CN100441402C - Method for fiber material adhesive forming - Google Patents
Method for fiber material adhesive forming Download PDFInfo
- Publication number
- CN100441402C CN100441402C CNB2006100518336A CN200610051833A CN100441402C CN 100441402 C CN100441402 C CN 100441402C CN B2006100518336 A CNB2006100518336 A CN B2006100518336A CN 200610051833 A CN200610051833 A CN 200610051833A CN 100441402 C CN100441402 C CN 100441402C
- Authority
- CN
- China
- Prior art keywords
- fiber material
- cloth
- auxiliary agent
- agent liquid
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a method of adhesive-bonding forming for a fiber material. The fiber material is formed by the compatibility of 80 to 90% of acrylics and 10 to 20% of polyamine lipid with 15 to 20% of water added by weight percentage; after auxiliary agent liquid is coated, brushed and sprinkled on the fiber material superposed on base cloth, the fiber material is leveled and ironed, and the base cloth is uncovered after the fiber material is cooled; contrarily, the fiber material is infiltrated in the auxiliary agent liquid, the fiber material is superposed for adhesive bonding and drying forming after being taken out, and cooling and mold releasing are carried out; contrarily, the fiber material is collected into bundles for tying forming and is infiltrated in the auxiliary agent liquid, and the fiber material is baked and formed after being taken out. A finished product can carry out paint printing, manual painting and fiber material dyeing; the present invention has the advantages of adjustable density of the fiber material, capability of water immersion and being smeared and washed, environment protection and completion of requirements for comparative complex shape; the finished product can be decorative cloth, cloth of a lamp box, a gift bag, a gift box, a container, a lamp cover, a shoe, a cap, a specific curtain, a handicraft and a filtering material of specific requirements, industrial, agricultural and garden appliances, appliances in other fields, etc.
Description
Technical field
The present invention relates to a kind of method of fiber material adhesive forming.
Background technology
Fiber in the textile is mainly used to weave, simultaneously weave with manufacturing process such as clothes in, its softness produces a large amount of waste silk and cloth waste, owing to can't be shaped, the main recovery produced regenerated fiber and lining, and waste silk and cloth waste composition complexity during owing to recovery are given to produce again and brought difficulty.Textile tapes and line, rope class are mainly used to braiding, decorate usefulness, can't endure with all one's will moulding.Existing nonwoven mainly is that short fiber forms by machine.
Summary of the invention
In order to overcome the problem that fibrous material can not bonding hard moulding, purpose of the present invention provides the method for bonding by hand a kind of fiber material adhesive forming in the street.
The technical solution adopted for the present invention to solve the technical problems is that its step is as follows:
1) is that 80～90% esters of acrylic acid and 10～20% polyurethanes are raw material with percentage by weight, becomes auxiliary agent liquid with the compatible that adds 15～20%;
2) will be superimposed upon fibrous material brushing on the base fabric, spray smooth flatiron behind the auxiliary agent liquid, cooling is thrown off base fabric and is got final product; Or fibrous material soaks in auxiliary agent liquid, takes out the back at bonding, the drying forming of die surface stack, and cooling and demolding get final product, or fibrous material boundling ligation moulding, soaks in auxiliary agent liquid, and drying forming gets final product after taking out.
Band modulus fibre material bake out temperature is 80～100 ℃, 20～30min.
Described fibrous material is fiber, cloth waste, band, line or rope.
The beneficial effect that the present invention has is: can be according to product requirement, soak into or brushing, spray by the non-toxic water soluble auxiliary agent, make and be with the liquid fibrous material, can add the hard moulding of heat bonding around song arbitrarily, the stackable any thickness of band liquid cloth waste adds the hard moulding of heat bonding, but the manufactured goods pigment printing, but also Freehandhand-drawing, but also fibrous material dyeing.Manufactured goods adjustable density joint, but water logging, smear and wash, manufacture craft is simple, and environmental protection can be finished the more complicated shape need.Manufactured goods can be decorating cloth, lamp house cloth, gift bag, gift box, container, lampshade, footwear, cap, special curtain, handicraft and specific (special) requirements filter material, industry, agricultural, gardens articles for use and other field articles for use etc.
