CN100510745C - 水泥砂浆开裂性能测试方法 - Google Patents
水泥砂浆开裂性能测试方法 Download PDFInfo
- Publication number
- CN100510745C CN100510745C CNB2006100009463A CN200610000946A CN100510745C CN 100510745 C CN100510745 C CN 100510745C CN B2006100009463 A CNB2006100009463 A CN B2006100009463A CN 200610000946 A CN200610000946 A CN 200610000946A CN 100510745 C CN100510745 C CN 100510745C
- Authority
- CN
- China
- Prior art keywords
- mortar
- crackle
- cement mortar
- glass plate
- cracking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种水泥砂浆开裂性能快速测试方法，是将待测水泥砂浆直接涂抹在已予以加热(＞40℃)规定尺寸的玻璃板上，厚度控制在3-10mm，并立刻置于已升温到50-80℃的烘箱中，烘6-8h后取出置于室温环境冷却，观察表面开裂情况，以砂浆是否出现裂纹、以及裂纹的数量及长度、宽度判定该水泥砂浆的抗裂性能。经实验验证，本发明方法对聚合物砂浆抹面材料抗裂性检验较严格，经用本发明方法检验合格的产品用在楼墙面大面积外保温层施工，经1-4年的观察没有出现任何裂纹，具有较高可信度。
Description
技术领域
本发明涉及建筑材料的测试，特别涉及对水泥砂浆开裂性能的快速测试方法。
背景技术
水泥砂浆(或混凝土)开裂测试方法有多种，如平板法、环状法等。如平板法的测试，采用内边尺寸为600mm×600mm×63mm的钢制方形模具，模具的每条边上同时分别装配11个Φ10×100mm的细钢柱(起约束作用)；试验时，先将混凝土拌合物浇入此模具中插捣成型，抹平表面，将试件带模分别置于风吹环境中，用专门观察裂缝的50倍读数显微镜对各混凝土板的开裂情况进行跟踪观测：开始每隔5min观察一次，当发现有裂纹产生时变为每10min观察一次，在风吹下的条件下，对试件进行24h观察，主要记录每个混凝土板上裂缝的初裂时间(开始出现裂缝的时间)、裂缝尺寸(24h时的最大裂缝宽度和最长裂缝长度)以及裂缝数量(24h时的裂缝总条数以及长度在5cm以上裂缝的条数)。这种测试方法设备复杂、操作过程繁琐、耗时，并且只能测试常规混凝土(或砂浆)，而对聚合物砂浆的测试没有明显的效果。
发明创造内容
本发明的目的是提供一种操作简单、快速、可用于现场使用的、适用于普通混凝土砂浆以及聚合物砂浆开裂性能的测试方法。
本发明提供的水泥砂浆开裂性能测试方法，包括以下步骤：
步骤一：将待测水泥砂浆直接涂抹在已预先加热至40℃的玻璃板上，砂浆厚度为3-10mm；
步骤二：立即将抹有砂浆的玻璃板置于已升温到50-80℃的烘箱中，烘6-8h后取出，置于室温环境自然冷却；
步骤三：观察砂浆表面开裂情况，得出测试结果：不出现裂纹，抗裂性能优良；出现裂纹、裂纹数量在1-2条，每条裂纹长度<20mm，宽度<0.4mm，则抗裂性能一般；出现裂纹、裂纹数量多于2条，每条裂纹长度>20mm，宽度>0.4mm，则抗裂性能较差。
上述方法中，砂浆厚度为5-8mm，烘箱温度为60-80℃。
上述方法中，所述玻璃板规格为长300-500mm，宽50-100mm，长宽比不小于5，最好为60×300×5mm。
本发明的方法特别适用于工程中聚合物水泥砂浆抗裂性的现场检测，可在数小时内检验出被测水泥砂浆的抗裂性能，并经验证，该方法的测试结果准确。
具体实施方式
以下结合实验详述本发明方法以及测试效果。
