CN100554625C - Composite stone slab - Google Patents
Composite stone slab Download PDFInfo
- Publication number
- CN100554625C CN100554625C CNB2007100032271A CN200710003227A CN100554625C CN 100554625 C CN100554625 C CN 100554625C CN B2007100032271 A CNB2007100032271 A CN B2007100032271A CN 200710003227 A CN200710003227 A CN 200710003227A CN 100554625 C CN100554625 C CN 100554625C
- Authority
- CN
- China
- Prior art keywords
- substrate layer
- resin
- brilliant
- stone slab
- protruding ridge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of composite stone slab, a substrate layer is arranged, its main points are: be compounded with brilliant hilllock stone decorative layer on the described substrate layer, many vertical protruding ridge and many horizontal protruding ridge are set on the described substrate layer, described substrate layer is composited by cloth or nonwoven and unsaturated-resin, described brilliant hilllock stone decorative layer is formed by quartz sand and mixed with resin curing, and described stone slab peripheral region is provided with metal edge frame.The present invention is specious, waterproof, acid and alkali-resistance, can be used for the decoration of wall, ceiling, floor, furniture.
Description
Technical field
The present invention relates to a kind of composite stone slab, this stone slab is a compound brilliant hilllock stone decorative layer on substrate layer, and many vertical protruding ridge and many horizontal protruding ridge are set on the described substrate layer, and this stone slab peripheral region is provided with metal edge frame.
Background technology
Chinese patent 01107481.7 discloses a kind of manufacture method of artificial slabstone, and this artificial slabstone adopts double-decker.The upper strata is the mixture of resin and clear glass grain or suprasil particulate, and lower floor is the mixture of colorant, building stones and resin.Because the reflection and the refraction principle of light make this product have high gloss, transparent feel and deep sense, marble or granitic tone sense are very obvious, feel magnificent unusually.The present invention makes full use of leftover bits and pieces or other industrial leftover bits and pieces of lithotome industry and produces.Because its surface layer is to be formed by multiple material and mixed with resin, so its intensity and hardness are lower, and the fire line of product is poor, and yielding, and the cost of product is higher.Therefore, need to propose a kind of composite stone slab.
Summary of the invention
The object of the present invention is to provide a kind of composite stone slab, this stone slab is a compound brilliant hilllock stone decorative layer on substrate layer, many vertical protruding ridge and many horizontal protruding ridge are set on the substrate layer, this stone slab peripheral region is provided with metal edge frame, have ornamental strong, be not easy distortion, breakage, the characteristics that the plate surface evenness is high.
The objective of the invention is to realize: a kind of composite stone slab by following technical proposals, a substrate layer is arranged, its main points are: be compounded with brilliant hilllock stone decorative layer on the described substrate layer, many vertical protruding ridge and many horizontal protruding ridge are set on the described substrate layer, described substrate layer is composited by cloth or nonwoven and unsaturated-resin, described brilliant hilllock stone decorative layer is formed by quartz sand and mixed with resin curing, and described stone slab peripheral region is provided with metal edge frame.
Compared with the prior art the present invention has following advantage:
1, because the present invention adopts light material to make, and product weight is light, can improve the safety factor of building thing.
2, because the present invention is provided with vertical protruding ridge, the horizontal protruding ridge and metal edge frame, product is not easy distortion, plate surface evenness height.
3, because the present invention does not contain radioactive substance, safe in utilization, the feature of environmental protection is strong.
4, no seam is easily spliced in the present invention, can improve decoration quality.
Description of drawings
The invention will be further described below in conjunction with drawings and Examples.
