CN100595663C - Diaphragm blade, method of manufacturing the same, and light quantity controller having the same - Google Patents
Diaphragm blade, method of manufacturing the same, and light quantity controller having the same Download PDFInfo
- Publication number
- CN100595663C CN100595663C CN200810004706A CN200810004706A CN100595663C CN 100595663 C CN100595663 C CN 100595663C CN 200810004706 A CN200810004706 A CN 200810004706A CN 200810004706 A CN200810004706 A CN 200810004706A CN 100595663 C CN100595663 C CN 100595663C
- Authority
- CN
- China
- Prior art keywords
- laser
- blade base
- resin
- vane member
- shaft component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A diaphragm blade and manufacturing method thereof as well as a light quantity controller containing the diaphragm. The diaphragm blade includes a light-shielding, thin-plate blade base made of laserabsorptive resin to regulate an aperture, and a first shaft portion made of laser transmissive resin and provided on one surface of the blade base. The first shaft portion includes a cylindrical member which is welded to the protruding weld portion, a protruding weld portion integrally formed with the blade base, and a recess formed at the back side of the protruding weld portion. The cylindricalmember has a first recess defined at one end thereof near the blade base and coming into contact with the protruding weld portion, and a second recess defined at the other end. A contact surface of the protruding weld portion is melted with laser beam transmitted through the cylindrical member, whereby the protruding weld portion is welded to the cylindrical member.
Description
Technical field
The present invention relates to a kind of being used for as the aperture blades of optical devices such as film camera, video camera and digital camera, the light controller of making the method for this aperture blades and having this aperture blades.
Background technology
Have the camera of solid-state image pickup and use the camera of film to have iris apparatus (light controller) usually as video camera and digital camera etc., this iris apparatus control aperture is with the depth of focus of checking camera lens and the light quantity that control focuses on the subject on film or the solid-state image pickup.In addition, the optical device of projected image can have light controller.Typically, this light controller comprise use a plurality of light shield blades (aperture blades) with change around as type and two aperture blades in the aperture of the optical axis of iris ring relatively move in opposite direction with the type in change aperture.
Last type can change the aperture continuously, therefore the aperture that can obtain to expect.Yet, in order to obtain the hole of sub-circular, must increase the quantity of aperture blades, increased cost thus.
On the other hand, back one type is used a spot of aperture blades, thereby can save cost.Yet, be difficult to obtain the hole of sub-circular.
Aperture blades has the light shield blade base usually and is used for the axial region of moving blade base portion.
Up to now,, arrange metal shaft at sheet metal or plastic plate place, perhaps at the vane plate place resin is set by injection mo(u)lding on the matrix (outsert molding) by mechanical filleting (caulking) in order to form axle at the blade place.These methods need a large amount of man-hours, and have integrity problem.In addition, the filleting vestige of axle or because the blade installation portion of the axle that injection mo(u)lding causes on the matrix may be outstanding from the dorsal part of blade with axle, and filleting vestige or blade installation portion may be hooked to plate when driven vane.
Therefore, shown in Figure 14 A, Japanese kokai publication hei 6-317826 communique proposes a kind of aperture blades 60, and this aperture blades 60 has blade substrate 61 and outstanding junction surface 62 and 63 of being made by synthetic resin, by injection moulding blade substrate 61 and outstanding junction surface 62 and 63 is formed.Therefore, can reduce the number and manufacturing cost in man-hour that is used to make aperture blades significantly.
In addition, as shown in Figure 14B, the special fair 6-68595 communique of Japan proposes a kind of exposure control blade 70, this exposure control blade 70 is manufactured into: the pin holding position at blade forms recess, blade is transported to the mould that is used for the injection moulding of shaping pin on blade, during clamping blade, the part by mould upwards pushes away recess so that it is projected in the chamber of mould, and the resin covering by pin and keep this recess when the injection moulding pin.Therefore, need not in aperture blades or blade manufacturing hole and just can cover with resin and keep pin, increase pin thus and keep intensity at the recess place.
Yet for the said aperture blade, the thickness of axial region is bigger than the thickness of blade base, thereby resin flow may be little during the injection moulding, and perhaps axial region may be out of shape.This may make the dimensional accuracy deterioration of axial region.Problem is more remarkable when the thickness of blade base reduces.On the contrary, if the thickness of blade base increases, then load may become big during the driven vane.Therefore, have to increase the size as vane drive devices such as motor, result, entire equipment may become big.
Summary of the invention
The light controller that the invention provides a kind of aperture blades, makes the method for this aperture blades and have this aperture blades, this aperture blades can reduce the size of equipment and increase its dimensional accuracy.
An aspect of of the present present invention comprises lamellar vane member and is arranged at least one lip-deep shaft component of vane member.Vane member is made by the laser absorption resin, and shaft component is made by the laser-transmissible resin.Utilize the laser beam that sees through shaft component that vane member is fused to shaft component, wherein, the fusing point of laser-transmissible resin is lower than the fusing point of laser absorption resin.
From below with reference to the explanation of accompanying drawing to exemplary embodiments, it is obvious that further feature of the present invention will become.
