CN100434360C - Multi-walled carbon nanotube, chestnut-shaped carbon nanotube assembly and preparation method of carbon nanotube ball - Google Patents
Multi-walled carbon nanotube, chestnut-shaped carbon nanotube assembly and preparation method of carbon nanotube ball Download PDFInfo
- Publication number
- CN100434360C CN100434360C CNB2005101303144A CN200510130314A CN100434360C CN 100434360 C CN100434360 C CN 100434360C CN B2005101303144 A CNB2005101303144 A CN B2005101303144A CN 200510130314 A CN200510130314 A CN 200510130314A CN 100434360 C CN100434360 C CN 100434360C
- Authority
- CN
- China
- Prior art keywords
- carbon nanotube
- tubes
- walled carbon
- carbon nano
- catalyst precursor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to the technical field of nano materials, and particularly relates to a method for preparing high-performance dispersed multi-walled carbon nanotubes, chestnut-shaped carbon nanotube aggregates and carbon nanotube spheres from low-cost polymers in a large scale. The method adopts a new in-situ preparation concept of the nano catalyst, synthesizes the high-activity nano catalyst in situ, and further prepares the high-performance dispersed multi-walled carbon nano tubes, the chestnut-shaped carbon nano tube aggregate and the carbon nano tube spheres. A number of physicochemical methods have been used to perform a series of characterizations and studies on these products. The invention can be used for continuously synthesizing high-performance dispersed multi-wall carbon nanotubes, chestnut-shaped carbon nanotube aggregates and carbon nanotube spheres in large scale and high quality.
Description
Technical field
The invention belongs to technical field of nano material, particularly a kind of preparation method who prepares high-performance dispersion multi-walled carbon nano-tubes, chestnut shape carbon nanotube aggregate and carbon nanotube ball from cheap polymkeric substance in a large number.
Background technology
Carbon nanotube is the 1-dimention nano hollow structure of a class carbon.Because its unique physics and chemical property, carbon nanotube is at (the M.S.Dresselhaus that is with a wide range of applications such as aspects such as structured material, energy and material, electron device, photonic devices, G.Dresselhaus, P.Avouris, Eds.CarbonNanotubes:Synthesis, Structure, Properties, and Applications, Sptinger:NewYork, 2002).Therefore, the low cost of carbon nanotube, serialization, preparation and purifying are that scientist and engineering technical personnel dream of always in a large number.Comprise in the reported method in the document: (Nature 1992,358 for T.W.Ebbesen, P.M.Ajayan for arc process, 220), laser evaporation method (A.Thess, R.Lee, P.Nikolaev, H.Dai, P.Petit, J.Robert, C.H.Xu, Y.H.Lee, S.G.Kim, A.G.Rinzler, D.T.Colbert, G.E.Scuseria, D.Tomanek, J.E.Fischer, R.E.Smalley, Science1996,273,483), chemical Vapor deposition process (Z.F.Ren, Z.P.Huang, J.W.Xu, J.H.Wang, P.Bush, M.P.Siegal, P.N.Provencio, Science 1998,282, and 1105) etc.Wherein, chemical Vapor deposition process is the method that is most widely used at present, and reason is that equipment is relatively inexpensive, and can prepare the carbon nanotube of more amount in the short period of time.Used catalyzer comprises metal nanoparticles loaded catalyzer (a) Z.Shi, Y.Lian, X.Zhou in the preparation, Z.Gu, Y.Zhang, S.Iijima, H.Li, K.T.Yue, S.-L.Zhang, J.Phys.Chem.B.1999,103,8698.b) M.Yudasaka, T.Komatsu, T.Ichihashi, Y.Achiba, S.Iijima, J.Phys.Chem.B.1998,102,4892), organometallic compound (a) L.C.Qin, J.Mater.Sci.Lett.1997,16,457.b) Y.-Y.Fan, F.Li, H.-M.Cheng, G.Su, Y.-D.Yu, Z.-H.Shen, J.Mater.Res.1998,13,2342) etc.The carbon source that the preparation carbon nanotube is used generally is the gas organic molecule, as (a) P.E.Nolan such as methane, ethane, propane, carbon monoxide, D.C.Lynch, A.H.Cutler, J.Phys.Chem.B11998,102,4165.b) G.Che, B.B.Lakshmi, C.R.Martin, E.R Fisher, R.S.Ruoff, Chem.Mater.1998,10,260.c) T.Kyotani, L.-F.Tsai, A.Tomita, Chem.Mater.1996,8,2109.d) B.Zheng, C.Lu, G..Gu, A.Makarovski, G.Finkelstein, J.Liu, Nano Lett.2002,2,895).