Fig. 1 is a structural representation of the present invention
Fig. 2 is cross-sectional view of the present invention (the A-A sectional drawing of Fig. 1)
Fig. 3 is decorative cover schematic diagram of the present invention (vertical view of Fig. 1)
The specific embodiment
Embodiment one:
Referring to Fig. 1, Fig. 2, Fig. 3 (Fig. 1, Fig. 2 are product profiles), composite stone slab of the present invention has a substrate layer 2, is compounded with brilliant hilllock stone decorative layer 1 on the described substrate layer, the compound employing routine techniques of substrate layer and decorative layer.Many vertical protruding ridge 4 and many horizontal protruding ridge 5 are set on the described substrate layer, described substrate layer is composited by cloth or nonwoven and unsaturated-resin, described brilliant hilllock stone decorative layer is formed by quartz sand and mixed with resin curing, and described stone slab peripheral region is provided with metal edge frame 3.In the present embodiment, the thickness of described substrate layer can be the 2-5 millimeter, and the thickness of brilliant hilllock stone decorative layer can be 0.5-2 millimeter (not comprising protruding ridge size).Being provided with of the described vertical protruding ridge and the horizontal protruding ridge can improve bending resistance of the present invention and non-deformability, when making the vertical protruding ridge of substrate layer and the horizontal protruding ridge, can increase the density of fibrous material at place, the protruding ridge or add metallic fiber.Quartz sand in the stone decorative layer of described brilliant hilllock can adopt colorful quartz sands, is used for changing the pattern of brilliant hilllock stone decorative layer.This resin and curing compound adopt conventional products and technology, and routine techniques is adopted in the processing on the surface of stone slab, is not described in detail at this.
In the present embodiment, described metal edge frame is the rectangle frame of a globality, adopts the corrosion resistant plate or the copper coin material of 0.3-1 millimeter thickness, is arranged between substrate layer and the brilliant hilllock stone decorative layer, can effectively prevent corner distortion, the fragmentation of composite stone slab, and can improve that it is ornamental.
Embodiment two:
Present embodiment is the improvement on the foregoing description basis, and in the present embodiment, the compound employing routine techniques of substrate layer and decorative layer comprises batching, mixing, mould, curing, grinding, polishing process.Used resin and curing compound adopt conventional products and technology, and routine techniques is adopted in the processing on the surface of stone slab, is not described in detail at this.
In order to produce more near the composite stone slab of granite pattern, the brilliant hilllock stone decorative layer of present embodiment comprises following raw material, and the percentage by weight of this raw material is:
Resin 30%
Quartzy coarse sand 20%
Quartzy fine sand 30%
Glass granules 4%
Silica 1 %
Alumina 1%
Titanium dioxide 0.1%
All the other are fillers, and filler can adopt 320 purpose microlith powder; Wherein, the proportioning of resin comprises curing compound, and quartzy coarse sand is a 20-40 order particle, and quartzy fine sand is 80 order particles, and glass granules adopts 100 order particles, also can use granite particulate instead of glass particulate; Silica, alumina, titanium dioxide adopt nano level raw material, and the particle diameter of this raw material is the 50-90 nanometer; Quartz sand in the stone decorative layer of described brilliant hilllock can adopt colorful quartz sands.
Composite stone slab of the present invention comprises following technical performance:
Glossiness is 95, and coefficient of thermal expansion is 16.1 * 10
-6, k, proportion is 2.7g/cm
3
Compressive strength 350kg/mm
2, rupture strength is 41N/mm
2, Mohs' hardness is 6.5
Acid resistance is 0.01mg/mm
2, alkali resistance is 0.01mg/mm
2
Composite stone slab of the present invention is specious, waterproof, acid-proof, anticorrosion, acid and alkali-resistance, can be used for the decoration of wall, ceiling, floor, furniture.
Claims (1)
1, a kind of composite stone slab, a substrate layer (2) is arranged, it is characterized in that: be compounded with brilliant hilllock stone decorative layer (1) on the described substrate layer, many vertical protruding ridge (4) and many horizontal protruding ridge are set on the described substrate layer, described substrate layer is composited by cloth or nonwoven and unsaturated-resin, described brilliant hilllock stone decorative layer is formed by quartz sand and mixed with resin curing, and described stone slab peripheral region is provided with metal edge frame (3); Described brilliant hilllock stone decorative layer comprises following raw material, and the percentage by weight of raw material is:
Resin 30%
Quartzy coarse sand 20%
Quartzy fine sand 30%
Glass granules 4%
Silica 1 %
Alumina 1%
Titanium dioxide 0.1%
All the other are fillers, and filler can adopt 320 purpose microlith powder;
Wherein, the proportioning of resin comprises curing compound, and quartzy coarse sand is a 20-40 order particle, and quartzy fine sand is 80 order particles, and glass granules adopts 100 order particles, also can use granite particulate instead of glass particulate; Silica, alumina, titanium dioxide adopt nano level raw material.