Description of drawings
Fig. 1 schematically shows to have the exploded perspective view of the structure of the light controller of aperture blades according to an embodiment of the invention;
Fig. 2 is the planimetric map that illustrates according to the aperture blades of first embodiment;
Fig. 3 is the partial sectional view according to the aperture blades of first embodiment that illustrates along Fig. 2 center line III-III intercepting;
Fig. 4 is the figure that the molten state when changing irradiation time and changing laser output for each irradiation time is shown;
Fig. 5 is the figure that the molten state when changing laser output for 1 second irradiation time is shown;
Fig. 6 is the planimetric map that illustrates according to the aperture blades of second embodiment;
Fig. 7 is the partial sectional view according to the aperture blades of second embodiment that illustrates along Fig. 6 center line VII-VII intercepting;
Fig. 8 A and Fig. 8 B illustrate the first axle part and cylindrical member respectively.Fig. 8 A is the cut-open view that illustrates near the first axle part of outstanding weld portion, and Fig. 8 B is the cut-open view that cylindrical member is shown;
Fig. 9 A to Fig. 9 D diagram forms the method according to the first axle part of the aperture blades of second embodiment, and Fig. 9 A illustrates first step, and Fig. 9 B illustrates second step, and Fig. 9 C illustrates third step;
Figure 10 is the planimetric map that illustrates according to the aperture blades of the 3rd embodiment;
Figure 11 is the partial sectional view according to the aperture blades of the 3rd embodiment that illustrates along Figure 10 center line XI-XI intercepting;
Figure 12 is the diagram that the variation of the first axle part among Figure 11 is shown;
Figure 13 is the diagram that another variation of the first axle part among Figure 11 is shown;
Figure 14 A and Figure 14 B are the cut-open views that illustrates according to the structure of the aperture blades of prior art, and Figure 14 A illustrates first prior art, and Figure 14 B illustrates second prior art.
Embodiment
First embodiment
Fig. 1 schematically shows the exploded perspective view that has according to the structure of the light controller of the aperture blades of the first embodiment of the present invention.
In Fig. 1, be provided with aperture blades 1,2,3,4,5 and 6.Aperture blades 1 comprises: thin plate blade base (vane member) 1a, and it regulates the hole of light path; The first axle part 1b, it is arranged on the surface of blade base 1a the motion with control blade base 1a; And the second axle part 1c, the motion with control blade base 1a is gone up on its another surface that is arranged on blade base 1a.Similar with aperture blades 1, aperture blades 2 to 6 comprises blade base 2a to 6a, the first axle part 2b to 6b and the second axle part 2c to 6c (although some in them are not shown) respectively.The structure of aperture blades 2 to 6 and the structure of aperture blades 1 are similar, therefore omit its explanation.
Revolving member 7 is ring-types, and has opening 7a in central authorities.Revolving member 7 comprises axis hole 7b to 7g, is divided into the rotation assembling teat 7h and the gear 7i of six parts.
Stepping motor 10 drives revolving member 7.Pinion wheel 11 is fixed to the top of the axle of stepping motor 10, and is installed to the 9c of motor mounting portion of pressing element 9.Pinion wheel 11 passes the hole 9b of pressing element 9, and with the gear 7i of revolving member 7 engagement.
Aperture blades 1 is arranged along circumference around optical axis equably to 6.Blade base 1a to 6a overlaps each other, thereby can control the hole of aperture.When overlapping areas increased, the hole of aperture reduced.
When stepping motor 10 drove, pinion wheel 11 rotated, and rotates revolving member 7 accordingly with the rotation of pinion wheel 11.The rotation of revolving member 7 makes the first axle part 1b to 6b of aperture blades 1 to 6 move, and makes the second axle part 1c to 6c move along the cam path 8b to 8g of cam member 8.Six aperture blades 1 to 6 rotate in a similar fashion, continuously change the state in hole thus between the stop down state of the opening 8a that full open position that aperture blades 1 to 6 is kept out of the way from the opening 8a of cam member 8 and aperture blades 1 to 6 are inserted into cam member 8.That is to say, change the aperture of aperture, thereby can come the amount (light quantity) of control bundle by control step motor 10.
Then, detailed description is according to the blade base of the aperture blades of first embodiment and the relation between the axial region.
Fig. 2 is the planimetric map that the aperture blades 1 among Fig. 1 is shown.Fig. 3 is the partial sectional view that illustrates along the aperture blades 1 of the intercepting of the line III-III among Fig. 2.Below with reference to Fig. 2 and Fig. 3 relation between blade base 1a and the first axle part 1b is described.Therefore the relation between relation between other blade base 2a to 6a and the first axle part 2b to 6b and blade base 2a to 6a and the second axle part 2c to 6c and the relation object of previous example seemingly omit its explanation.
Fig. 2 and Fig. 3 illustrate the shape of the first axle part 1b after laser beam irradiation, perhaps the first axle part 1b and the integrally formed state of blade base 1a.Before laser beam irradiation, the first axle part 1b is by constituting with the lower part: outstanding weld portion 31, and cylindrical member 40 (explanation after a while) is welded to this outstanding weld portion 31; Recess 32, it is formed on the dorsal part of outstanding weld portion 31; And cylindrical member (protruding member) 40, it is welded to outstanding weld portion 31.
For cylindrical member 40 is fused to blade base 1a, at first, cylindrical member 40 is arranged in outstanding weld portion 31 places of blade base 1a, and will be arranged in second recess, 42 sides of cylindrical member 40 as one of the pressing plate clear glass (not shown) of determining.By clear glass cylindrical member 40 is crimped onto blade base 1a.The periphery of cylindrical member 40 is coated with the shadow shield that can not see through laser beam.Because the periphery of cylindrical member 40 is coated with shadow shield, therefore only required zone can be by laser beam irradiation.