The specific embodiment
The step of this method is as follows:
1) is that 80～90% esters of acrylic acid and 10～20% polyurethanes are raw material with percentage by weight, becomes auxiliary agent liquid with the compatible that adds 15～20%;
2) will be superimposed upon fibrous material brushing on the base fabric, spray smooth flatiron behind the auxiliary agent liquid, cooling is thrown off base fabric and is got final product; Or fibrous material soaks in auxiliary agent liquid, takes out the back at bonding, the drying forming of die surface stack, and cooling and demolding get final product, or fibrous material boundling ligation moulding, soaks in auxiliary agent liquid, and drying forming gets final product after taking out.
Band modulus fibre material bake out temperature is 80～100 ℃, 20～30min.
Described fibrous material is fiber, cloth waste, band, line or rope etc.
The processing method type:
1, straight forming becomes cloth, and the back is pressed to scald and added thermal finalization;
2, be attached on the mould and finalize the design, dry, train baking again and handle.
3, ligation moulding is dried, is trained baking again and handles.
But fiber, band, line class be around song stack geometry, but also free shape, and cloth waste can be cut into geometry, but also arbitrary shape stack.Manufactured goods hardness can be regulated, and stack thickness can be any, and auxiliary agent is nontoxic, do not fire, and is not quick-fried.Manufactured goods can be industrial goods such as decorating cloth, lamp house cloth, gift bag, container, lampshade, footwear, cap, special curtain, handicraft and specific (special) requirements filter material, agriculture soilless culture base cloth, agriculture fruit tree packaging bag, garden lawn base cloth etc.But pigment printing on the manufactured goods, but also Freehandhand-drawing.The manufactured goods adjustable density, but water logging, smear and wash, cohesive force is strong, and stiffness is good, and manufacture craft is simple, and environmental protection can be finished the more complicated shape need, can make the textile waste comprehensive utilization, forms recycling economy.
One, the making of the hard cloth of fiber
1, is that 80% esters of acrylic acid and 20% polyurethanes are raw material with percentage by weight, becomes auxiliary agent liquid, stir evenly with the compatible that adds 15%;
2, tiling has been superimposed upon on the base fabric according to door width of cloth size with fiber;
3, liquid additive is brushed or is sprayed on the fiber, till infiltration;
4, coverage rate cloth thereon again, smooth flatiron on face cloth (the also not direct smooth flatiron of capping cloth);
5, treat its cooling, throw off face, base fabric, the hard cloth of fiber.
Two, the making of shaped article
1, is that 90% esters of acrylic acid and 10% polyurethanes are raw material with percentage by weight, becomes auxiliary agent liquid, stir evenly with the compatible that adds 15%;
2, make mould (also can have one deck demoulding base fabric) at die surface;
3, cloth waste is put into liquid additive, till infiltration, taking out the cloth waste liquid holdup is about 70%;
4, cloth waste stack is bonded to mould surface or, regulates stack thickness as required with on one deck demoulding base fabric;
5, (bake out temperature is 80～100 ℃, 20～30min) oven dry mould to be put into baking oven or micro-wave oven;
6, in baking oven, bake 100～140 ℃ again, 1～5min;
7, take out, cooling and demolding gets final product.
Three, the butting shaped article is made
1, is that 85% esters of acrylic acid and 15% polyurethanes are raw material with percentage by weight, becomes auxiliary agent liquid, stir evenly with the compatible that adds 20%;
2, with fiber and band, line or rope class, according to product requirement boundling ligation moulding;
3, with fiber and band, line or rope class moulding boundling, put into liquid additive, till infiltration, taking out liquid holdup is about 70%;
4, with hot blast drying or oven dry (bake out temperature is 80～100 ℃, 20～30min);
5, small-sizedly can bake 100～140 ℃ again in baking oven, 1～5min takes out and gets final product;
6, large product dries up.
Claims (1)
1. the method for a fiber material adhesive forming is characterized in that the step of this method is as follows:
1) is that 90% esters of acrylic acid and 10% polyurethanes are raw material with percentage by weight, becomes auxiliary agent liquid, stir evenly with the compatible that adds 15%;
2) make mould or at die surface with one deck demoulding base fabric;
3) cloth waste is put into liquid additive, till infiltration, taking out the cloth waste liquid holdup is about 70%;
4) cloth waste stack is bonded to mould surface or, regulates stack thickness as required with on one deck demoulding base fabric;
5) mould is put into baking oven or micro-wave oven, bake out temperature is 80～100 ℃, 20～30min oven dry;
6) in baking oven, bake 100～140 ℃ again, 1～5min;
7) take out, cooling and demolding gets final product.