CN100580160C - 生产细旦或超细旦尼龙纤维的组合物以及生产细旦或超细旦尼龙纤维的方法 - Google Patents
生产细旦或超细旦尼龙纤维的组合物以及生产细旦或超细旦尼龙纤维的方法 Download PDFInfo
- Publication number
- CN100580160C CN100580160C CN200710099455A CN200710099455A CN100580160C CN 100580160 C CN100580160 C CN 100580160C CN 200710099455 A CN200710099455 A CN 200710099455A CN 200710099455 A CN200710099455 A CN 200710099455A CN 100580160 C CN100580160 C CN 100580160C
- Authority
- CN
- China
- Prior art keywords
- nylon
- lanthanide rare
- compound
- weight
- rare metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种生产细旦或超细旦尼龙纤维的组合物以及一种生产细旦或超细旦尼龙纤维的方法。该组合物包含尼龙和一种镧系稀土金属化合物,其中,基于所用尼龙的重量计,稀土金属的化合物中稀土金属元素的重量为50ppm~10%。用于生产细旦或超细旦尼龙纤维的方法是熔融纺丝方法,该方法包括在尼龙的熔融纺丝过程中加入一种稀土金属的化合物。本发明可以得到纤度小于1旦的细旦或超细旦尼龙纤维。
Description
技术领域
本发明涉及纺丝材料领域,尤其涉及一种生产细旦或超细旦尼龙纤维的组合物以及一种生产细旦或超细旦尼龙纤维的方法。
背景技术
一般说来,可纺织用的高分子材料包括尼龙(聚酰胺)、丙纶(聚丙烯)、涤纶(聚对苯二甲酸乙二醇酯)和腈纶(聚丙烯腈)等。这些材料可以通过纺丝而形成纤维丝,从而用于纺织工业。熔融纺丝是一种常用的纺丝方法,通过熔融纺丝可以得到适于纺织用的纤维细丝。通常,使用熔融纺丝方法得到的纤维细丝可达到几旦的纤细程度(纤度)。用这样纤度的纤维细丝纺织、编制而得的产品,例如服装面料等,具有很多优点,因此市场应用空间广阔。
然而,随着人们生活水平的提高,对于纺织品的要求也越来越高,非常需要能够克服纺织品的一些现有缺陷。例如,上述提及的诸如服装面料等产品,由于其纤维丝较粗因此手感粗糙、柔软性差、透气性差、吸水性差、易于起毛起球等。为了解决这些问题,纺织纤维的细旦或超细旦化成为一个重要研究课题。
目前,已进行很多关于纺织纤维细旦或超细旦化的研究,而且有很多相关报道。例如,就中国而言,聚酯纤维细旦或超细旦化技术于世纪八十年代开发成功。聚丙烯纤维的细旦或超细旦化于上世纪九十年代由中科院化学所徐端夫院士开发出来,该技术目前已实现产业化,相关技术信息在中国专利CN1073595、CN1058062、CN1076032和CN1068075中有所描述。
但对尼龙而言,运用常规熔融纺丝方法制造(超)细旦尼龙纤维的技术尚不成熟。
