CN100369996C - Colored road surface spray coating material and production method thereof - Google Patents
Colored road surface spray coating material and production method thereof Download PDFInfo
- Publication number
- CN100369996C CN100369996C CNB2006100456274A CN200610045627A CN100369996C CN 100369996 C CN100369996 C CN 100369996C CN B2006100456274 A CNB2006100456274 A CN B2006100456274A CN 200610045627 A CN200610045627 A CN 200610045627A CN 100369996 C CN100369996 C CN 100369996C
- Authority
- CN
- China
- Prior art keywords
- coating material
- road surface
- colored
- bitumen
- colorized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a colorized road surface spraying coating material used in the engineering of traffic roads and bridges and a production method thereof. The spray coating material comprises light-colored bitumen, emulsifier, modifier, tackifier, water, titanium white powder and pigment. The light-colored bitumen is heated to 130 DEG C to 160 DEG C; simultaneously, the emulsifier, the modifier, and the water heated to 60 DEG C to 80 DEG C are proportionally mixed into emulsion water solution; then, the emulsion water solution and light-colored bitumen are proportionally emulsified by an emulsion machine for making polymer modification light-colored rubber latex; the emulsifier is added and stirred for making polymer modification light-colored emulsion; the pigment and a slide resistant agent are added according to color requirements for fully stirring; thereby, colorized bitumen spraying coating material is made. The production technology of the present invention has the advantages of reasonableness, strong sticking performance with a lower bearing layer, good sliding resistance, short solidification time, wear resistance and good high temperature stability, the spraying coating material can be used as a sealing layer on a colorized road surface and can also be used as a colorized sealing layer through being directly sprayed on a dark road surface; thereby, the cost for laying colorized bitumen road surfaces is reduced. The present invention is widely used in the engineering, such as traffic road and bridge surfaces, amusement parks, squares, etc.
Description
Technical field
The present invention relates to the material of making bridge circuit face in a kind of traffic road and bridge engineering, particularly a kind of colored road surface spray coating material and production method.
Background technology
At present, it is fine and happy that the appearance of colored road surface has brought for people's life, but owing to the pollution to the city of climate change, sand and dust, factor such as artificial, and it is initial gorgeous and honorable that colored road surface has been lost.Dust from level to level, a piece spot becomes dimness to beautiful originally road surface.Look laying of roadway material mainly is that color asphalt and corresponding color aggregate are formed, and its expensive raw material price has limited applying of they.Introducing some colored road surface processing according to the data that can retrieve all is that color oil is brushed, and it is not wear-resisting easily to fade.How to address the above problem, colored road surface spray coating material is the new problem of current urgency scientific research to be solved for this reason.
Summary of the invention
The purpose of this invention is to provide a kind of colored road surface spray coating material and production method, improve viewing and admiring and utility function of colored road surface, reduce colored road surface making expense.
The objective of the invention is to be achieved through the following technical solutions: the composition and the part by weight of product are as follows:
Albino bitumen 60-65,
Emulsifying agent 2-3,
Properties-correcting agent 2-4,
Tackifier 0.5-1,
Water 35-40,
Titanium dioxide 30-45,
Pigment 8-10.
Preparation technology of the present invention is: will split the fast water that coagulates emulsifying agent, properties-correcting agent and heating 60-80 ℃ earlier slowly and make aqueous emulsion by stirring in the above-mentioned part by weight input jar, heat 130-160 ℃ albino bitumen while and evenly enter into above-mentioned part by weight then and manufacture jar by mulser, make polymer modification light color latex, add tackifier more by weight proportion and stir and make polymer modification light color emulsion.Add pigment by weight proportion and titanium dioxide fully stirs, make the color asphalt spray material.
To be pitch be sprayed at the road surface with very little particles dispersed formed low viscosity, milk sap that can satisfy different construction requirements in water to emulsified bitumen of the present invention.Have good associativity and high-temperature stability with sub-layer behind the emulsion breaking.Additive, tackiness agent are mixed and are mixed with polymer modification light color latex, reduce the emulsion adsorptive power, increase toughness simultaneously.
The present invention compared with prior art has following advantage: the prescription and the preparation technology of employing are scientific and reasonable, strong with the sub-layer adhesivity, anti-skid is good, set time is short, wear-resisting, high-temperature stability good, can on colored road surface, do seal and can be sprayed directly on dark-coloured pavement again and be colored seal, thereby reduce the expense on making color asphalt road surface.
Embodiment
The composition and the part by weight of product are as follows: albino bitumen 60-65, emulsifying agent adopt and split fast emulsifying agent (Jiangyin, Jiangsu seven-star are built the production and sales of the agent company limited) 2-3 of coagulating, properties-correcting agent employing styrene-butadiene-styrene block copolymer (SBS) or styrene-butadiene rubber(SBR) (SBR) 2-4, tackifier employing rosin or terpine resin 0.5-1, water 35-40, titanium dioxide 30-45, pigment 8-10 slowly.
To split the fast water that coagulates emulsifying agent, properties-correcting agent and heating 60-80 ℃ earlier slowly and make aqueous emulsion by stirring in the above-mentioned part by weight input jar, heat 130-160 ℃ albino bitumen while and evenly enter into above-mentioned part by weight then and manufacture jar by mulser, make polymer modification light color latex, add tackifier more by weight proportion and stir and make polymer modification light color emulsion.Add pigment by weight proportion and titanium dioxide fully stirs, make the color asphalt spray material.
The present invention is widely used in the engineerings such as traffic road and bridge surface layer, recreation ground, square.
Claims (2)
1. colored road surface spray coating material is characterized in that the composition of product and part by weight are as follows:
Albino bitumen 60-65,
Emulsifying agent 2-3,
Properties-correcting agent 2-4,
Tackifier 0.5-1,
Water 35-40,
Titanium dioxide 30-45,
Pigment 8-10.
2. production method of colored road surface spray coating material according to claim 1, it is characterized in that: will split the fast emulsifying agent that coagulates earlier slowly, the water that properties-correcting agent and heating are 60-80 ℃ is made aqueous emulsion by stirring in the above-mentioned part by weight input jar, heat 130-160 ℃ albino bitumen while and evenly enter into above-mentioned part by weight then and manufacture jar by mulser, make polymer modification light color latex, adding tackifier more by weight proportion stirs and makes polymer modification light color emulsion, add pigment by weight proportion and titanium dioxide fully stirs, make the color asphalt spray material.