Then, laser beam is transmitted into blade base 1a from second recess, 42 sides of cylindrical member 40.From second recess, 42 side emitted laser bundles see through cylindrical member 40, arrive blade base 1a outstanding weld portion 31, be absorbed then.At this moment, the laser beam that absorbs at the surface of contact place that first recess 41 of cylindrical member 40 contacts with the outstanding weld portion 31 of blade base 1a is gathered as energy.Therefore, the surface of contact of outstanding weld portion 31 is heated and melts, and owing to the face of weld transmission of heat from blade base 1a, therefore, the surface of contact of first recess 41 of cylindrical member 40 is heated and melts.Therefore, blade base 1a is fused to cylindrical member 40 integratedly.
The height H of cylindrical member 40 is 0.8mm for example, and the thickness t of blade base 1a is 0.14mm (Fig. 3) for example.The thickness t of the blade base 1a that is made by the laser absorption resin is significantly less than the height H of the cylindrical member of being made by the laser-transmissible resin 40; Blade base 1a is subjected to the heat affecting of laser radiation easily, and to the laser radiation sensitivity.If the energy of laser beam is excessive, then may in blade base 1a, produce the hole, and the heat that is delivered to cylindrical member 40 may increase.Therefore, the fusing amount of cylindrical member 40 may increase, and is difficult to keep dimensional accuracy.On the contrary, if the energy of laser beam is too small, then welding may become incomplete.Thereby, must under blade base 1a and cylindrical member 40 indeformable situations, cylindrical member 40 be fused to blade base 1a, and must obtain to have the good molten state of given welding power.
In the present embodiment, blade base 1a is made by the laser absorption resin.For example, this laser absorption resin is the material that mainly is made of the polyethylene terephthalate (PET) that contains black paint, carbon etc.Cylindrical member 40 is made by the laser-transmissible resin.For example, this laser-transmissible resin is made of the polycarbonate that contains glass material (PC).By coming welding blade base 1a and cylindrical member 40 with laser beam irradiation blade base 1a.The fusing point of laser-transmissible resin is lower than the fusing point of laser absorption resin.In addition, the difference of the fusing point of the fusing point of laser-transmissible resin and laser absorption resin can be less than 20 ℃.
In the present embodiment, blade base 1a is made by the laser absorption resin, and a lip-deep cylindrical member 40 that is arranged on blade base 1a is made by the laser-transmissible resin, and with the laser beam welding blade base 1a and the cylindrical member 40 that see through cylindrical member 40.In addition, the fusing point of laser-transmissible resin is lower than the fusing point of laser absorption resin.Therefore, can come welding blade base 1a and cylindrical member 40 by laser radiation, can be under blade base 1a and cylindrical member 40 indeformable situations welding blade base 1a and cylindrical member 40, and can obtain to have the good molten state of given welding power.Thereby, can keep the intensity of protruding member, the dimensional accuracy of protruding member can be increased, and manufacturing cost can be reduced.
In the present embodiment, though the laser absorption resin is made by the material that mainly is made of the polyethylene terephthalate that contains black paint, carbon etc., be not limited thereto.The laser absorption resin can be made by the material that mainly is made of PC resin that contains black paint, carbon etc. or ABS resin.
In addition, though the laser-transmissible resin is made by the polycarbonate that contains glass material, be not limited thereto.The laser-transmissible resin can be made by the material that mainly is made of the polycarbonate that contains glass material.As selection, the laser-transmissible resin can be made by the colourless or transparent POM resin that contains glass material.
In the present embodiment, though second recess 42 that cylindrical member 40 has the end of the close blade base 1a that is arranged on cylindrical member 40 and first recess 41 that contacts with outstanding weld portion 31 and is arranged on the other end is not limited thereto.Cylindrical member 40 can only have the end of the close blade base 1a that is arranged on cylindrical member 40 and first recess 41 that contacts with outstanding weld portion 31.
In addition, in the present embodiment, though the height H of cylindrical member 40 is 0.8mm, and the thickness t of blade base 1a is 0.14mm, can change these sizes according to operating position.
Then, the following describes according to the blade base 1a of the aperture blades 1 of first embodiment and the welding performance of cylindrical member 40.
Selection is used for the material of laser-transmissible resin and laser absorption resin, with the condition of the condition that satisfies (fusing point of laser-transmissible resin)＜(fusing point of laser absorption resin) and 0 ℃＜(fusing point of laser absorption resin)-(fusing point of laser-transmissible resin)＜20 ℃.That is to say that the difference that the fusing point of combination laser permeability resin is lower than the material of fusing point of laser absorption resin and laser absorption resin and laser-transmissible resin is less than 20 ℃ material.Especially, the blade base of making the cylindrical member made by the polycarbonate that contains glass material (fusing point=245 ℃) and making by the material that mainly constitutes by the polyethylene terephthalate that contains material with carbon element (fusing point=255 ℃).Then, with the surface of contact between semiconductor laser irradiation blade base and the cylindrical member 1 second, and form face of weld.Change the laser output of this irradiation time of 1 second, and export, observe the molten state of blade base and cylindrical member for the laser of each change.Table 1 illustrates observations.
Table 1
| Laser output (W) | 11.0 | 12.0 | 13.0 | 14.0 | 15.0 | 16.0 | 17.0 | 18.0 |
| The molten state of cylindrical member | △ | △ | △ | △ | ○ | ○ | × | × |
| The molten state of blade base | △ | △ | △ | ○ | ○ | ○ | × | × |
| Observations | NG | NG | NG | NG | OK | OK | NG | NG |
Irradiation time: 1 second, cylindrical member: contain the PC of glass, blade base: PET
In table 1, " △ " represents that the molten state of face of weld of each parts is insufficient, " * " expression deforms except face of weld, expands or bore a hole owing in excessive each parts of molten state, and " zero " represents that the molten state of the face of weld of each parts is kilters sufficient and that have given welding power.In observations, " OK " expression completes successfully the laser welding of resin, and " NG " represents to fail to finish the laser welding of resin.
