CN100564465C - Environment-friendly water-based priming paint - Google Patents
Environment-friendly water-based priming paint Download PDFInfo
- Publication number
- CN100564465C CN100564465C CNB2005100191936A CN200510019193A CN100564465C CN 100564465 C CN100564465 C CN 100564465C CN B2005100191936 A CNB2005100191936 A CN B2005100191936A CN 200510019193 A CN200510019193 A CN 200510019193A CN 100564465 C CN100564465 C CN 100564465C
- Authority
- CN
- China
- Prior art keywords
- kinds
- oxide
- component
- magnetic iron
- iron powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of environment-friendly water-based priming paint, its weight percentages of components is: component one: silicate liquid 50～60%; Metal oxide 20～30%; ACRYLIC EMULSION 15～20%; Auxiliary agent 1-10%.Component two: zinc powder 70～80%; Active magnetic iron powder 20～30%.Its advantage is: with water solvent, and nontoxic pollution-free, zero VOC discharging; Behind the surface drying 30min, get final product water-fast flushing; Coatingsurface can be supporting with all kinds of protective systems, can satisfy the needs of all kinds of long-acting heavy antiseptic projects; The organic solvent resistance excellence, filming has excellent electrochemical anti-corrosive performance; Can high temperature resistantly continuously reach 650 ℃ and can continue to use, can weld, cut, cutting property is good; But the low anti-electrostatic of resistivity, radioprotective, UV resistant, salt spray resistance have the long-effective corrosion effect; This product snappiness is better than general inorganic zinc coating.
Description
Technical field
The present invention relates to system lacquer technical field, specifically a kind of environmental protection high efficiency water priming paint.
Background technology
Hardware adopts materials such as carbon steel, manganese steel, cast steel mostly and is in for a long time in the environment such as alternation of wetting and drying, solar exposure, high velocity flow, salt fog and water medium, microorganic adhesion, generally the burn into that takes place in various degree all wants the visual range degree to carry out rotproofing at set intervals, to prolong its work-ing life.General protective system, as: coating such as chlorinated rubber, iron oxide red epoxy, epoxy all only have shielding effect.Hot spray painted zinc, aluminium are will wire rod to be sprayed on the metal base after the fusing, atomizing, and it is poor to exist unrelieved stress, porosity height, shielding properties, must add the sealing coating again, and the zinc mist that produces in the construction, and the personnel of construction team are had very big harm.It is raw material that organic and inorganic zinc-rich paint all adopts high fineness zinc powder, good to the shielding of metal base, but organic many employing epoxy resins are base-material, do not possess electroconductibility, so its anodic protection performance is far away from hot spray painted zinc, aluminium and inorganic zinc coating.The FMS-E of my company's exploitation
nEnvironment-friendly high-efficiency coating is the supporting aqueous inorganic zinc-enriched coating in a kind of bottom surface, and this coating has been gathered the feature performance benefit of hot spray painted zinc, aluminium and organic zinc-rich paint, is the environment-friendly type coating of tool development prospect in the present industry.In recent years, we obtained good market and economic benefit through testing many times, explore, using.
Summary of the invention
The objective of the invention is to make a kind of is solvent with water, pollution-free, the environmental protection high efficiency water priming paint of zero release antiseptic property excellence.
Environmental protection high efficiency water priming paint of the present invention, its weight percentages of components is:
Component one:
Silicate liquid 50-60%
Metal oxide is sodium oxide, Lithium Oxide 98min, potassium oxide 20-30%
ACRYLIC EMULSION 15-20%
Auxiliary agent 1-10%
Component two:
Zinc powder 70-80%
Active magnetic iron powder 20-30%
Metal oxide comprises: sodium oxide, and Lithium Oxide 98min, potassium oxide, a kind of, two kinds or three kinds of mixing uses, blending ratio is: two kinds are: 3: 7, three kinds were: 65: 25: 10.
Auxiliary agent comprises: Virahol, magnesium oxide.
Blending ratio is: two kinds is 4: 6.
Active magnetic iron powder weight percentages of components:
Magnetic iron powder 55-75%
Special addition agent 1-10%
Face, filler 20-40%
Face, filler comprise: titanium dioxide, fine particle calcium carbonate, talcum powder or other products be one or two or three mixtures wherein.Wherein two ratio of mixture are 1: 3, three ratio of mixture 1: 3: 2.
Special addition agent is a dispersion agent, 923S dispersion agent, YB201A dispersion agent or other products.Preceding two kinds of dispersion agents are Deuchem Co., Ltd. and changzhou Ya Bang auxiliary reagent factory's production and sales.
Component two: the ratio of component one is 72: 28, puts into container during use and stirs, and can use.
The advantage of environmental protection high efficiency water priming paint of the present invention is:
1) with water is solvent, nontoxic pollution-free, zero VOC discharging
2) behind the surface drying 30min, can water-fast flushing
3) coatingsurface can be supporting with all kinds of protective systems, can satisfy the needs of all kinds of long-acting heavy antiseptic projects.