Preparing carbon nanotube with polymkeric substance as carbon source is the method that occurs recently, and document has been reported under the inert atmosphere from polyethylene, polyvinyl alcohol, polymethylmethacrylate/polypropylene nitrile, tetrafluoroethylene can prepare carbon nanotube (a) E.F.Kukovitskii, L.A.Chernozatonskii, S.G.L ' vov, N.N.Mel ' nik, Chem.Phys.Lett.1997,266,323.b) N.I.Maksimova, O.P.Krivoruchko, G.Mestl, V.I.Zaikovskii, A.L.Chuvilin, A.N.Salanov, E.B.Burgina, J.Mol.Cat.A:Chem.2000,158,301.c) O.P.Krivoruchko, N.I.Maksimova, V.I.Zaikovskii, A.N.Salanov, Carbon 2000,38,1075.d) D.Hulicova, K.Hosoi, S-I.Kuroda, H.Abe, A.Oya, Adv.Mater.2002,14,452.e) A.Huczko, H.Lange, G.Chojecki, S.Cudzilo, Y.Q.Zhu, H.W.Kroto, D.R.M.Walton, J.Phys.Chem.B.2003,107,2519).Recently, also reported in the document by the burning polypropylene/ni-loaded catalyst/polynite mixture prepare carbon nanotube (T.Tang, X.C.Chen, X.Y, Meng, H.Chen, Y.P.Ding, Angew.Chem.Int.Ed.2005,44,1517).In the method, must utilize the catalyzer of special nickel-loaded nanoparticle, otherwise can not generate carbon nanotube.
Summary of the invention
A purpose of the present invention is to overcome the shortcoming that must use the catalyzer of nickel-loaded nanoparticle in the aforesaid method, preparation technology's flow process is shortened greatly, and easily serialization, thereby improve the stability of preparation efficiency and quality product, provide a kind of and prepare the preparation method that high-performance is disperseed multi-walled carbon nano-tubes, chestnut shape carbon nanotube aggregate and carbon nanotube ball in a large number from cheap polymkeric substance.
Another object of the present invention is significantly to reduce the preparation cost of carbon nanotube, for the suitability for industrialized production carbon nanotube provides a method that economic and technical norms are all feasible.
The present invention adopts the catalyzer original position to prepare new concept and new technology, and the preparation method of design optimization has repeatedly shortened the preparation flow of carbon nanotube greatly, has reduced production cost, has improved the productive rate and the quality of stability of carbon nanotube.The material of multiple pattern be can prepare by the inventive method, dispersing Nano carbon tubes, chestnut shape carbon nanotube aggregate, carbon nanotube ball etc. comprised.
The preparation method of multi-walled carbon nano-tubes of the present invention, chestnut shape carbon nanotube aggregate and carbon nanotube ball does not need the nanocatalyst that adopts with traditional method, and uses catalyst precursor instead, and this method may further comprise the steps:
(1). catalyst precursor is carried out heat pre-treatment, to slough volatile constituent wherein;
(2). the catalyst precursor and the promotor of organic filler, mineral filler, pretreated step (1) are mixed, and in blending equipment, under 20~500 ℃ of temperature, carry out mixing, each component is further mixed, and environment controlled atmosphere is inert atmosphere, air atmosphere, vacuum atmosphere or mixed-gas atmosphere;
Catalyst precursor is 0.1~80wt% in the described mixture, and promotor is 0~10wt%, and mineral filler is 1~90wt%, and organic filler is 1~95wt%;
(3) the pretreated catalyst precursor of step (1) is put into 100~1500 ℃ High Temperature Furnaces Heating Apparatus reaction after, from High Temperature Furnaces Heating Apparatus, take out, allow it be cooled to room temperature; Obtain multi-walled carbon nano-tubes and twine the chestnut shape carbon nanotube aggregate that constitutes with mineral filler mutually by multi-walled carbon nano-tubes;
(4) multi-walled carbon nano-tubes that step (3) is obtained and chestnut shape carbon nanotube aggregate are put into inorganic acid solution and are handled (under normal temperature or the heating condition), remove mineral filler, by centrifugation, cleaning, drying, obtain multi-walled carbon nano-tubes and carbon nanotube ball.