尼龙纤维织物具有吸汗、轻质、韧性佳、回弹性好、抗酸碱等特点,是最适合人类穿着的人造织物之一。在服装上的应用也是尼龙纤维的主要用途之一。尼龙纤维的粗细可用单丝纤度加以表征,通常,单丝纤度为1旦左右的化学纤维叫细旦纤维而单丝纤度为0.5旦左右的化学纤维称为超细旦纤维。尼龙纤维越细,其织物的穿着舒适性越高。细旦或超细旦纤维可织成手感柔软,穿着舒适的高档纺织物,有很高的经济价值。因而,细旦纤维和超细旦纤维制造技术的开发是近年来各国都重视的高新技术。如果能够将尼龙纤维进行细旦或超细旦化,那将为纺织行业开辟又一广阔的应用领域。
细旦纤维和超细旦纤维的直径比常规化学纤维(单丝纤度一般为3-6旦左右)细得多,制造这类化学纤维的技术难度相当大,需要选用恰当的纺丝原料和助剂。还需要合理选择纺丝的技术方案和严格控制纺丝,牵伸等各项生产工艺过程。
然而,到目前为止,通过改性方式提高尼龙可纺性的研究报道并不多,改性的主要方面在于通过共聚或添加助剂来减少尼龙在卷绕时的分子取向从而提高单丝的延伸能力。例如,(1)通过共聚引入不对称单元,以减少分子取向的能力,如,普通尼龙聚合时加入不对称的二元酸、二元胺或带侧基的已内酰胺和氮环杂己烷;(2)在纺丝时加入丙烯酸衍生物,如甲基丙烯酸甲聚合酯;(3)采用长链尼龙进行纺丝或在基体尼龙的单体聚合时加入长链尼龙及其盐等等。
另一方面,在纺丝过程中的改进主要有以下方面:(1)减小喷丝板的孔径,如使用直径0.2mm甚至更细孔径的喷丝的喷丝板,并相应增加喷丝板的孔数;(2)通过高精度过滤以提高纺丝熔体的纯净度;(3)降低喷丝到卷绕过程中丝束的拉伸程度和分子取向程度以更多保留丝束延伸能力;(4)采取更高的牵伸倍数。
尼龙纤维织物具有吸汗、轻质、韧性佳、回弹性好、抗酸碱等特点,是最适合人类穿着的人造织物之一。因此,将尼龙纤维单丝进行细旦或超细旦化非常重要。而提出合适的纺丝原料对于能够生产出细旦或超细旦尼龙纤维无疑是非常重要的。
可是,就所提及的现有技术而言,都无法合理地将尼龙纤维细旦或超细旦化,所得纤维的纤度一般仍至少大于1旦。
发明内容
本发明的目的在于提供一种用来生产细旦或超细旦尼龙纤维的组合物,由该组合物能够生产出纤度小于1旦的细旦或超细旦尼龙纤维。
本发明的另一目的在于提供一种生产细旦或超细旦尼龙纤维的方法。
本发明的主要技术构思在于,通过向纺丝用的尼龙中添加一种稀土金属的化合物而得到能够生产细旦或超细旦尼龙纤维的组合物,该组合物具有非常好的性能,例如能够通过本发明的方法而纺成细旦或超细旦尼龙纤维。
文中术语“纤度”用来表示尼龙纤维的粗细程度,通常以“旦”为单位进行表示。
本发明提供了一种生产细旦或超细旦尼龙纤维的组合物,该组合物包含尼龙和一种稀土金属的化合物,尤其是一种镧系稀土金属的化合物,该组合物还可以包含其他助剂。
其中,尼龙是所述组合物的基本成分,本发明中可以使用纺丝用的常见尼龙,因此对尼龙并没有特别限定,例如可以使用尼龙6、尼龙66等。
稀土金属的化合物非限定性地包括稀土金属盐、络合物或氧化物。所述镧系稀土金属元素选自镧、铈、镨、钕、钐、铕、钆、铽、镝、钬、铒、铥、镱和镥。所述金属盐的阴离子或络合物的配体选自磷酸根、碳酸根、羧酸根、硝酸根、硫酸根、磺酸根、亚硫酸根、卤素阴离子(如氟离子、氯离子和溴离子等)、拟卤素离子(例如,硫氰酸根)以及其他含氮和/或含氧(如羧酸根)和/或含硫有机配体(如β-二酮类,例如乙酰丙酮)等,也可以是混合配体。但并不限于此。
