminium chloride (AlCl of pure A.R 3), potassium fluoride (KF) adopts the potassium fluoride (KF) of chemical pure CP, and poly-hexylene glycol (PEG4000) adopts the poly-hexylene glycol (PEG4000) of chemical pure CP.
4. preparation method according to claim 1 is characterized in that: above-mentioned dispersant addition is 8~13% of a solution concentration, and wherein preferred addition is 10%, 12%.
5. preparation method according to claim 1 is characterized in that: the reaction temperature of above-mentioned preparation process is 65~75 ℃; Aluminium chloride (AlCl 3), the concentration of potassium fluoride (KF) solution is 1mol/L.
6. preparation method according to claim 1 is characterized in that: used magnetic stirrer constant temperature to stir supersonic oscillations 20 minutes 1 hour in the above-mentioned preparation process.
7. preparation method according to claim 1 is characterized in that: with dried reactant in 250 ℃ of sintering 2 hours.
CNB200710026305XA 2007-01-15 2007-01-15 Preparation method of nano-powder aluminum alloy brazing flux Expired - Fee Related CN100469496C (en)