4) organic solvent resistance excellence, filming has excellent electrochemical anti-corrosive performance.
5) can high temperature resistantly continuously reach 650 ℃ and can continue to use, can weld, cut, cutting property is good.
6) but the low anti-electrostatic of resistivity, radioprotective, UV resistant, salt spray resistance have the long-effective corrosion effect.
7) this product snappiness is better than general inorganic zinc coating.
Embodiment
Embodiment one:
Environmental protection high efficiency water priming paint of the present invention, its composition weight are Kg:
Component one:
Silicate liquid 60
Sodium oxide, potassium oxide mixed oxide 20
ACRYLIC EMULSION 15
Virahol 5
Component two:
Zinc powder 80
Active magnetic iron powder 20
1, with the silicate liquid 60Kg in the component one, the potassium oxide in the metal oxide, sodium oxide mixture 20Kg, ACRYLIC EMULSION 15Kg, Virahol 5Kg, join in the reactor, under temperature 50-100 ℃ condition, mix, react after 3-72 hour, the after-filtration that is up to the standards, the storehouse is entered in barrelling.
2, with the zinc powder 50Kg in the component two, active magnetic iron powder 30Kg pulverizes, grind, and after mixing, check, packing is dispatched from the factory.
Embodiment two:
Environmental protection high efficiency water priming paint of the present invention, its composition weight are Kg:
Component one:
Silicate liquid 50
Lithium Oxide 98min 30
ACRYLIC EMULSION 13
Catalyzer, magnesia mixture 7
Component two:
Zinc powder 70
Active magnetic iron powder 30
1, with the silicate liquid 50Kg in the component one, Lithium Oxide 98min mixture 30Kg in the metal oxide, ACRYLIC EMULSION 13Kg, catalyzer, magnesia mixture 5Kg join in the reactor, mix under temperature 50-100 ℃ condition, react after 3-72 hour, the after-filtration that is up to the standards, the storehouse is entered in barrelling.
2, with the zinc powder 70Kg in the component two, active magnetic iron powder 30Kg pulverizes, grind, and after mixing, check, packing is dispatched from the factory.
Embodiment three:
Environmental protection high efficiency water priming paint of the present invention, its composition weight are Kg:
Component one:
Silicate liquid 45
Potassium oxide 25
ACRYLIC EMULSION 20
Catalyzer, magnesia mixture 10
Component two:
Zinc powder 75
Active magnetic iron powder 25
1, with the silicate liquid 45Kg in the component one, the potassium oxide 25Kg in the metal oxide, ACRYLIC EMULSION 20Kg, catalyzer, magnesia mixture 10Kg, join in the reactor, under temperature 50-100 ℃ condition, mix, react after 3-72 hour, the after-filtration that is up to the standards, the storehouse is entered in barrelling.
2, with the zinc powder 75Kg in the component two, active magnetic iron powder 25Kg pulverizes, grind, and after mixing, check, packing is dispatched from the factory.
Active magnetic iron powder production process is as follows:
Method for making 1: with magnetic iron powder 75Kg, dispersion agent 923S 5Kg special addition agent, titanium dioxide, talcum powder mixture 20Kg face, filler are put together, after mixing, place standbyly, and this mixture is active magnetic iron powder.
Method for making 2: with magnetic iron powder 55Kg, dispersion agent YB201A 20Kg special addition agent, fine particle calcium carbonate, talcum powder mixture 35Kg face, filler are put together, after mixing, place standbyly, and this mixture is active magnetic iron powder.
Method for making 3: with magnetic iron powder 65Kg, dispersion agent YB201A 5Kg special addition agent, titanium dioxide, fine particle calcium carbonate, talcum powder mixture 30Kg face, filler are put together, after mixing, place standbyly, and this mixture is active magnetic iron powder.
Performance index
Environment-friendly high-efficiency coating and like product are relatively
Claims (1)
1, a kind of environment-friendly water-based priming paint, it is characterized in that: its weight percentages of components is:
Component one:
Silicate liquid 50～60%
Metal oxide is sodium oxide, Lithium Oxide 98min, potassium oxide 20～30%
ACRYLIC EMULSION 15～20%
Auxiliary agent 1～10%
Metal oxide is sodium oxide, Lithium Oxide 98min, potassium oxide, a kind of, two kinds or three kinds of mixing uses, and blending ratio is: two kinds is 3: 7, three kinds is 65: 25: 10;
Auxiliary agent comprises: Virahol or magnesium oxide;
Component two:
Zinc powder 70～80%
Active magnetic iron powder 20～30%
Its active magnetic iron powder weight percentages of components:
Magnetic iron powder 55-75%
Special addition agent 1-10%
Face, filler 20-40%
Face, filler comprise: titanium dioxide, fine particle calcium carbonate, talcum powder be one or two or three mixtures wherein; Wherein two ratio of mixture are 1: 3, three ratio of mixture 1: 3: 2;
Special addition agent is a dispersion agent, is specially 923S dispersion agent, YB201A dispersion agent.