具体而言,稀土金属化合物的实例包括:氯化镧、氯化铈、氯化镨、氯化钕、氯化钐、氯化铕、氯化钆、氯化铽、氯化镝、氯化钬、氯化铒、氯化铥、氯化镱、氯化镥、磺酸镧、磺酸铈、磺酸镨、磺酸钕、磺酸钐、磺酸铕、磺酸钆、磺酸铽、磺酸镝、磺酸钬、磺酸铒、磺酸铥、磺酸镱、磺酸镥、乙酰丙酮镧、乙酰丙酮铈、乙酰丙酮镨、乙酰丙酮钕、乙酰丙酮钐、乙酰丙酮铕、乙酰丙酮钆、乙酰丙酮铽、乙酰丙酮镝、乙酰丙酮钬、乙酰丙酮铒、乙酰丙酮铥、乙酰丙酮镱、乙酰丙酮镥、氧化镧、氧化铈、氧化镨、氧化钕、氧化钐、氧化铕、氧化钆、氧化铽、氧化镝、氧化钬、氧化铒、氧化铥、氧化镱和氧化镥等。
镧系稀土金属的化合物会使得尼龙纤维在熔融纺丝过程中表现出良好的性能,例如高强度、高粘性、高可纺性等,从而使得本发明的组合物能够被纺成纤度小于1旦的细旦或超细旦纤维丝。为了确保组合物能被纺成细旦或超细旦尼龙纤维的效果,镧系稀土金属的化合物的使用量如下:基于所用尼龙的重量计,镧系稀土金属的重量为50ppm~10wt%,优选为0.01%~5wt%,更优选为0.1%~5wt%,特别优选为0.5%~3wt%。若镧系稀土金属的化合物的使用量低于50ppm,则其对尼龙的改性效果不够好,导致组合物难以被纺成细旦或超细旦纤维。若稀土金属的化合物的使用量大于10wt%,则添加的镧系稀土金属的化合物的量过多,使得组合物纺丝的效果差,致使纤维丝的质量差,纤度会高于1旦。
本发明中,所述助剂例如是抗氧化剂、紫外线吸收剂、光稳定剂和抗静电剂等。可以使用其中的一种或多种助剂。
其中,所述抗氧剂是受阻酚类和亚磷酸盐,例如:抗氧剂1010、抗氧剂CA、抗氧剂163、抗氧剂168、抗氧剂3114、抗氧剂DLTP和抗氧剂TNP等。可以使用其中的一种或多种。抗氧化剂的添加量优选为0.001wt%-1wt%,以所用尼龙的重量计。
所述紫外线吸收剂是苯并三唑类、苯酮类等有机芳香物质,如2-(2-羟基-3-叔丁基-5-甲基苯基)-5-氯代苯并三唑、2-(2-羟基-3,5-二叔丁基苯基)-5-氯代苯并三唑、2-羟基-4-正辛氧基二苯甲酮、2-(2-羟基-5-辛基苯基)-苯并三唑、2-(2-羟基-3,5-二叔丁基苯基)-苯并三唑、2-(2-羟基-5-甲基苯基)-苯并三唑;碳黑、氧化锌、二氧化钛等无机物质。可以使用其中的一种或多种。紫外线吸收剂的添加量优选为0.001wt%-1wt%,以所用尼龙的重量计。
所述光稳定剂是卤化铜、受阻胺类、酚类、二苯甲酮系、三唑系。可以使用其中的一种或多种。所述光稳定剂的添加量优选为0.001wt%-1wt%,以所用尼龙的重量计。
所述抗静电剂是脂肪醇磷酸盐、脂肪醇氧化烯醚磷酯盐、脂肪醇磷酸酯钾、十二烷基硫酸钠盐、硬脂酸甘油单酯、月桂醇氧乙烯醚磷酸酯钾盐、聚乙二醇等。可以使用其中的一种或多种。所述抗静电剂的添加量优选为0.001%-1wt%,以所用尼龙的重量计。