As shown in table 1, for 14W or the output of lower laser, the molten state of the surface of contact of cylindrical member is insufficient, and for the laser output of the scope of 15W～16W, the molten state of the surface of contact of cylindrical member is sufficient.For 17W or higher laser output, molten state is excessive, and deforms, expands or bore a hole.For 13W or the output of lower laser, the molten state of blade base is insufficient, and for the laser output of the scope of 14W～16W, the molten state of blade base is sufficient.For 17W or higher laser output, molten state is excessive, and bores a hole.
Reference table 1, for 1 second irradiation time, if the laser output area is 15W～16W, then the molten state of cylindrical member and blade base all became fully, completes successfully the laser welding of resin thus.
Then, Fig. 4 illustrates the molten state when changing irradiation time (0.7 second and 0.5 second) and changing laser and export for each irradiation time.Notice that in Fig. 4, " white square " is used to represent excessive molten state, and " black triangle " is used to represent inadequate molten state.
As shown in Figure 4, when irradiation time is configured to 0.5 second, for 18W or lower laser output, molten state insufficient (being plotted as " black triangle ").For 19W or higher laser output, cylindrical member 40 distortion (being plotted as " white square ").
When irradiation time is configured to 0.7 second, for 15W or lower laser output, molten state insufficient (being plotted as " black triangle ").For 19W or higher laser output, cylindrical member 40 distortion (being plotted as " white square ").On the contrary, for the laser output of the scope of 16W～18W, welding cylindrical member 40 and blade base 1a under cylindrical member 40 indeformable situations, and can obtain to have the good molten state (being plotted as " dark circles ") of given welding power.
When irradiation time is configured to 1.0 seconds, for 14W or lower laser output, molten state insufficient (being plotted as " black triangle ").For 17W or higher laser output, cylindrical member 40 distortion (being plotted as " white square ").On the contrary, so laser output to the scope of 15W～16W, welding cylindrical member 40 and blade base 1a under cylindrical member 40 indeformable situations, and can obtain to comprise the zone (being plotted as " dark circles ") of good molten state with given welding power.
With reference to figure 4, can realize the resin laser welding between cylindrical member and the blade base under the following conditions: the fusing point of laser-transmissible resin (245 ℃) is lower than the fusing point (255 ℃) of laser absorption resin, the difference of the fusing point of laser absorption resin and laser-transmissible resin is less than 20 ℃, and for 1.0 seconds irradiation time, the laser output area was 15W～16W.In addition, can be under the following conditions realize resin laser welding between cylindrical member and the blade base with high dimensional accuracy: the fusing point of laser-transmissible resin is lower than the fusing point of laser absorption resin, the difference of the fusing point of laser absorption resin and laser-transmissible resin is less than 20 ℃, and for 0.7 second irradiation time, the laser output area was 16W～18W.
Then, as a comparative example, the cylindrical member of making the blade base made by the material that mainly constitutes and making by polycarbonate (fusing point=225 ℃) by the polyethylene terephthalate that contains material with carbon element (fusing point=255 ℃).Especially, the difference of this comparative example and above-mentioned example only is: the polycarbonate that is used for cylindrical member does not contain glass component.With the surface of contact between semiconductor laser irradiation blade base and the cylindrical member 1 second, and form face of weld.Change the laser output of this irradiation time of 1 second, and export, observe the molten state of blade base and cylindrical member for the laser of each change.Table 2 illustrates observations.
Table 2
| Laser output (W) | 11.0 | 12.0 | 13.0 | 14.0 | 15.0 | 16.0 | 17.0 | 18.0 |
| The molten state of cylindrical member | △ | ○ | ○ | × | × | × | × | × |
| The molten state of blade base | △ | △ | △ | ○ | ○ | ○ | × | × |
| Observations | NG | NG | NG | NG | NG | NG | NG | NG |
Irradiation time: 1 second, cylindrical member: PC, blade base: PET
In table 2, " △ " represents that the molten state of face of weld of each parts is insufficient, " * " expression deforms except face of weld, expands or bore a hole owing in excessive each parts of molten state, and " zero " represents that the molten state of the face of weld of each parts is kilters sufficient and that have given welding power.In observations, " OK " expression completes successfully the laser welding of resin, and " NG " represents to fail to finish the laser welding of resin.
As shown in table 2, for 11W or the output of lower laser, the molten state of the surface of contact of cylindrical member is insufficient, and for the laser output of the scope of 12W～13W, the molten state of the surface of contact of cylindrical member is sufficient.For 14W or higher laser output, molten state is excessive, and deforms, expands or bore a hole.For 13W or the output of lower laser, the molten state of blade base is insufficient, and for the laser output of the scope of 14W～16W, the molten state of blade base is sufficient.For 17W or higher laser output, molten state is excessive, and bores a hole.Reference table 2, only by the output of control laser, the molten state of cylindrical member and blade base is all insufficient, therefore can not obtain good molten state.
Fig. 5 illustrates to change the figure of molten state that irradiation time is 1 second laser output.Notice that in Fig. 5, " white square " is used to represent excessive molten state, and " black triangle " is used to represent inadequate molten state.
As shown in Figure 5, for 14W or higher laser output, the heat that is delivered to cylindrical member 40 becomes big, and deform, expand or bore a hole in cylindrical member 40 (being plotted as " white square " among the figure).On the contrary, for 13W or lower laser output, welding insufficient (being plotted as " black triangle ").
Therefore, in this comparative example, can not obtain with the zone of given welding power welding cylindrical member 40 with the good molten state of blade base 1a.
