CN100572094C

CN100572094C - A kind of method of PVC plastic uptake transfer film plastic uptake being transferred to plate surface

Info

Publication number: CN100572094C
Application number: CNB2008100271648A
Authority: CN
Inventors: 邝干辉
Original assignee: Individual
Current assignee: Individual
Priority date: 2008-04-01
Filing date: 2008-04-01
Publication date: 2009-12-23
Anticipated expiration: 2028-04-01
Also published as: CN101259813A

Abstract

The invention discloses a kind of PVC plastic uptake transfer film, comprise the PVC rete, described PVC rete bottom surface is provided with from the shape layer, at the ink lay that is printed with the band texture from shape layer bottom surface; The invention also discloses and a kind of PVC plastic uptake transfer film is transferred to the method for plate surface, its processing step is as follows: (1) is at first at middle and higher density plank or artificial stone plate surface spraying glue; (2) the described sheet material of step (1) and PVC plastic uptake transfer film together being put into temperature is that 120-150 degree centigrade Packing Machine is carried out vacuum forming, makes the ink lay bottom surface on the PVC plastic uptake transfer film be adsorbed on plate surface closely; (3) the PVC rete with the described PVC plastic uptake of step (2) transfer film top layer tears it down, and makes ink lay transfer to plate surface from PVC plastic uptake transfer film; The present invention is simple and reasonable for structure to be used corresponding method that it is firmly sticked on the sheet material and after long-time the use still to be difficult to come off, to have improved the service life of furniture or sheet material simultaneously.

Description

A kind of method of PVC plastic uptake transfer film plastic uptake being transferred to plate surface

Technical field

The present invention relates to a kind of method of PVC plastic uptake transfer film plastic uptake being transferred to middle and higher density plank sheet material or artificial stone plate's plate surface.

Background technology

At present, used furniture is essentially timber and makes in people's daily life, in some top-grade furnitures, usually adopt solid wood as raw material, wood grain that it is exclusive and firm structure seem very generous, style, extremely the people parent looks at, but, along with the mankind constantly fell the limited forest reserves, the remaining forest reserves are fewer and feweri on the earth, the seriously broken ecological balance of having encircled of a large amount of disafforestation resources, to the mankind are hundred none profits of evil, in addition, the furniture made from solid wood is easy to generate crackle under the climate change rugged environment, also influenced simultaneously its service life, expensive price and its also are that people can not bear than short service life, during people have just invented like this, high density plank or artificial stone plate make furniture or decorative panel, in order to make its surface have the texture that natural timber has, the manufacturer makes outward appearance it reaches the effect of natural timber by grained PVC decorating film being sticked on plate surface, so both played the effect of environmental protection, also reduced production cost, attracted large quantities of consumers to buy, common this PVC decorating film structure comprises two-layer PVC layer up and down, between two-layer PVC layer, be provided with ink lay, ink lay tightly sticks together almost to combine together with PVC layer up and down and can not separate, after furniture has used a period of time or at weather, cause the aging viscosity that loses of viscose glue under the temperature transition environment repeatedly, separate with colloid easily with the bonding PVC layer of sheet material and come off, and the PVC decorating film is big block coming off when coming off, make furniture or sheet material lose aesthetic feeling immediately, reduced its service life, at above-mentioned shortcoming, be necessary to make improvements.

Summary of the invention

In order to overcome the deficiencies in the prior art, the invention provides a kind of simple and reasonable for structure and can firmly stick on and be difficult to the PVC plastic uptake transfer film that comes off on the sheet material.

Another object of the present invention provides a kind of method of this PVC plastic uptake transfer film plastic uptake being transferred to plate surface.

The technical solution adopted for the present invention to solve the technical problems is:

A kind of PVC plastic uptake transfer film comprises the PVC rete, and described PVC rete bottom surface is provided with from the shape layer, at the ink lay that is printed with the band texture from shape layer bottom surface.

In the present invention, described ink lay is made up of rippled oil layer and printing ink background color layer.

In the present invention, described PVC thicknesses of layers is 50-100 μ m, and described ink film thickness is 3-7 μ m.