本发明还提供了一种用上述组合物生产细旦或超细旦尼龙纤维的方法,该生产方法是熔融纺丝方法,包括在尼龙的熔融纺丝过程中加入一种稀土金属的化合物;任选还包括在尼龙的熔融纺丝过程中加入前述助剂。
文中术语“熔融纺丝方法”是指将纺丝用的原料加热熔融,熔融体通过螺杆挤出机挤出后送至纺丝机,经计量泵将熔融体定量压入纺丝部件中,通过喷丝板上的喷丝孔使熔融体以细丝态流出,上油卷绕,或者还经过热牵伸,即得细旦或超细旦尼龙纤维。
文中术语“熔融纺丝过程”包括从原料到成丝的所有过程,例如对要进行纺丝用的原料进行的预处理过程、原料的熔融过程和熔融体的成丝过程。
在本发明生产细旦或超细旦尼龙纤维的方法中,镧系稀土金属的化合物可以在熔融纺丝过程中的任意时间加入,对此并没有特别限定。然而,考虑到添加的方便性,优选在尼龙加热熔融之前或加热熔融期间加入该化合物。对该化合物的加入方式也没有特别限定,可以直接加入,但优选也可以将其与部分尼龙制成包含镧系稀土金属的化合物的添加剂之后再加入。
在本发明细旦或超细旦尼龙纤维的生产方法中,一个优选的实施方式在于:将所述镧系稀土金属的化合物与部分尼龙预先熔融共混挤出成型,得到添加剂母粒,然后再将添加剂母粒与其余部分的尼龙一起进行熔融纺丝。该添加剂母粒可以被视为高浓度的镧系稀土金属的化合物在尼龙中的分散体,其中镧系稀土金属的化合物的浓度优选为5~50wt%。熔融共混挤出成型例如可以通过单螺杆挤出机、双螺杆挤出机等设备进行。
本发明生产细旦或超细旦尼龙纤维的方法中,和镧系稀土金属的化合物一样,所述助剂例如抗氧化剂、紫外线吸收剂、光稳定剂和/或抗静电剂等可以在熔融纺丝过程中的任意时间加入,对此并没有特别限定。这些功能性助剂可以与镧系稀土金属的化合物同时加入,也可以在其加入之前或之后加入;若同时使用多种助剂,则它们可以同时加入,也可以先后加入。为了提高操作的简便性,优选这些助剂与稀土金属的化合物同时加入使用。
例如,在一个优选的实施方案中,通过熔融共混,由镧系稀土金属的化合物、助剂与部分尼龙得到一种含镧系稀土金属的化合物的添加剂,再将该添加剂与其余部分的尼龙一起进行熔融纺丝。
在另一个优选的实施方案中,将含镧系稀土金属的化合物、助剂与尼龙一起进行熔融纺丝。
在本发明细旦或超细旦尼龙纤维的生产方法中,熔融纺丝方法的一个优选实施方式是:在纺丝过程中,所述尼龙熔融体的温度优选在130~320℃范围内,更优选在160~280℃范围内,最优选在250~270℃范围内,喷丝板的孔数为30-200个,孔径0.1-0.6mm,卷绕的速度优选为100-8000米/分钟。
在一种优选的实施方式中,在熔融之前对所用的物料,包括镧系稀土金属的化合物(也可以是其添加剂)、尼龙切片和任选的助剂进行干燥,以除去水分和小分子物质。干燥温度为90-100℃,干燥时间为24-48小时。
本发明的生产方法,工序简单,便于操作,可得到纤度小于1旦的细旦或超细旦尼龙纤维,而且在生产过程中,尼龙纤维丝基本上不会发生断裂,所得细旦或超细旦纤维的力学性能很好,纤度最低可以达到约0.25旦。
在一种优选的实施方式中,所述工艺优选还包括将所得细旦或超细旦尼龙纤维丝进行热牵伸,是在经上油卷绕得到卷绕丝之后进行的,热牵伸的温度可以在50-160℃范围内。
文中出现的表示范围的词语,如“小于”、“大于”和“在......范围内”等,其所表示的范围包括相应范围的端点数值。