Second embodiment
Light controller with aperture blades according to a second embodiment of the present invention is described.The difference of the light controller of the light controller of second embodiment and first embodiment only is aperture blades.The essential structure of the essential structure of the light controller of second embodiment and light controller shown in Figure 1 is similar, therefore omits its explanation.
Thereafter, detailed description is according to the blade base 101a of the aperture blades 101 of second embodiment and the relation between the first axle part 101b.
Fig. 6 is the planimetric map that the aperture blades 101 that is applied to the structure among Fig. 1 is shown.Fig. 7 is the partial sectional view that illustrates along the aperture blades 101 of the intercepting of the line VII-VII among Fig. 6.Below with reference to Fig. 6 and Fig. 7 relation between blade base 101a and the first axle part 101b is described.
In Fig. 6 and Fig. 7, the first axle part 101b comprises: outstanding weld portion 131, and it is integrally formed with blade base 101a, and cylindrical member 140 (illustrating after a while) is welded to this outstanding weld portion 131; Recess 132, it is formed on the dorsal part of outstanding weld portion 131; And cylindrical member 140 (shaft component), it is welded to outstanding weld portion 131.
Fig. 8 A and Fig. 8 B be diagram the first axle part 101b and cylindrical member 140 respectively.Fig. 8 A is near the cut-open view that illustrates the outstanding weld portion 131 of the first axle part 101b.Fig. 8 B is the cut-open view that cylindrical member 140 is shown.
Shown in Fig. 8 A, outstanding weld portion 131 has the surface of contact 131a (first surface of contact) that contacts with cylindrical member 140, and cylindrical member 140 has the surface of contact 141a (second surface of contact) that contacts with outstanding weld portion 131.Suppose that h2 is the outstanding length (length from the first type surface of blade base 101a to surface of contact 131a) of outstanding weld portion 131, and h 1 is the recessed degree of depth (degree of depth from the end face of cylindrical member 140 to surface of contact 141a) of first recess 141, and then degree of depth h1 and outstanding length h2 satisfy the relation of h1＞h2.
Fig. 9 A to Fig. 9 D diagram forms the method for the first axle part 101b of aperture blades 101.Fig. 9 A illustrates first step, and Fig. 9 B illustrates second step, and Fig. 9 C illustrates third step.The method that forms the second axle part 101c is similar with the method that forms the first axle part 101b, therefore omits its explanation.
In Fig. 9 A to Fig. 9 C, make the blade base 101a that makes and have from the teeth outwards outstanding weld portion 131 by the laser absorption resin by pressurization, and make the cylindrical member 140 of making and on both ends of the surface, having first recess 141 and second recess 142 by the laser-transmissible resin.Then, use the align member (not shown), cylindrical member 140 contacts with blade base 101a, makes the recess 141 of winning roughly arrange (first step among Fig. 9 A) coaxially with outstanding weld portion 131.Then, use the assembling tool (not shown), the recess 132 of blade base 101a is pressed to first recess 141 (along the direction shown in the arrow among the figure) of cylindrical member 140, make the surface of contact 131a of outstanding weld portion 131 contact (second step among Fig. 9 B) with the surface of contact 141a of first recess 141.Although under the relation of above-mentioned h1＞h2, the surface of contact 131a of outstanding weld portion 131 does not contact (Fig. 9 A) with the surface of contact 141a of first recess 141 in the normal state, but press to first recess 141 by giving prominence to weld portion 131, make blade base 101a elastic deformation, therefore, the surface of contact 131a of outstanding weld portion 131 contacts with the surface of contact 141a of first recess 141.
Then, under the surface of contact 141a state of contact of the surface of contact 131a of outstanding weld portion 131 and first recess 141, be used to laser beam irradiation cylindrical member 140 (third step among Fig. 9 C) from the laser irradiation device of second recess, 142 sides of cylindrical member 140.Because cylindrical member 140 is made by the laser-transmissible resin, so laser beam is transmitted on the surface of contact 131a of outstanding weld portion 131 then through cylindrical member 140.The laser beam that is transmitted on the surface of contact 131a that gives prominence to weld portion 131 makes the surface of contact 131a of outstanding weld portion 131 melt, and will give prominence to weld portion 131 thus and be fused to cylindrical member 140.At this moment, between outstanding weld portion 131 and cylindrical member 140, form welding layer 150 (Fig. 9 D).Therefore, can strengthen adhesion between the surface of contact 141a of the surface of contact 131a of outstanding weld portion 131 and first recess 141.In addition, because the dorsal part in outstanding weld portion 131 forms recess 132, therefore resin can be not outstanding from the back side as the blade base 101a of the slipping plane of the cam member 8 Fig. 1, therefore, can keep sliding condition (sliding condition) between cam member 8 and the aperture blades 101 reliably.In addition, because cylindrical member 140 is made by the laser-transmissible resin, the decay of laser beam when seeing through cylindrical member 140 minimized.Thereby, the surface of contact 131a that gives prominence to weld portion 131 can be fused to effectively the surface of contact 141a of first recess 141.
When being formed on welding layer 150 surface of contact 131a and surface of contact 141a between being cured, with pressing mode the first axle part 101b be fixed to blade base 101a thereafter.Therefore, the first axle part 101b is fixed to blade base 101a with being stabilized, and can not unclamp with blade base 101a.
For present embodiment, because blade base 101a is made by the laser absorption resin, and cylindrical member 140 is made by the laser-transmissible resin, and utilize the laser beam that sees through cylindrical member 140 that blade base 101a is fused to cylindrical member 140, so even can on thin blade base, easily form axial region.Thereby, can reduce the size of equipment, and can improve dimensional accuracy.In addition, because by using the laser beam welding to form axial region, therefore with by machinery pressurization or the axial region that on vane plate, forms by using injection mo(u)lding on the resin matrix compare, can not produce outstanding at the dorsal part of the axial region of blade base.Therefore, can keep sliding condition between cam member 8 and the aperture blades 101 reliably.
