CN100551970C - 无溶剂型环氧树脂血管铸型剂 - Google Patents
无溶剂型环氧树脂血管铸型剂 Download PDFInfo
- Publication number
- CN100551970C CN100551970C CNB2006101616641A CN200610161664A CN100551970C CN 100551970 C CN100551970 C CN 100551970C CN B2006101616641 A CNB2006101616641 A CN B2006101616641A CN 200610161664 A CN200610161664 A CN 200610161664A CN 100551970 C CN100551970 C CN 100551970C
- Authority
- CN
- China
- Prior art keywords
- parts
- blood vessel
- casting mold
- agent
- type epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
无溶剂型环氧树脂血管铸型剂，其组成如下：E-52D型环氧树脂100份；固化剂二乙烯三胺12～20份；增塑剂磷酸三丁酯10～20份；柔软剂四氯乙烯8～10份；着色剂0.3份，血管铸型前将上述原料按比例混合均匀。所述E-52D型环氧树脂的粘度为1.1～1.4Pa.s。着色剂可采用红色油画颜料。本发明工艺简单，操作容易，在混合后二至三小时内体系粘度保持不变，从而保证铸型操作的顺利完成；并在24小时内可以实现完全固化，从而保证铸型后血管的及时成型。由于不含可挥发性溶剂，因此无需二次补注，且不会造成铸型血管空洞、变形现象的发生。本配方铸型样品，切片容易尤其适合血管三维图像的扫描制作。
Description
技术领域
本发明涉及一种无溶剂型环氧树脂血管铸型剂。
背景技术
血管铸型是解剖学标本制作的一项专门技术，广泛应用于各种动物和人体器官的血管脉络模型的制作。在医学教学科研和显微维克研究中具有很高的应用价值。近年来，随着计算机在医学上应用的不断加强，将已铸型的血管通过包埋切片，然后进行扫描，并通过计算机合成血管脉络的三维图像，已逐渐成为血管脉络研究的一个重要方法。
常用的血管铸型用铸型剂大多采用牙脱粉、ABS工程塑料、过氯乙烯添加乙酸乙酯等溶剂形成。但是目前所用的牙脱粉和过氯乙烯自身的粘合性较差，定型能力不强，而ABS溶解所配制的溶液粘度太大，难以通过直径较小的血管，且溶剂挥发后会形成空洞，无法满足进一步制作计算机三维图像时切片扫描的需要。
因此，人们常常选用E-44环氧树脂和乙二胺固化体系加以代替。但是由于该体系粘度过大，固化速度过快，无法实现铸型，必须加入一定量的乙酸乙酯溶剂进行稀释，以降低体系粘度，延长固化时间。而溶剂的挥发则会导致铸型血管内部形成空洞，难以满足制作计算机三维图像时切片扫描的需要。同时，当溶剂挥发后，体系固化反应过于激烈，容易引起血管的变形，导致铸型产生偏差。
发明内容
本发明针对上述问题，通过选择粘度较低的E-52D型环氧代替目前普遍使用E-44型环氧，降低体系粘度，并以二乙烯三胺代替乙二胺，同时适当降低二乙烯三胺在固化反应体系中的当量浓度，以推迟固化反应的进行时间，保证铸型操作的顺利进行。由于本配方未加入任何挥发性溶剂，因此无需二次补注，且不会造成铸型血管空洞、变形现象的发生。本配方铸型样品，切片容易尤其适合血管三维图像的扫描制作。
本发明的目的是通过以下措施来实现的：
一种无溶剂型环氧树脂血管铸型剂，其组成如下：
E-52D型环氧树脂，用量为100份。
固化剂：二乙烯三胺，用量为12～20份。
增塑剂：磷酸三丁酯，用量为10～20份。
柔软剂：四氯乙烯，用量为8～10份。
着色剂，用量为0.3份。
所述的E-52D型环氧为市售，其粘度为1.1-1.4Pa.s。
所述的磷酸三丁酯、四氯乙烯和着色剂(例如，油画颜料)均为市场销售的常规产品。
血管铸型前将上述原料按一定比例混合均匀即可使用。
本血管铸型剂适用于各种不同直径的血管铸型使用。
本发明的最优化方案是：将100份E-52D型环氧，15份二乙烯三胺，15份磷酸三丁酯，10份四氯乙烯和0.3份着色剂(采用红色油画颜料)混合均匀，即可作为血管铸型使用。该配方在混合后三小时内体系粘度保持不变，并在24小时内可以实现完全固化，本配方无需二次补注，且铸型的血管无空洞、变形现象发生，切片容易，适合血管三维图像的扫描制作。
本发明的优点：
本发明工艺简单，操作容易，该配方在混合后二至三小时内体系粘度保持不变，从而保证铸型操作的顺利完成；并在24小时内可以实现完全固化，从而保证铸型后血管的及时成型。由于本配方不含可挥发性溶剂，因此无需二次补注，且不会造成铸型血管空洞、变形现象的发生。本配方铸型样品，切片容易尤其适合血管三维图像的扫描制作。
具体实施方式
实施例1：
将100份E-52D型环氧，15份二乙烯三胺，15份磷酸三丁酯，10份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
实施例2：
将100份E-52D型环氧，12份二乙烯三胺，10份磷酸三丁酯，8份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
实施例3：
将100份E-52D型环氧，15份二乙烯三胺，10份磷酸三丁酯，8份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
实施例4：
将100份E-52D型环氧，20份二乙烯三胺，15份磷酸三丁酯，8份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
实施例5：
将100份E-52D型环氧，20份二乙烯三胺，20份磷酸三丁酯，8份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
实施例6：
将100份E-52D型环氧，12份二乙烯三胺，10份磷酸三丁酯，10份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
实施例7：
将100份E-52D型环氧，20份二乙烯三胺，15份磷酸三丁酯，8份四氯乙烯和0.3份红色油画颜料混合均匀，即可作为血管铸型使用。
Claims (3)
1、一种无溶剂型环氧树脂血管铸型剂，其组成如下：
E-52D型环氧树脂 100份
固化剂二乙烯三胺 12～20份
增塑剂磷酸三丁酯 10～20份
柔软剂四氯乙烯 8～10份
着色剂 0.3份，
血管铸型前将上述原料按比例混合均匀。
2、按照权利要求1所述的无溶剂型环氧树脂血管铸型剂，其特征在于，所述的E-52D型环氧的粘度为1.1-1.4Pa.s。
3、按照权利要求1或2所述的无溶剂型环氧树脂血管铸型剂，其特征在于，所述各组分的比例是：
E-52D型环氧树脂 100份
二乙烯三胺 15份
磷酸三丁酯 15份
四氯乙烯 10份
着色剂 0.3份，
所述的着色剂采用红色油画颜料。