加入稀土金属的化合物可以明显提高尼龙的可纺性和纺织安全性,从而可以得到纤度小于1旦的细旦或超细旦尼龙纤维。虽然没有任何现有的可适用理论对其进行解释,但本发明人认为可能的机理如下:镧系稀土金属的化合物可以提高尼龙熔融体的强度,提高熔融体的粘性,降低熔体指数MFR,从而使得其能够经受较大的拉伸力,即使是在熔融体经喷丝后变为半熔融体时仍具有较好的强度,因此能够耐受较大的拉伸力,使得纤维丝在熔融纺丝过程中能够承受拉细步骤中所承受的力而不会发生断裂,从而提高尼龙纤维的可纺性,得到细旦或超细旦纤维。但本发明的效果并不受该理论的束缚。
使用本发明的组合物和生产方法可以得到纤度约为0.25~1旦的细旦或超细旦尼龙纤维丝,该纤维丝的强度大,断裂伸长率高。
具体实施方式
以下通过具体实施例来进一步描述本发明。本发明的特点和优点会随着这些描述而变得更为清楚。但是,这些实施例仅仅是范例性的,用于对本发明进行解释说明,而并不对本发明的范围构成任何限制。本领域的技术人员应该理解,在不违背本发明的精神和范围情况下,可以在细节方面对本发明进行修饰和/或改变和/或等价替换,这些修饰/修改/替换均应落入本发明所请求保护的范围内。
所用原料
尼龙6切片:宁波亨润公司生产的高速纺纯尼龙6切片
实施例1
按下表1的比例使用双螺杆挤出机制备LaCl3添加剂母粒,其中挤出机各区的温度分别为:260℃、305℃、290℃和290℃。。
表1:含LaCl3的添加剂母粒配方
成份 | 质量份数 |
尼龙6切片 | 80 |
金属盐LaCl<sub>3</sub> | 20 |
抗氧化剂(抗氧剂1010/抗氧剂168) | 1 |
PEG600 | 12 |
PEG20000 | 3 |
将所得LaCl3的添加剂母粒与尼龙6切片在真空烘箱中进行干燥,以除去水分和小分子物质。干燥温度在90-100℃之间,干燥时间为24-48小时。
然后再将LaCl3的添加剂母粒与尼龙6切片以重量比8∶1000混合后进行熔融纺丝,熔体在螺杆挤出机中各区的的温度分别是250℃、270℃、270℃、275℃,纺丝温度是250℃。采用的喷丝板孔径为0.35mm,长度为0.7mm,卷绕速度为1700m/min,可以得到卷绕丝纤度为0.79旦的细旦尼龙纤维,力学性能测试强度可以达到3.7cN/dtex,断裂伸长率在41%。
实施例2
按照实施例1的方法制备细旦或超细旦尼龙纤维,区别在于,按下表2的比例使用双螺杆挤出机制备EuCl3添加剂母粒,添加剂母粒与尼龙6切片的重量比为1∶1000纺丝温度是255℃,卷绕速度为1400m/min,所得到卷绕丝在牵伸机上进行1.20倍的热牵伸。得到纤度为0.70旦的细旦尼龙纤维。力学性能测试纤维丝强度达到4.0cN/dtex,断裂伸长率19%。
表2:EuCl3添加剂母粒配方
成份 | 质量份数 |
尼龙6切片 | 80 |
金属盐EuCl<sub>3</sub> | 40 |
抗氧化剂(抗氧剂1010/抗氧剂168) | 1 |
实施例3
