CN100493867C - Method for producing plywood of solidified flame retardant paint - Google Patents
Method for producing plywood of solidified flame retardant paint Download PDFInfo
- Publication number
- CN100493867C CN100493867C CNB2007101071396A CN200710107139A CN100493867C CN 100493867 C CN100493867 C CN 100493867C CN B2007101071396 A CNB2007101071396 A CN B2007101071396A CN 200710107139 A CN200710107139 A CN 200710107139A CN 100493867 C CN100493867 C CN 100493867C
- Authority
- CN
- China
- Prior art keywords
- lamp
- coated
- paint
- road
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A plywood with solidified flame-retarding paint is prepared through combining the core plywood, cold pressing, repairing, hot pressing, veneering, cold pressing, repairing, hot pressing, abrading, repairing, removing powder, painting, UV drying, abrading, painting, UV drying, abrading, painting, painting, UV drying, abrading, coating surface paint, UV drying, coating surface paint again, and UV drying.
Description
Technical field the invention belongs to the plywood production technical field, relates to a kind of production method of plywood of solidified flame retardant paint.
The background technology plywood of solidified flame retardant paint, technical term appellation: UV coats with lacquer glued board.Prior art produce glued board it comprise central layer group embryo, cold pressing, repairing, hot pressing, veneer, cold pressing, repairing, hot pressing, sanding operation make the finished product glued board.The glued board that prior art is produced in use, need to paint or spray paint at its plate face, normally used paint all contains environmental contaminants such as benzene lead, and the formaldehyde of conventional glued board, be the primary pollution source of present house fitting-up, common paint itself belongs to the inflammability material simultaneously, has disaster hidden-trouble.
Summary of the invention the objective of the invention is to solve when glued board that prior art produces uses needs actual spot painting to have the technical problem of aspects such as using inconvenience, contaminated environment and disaster hidden-trouble, provide a kind of production method of plywood of solidified flame retardant paint, to overcome the deficiencies in the prior art.
To achieve these goals, the production method of plywood of solidified flame retardant paint of the present invention, be to improve realization on the basis of existing technology, it comprises central layer group embryo, cold pressing, repair, hot pressing, veneer, cold pressing, repair, hot pressing, the sanding operation is made glued board, its main points are that prepared glued board is again through repairing, remove dust, be coated with the first road priming paint, UV lamp drying 1, sanding, be coated with the second road priming paint, UV lamp drying 2, be coated with the 3rd road priming paint, UV lamp drying 3, sanding, be coated with the first road finish paint, UV lamp drying 4, be coated with the second road finish paint and make plywood of solidified flame retardant paint through dry 5 operations of UV lamp again, said to be coated with the first road priming paint coating weight be 30～35g/m
2, being coated with the second road priming paint coating weight is 25～30g/m
2, being coated with the 3rd road priming paint coating weight is 20～25g/m
2, being coated with the first road finish paint coating weight is 10～15g/m
2, being coated with the second road finish paint coating weight is 8～10g/m
2Said its linear velocity of UV lamp drying process is respectively 12～15m/min.
Said UV lamp drying 1, UV lamp drying 2, UV lamp drying 3, UV lamp dry 4 and dry 5 operations of UV lamp adopt two high light UV of 9.6Kw lamp, a low light level UV of 9.6Kw lamp, two high light UV of 9.6Kw lamp, 9.6Kw two low light level UV lamp and three high light UV of 9.6Kw lamp respectively.
The said lacquer of the present invention is: the UV lacquer that Suzhou Mingda Macromolecule Technology Material Co., Ltd. produces.
This paint is compared pollutants such as not containing any lead, potassium, mercury, benzene with common paint, thereby UV of the present invention lacquer glued board compares with normal plywood, has the remarkable environmental characteristics; UV lacquer itself does not have flammable, even use naked light, can not burn yet, and it is covered with paint, lacquer, colour wash, etc. at plate surface, can isolate burning things which may cause a fire disaster, reaches fire-retardant effect; The UV finish paint is a kind of super-antiwear floor paint, contains the composition that abrasion-resistant powder etc. strengthens anti-wear performance, and wear-resisting wiping is effective; UV coats with lacquer curing, is that wherein the sensitising agent composition absorbs the change of ultraviolet light triggering paint character, forms hard solid, not only has wearability, simultaneously, also has scratch resistance.