The diameter of described multi-walled carbon nano-tubes is 25~50 nanometers, and chestnut shape carbon nanotube aggregate size is at 2~11 microns; Carbon nanotube ball size is at 2~11 microns.
Described catalyst precursor pretreatment temperature is 30~600 ℃.
The content of described catalyst precursor is preferably 2~75% of reactant gross weight.Catalyzer is by the reaction in-situ preparing of catalyst precursor, and the preparation of catalyzer original position refers to that catalyzer forms in the product generative process, and catalyzer generative process and product generative process are inseparable.
Described catalyst precursor is selected from a kind of in water miscible zinc acetate, strontium acetate, neutralized verdigris, iron acetate, acetic acid brill, nickel acetate, zinc formate, strontium formate, Tubercuprose, ironic formiate, cobaltous formate, nickel formate, zinc nitrate, strontium nitrate, cupric nitrate, iron nitrate, Xiao Suangu, the nickelous nitrate etc., or selects wherein 2~5 kinds to mix and use.
The rare gas element of described inert atmosphere is a kind of in helium, nitrogen or the argon gas.
Described mixed-gas atmosphere is selected from a kind of in helium/nitrogen, argon gas/nitrogen, the argon/helium etc.
Described promotor is selected from a kind of in zinc carbonate, copper carbonate, iron carbonate, strontium oxalate, caoxalate, sodium oxalate, water glass, pure aluminium silicate, the lead silicate etc.
Described mineral filler is selected from a kind of in silicon-dioxide, titanium dioxide, lime carbonate, yellow soda ash, kaolin, clay, modified clay, mica, white mica, phlogopite, zinc oxide, the cupric oxide etc.
Described organic filler is selected from a kind of than in Lip river alkane ketone, Mierocrystalline cellulose, starch, wood pulp, polyacrylamide, the polyvinyl acetate (PVA) etc. of polymethylmethacrylate, polystyrene, polyethylene, Resins, epoxy, polypropylene, polybutene, polyisoprene, polyethylene.
Described mineral acid is selected from a kind of in nitric acid, hydrofluoric acid, sulfuric acid, hydrochloric acid, perchloric acid, the silicic acid etc.
The X-powder diffraction pattern shows the catalyzer that has successfully prepared the catalyzed carbon nanotube growth by in-situ synthetic method, and these catalyzer have very high activity.The X-powder diffraction pattern is further illustrated under the catalysis of original position synthetic catalyzer, and polymkeric substance successfully is converted into the graphite carbon structure.The X-powder diffraction pattern shows that also catalyzer can remove by suitable acid-alkali treatment.The inorganics (Fig. 1) that also has other that can remove with soda acid.
Sem observation shows, has obtained dispersing Nano carbon tubes, chestnut shape carbon nanotube aggregate, carbon nanotube ball (Fig. 2) by the present invention.Carbon nanotube can be intertwined mutually, forms stable spherical and chestnut shape aggregate, also can separate to twine and obtain single-root carbon nano-tube.Admixture provides growing environment and a plurality of carbon nano tube growths site of a carbon nanotube.The diameter of carbon nanotube is approximately 25~50 nanometers, and the size of carbon nanotube ball and chestnut shape carbon nanotube aggregate is in 2~11 micrometer ranges.
Transmission electron microscope observation shows that carbon nanotube is a hollow structure, and external diameter is in 25~50 nanometer range, and internal diameter is in 5~10 nanometer range, and wall thickness is in 10~20 nanometer range.High resolution transmission electron microscopy is observed and is shown that dispersing Nano carbon tubes, chestnut shape carbon nanotube aggregate, carbon nanotube ball have very regular greying laminate structure.
