CN1004547B - Process for manufacturing clay brick by non-sintering - Google Patents
Process for manufacturing clay brick by non-sintering Download PDFInfo
- Publication number
- CN1004547B CN1004547B CN 88100276 CN88100276A CN1004547B CN 1004547 B CN1004547 B CN 1004547B CN 88100276 CN88100276 CN 88100276 CN 88100276 A CN88100276 A CN 88100276A CN 1004547 B CN1004547 B CN 1004547B
- Authority
- CN
- China
- Prior art keywords
- weight
- brick
- sintering
- present
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
The present invention relates to a formula of a non-sintering clay brick which is mainly composed of 80 to 85 % (weight) of clay (dry basis), 0.1 to 0.6 % (weight) of compound activity additive, 3 to 10 % (weight) of cement and equilibrium amount of water; the material is mixed and shaped by pressing. The quality of the clay brick produced by the present invention conforms to the requirement of a common clinker brick GB5101-81; the cost is lower than that of a clinker brick and a red brick. The present invention has the advantages of rich mud source, low energy consumption and no environment pollution, and is beneficial to popularization; the present invention also has obvious social and economic benefit.
Description
The present invention is the manufacture method of a kind of manufacture method of sintering-free clay material of construction, particularly sintering-free clay brick.
As everyone knows, the red soil brick of architectural use since ancient times, generally taking clay as material, forms with fuel sintering, and its drawback is that energy consumption is large, damages good farmland, contaminate environment and the destruction eubiosis.And sintering-free clay brick is generally divided into two classes, a class is to mix compression moulding with red soil lime etc.Form through steam-cured and maintenance, but complex process, energy consumption are large, contaminate environment, unfavorable popularization; Another kind of is to mix compression moulding with clay, cement, admixture etc., and natural curing forms, but because admixture is single, poor activity, thereby cement consumption is generally more than 10%, production cost is too high, is difficult to implement.
Task of the present invention is the component by changing admixture, a kind of composite reactive admixture is provided, thereby makes greatly to reduce the cement consumption of sintering-free clay brick, prepares the sintering-free clay brick that a kind of energy consumption is low, free from environmental pollution, production cost is low.
The manufacture method of sintering-free clay brick, contain clay (butt) 80~85% (weight), composite reactive admixture 0.1~0.6% (weight), cement 3~10% (weight) and balance water gaging and form, composite reactive admixture mainly contains silica 1 2~17% (weight), sulphur trioxide 30~50% (weight), sodium oxide 5~10% (weight), aluminium sesquioxide 5~10% (weight), low-molecular-weight resin 10~15% (weight) and balance water gaging and forms.
The manufacture method of sintering-free clay brick, wherein contains cement and is preferentially chosen as 3.5~7% (weight).
The manufacture method of sintering-free clay brick provided by the present invention, made sintering-free clay brick quality meets the requirement of ordinary fired brick α B5101-85, cost is all lower than vitrified brick and steam-cured red soil brick, there is low free from environmental pollution, the advantage such as technique is simple, production cost is low of energy consumption, easy to implement, there are larger economic results in society.
Embodiment
The manufacture method of sintering-free clay brick of the present invention, selection contains clay (butt) 85% (weight), composite reactive admixture 0.3% (weight), cement 5% (weight) and balance water gaging and forms, and composite reactive admixture contains silica 1 5% (weight), sulphur trioxide 35% (weight), sodium oxide 5% (weight), aluminium sesquioxide 5% (weight), low-molecular-weight resin 10% (weight) and balance water gaging and forms.First by above-mentioned clay (butt) 85% (weight) drying and fragmentation, add No. 425 ordinary Portland cements 5% (weight) to stir 30 minutes, adding the composite reactive admixture 0.3% (weight) of said ratio and balance water gaging mix and blend 30 minutes, is 1.962 × 10 through forming pressure again
7-2.943 × 10
7newton/meter
2the compression moulding of brick pressing machine semidrying, natural curing can be delivered for use for 1~2 week.
Claims (2)
1. the manufacture method of a sintering-free clay brick, contain clay (butt) 80~85% (weight), composite reactive admixture 0.1~0.6% (weight), cement 3~10% (weight) and balance water gaging and form, it is characterized in that composite reactive admixture mainly contains (% by weight)
And balance water gaging forms.
2. manufacture method as claimed in claim 1, is characterized in that containing cement and is preferentially chosen as 3.5~7% (weight).