按照实施例1的方法制备细旦或超细旦尼龙纤维,区别在于,按下表3的比例使用双螺杆挤出机制备Tb(乙酰丙酮)3添加剂母粒,添加剂母粒与尼龙6切片的重量比为5∶100,纺丝温度是255℃,卷绕速度为4000m/min。得到纤度为0.40旦的细旦尼龙纤维。力学性能测试纤维丝强度达到3.9cN/dte,断裂伸长率24%。
表3:Tb(乙酰丙酮)3添加剂母粒配方
成份 | 质量份数 |
尼龙6切片 | 80 |
金属盐Tb(乙酰丙酮)<sub>3</sub> | 60 |
实施例4
使用6份磺酸镧与100份(均为重量份)尼龙6切片一起进行熔融纺丝,熔体在螺杆挤出机中各区的的温度分别是250℃、265℃、265℃、270℃,纺丝温度是265℃。采用的喷丝板孔径为0.35mm,长度为0.7mm,卷绕速度为6000m/min,可以得到卷绕丝纤度为0.30旦的细旦尼龙纤维,力学性能测试强度可以达到3.5cN/dtex,断裂伸长率在42%。
比较实施例1
未添加任何其他物质只使用尼龙6切片进行熔融纺丝,熔体在螺杆挤出机中各区的的温度分别是260℃,305℃,290℃290℃,纺丝温度为295℃,卷绕速度为900米/分,喷丝板孔数为48,孔径为0.3毫米,长径比3∶1。得到单丝纤度为2.7旦的尼龙6卷绕丝。对所得到的尼龙6卷绕丝进行3倍的热牵伸,罗拉温度90度,热板温度160度,试图制造单丝纤度为0.9旦的尼龙6细旦纤维,实验结果表明,卷绕丝条每隔数分钟即发生断裂,不能得到尼龙6细旦纤维,无法实现稳定生产。
比较实施例2
将1000份尼龙6切片、1份抗氧化剂(抗氧剂1010/抗氧剂168)、12份PEG600和3份PEG20000混合后进行熔融纺丝,熔融纺丝方法如实施例1中所述,得到卷绕丝纤度为10旦的细旦尼龙纤维,在100℃进行力学3.3倍的热牵伸,得到3旦的尼龙纤维丝。性能测试其强度3.6cN/dtex,断裂伸长率在35%。
比较实施例3
将尼龙6切片按照实施例4的方法进行熔融纺丝,卷绕速度为3000米/分钟。所得纤维丝的纤度为3旦。强度为4.3cN/dtex,断裂伸长率在28%。
通过实施例1-4和比较实施例1-3比较可以看到,添加了稀土金属的化合物的尼龙可以纺成纤度小于1旦的细旦或超细旦尼龙纤维,而没有添加稀土金属的化合物的尼龙只能纺出纤度为3旦左右的尼龙纤维,根本无法纺出细旦或超细旦尼龙纤维。
Claims (15)
1、一种生产细旦或超细旦尼龙纤维的组合物,该组合物包含尼龙和一种镧系稀土金属的化合物,其中,基于所用尼龙的重量计,镧系稀土金属的化合物中镧系稀土金属元素的重量为50ppm~10%,所述尼龙是尼龙6或尼龙66,所述镧系稀土金属的化合物是镧系稀土金属的盐或络合物。
2、根据权利要求1所述的组合物,其特征在于,基于所用尼龙的重量计,所述镧系稀土金属元素的重量为0.005%~10%。
3、根据权利要求2所述的组合物,其特征在于,基于所用尼龙的重量计,所述镧系稀土金属元素的重量为0.1%~5%。
4、根据权利要求3所述的组合物,其特征在于,基于所用尼龙的重量计,所述镧系稀土金属元素的重量为0.5%~3%。
5、根据权利要求1至4中任一项所述的组合物,其特征在于,所述镧系稀土金属元素选自镧、铈、镨、钕、钐、铕、钆、铽、镝、钬、铒、铥、镱和镥,所述金属盐的阴离子或络合物的配体选自磷酸根、碳酸根、羧酸根、硝酸根、硫酸根、磺酸根、亚硫酸根、卤素阴离子、拟卤素离子以及含氮和/或含氧和/或含硫有机配体。