The Raman spectrum experimental result shows dispersing Nano carbon tubes, chestnut shape carbon nanotube aggregate, the well-regulated six ashlar ink structures of carbon nanotube ball, and the part surface defect structure is arranged simultaneously.These special six ashlar ink structures and surface imperfection structures have specific absorption peak in Raman spectrum, interrelate with the specific atom and the vibration modes of aggregated structure thereof.These special six ashlar ink structures and surface imperfection structures have great importance, and may be applied in multiple material and the device.
Compare with the method in past, the present invention has adopted brand-new catalyzer original position to prepare new concept and new technology, has synthesized dispersing Nano carbon tubes, chestnut shape carbon nanotube aggregate, carbon nanotube ball.Used active catalytic dosage is lower than general method, and the productive rate of graphitized carbon nano tubular construction has improved 10~20 times.In the method for the invention, the inertia of polymkeric substance, inorganic fillings, catalyst precursor, promotor, reaction atmosphere all plays an important role with active, acid.By optimizing these controlled variable, can obtain high yield and high-quality carbon nanotube, chestnut shape carbon nanotube aggregate, carbon nanotube ball.Carbon nanotube, chestnut shape carbon nanotube aggregate, carbon nanotube ball output can reach 45~80%.This output is that the add-on with polymkeric substance is that benchmark calculates.
The inventive method adopts the in-situ preparing new concept of nanocatalyst, and original position has been synthesized highly active nanocatalyst, and has further prepared high-performance dispersion multi-walled carbon nano-tubes, chestnut shape carbon nanotube aggregate, carbon nanotube ball.Adopt multiple physico-chemical process that these products have been carried out the series of tables research of seeking peace.The present invention can be used for continuously, extensive, high quality synthesized high-performance disperses multi-walled carbon nano-tubes, chestnut shape carbon nanotube aggregate, carbon nanotube ball.
In a word, the present invention relates to the novel method of one one step, in-situ preparing carbon nanotube, chestnut shape carbon nanotube aggregate, carbon nanotube ball.The present invention utilizes no longer in advance that synthetic has the nanocatalyst of complex construction, but has proposed the new concept of original position synthetic catalyst, and synthesizes highly active carbon nano-tube catalyst by in-situ synthesis.On this basis, the present invention has successfully synthesized carbon nanotube, chestnut shape carbon nanotube aggregate, carbon nanotube ball.The present invention has the productive rate height, is easy to the characteristics of synthetic in a large number and industrialization, and synthetic carbon nanotube, chestnut shape carbon nanotube aggregate, carbon nanotube ball have high-quality characteristics.The present invention can prepare carbon nanotube, chestnut shape carbon nanotube aggregate, carbon nanotube ball in a large number, at low cost.High-performance conversion, catalyzer, energy field and the susceptible device susceptor etc. that can be widely used in material preparation, environment protection, waste treatment, material.
Description of drawings
Fig. 1. the X-ray powder diffraction pattern of the embodiment of the invention 1.
The scanning electron microscope image of Fig. 2 a, b, the c. embodiment of the invention 2.
Fig. 3 a, b, the c. embodiment of the invention 3 images of transmissive electron microscope.
Fig. 4. the Raman spectrum of the embodiment of the invention 4.