A kind of PVC plastic uptake transfer film plastic uptake is transferred to the method for plate surface, its processing step is as follows:

(1) at first at middle and higher density plank sheet material or the thick glue of artificial stone plate's plate surface spraying 1-2 μ m;

(2) the described sheet material of step (1) and PVC plastic uptake transfer film together being put into temperature is that 120-150 degree centigrade Packing Machine is carried out vacuum forming, makes the ink lay bottom surface on the PVC plastic uptake transfer film be adsorbed on plate surface closely.

(3) the PVC rete with the described PVC plastic uptake of step (2) transfer film top layer tears it down, and makes ink lay transfer to plate surface and combine closely with the glue of plate surface from PVC plastic uptake transfer film.

In the present invention, the plate surface after the step (3) is sprayed paint.

The invention has the beneficial effects as follows: by the ink lay on the PVC plastic uptake transfer film and the glue of plate surface being combined closely with the PVC plastic uptake transfer film among the present invention and by the made decorative panel of corresponding method, even between ink lay under weather, the temperature transition environment repeatedly and glue, can not come off yet, separate, can substitute natural wooden skin fully uses, played environmental-protection function fine, improved the service life of furniture or sheet material, for the consumer has saved fund.

Description of drawings

The present invention is further described below in conjunction with drawings and Examples.

Fig. 1 is a structural representation of the present invention;

The specific embodiment

With reference to Fig. 1, a kind of PVC plastic uptake transfer film comprises PVC rete 1, and described PVC rete 1 bottom surface is provided with from shape layer 2, at the ink lay 3 that is printed with the band texture from shape layer 2 bottom surface, this ink lay can modulate the figure layer of various different texture and pattern according to actual conditions except that the wood grain pattern.

In the present invention, ink lay 3 is made up of rippled oil layer 31 and printing ink background color layer 32.

In the present invention, PVC rete 1 thickness is 50-100 μ m, and described ink lay 3 thickness are 3-7 μ m.

(1) at first at middle and higher density plank sheet material or the thick glue of artificial stone plate's plate surface spraying 1-2 μ m, this glue is common oiliness glue usually;

(2) the described sheet material of step (1) and PVC plastic uptake transfer film together being put into temperature is that 120-150 degree centigrade Packing Machine is carried out vacuum forming, makes the ink lay bottom surface on the PVC plastic uptake transfer film be adsorbed on plate surface closely; Because PVC film pulling force is good, even the absorption that this PVC plastic uptake transfer film of the sheet material of surface irregularity also can be very smooth thereon.

By the ink lay 3 on the PVC plastic uptake transfer film is combined closely with the glue of plate surface with the PVC plastic uptake transfer film among the present invention and by the made decorative panel of corresponding method, even ink lay 3 can not come off yet, separate with glue under weather, temperature transition environment repeatedly, can substitute natural wooden skin fully uses, played environmental-protection function fine, improved the service life of furniture or sheet material, for the consumer has saved fund.

After through above-mentioned steps (3), can also can play the effect of protection ink lay on the one hand by spraying paint, can make plate surface more bright and clean on the other hand, use the made furniture appearance of this sheet material more attractive in appearance, generous at ink lay 3 surperficial spray paints.

The present invention is simple and reasonable for structure to be used corresponding method that it is firmly sticked on the sheet material and after long-time the use still to be difficult to come off, to have improved the service life of furniture or sheet material, for the consumer has saved fund simultaneously.

Claims

1. one kind PVC plastic uptake transfer film plastic uptake transferred to the method for plate surface, employed PVC plastic uptake transfer film comprises the PVC rete, and this PVC rete bottom surface is provided with from the shape layer, at the ink lay that is being printed with the band texture from shape layer bottom surface; It is characterized in that processing step is as follows:

(2) the described sheet material of step (1) and described PVC plastic uptake transfer film together being put into temperature is that 120-150 degree centigrade Packing Machine is carried out vacuum forming, makes the ink lay bottom surface on the described PVC plastic uptake transfer film be adsorbed on plate surface closely;

2. according to claim 1ly a kind of PVC plastic uptake transfer film plastic uptake is transferred to the method for plate surface, it is characterized in that the plate surface after the step (3) is sprayed paint.