In the present embodiment, though second recess 142 that cylindrical member 140 has the end of the close blade base 101a that is arranged on cylindrical member 140 and first recess 141 that contacts with outstanding weld portion 131 and is arranged on the other end is not limited thereto.Cylindrical member 140 can only have the end of the close blade base 101a that is arranged on cylindrical member 140 and first recess 141 that contacts with outstanding weld portion 131.
The 3rd embodiment
The light controller of the aperture blades with a third embodiment in accordance with the invention is described.The difference of the light controller of the light controller of the 3rd embodiment and first embodiment only is aperture blades.The essential structure of the essential structure of the light controller of the 3rd embodiment and light controller shown in Figure 1 is similar, therefore omits its explanation.
Thereafter, detailed description is according to the blade base 201a of the aperture blades 201 of the 3rd embodiment and the relation between the first axle part 201b.
Figure 10 is the planimetric map that the aperture blades 201 that is applied to the structure among Fig. 1 is shown.Figure 11 is the partial sectional view that illustrates along the aperture blades 201 of the intercepting of the line XI-XI among Figure 10.Below with reference to Figure 10 and Figure 11 relation between blade base 201a and the first axle part 201b is described.
With reference to Figure 10 and Figure 11, blade base 201a has the light shield performance.The first axle part 201b is engaged to blade base 201a.Especially, by to as mainly board member that laser absorption resins such as material that the polyethylene terephthalate of black paint for example constitutes make is exerted pressure and blade base 201a is made in punching press by containing.For example utilize laser-transmissible ester moulding the first axle part 201b such as material as transparent natural standard polycarbonate (not being filled with) as other materials such as carbon.
The first axle part 201b has chamfered section 232 at 231 places, end that join blade base 201a to.In the present embodiment, form chamfered section 232 by cutting sth. askew.The first axle part 201b is the entity component (entity cylinder) with round section.The first axle part 201b has surface of contact 233 at 231 places, end that join blade base 201a to, and this surface of contact 233 contacts with blade base 201a.Suppose that D2 is the diameter of surface of contact 233, and D1 is the external diameter of the first axle part 201b, then the diameter D2 of surface of contact 233 is less than the outer diameter D 1 of the first axle part 201b.When the first axle part 201b was assembled to the hole of plate as center of rotation, outer diameter D 1 was an effective value.
In the aperture blades 201 of so constructing, for blade base 201a is arrived in the first axle part 201b welding (joint), under the first type surface state of contact of the surface of contact 233 of the first axle part 201b and blade base 201a, make the first axle part 201b remain on the precalculated position of blade base 201a, then, launch the laser beam of the schedule time from the last direction blade base 201a of the first axle part 201b.
See through the first axle part 201b of laser-transmissible resin from the top emitted laser bundle of the first axle part 201b, be transmitted into then on the blade base 201a.Therefore, (on the thin-plate element) forms point of irradiation on blade base 201a, and absorbs laser beam by the blade base 201a of laser absorption resin.At this moment, the plane of illumination of blade base 201a (point of irradiation) produces heat.Utilize this heat, blade base 201a reaches the fusing point of resin and is melted.In addition, this heat is delivered to the surface of contact 233 of the first axle part 201b from the surface of contact 235 of blade base 201a.Therefore, the surface of contact 233 of the first axle part 201b is heated and is melted.At this moment, the resin that is melted can be not outstanding from the periphery of the first axle part 201b, and rest on the gap location between chamfered section 232 and the blade base 201a.As a result, the fusion of the melt portions of the melt portions of blade base 201a and the first axle part 201b, after the irradiation that stops laser beam, along with temperature reduces, this melt portions is cured, and therefore, blade base 201a and the first axle part 201b are by welding integratedly.
Under a lot of welding situations such as use laser beam, must think better of the welding condition, to realize stable batch process.Especially, this condition can comprise suitable laser output and laser irradiation time, so that corresponding with the variation of workpiece material and combination of materials and material and shape.
Then, the laser welding condition that is suitable for making aperture blades 201 is described.
Table 3 and table 4 illustrate when be welded to by the first axle part 201b that makes as the polycarbonate (fusing point: about 225 ℃) of laser-transmissible resin that the material that mainly is made of the polyethylene terephthalate (fusing point: about 255 ℃) as the laser absorption resin makes contain the blade base 201a of light shielding member the time, the molten state of blade base 201a and the first axle part 201b.Being used as laser beam, irradiation time at semiconductor laser is set to constant (for example, 1 second) and changes under the condition of laser output and realize welding.
At first, the experimental result of example shown in the table 3.This is that the shape of the first axle part is the situation of the external diameter of entity cylinder and surface of contact less than the external diameter of the first axle part (having chamfered section).
Table 3
| Laser output (W) | 11.0 | 12.0 | 13.0 | 14.0 | 15.0 | 16.0 | 17.0 |
| The molten state of the first axle part | △ | ○ | ○ | ○ | × | × | × |
| The molten state of blade base | △ | △ | △ | ○ | ○ | ○ | × |
| Observations | NG | NG | NG | OK | NG | NG | NG |
Irradiation time: 1 second, the first axle part: have chamfered section
In table 3, the molten state of the surface of contact of " △ " expression blade base or the first axle part is insufficient, " * " expression deforms except surface of contact, expands or bore a hole owing in excessive each parts of molten state, and " zero " expression has the good molten state of given welding power." OK " is illustrated between blade base and the first axle part and completes successfully welding.
