CN100567640C - A kind of manufacture method of laser direct plating tipping paper - Google Patents
A kind of manufacture method of laser direct plating tipping paper Download PDFInfo
- Publication number
- CN100567640C CN100567640C CNB2007100237657A CN200710023765A CN100567640C CN 100567640 C CN100567640 C CN 100567640C CN B2007100237657 A CNB2007100237657 A CN B2007100237657A CN 200710023765 A CN200710023765 A CN 200710023765A CN 100567640 C CN100567640 C CN 100567640C
- Authority
- CN
- China
- Prior art keywords
- laser direct
- direct plating
- tipping paper
- manufacture method
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of manufacture method of laser direct plating tipping paper, may further comprise the steps: after (1) carries out mixing and stirring with cinnamic acid emulsion and water-based thickener, leave standstill more than 12 hours, make water paint, the percentage by weight of cinnamic acid emulsion and water-based thickener is 97%～99% and 1%～3%; (2) on the Biaxially oriented polypropylene BOPP film that goes out the holographic laser pattern with the moulding press mold pressing, be coated with water paint, wet coating weight be 8-10 gram/square metre; (3) yew paper body paper is fitted on the water paint face of Biaxially oriented polypropylene BOPP film, with enter after the compression roller extruding press polish baking oven dry by the fire to moisture between 5%-8%, peel off Biaxially oriented polypropylene BOPP film, yew paper substrate body; (4) yew paper substrate body put into vacuum aluminum-coated machine aluminize after, make laser direct plating tipping paper.Technology of the present invention is advanced rationally simple, and the selection science helps improving grade of cigarette, reduces cigarette to health effects.
Description
Technical field
The present invention relates to the manufacture method of yew paper, particularly a kind of laser direct plating tipping paper that cigarette uses.
Background technology
At present, it is gold stamping and mainly to be that literal is gold stamping form that the cigarette yew paper on the market is that printing is earlier carried out small size with electrochemical aluminium again, and gold stamping yew paper brings the technical difficulty of straight plating method process implementing because of the ultra-thin characteristic of body paper.Electrochemical aluminium gold-stamped coating all is the coating of solvent borne at present simultaneously, and its toxic and side effect is relatively large, owing to yew paper directly contacts with smoker's lip, so unfavorable to health.Therefore, researching and developing a kind of yew paper that does not have toxic and side effect, is cigarette enterprise, and numerous smokers' heartfelt wishes have important practical significance especially.
Summary of the invention
Purpose of the present invention is exactly that a kind of manufacture method that does not have the laser direct plating tipping paper of toxic and side effect will be provided.
First technical scheme that realizes the object of the invention is that a kind of manufacture method of laser direct plating tipping paper is characterized in that may further comprise the steps:
(1) cinnamic acid emulsion and water-based thickener LD-60 are carried out (water-based thickener LD-60 after the mixing and stirring, Yangzhou Lida Resin Co., Ltd.'s production and sales), leave standstill more than 12 hours, make water paint, the percentage by weight of cinnamic acid emulsion and water-based thickener is respectively 97%～99% and 1%～3%;
(2) on the Biaxially oriented polypropylene BOPP film that goes out the holographic laser pattern with the moulding press mold pressing, be coated with water paint, wet coating weight be 8-10 gram/square metre;
(3) yew paper body paper is fitted on the water paint face of Biaxially oriented polypropylene BOPP film, with enter after the compression roller extruding press polish baking oven dry by the fire to moisture between 5%-8%, peel off Biaxially oriented polypropylene BOPP film, yew paper substrate body;
(4) yew paper substrate body put into vacuum aluminum-coated machine aluminize after, make laser direct plating tipping paper.
The solid content of described cinnamic acid emulsion is 35%-55%;
The vacuum degree control of the coiling chamber in the described vacuum aluminum-coated machine is 5 * 10
-2Below the MPa, the vacuum in the deposited chamber is 6 * 10
-4Below the MPa, the temperature of plated film drum is-10--2 ℃.The indoor device that cryogenic trap is removed steam that is provided with of reeling.
Second technical scheme that realizes the object of the invention is that a kind of manufacture method of laser direct plating tipping paper is characterized in that may further comprise the steps:
1. extrude the holographic laser pattern with moulding press at Biaxially oriented polypropylene BOPP film patrix;
2. on yew paper body paper, be coated with the cinnamic acid emulsion earlier, wet coating weight be 8-10 gram/square metre, the applying mold pressing goes out the Biaxially oriented polypropylene BOPP film of holographic laser pattern on the coating of cinnamic acid emulsion then, again with enter after the compression roller extruding press polish baking oven dry by the fire to moisture between 5%-8%, peel off Biaxially oriented polypropylene BOPP film, get yew paper substrate body;
3. after yew paper substrate body being put into vacuum aluminum-coated machine and aluminizing, make laser direct plating tipping paper.
The solid content of described cinnamic acid emulsion is 35%-55%;
The vacuum degree control of the coiling chamber in the described vacuum aluminum-coated machine is 5 * 10
-2Below the MPa, the vacuum in the deposited chamber is 6 * 10
-4Below the MPa, the temperature of plated film drum is-10--2 ℃.The indoor device that cryogenic trap is removed steam that is provided with of reeling.