6、根据权利要求1至4中任一项所述的组合物,其特征在于,该组合物还包含助剂,所述助剂是抗氧化剂、紫外线吸收剂、光稳定剂和抗静电剂中的一种或多种,
其中,所述抗氧剂是受阻酚类和亚磷酸盐,抗氧化剂的添加量为0.001wt%-1wt%,以所用尼龙的重量计;
所述紫外线吸收剂是苯并三唑类、苯酮类有机芳香物质,碳黑、氧化锌、二氧化钛,可以使用其中的一种或多种,紫外线吸收剂的添加量为0.001wt%-1wt%,以所用尼龙的重量计;
所述光稳定剂是卤化铜、受阻胺类、酚类、二苯甲酮系、三唑系,使用其中的一种或多种,所述光稳定剂的添加量为0.001wt%-1wt%,以所用尼龙的重量计;
所述抗静电剂是脂肪醇磷酸盐、脂肪醇氧化烯醚磷酯盐、脂肪醇磷酸酯钾、十二烷基硫酸钠盐、硬脂酸甘油单酯、月桂醇氧乙烯醚磷酸酯钾盐、聚乙二醇,使用其中的一种或多种,所述抗静电剂的添加量为0.001wt%-1wt%,以所用尼龙的重量计。
7、根据权利要求6所述的组合物,其特征在于,所述紫外线吸收剂选自2-(2-羟基-3-叔丁基-5-甲基苯基)-5-氯代苯并三唑、2-(2-羟基-3,5-二叔丁基苯基)-5-氯代苯并三唑、2-羟基-4-正辛氧基二苯甲酮、2-(2-羟基-5-辛基苯基)-苯并三唑、2-(2-羟基-3,5-二叔丁基苯基)-苯并三唑、2-(2-羟基-5-甲基苯基)-苯并三唑。
8、一种生产细旦或超细旦尼龙纤维的添加剂,该添加剂包含尼龙和一种镧系稀土金属的化合物,或者还包含权利要求6中所述的助剂,其中镧系稀土金属的化合物占添加剂总重量的5~50wt%,所述尼龙是尼龙6或尼龙66,所述镧系稀土金属的化合物是镧系稀土金属的盐或络合物。
9、一种生产细旦或超细旦尼龙纤维的方法,该生产方法是熔融纺丝方法,包括在尼龙的熔融纺丝过程中加入镧系稀土金属的化合物,其中,基于所用尼龙的重量计,镧系稀土金属的化合物中镧系稀土金属元素的重量为50ppm~10%;任选还包括在尼龙的熔融纺丝过程中加入在权利要求6中所述的助剂,所述尼龙是尼龙6或尼龙66,所述镧系稀土金属的化合物是镧系稀土金属的盐或络合物。
10、根据权利要求9所述的方法,其特征在于,在尼龙加热熔融之前或加热熔融期间加入一种镧系稀土金属的化合物,
和/或
在尼龙加热熔融之前或加热熔融期间加入所述助剂。
11、根据权利要求10所述的方法,其特征在于,将所述镧系稀土金属的化合物与部分尼龙预先熔融共混挤出成型,得到添加剂母粒,然后再将母粒与其余部分的尼龙一起进行熔融纺丝。
12、根据权利要求9所述的方法,其特征在于,在纺丝过程中,所述尼龙熔融体的温度在130~320℃范围内,喷丝板的孔数为30-200个,孔径为0.1-0.6mm,卷绕的速度为100-8000米/分钟。
13、根据权利要求12所述的方法,其特征在于,在纺丝过程中,所述尼龙熔融体的温度在160~280℃范围内。
14、根据权利要求12所述的方法,其特征在于,在纺丝过程中,所述尼龙熔融体的温度在250~270℃范围内。
15、一种细旦或超细旦尼龙纤维,该纤维是以权利要求1-7任一项所述的组合物为原料制成的,该纤维的纤度为0.25~1旦。