Then, table 4 illustrates the experimental result of comparative example.This is that the shape of the first axle part is the situation that the external diameter of entity cylinder and surface of contact equals the external diameter of the first axle part (not having chamfered section).
Table 4
| Laser output (W) | 11.0 | 12.0 | 13.0 | 14.0 | 15.0 | 16.0 | 17.0 |
| The molten state of the first axle part | △ | ○ | ○ | × | × | × | × |
| The molten state of blade base | △ | △ | △ | ○ | ○ | ○ | × |
| Observations | NG | NG | NG | NG | NG | NG | NG |
Irradiation time: 1 second, the first axle part: do not have chamfered section
In table 4, if the external diameter of the first axle part equals the external diameter of surface of contact, then for 11W or lower laser output, near the molten state the surface of contact of the first axle part is insufficient.For the laser output of 12W or 13W, molten state is good.For 14W or higher laser output, molten state is excessive, makes molten resin outstanding along the radially periphery from the first axle part of the first axle part, causes the original outer diameter of the external diameter of the first axle part greater than the first axle part.For 13W or lower laser output, near the molten state the surface of contact of blade base is insufficient.For the laser output of 14～16W, it is good that molten state becomes.For 17W or higher laser output, because excessive molten state is bored a hole in blade base.
The result of reference table 4 equals at the external diameter of the first axle part under the situation of external diameter of surface of contact, and only the laser output that is transmitted on the surface of contact by control can not make blade base and the first axle part melt fully, thereby, can not obtain given heat seal strength.
On the contrary, reference table 3, for the first axle part that has as shown in figure 11 the chamfered section that is provided with, for the laser output of 14W, although the resin of fusing is along radially the expanding a little of the first axle part, also the periphery from the first axle part is outstanding for molten resin.As a result, the external diameter of the first axle part after the laser welding is equal to or less than the original outer diameter of the first axle part.Therefore, the molten state of the first axle part shows as " zero ".The molten state of blade base and the molten state of the blade base shown in the table 4 are similar, therefore omit its explanation.
The result of reference table 3, have as shown in figure 11 in use under the situation of the first axle part of the chamfered section that is provided with, when 1 second laser of emission on surface of contact, for the laser output of 14W, can complete successfully the welding between blade base and the first axle part, and obtain given heat seal strength.
The result of reference table 3 and table 4 under the situation of shaft component that welding is made by different resin materials and blade base, because the first axle part has chamfered section at its axial end portion, therefore can relax successfully the condition and range of welding.In addition, owing to relaxed the condition and range of laser welding, so this scope can be corresponding with the variation of the state of the variation of the control of laser output and parts, realizes stable batch process thus in the manufacturing step of aperture blades.
As mentioned above, for present embodiment, the first axle part 201b has chamfered section 232 at 231 places, end that contact with blade base 201a.Therefore, when by laser beam the first axle part 201b being fused to blade base 201a, molten resin rests in the gap between chamfered section 232 and the blade base 201a, and can be outstanding from the periphery of the first axle part 201b.Thereby, can prevent the periphery distortion of the first axle part 201b.In addition, because molten resin can be outstanding from the periphery of the first axle part 201b, therefore can relax the condition and range of the energy of the laser beam that is used to realize good molten state.In addition, owing to utilize laser beam that the first axle part 201b is fused to blade base 201a, therefore can reduce the manufacturing cost of fader control blade.Therefore, can reduce manufacturing cost, can improve dimensional accuracy, and can realize stable welding.
In the present embodiment, though the first axle part 201b is made by the laser-transmissible resin, and blade base 201a is made by the laser absorption resin, can exchange material.Especially, the first axle part can be made by the laser absorption resin with light shield performance, and the part that blade base contacts with the first axle part can be made by the laser-transmissible resin.In this case, the remainder that does not contact with the first axle part of blade base is coated with or deposits light shielding material.In addition, when welding blade base and the first axle part, laser beam is transmitted into the first axle part from the top of blade base.Utilize this structure, can obtain and above-mentioned advantage confers similar advantages.
In the present embodiment, though the laser-transmissible resin is made of polycarbonate, be not limited thereto, the laser-transmissible resin can be the material that mainly is made of polycarbonate.In addition, laser-transmissible resin and laser absorption resin can be made of the material except above-mentioned material.
In addition, in the present embodiment,, be not limited thereto though form chamfered section 232 by cut sth. askew (C-cuts sth. askew), and can be by the R-formation chamfered section of cutting sth. askew.As selection, as long as limit the gap between chamfered section and blade base 201a, chamfered section just can have Any shape.
Figure 12 is the diagram that the variation of the first axle part 201b among Figure 11 is shown.
In Figure 12, the first axle part 240 has chamfered section 242 at 241 places, end that are welded to blade base 201a.Chamfered section 242 has step shape.In addition, the first axle part 240 is the entity components (entity cylinder) with round section.The first axle part 240 has surface of contact 243 at 241 places, end that are engaged to blade base 201a, and this surface of contact 243 contacts with blade base 201a.
For this variation, because chamfered section 242 has step shape, therefore when the first axle part 240 is fused to blade base 201a, molten resin rests in the gap between chamfered section 242 and the blade base 201a, and can not give prominence to from the periphery of the first axle part 240.Thereby, can prevent the periphery distortion of the first axle part 240 reliably.
Figure 13 is the diagram that another variation of the first axle part 201b among Figure 11 is shown.