The plywood of solidified flame retardant paint that the inventive method is produced has characteristics such as environmental protection, fire-retardant, wear-resisting, scratch-resistant, and easy to install and use.
The specific embodiment
Embodiment 1 plywood of solidified flame retardant paint is by following processing step production: central layer through the group embryo, cold pressing, repairing, hot pressing, veneer, cold pressing, repairing, hot pressing, the conventional operation of sanding make glued board, through repairing, remove dust, be coated with the first road priming paint, UV lamp drying 1, sanding, be coated with the second road priming paint, UV lamp drying 2, be coated with the 3rd road priming paint, UV lamp drying 3, sanding, being coated with the first road finish paint, UV lamp drying 4, being coated with the second road finish paint and making plywood of solidified flame retardant paint through dry 5 operations of UV lamp again, being coated with the first road priming paint coating weight is 30g/m with the glued board that makes
2, being coated with the second road priming paint coating weight is 30g/m
2, being coated with the 3rd road priming paint coating weight is 20g/m
2, being coated with the first road finish paint coating weight is 10g/m
2, being coated with the second road finish paint coating weight is 10g/m
2Said its linear velocity of UV lamp drying process is respectively 15m/min; UV lamp drying 1, UV lamp drying 2, UV lamp drying 3, UV lamp dry 4 and dry 5 operations of UV lamp adopt two high light UV of 9.6Kw lamp, a low light level UV of 9.6Kw lamp, two high light UV of 9.6Kw lamp, 9.6Kw two low light level UV lamp and three high light UV of 9.6Kw lamp respectively; The lacquer that is coated with is: the UV lacquer that Suzhou Mingda Macromolecule Technology Material Co., Ltd. produces.
Embodiment 2 is according to embodiment 1, and being coated with the first road priming paint coating weight is 35g/m
2, being coated with the second road priming paint coating weight is 25g/m
2, being coated with the 3rd road priming paint coating weight is 25g/m
2, being coated with the first road finish paint coating weight is 15g/m
2, being coated with the second road finish paint coating weight is 8g/m
2
Embodiment 3 is according to embodiment 1, and being coated with the first road priming paint coating weight is 32g/m
2, being coated with the second road priming paint coating weight is 28g/m
2, being coated with the 3rd road priming paint coating weight is 22g/m
2, being coated with the first road finish paint coating weight is 13g/m
2, being coated with the second road finish paint coating weight is 9g/m
2
Described UV lamp drying 1, UV lamp drying 2, UV lamp drying 3, UV lamp drying 4, UV lamp drying 5 are meant that the present invention produces UV lacquer glued board, altogether through five uviol lamp drying processes.
Claims (2)
1, a kind of production method of plywood of solidified flame retardant paint, it comprises central layer group embryo, cold pressing, repair, hot pressing, veneer, cold pressing, repair, hot pressing, the sanding operation is made glued board, it is characterized in that prepared glued board is again through repairing, remove dust, be coated with the first road priming paint, UV lamp drying for the first time, sanding, be coated with the second road priming paint, UV lamp drying for the second time, be coated with the 3rd road priming paint, UV lamp drying for the third time, sanding, be coated with the first road finish paint, the 4th UV lamp drying, be coated with the second road finish paint and make plywood of solidified flame retardant paint through the 5th UV lamp drying process again, used paint is not leaded, potassium, mercury, the UV lacquer of benzene pollutant; It is said that to be coated with the first road priming paint coating weight be 30～35g/m
2, being coated with the second road priming paint coating weight is 25～30g/m
2, being coated with the 3rd road priming paint coating weight is 20～25g/m
2, being coated with the first road finish paint coating weight is 10～15g/m
2, being coated with the second road finish paint coating weight is 8～10g/m
2Said its linear velocity of UV lamp drying process is respectively 12～15m/min.
2, the production method of plywood of solidified flame retardant paint according to claim 1, it is characterized in that said first time of UV lamp drying, for the second time UV lamp drying, for the third time UV lamp drying, the 4th UV lamp is dry and the 5th UV lamp drying process adopts two high light UV of 9.6Kw lamp, a low light level UV of 9.6Kw lamp, two high light UV of 9.6Kw lamp, 9.6Kw two low light level UV lamp and three high light UV of 9.6Kw lamp respectively.