本发明水泥砂浆开裂性能快速测试方法，是将待测水泥砂浆直接涂抹在已予以加热(>40℃)规定尺寸的玻璃板上，砂浆厚度控制在3-10mm，然后立即将载有砂浆的玻璃置于已升温到50-80℃的烘箱中，烘6-8h后取出，置于室温环境冷却后观察表面开裂情况，以砂浆是否出现裂纹、以及裂纹的数量及长度、宽度判定该水泥砂浆的抗裂性能。不出现裂纹，抗裂性能优良；出现裂纹、裂纹数量在1-2条，每条裂纹长度<20mm，宽度<0.4mm，则抗裂性能一般；出现裂纹、裂纹数量多于2条，每条裂纹长度>20mm，宽度>0.4mm，则抗裂性能较差。
实验一
测试条件：玻璃板规格60×300×5mm；砂浆厚度5mm；烘箱80℃，烘烤时间8h。1#砂浆实验：
按水泥：砂：ABW-I型胶粘剂(固含量25％)＝1：2.5：0.7比例配制的聚合物砂浆材料，直接抹在已予以晒热(>40℃)的玻璃板上(60×300×5mm)，砂浆厚度5mm。置于已升温到80℃的烘箱中，烘8h后观察，用5倍放大镜观察，结果砂浆表面无裂纹，砂浆与玻璃板粘结牢固。判断该号砂浆抗裂性能良好。
2#砂浆实验：
按水泥：砂：ABW-I型胶粘剂(固含量25％)＝1：2.0：0.7比例配制的聚合物砂浆材料，重复上述实验，用5倍放大镜观察，结果砂浆表面出现多条可见微裂纹，裂纹宽度明显增大，约0.6mm。判断该号砂浆抗裂性能较差。
3#砂浆实验：
按水泥：砂：ABW-I型胶粘剂(固含量30％)＝1：2.0：0.7比例配制的聚合物砂浆材料，重复上述实验，用5倍放大镜观察，结果砂浆表面无裂纹，砂浆与玻璃板粘结牢固。判断该号砂浆抗裂性能良好。
工程验证实验：
将以上三种砂浆在外墙外保温工程中作为聚合物砂浆抹面材料(厚度3mm)，结果发现2#砂浆在施工后一个月左右出现可见裂纹，横向和纵向都有裂纹出现。1#和3#砂浆施工的同样工程已经过4个冬雨季(4年)的考验，未出现可见裂纹，使用效果良好。
实验二
测试条件：玻璃板规格60×350×5mm；砂浆厚度3mm；烘箱70℃，烘烤时间6h。
在该测试条件下，同样对1#、2#、3#砂浆进行测试，结果1#、3#没有裂纹，2#出现裂纹，裂纹宽度约0.5mm。
实验三
测试条件：玻璃板规格50×350×5mm；砂浆厚度8mm；烘箱50℃，烘烤时间8h。
在该测试条件下，同样对1#、2#、3#砂浆进行测试，结果1#、3#没有裂纹，2#出现裂纹，裂纹宽度约0.4mm。
实验二、实验三测试结果与工程验证实验结果相同，说明本发明方法测试准确度高。
以上实验仅为说明本发明。大量试验证明，本发明优选的方法是将配制好的聚合物砂浆材料抹在60×300×5mm的玻璃板上，抹层厚度不小于5mm，然后直接放入已预热80℃的烘箱中，直到烘干，一般不小于6h，观察其表面是否开裂。多次试验发现，本发明方法对聚合物砂浆抹面材料抗裂性检验较严格，经用这种方法检验合格的产品用在楼墙面大面积外保温层施工，经1—4年的观察没有出现任何裂纹，说明本发明测试方法有较高可信度。
Claims (4)
1、一种水泥砂浆开裂性能测试方法，包括以下步骤：
步骤一：将待测水泥砂浆直接涂抹在已预先加热至40℃的玻璃板上，砂浆厚度为3-10mm；
步骤二：立即将抹有砂浆的玻璃板置于已升温到50-80℃的烘箱中，烘6-8h后取出，置于室温环境自然冷却；
步骤三：观察砂浆表面开裂情况，得出测试结果：不出现裂纹，抗裂性能优良；出现裂纹、裂纹数量在1-2条，每条裂纹长度<20mm，宽度<0.4mm，则抗裂性能一般；出现裂纹、裂纹数量多于2条，每条裂纹长度>20mm，宽度>0.4mm，则抗裂性能较差。
2、根据权利要求1所述的水泥砂浆开裂性能测试方法，其特征在于，砂浆厚度为5-8mm，烘箱温度为60-80℃。
3、根据权利要求1或2所述的水泥砂浆开裂性能测试方法，其特征在于，所述玻璃板规格为长300-500mm，宽50-100mm，长宽比不小于5。
4、根据权利要求3所述的水泥砂浆开裂性能测试方法，其特征在于，所述玻璃板规格为60×300×5mm。