As shown in figure 13, the first axle part 250 is the entity components with round section.The first axle part 250 has surface of contact 253 at 251 places, end that are welded to blade base 201a, and this surface of contact 253 contacts with blade base 201a.In addition, the surface of contact 253 of the first axle part 250 has recess 254.
Therefore, surface of contact 253 has roughly circular (ring-type).
In addition, be provided with a portion (gate portion) (not shown) in the bottom surface of recess 254, when with ester moulding the first axle part 250, need this one.Utilize this structure, the outside surface of the first axle part 250, upper surface and surface of contact 253 do not have outshot owing to door portion, can prevent the operating troubles that outshot causes welding to lose efficacy and caused aperture blades 201.
Be fused under the situation of blade base 201a at the first axle part 250 that will have above-mentioned structure, shadow shield 260 is arranged in the top of the first axle part 250, be launched on the first axle part 250 by the laser beam that is formed on the roughly circular hole 261 among the shadow shield 26C.At this moment, the outer diameter D of the point of irradiation of the laser beam on the aperture blades 201 4 satisfies and concerns D3＜D4＜D1, and wherein D1 is the external diameter of the first axle part 250, and D3 is the internal diameter of recess 254.The laser beam in the hole 261 by shadow shield 260 only is transmitted into the central portion of surface of contact 253, and can not be transmitted into peripheral part.Therefore, by the interior perimembranous of laser beam fusing surface of contact 253, and molten resin is projected into the inner space of recess 254.Yet the peripheral part of surface of contact 253 is not melted, and not outstanding from the outstanding molten resin of the peripheral part of blade base 201a.
For this variation, because recess 254 is arranged on the surface of contact 253 of the first axle part 250, therefore, when using laser beam that the first axle part 250 is fused to blade base 201a, molten resin rests in the recess 254, and can be not outstanding from the peripheral part of the first axle part 250.Thereby, can prevent the peripheral part distortion of the first axle part 250 reliably.In addition, because laser beam is launched on the first axle part 250, make the diameter of the point of irradiation on the blade base 201a become D4 (D3＜D4＜D1), therefore, the peripheral part of surface of contact 253 is not melted, thereby, can further prevent the peripheral part distortion of the first axle part 250 reliably.
In this variation,, be not limited thereto though recess 254 is arranged on the surface of contact 253 of the first axle part 250.Recess 254 is not the surface of contact 253 that must be arranged on the first axle part 250.In this case, the inside diameter D 4 that is formed on the hole 261 in the shadow shield 260 can be set at and satisfy the value that concerns D4＜D1, wherein D1 is the external diameter of the first axle part 250.
In addition, in this variation,, be not limited thereto though when using the central portion of laser beam irradiation the first axle part 250, use shadow shield 260.Can use as optical systems such as lens.
Though with reference to exemplary embodiments the present invention has been described, what it should be understood that is to the invention is not restricted to disclosed exemplary embodiments.The scope of appended claims meets the wideest explanation, to comprise all distortion, equivalent structure and function.
Claims (9)
1. light controller, it comprises:
Aperture blades; And
Drive source, it is configured to drive described aperture blades,
Wherein said aperture blades comprises lamellar vane member and is arranged at least one lip-deep shaft component of described vane member, described vane member is made by the laser absorption resin, described shaft component is made by the laser-transmissible resin, utilize the laser beam that sees through described shaft component that described vane member is fused to described shaft component, and
Wherein, the fusing point of described laser-transmissible resin is lower than the fusing point of described laser absorption resin.
2. light controller according to claim 1 is characterized in that, the difference of the fusing point of the fusing point of described laser-transmissible resin and described laser absorption resin is less than 20 ℃.
3. light controller according to claim 2 is characterized in that, described vane member is made by the material of mainly being made up of polyethylene terephthalate, and described shaft component is made by the material of mainly being made up of the polycarbonate that contains glass material.
4. light controller according to claim 1 is characterized in that described vane member has teat in its surface, and described shaft component has recess at its end towards described vane member, and
Wherein, under described teat and described recess state of contact, described vane member is fused to described shaft component by utilizing the described teat of laser beam irradiation that sees through described shaft component.
5. light controller according to claim 4 is characterized in that, relational expression h1＞h2 sets up, and wherein h2 is the length that described teat is given prominence to from the described surface of described vane member, and h1 is a described end recessed degree of depth of described recess from described shaft component.
6. light controller according to claim 4 is characterized in that, described teat has first surface of contact that contacts with described recess, and described recess has second surface of contact that contacts with described teat, and
Wherein, by press described teat to make under described first surface of contact and the described second surface of contact state of contact to described recess, described vane member is fused to described shaft component.
7. light controller according to claim 4 is characterized in that, described vane member has another recess of the dorsal part that is formed on described teat.
8. aperture blades, at least one lip-deep shaft component that it comprises lamellar vane member and is arranged on described vane member, described vane member is made by the laser absorption resin, described shaft component is made by the laser-transmissible resin, utilize the laser beam that sees through described shaft component that described vane member is fused to described shaft component, the fusing point of wherein said laser-transmissible resin is lower than the fusing point of described laser absorption resin.
9. method of making aperture blades, described aperture blades comprise lamellar vane member and are arranged at least one lip-deep shaft component of described vane member that described method comprises:
The described vane member of teat is made and is had in its surface in manufacturing by the laser absorption resin, and makes the described shaft component of being made and being had at the one end at least recess by the laser-transmissible resin; And
Under described teat and described recess state of contact, by utilizing the described teat of laser beam irradiation that sees through described shaft component described vane member is fused to described shaft component, and
Wherein, the fusing point of described laser-transmissible resin is lower than the fusing point of described laser absorption resin.