Technology of the present invention is rationally advanced, adopt water paint, radium-shine carrier mould holographic laser pattern and vacuum aluminizing method, overcome the environmental protection difficult problem that gold stamping type yew paper produces, also create simultaneously the thinnest domestic direct plating tipping paper, the yew paper laser pattern of manufacturing, figure line are clear, metal-like is strong, antifalsification is strong, and laser direct plating manufactured yew paper technology is simple, and operating cost is low, more be applicable to suitability for industrialized production, played energy-saving and cost-reducing good society effect.The cigarette that the laser direct plating tipping paper that adopts the present invention to produce rolls has been improved grade of cigarette, has reduced cigarette to health effects.
The specific embodiment
Example 1: at first cross the last coating of bidirectional stretching polypropylene film (BOPP) water paint---the cinnamic acid emulsion of holographic laser pattern in mold pressing, solid content is the mixture of 35%-55% and water-based thickener LD-60; Proportioning is 98: 2, after fully stirring, leaves standstill more than 12 hours; During coating wet coating weight reach the 8-10 gram/square metre; And then fit up with former yew paper, enter baking oven through compression roller extruding press polish, the moisture that thereby the control oven temperature reaches control yew paper in baking oven is peelled off bidirectional stretching polypropylene film (BOPP) behind 5%-8%, then the yew paper of handling well being put into vacuum aluminum-coated machine aluminizes, the indoor device that must have cryogenic trap to remove steam of the coiling of vacuum aluminum-coated machine, the vacuum of coiling chamber will remain on 5 * 10
-2Below the MPa, the vacuum in the deposited chamber wants 6 * 10
-4Below the MPa, simultaneously the temperature of plated film drum is set in-10--2 ℃, begins to aluminize after these conditions are finished.Aluminize and to obtain laser direct plating tipping paper after finishing.
Example 2: at first be coated with water paint on former yew paper---cinnamic acid emulsion, solid content are 35%-55%; During coating wet coating weight reach the 8-10 gram/square metre; And then the bidirectional stretching polypropylene film (BOPP) of crossing the holographic laser pattern with mold pressing fits, enter baking oven through compression roller extruding press polish, the moisture that thereby the control oven temperature reaches control yew paper in baking oven is peelled off bidirectional stretching polypropylene film (BOPP) behind 5%-8%, then the yew paper of handling well being put into vacuum aluminum-coated machine aluminizes, the indoor device that must have cryogenic trap to remove steam of the coiling of vacuum aluminum-coated machine, the vacuum of coiling chamber will remain on 5 * 10
-2Below the MPa, the vacuum in the deposited chamber wants 6 * 10
-4Below the MPa, simultaneously the temperature of plated film drum is set in-10--2 ℃, begins to aluminize after these conditions are finished.Aluminize and to obtain laser direct plating tipping paper after finishing.
Claims (8)
1, a kind of manufacture method of laser direct plating tipping paper is characterized in that may further comprise the steps:
(1) cinnamic acid emulsion and water-based thickener LD-60 are carried out mixing and stirring after, leave standstill more than 12 hours, make water paint, the percentage by weight of cinnamic acid emulsion and water-based thickener is respectively 97%～99% and 1%～3%;
(2) on the Biaxially oriented polypropylene BOPP film that goes out the holographic laser pattern with the moulding press mold pressing, be coated with water paint, wet coating weight be 8-10 gram/square metre;
(3) yew paper body paper is fitted on the water paint face of Biaxially oriented polypropylene BOPP film, with enter after the compression roller extruding press polish baking oven dry by the fire to moisture between 5%-8%, peel off Biaxially oriented polypropylene BOPP film, yew paper substrate body;
(4) yew paper substrate body put into vacuum aluminum-coated machine aluminize after, make laser direct plating tipping paper.
2, the manufacture method of laser direct plating tipping paper according to claim 1, the solid content that it is characterized in that described cinnamic acid emulsion is 35%-55%.
3, the manufacture method of laser direct plating tipping paper according to claim 1, the vacuum degree control that it is characterized in that the coiling chamber in the described vacuum aluminum-coated machine is 5 * 10
-2Below the MPa, the vacuum in the deposited chamber is 6 * 10
-4Below the MPa, the temperature of plated film drum is-10--2 ℃.
4, the manufacture method of laser direct plating tipping paper according to claim 3 is characterized in that the indoor device that is provided with cryogenic trap except that steam of described coiling.
5, a kind of manufacture method of laser direct plating tipping paper is characterized in that may further comprise the steps:
1. extrude the holographic laser pattern with moulding press at Biaxially oriented polypropylene BOPP film patrix;
2. on yew paper body paper, be coated with the cinnamic acid emulsion earlier, wet coating weight be 8-10 gram/square metre, the applying mold pressing goes out the Biaxially oriented polypropylene BOPP film of holographic laser pattern on the coating of cinnamic acid emulsion then, again with enter after the compression roller extruding press polish baking oven dry by the fire to moisture between 5%-8%, peel off Biaxially oriented polypropylene BOPP film, get yew paper substrate body;
3. after yew paper substrate body being put into vacuum aluminum-coated machine and aluminizing, make laser direct plating tipping paper.
6, the manufacture method of laser direct plating tipping paper according to claim 5, the solid content that it is characterized in that described cinnamic acid emulsion is 35%-55%.
7, the manufacture method of laser direct plating tipping paper according to claim 5, the vacuum degree control that it is characterized in that the coiling chamber in the described vacuum aluminum-coated machine is 5 * 10
-2Below the MPa, the vacuum in the deposited chamber is 6 * 10
-4Below the MPa, the temperature of plated film drum is-10--2 ℃.
8, the manufacture method of laser direct plating tipping paper according to claim 5 is characterized in that the indoor device that is provided with cryogenic trap except that steam of described coiling.