CN100404617C - Wall insulation material made of gel powder polyphenyl granul - Google Patents
Wall insulation material made of gel powder polyphenyl granul Download PDFInfo
- Publication number
- CN100404617C CN100404617C CNB2006100460087A CN200610046008A CN100404617C CN 100404617 C CN100404617 C CN 100404617C CN B2006100460087 A CNB2006100460087 A CN B2006100460087A CN 200610046008 A CN200610046008 A CN 200610046008A CN 100404617 C CN100404617 C CN 100404617C
- Authority
- CN
- China
- Prior art keywords
- present
- wall bodies
- powder polyphenyl
- granul
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a glue powder polyphenyl granule heat-insulating material for wall bodies, which solves the problem of the low adhesion of the present glue powder polyphenyl granule heat-insulating material for wall bodies. The present invention is composed of raw materials with weight ratios of 1 to 6% of redispersable glue powders, 1 to 6% of cellulose ether, 10 to 13% of polyphenyl granules, 50 to 60% of cement, 0.2 to 1.5% of water repellents, 8 to 20% of fly ash, 3.5 to 10% of calcium hydroxide, 1 to 3% of plasticizing agents, 0.5 to 1% of water-retaining agents and 1.5 to 3% of thickening reagents. The present invention has large adhesion, can be plastered by more than 5cm once during construction, does not need secondary thickness plastering construction, and can satisfy the regulations of national standards to the wall bodies to the normal wall bodies of the northeast. The construction efficiency can be increased and the cost can be reduced by adopting the heat-insulating material.
Description
Technical field
The invention belongs to the composition of macromolecular compound, particularly is the wall heat insulation material of main component with the granular polystyrene.
Background technology
Buildings is incubated, often adopts styrofoam etc.,, influence heat insulation effect owing between the solid plate seam is arranged.And the glue powder polyphenyl granule insulating material that uses is at present compared with styrofoam, has high insulating effect, easy construction, advantages such as low price.In order to make the energy-conservation national standard that reaches more than 50% of body of wall, for the normal body of wall in China the Northeast, thermal conductivity according to present glue powder polyphenyl particle wall heat insulation material calculates, the thickness of thermal insulation layer should be for more than the 5cm, and existing glue powder polyphenyl particle wall heat insulation material is owing to reasons such as its material selected for use and prescriptions, bonding force is poor, once smears 4cm at most, just comes off easily if surpass this numerical value.As CN02144859.0＜＜the glue powder polyphenyl granule exterior wall heat preserving material as described in.In order to reach the thickness of regulation, can only take to smear two times way.Under normal weather condition, smear the first pass thermal insulation layer after, need could to carry out thickening second time on its surface in 24 hours at least and construct, this just brings difficulty to construction, has prolonged the activity duration, has increased construction cost.
Summary of the invention
The objective of the invention is to solve low, the little problem of thickness of constructing once of existing glue powder polyphenyl particle wall heat insulation material bonding force, for this reason, propose following technical scheme.
A kind of wall insulation material made of gel powder polyphenyl granul, it is made up of following raw materials by weight percent:
Re-dispersible glue powder 1------6%, ether of cellulose 1------6%, granular polystyrene 10----13%, cement 50----60%, hydrophober .2----1.5%, flyash 8-----20%, calcium hydroxide 3.5----10%, fluidizer 1------3%, water-holding agent 0.5---1%, thickening material the 1.5----3% copolymerization of ethene----vinyl acetate between to for plastic or that form based on the homopolymer of vinyl acetate between to for plastic, tertiary ethylene carbonate and acrylate monomer, multipolymer and terpolymer.
Above-mentioned re-dispersible glue powder be meant China that national of the United States's starch chemistry company limited sets up in Shanghai sell the re-dispersible glue powder (EVA) of ethene----the vinyl acetate between to for plastic copolymerization that the said firm that general headquarters sell produces, as ELOTEX10211, FX2350, or based on homopolymer, multipolymer and the terpolymer of vinyl acetate between to for plastic, tertiary ethylene carbonate and acrylate monomer.Ether of cellulose can be a Vltra tears, as HPMC.Granular polystyrene can be pulverized by waste polystyrene foam and form, hydrophober can be the silylation powder, and as Elotex SEAL80, fluidizer can be a polyvinyl alcohol, water-holding agent can be Natvosol, as HEC, thickening material can be starch ethers, as ELOSET5410.
The production method of this wall insulation material made of gel powder polyphenyl granul is according to said ratio, the block thing of the polystyrene of specified amount (10---13%) is ground into granular, is packaged into bag, all the other materials (87---90%) are dropped into mixing in the powder stirrer, the rubber powder material, other dresses up bag.When using at the construction field (site), pour earlier the water of regulation ratio in the concrete mixer into, the back adds the rubber powder material and stirs into the thin pulp shape, pour granular polystyrene again into and stir into paste, just can directly smear on the wall, once can smear the above thickness of 5cm, must not carry out secondary and smear thick construction, promptly meet design requirement, the saving of labor, save time, save money.If the circulation, operation can reach more than the 8cm repeatedly.Because the re-dispersible glue powder that this wall insulation material made of gel powder polyphenyl granul adopts national of the United States's starch chemistry company limited to produce, and developed new prescription, improved the adhesiveproperties of lagging material greatly, can realize once smearing more than the thick 5cm, can not come off, not produce the hollowing phenomenon.Adopt this lagging material can improve operating efficiency, reduce cost.
Embodiment
Embodiment
| The sequence number material content | 1 | 2 | 3 | 4 | 5 | 6 |
| Re-dispersible glue powder | 5 | 2 | 4 | 6 | 3 | 1 |
| Ether of cellulose | 2 | 5 | 3 | 1 | 4 | 6 |
| Granular polystyrene | 10 | 12 | 12 | 13 | 12 | 11 |
| Cement | 60 | 52 | 56 | 50 | 55 | 58 |
| Hydrophober | 0.5 | 1.0 | 0.5 | 1.5 | 1.0 | 0.2 |
| Flyash | 10 | 17 | 12 | 20 | 15 | 8 |
| Calcium hydroxide | 8 | 5 | 7 | 3.5 | 5 | 10 |
| Fluidizer | 2.5 | 3.5 | 2 | 3 | 2 | 1 |
| Water-holding agent | 0.5 | 1.0 | 1.5 | 1.0 | 1.0 | 1.8 |
| Thickening material | 1.5 | 1.5 | 2 | 1.0 | 2 | 3 |
Each component content is weight percentage in the last table.
Claims (1)
1. wall insulation material made of gel powder polyphenyl granul, it is made up of following raw materials by weight percent:
Re-dispersible glue powder 1------6%, the ether of cellulose 1------6%, granular polystyrene 10----13%, cement 50----60%, hydrophober 0.2----1.5%, flyash 8-----20%, calcium hydroxide 3.5----10%, fluidizer 1------3%, water-holding agent 0.5---1%, the thickening material 1.5----3% that form based on the homopolymer of vinyl acetate between to for plastic, tertiary ethylene carbonate and acrylate monomer, multipolymer and terpolymer.