Embodiment
Embodiment 1
Cobaltous diacetate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With the Cobaltous diacetate (2 gram) of accurate weighing, polyethylene (34 gram), clay (4 gram) and iron carbonate (0.2 gram) add in the sweet refining machine, in 180 ℃ of following blend 20 minutes, discharging.After the cooling, mixture 20 grams are put in the porcelain crucible, put into then retort furnace 1100 ℃ down heating take out after 60 minutes, the size that obtains the multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually is at 2~11 microns product.Hydrofluoric acid dips centrifugation after 12 hours with 10%.After cleaning 3 times with distilled water, be put in the nitric acid of 1 mol and refluxed 48 hours.By centrifugation, cleaning, drying, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and carbon nanotube ball is at 2~11 microns product.Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOEL JEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Embodiment 2
Cobaltous formate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With the cobaltous formate (4 gram) of accurate weighing, polyisoprene (60 gram), silicon-dioxide (10 gram) and lead silicate (0.1 gram) mix.Mixture 22 grams are put in the porcelain crucible, put into retort furnace then 800 ℃ of heating taking-ups after 80 minutes down.The size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually is at 2~11 microns product (seeing Fig. 2 a and b).Hydrofluoric acid dips centrifugation after 20 hours with 10%.After cleaning 3 times with distilled water, be put in the nitric acid of 1 mol and refluxed 48 hours.By centrifugation, cleaning, drying, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and carbon nanotube ball is at 2~11 microns product (seeing Fig. 2 c).Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOEL JEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Embodiment 3
Nickel formate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With the nickel formate of accurate weighing (2 gram), polypropylene (34 gram) and polynite (4 restrain) in Banbury mixer in 170 ℃ of following blend 7 minutes, discharging.Take out about an about fritter 2 gram and be put in the porcelain crucible, put into then retort furnace 900 ℃ down heating take out after 5 minutes.The size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually is at 2~11 microns product.Hydrofluoric acid dips centrifugation after 24 hours with 20%.After cleaning 3 times with distilled water, be put in the nitric acid of 3 mol and refluxed 24 hours.Through centrifugation, cleaning, drying, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and carbon nanotube ball 2~11 microns product (Fig. 3 a, b, c).Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOEL JEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Embodiment 4
Nickel formate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With 4.625 gram starch of accurate weighing, 0.25 gram polynite, 0.125 gram nickel formate ultra-sonic dispersion in 50 ml waters.Stir down, be heated to 90 ℃ to gelation takes place.Be incubated 10 minutes, take out and put into mould of plastics, room temperature was placed 15 hours, and lyophilize is 15 hours then, and room temperature is melted.With acetone displacement moisture wherein, 40 ℃ of vacuum-dryings, standby.Under nitrogen, in 800 ℃ of carbonizations 120 minutes, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually was at 2~11 microns product.Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOELJEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Embodiment 5
Nickel formate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With 4.625 gram starch of accurate weighing, 0.25 gram polynite, 0.125 gram nickel formate ultra-sonic dispersion in 50 ml waters.Stir down, be heated to 90 ℃ to gelation takes place.Be incubated 10 minutes, take out and put into mould of plastics, room temperature was placed 15 hours, and lyophilize is 15 hours then, and room temperature is melted.With acetone displacement moisture wherein, 40 ℃ of vacuum-dryings, standby.In retort furnace, in 600 ℃ of carbonizations 120 minutes, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually was at 2~11 microns product.Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOELJEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Embodiment 6
Nickel formate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With 4.625 gram starch of accurate weighing, 0.25 gram kaolin, 0.125 gram nickel formate ultra-sonic dispersion in 50 ml waters.Stir down, be heated to 90 ℃ to gelation takes place.Be incubated 10 minutes, take out and put into mould of plastics, room temperature was placed 15 hours, and lyophilize is 15 hours then, and room temperature is melted.With acetone displacement moisture wherein, 40 ℃ of vacuum-dryings, standby.Under nitrogen, in 800 ℃ of carbonizations 120 minutes, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually was at 2~11 microns product.Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOELJEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Embodiment 7
Nickel formate is 30~600 ℃ in temperature carries out pre-treatment, to slough volatile constituent wherein.
With 4.625 gram starch of accurate weighing, 0.25 gram kaolin, 0.125 gram nickel formate ultra-sonic dispersion in 50 ml waters.Stir down, be heated to 90 ℃ to gelation takes place.Be incubated 10 minutes, take out and put into mould of plastics, room temperature was placed 15 hours, and lyophilize is 15 hours then, and room temperature is melted.With acetone displacement moisture wherein, 40 ℃ of vacuum-dryings, standby.In retort furnace, in 600 ℃ of carbonizations 120 minutes, the size that obtains multi-walled carbon nano-tubes that diameter is 25~50 nanometers and twined the chestnut shape carbon nanotube aggregate that constitutes with mineral filler by multi-walled carbon nano-tubes mutually was at 2~11 microns product.Products obtained therefrom is analysed general powder diffractometer X-2 and is recorded powder diffraction pattern with general, and the pattern difference in each stage relatively.The product of gained is observed surface topography and overall structure with the field emission scanning electron microscope Hitachi S-4300 of Hitachi, and compares the pattern difference in each stage.The product of gained is observed its internal structure and atom phase structure with NEC transmission electron microscope JOELJEM-2010.Products obtained therefrom JY-HR800 studied with laser Raman spectrum carbonization structure, the wavelength of excitation laser is arranged on 532 nanometers.
Claims (8)
1. the preparation method of a multi-walled carbon nano-tubes, chestnut shape carbon nanotube aggregate and carbon nanotube ball is characterized in that: this method may further comprise the steps:
(1) catalyst precursor is carried out heat pre-treatment, to slough volatile constituent wherein;
(2). the catalyst precursor and the promotor of organic filler, mineral filler, pretreated step (1) are mixed, and in blending equipment, under 20~500 ℃ of temperature, carry out mixingly, each component is further mixed; Environment controlled atmosphere is inert atmosphere, air atmosphere, vacuum atmosphere or mixed-gas atmosphere;
Catalyst precursor is 0.1~80wt% in the described mixture, and promotor is 0~10wt%, and mineral filler is 1~90wt%, and organic filler is 1~95wt%;
(3). after the pretreated catalyst precursor of step (1) being put into 100~1500 ℃ High Temperature Furnaces Heating Apparatus reaction, from High Temperature Furnaces Heating Apparatus, take out, allow it be cooled to room temperature, obtain multi-walled carbon nano-tubes and twine the chestnut shape carbon nanotube aggregate that constitutes with mineral filler mutually by multi-walled carbon nano-tubes;
Described catalyst precursor is selected from a kind of in water miscible zinc acetate, strontium acetate, neutralized verdigris, iron acetate, Cobaltous diacetate, nickel acetate, zinc formate, strontium formate, Tubercuprose, ironic formiate, cobaltous formate, nickel formate, zinc nitrate, strontium nitrate, cupric nitrate, iron nitrate, Xiao Suangu, the nickelous nitrate, or selects wherein 2~5 kinds to mix and use;
Described promotor is selected from a kind of in zinc carbonate, copper carbonate, iron carbonate, strontium oxalate, caoxalate, sodium oxalate, water glass, pure aluminium silicate, the lead silicate;
Described mineral filler is selected from a kind of in silicon-dioxide, titanium dioxide, lime carbonate, yellow soda ash, kaolin, clay, modified clay, mica, white mica, phlogopite, zinc oxide, the cupric oxide;
Described organic filler is selected from a kind of than in Lip river alkane ketone, Mierocrystalline cellulose, starch, wood pulp, polyacrylamide, the polyvinyl acetate (PVA) of polymethylmethacrylate, polystyrene, polyethylene, Resins, epoxy, polypropylene, polybutene, polyisoprene, polyethylene.
2. method according to claim 1, it is characterized in that: multi-walled carbon nano-tubes and chestnut shape carbon nanotube aggregate are put into inorganic acid solution handle, remove mineral filler,, obtain multi-walled carbon nano-tubes and carbon nanotube ball by centrifugation, cleaning, drying.
3. method according to claim 1 is characterized in that: the diameter of described multi-walled carbon nano-tubes is 25~50 nanometers, and chestnut shape carbon nanotube aggregate size is at 2~11 microns.
4. method according to claim 2 is characterized in that: the diameter of described multi-walled carbon nano-tubes is 25~50 nanometers, and carbon nanotube ball size is at 2~11 microns.
5. method according to claim 1 is characterized in that: described catalyst precursor pretreatment temperature is 30~600 ℃.
6. method according to claim 1 is characterized in that: the rare gas element of described inert atmosphere is a kind of in helium, nitrogen or the argon gas; Described mixed-gas atmosphere is selected from a kind of in helium/nitrogen, argon gas/nitrogen, the argon/helium.
7. method according to claim 2 is characterized in that: described mineral acid is selected from a kind of in nitric acid, hydrofluoric acid, sulfuric acid, hydrochloric acid, perchloric acid, the silicic acid.
8. method according to claim 1 is characterized in that: in the product generative process, obtained the catalyzer of catalyzed carbon nanotube growth by the reaction in-situ preparing of catalyst precursor.